ASTM B606-2002 Standard Specification for High-Strength Zinc-Coated (Galvanized) Steel Core Wire for Aluminum and Aluminum-Alloy Conductors Steel Reinforced《钢芯铝和铝合金导线用高强度镀锌(电镀)钢芯线的.pdf

《ASTM B606-2002 Standard Specification for High-Strength Zinc-Coated (Galvanized) Steel Core Wire for Aluminum and Aluminum-Alloy Conductors Steel Reinforced《钢芯铝和铝合金导线用高强度镀锌(电镀)钢芯线的.pdf》由会员分享，可在线阅读，更多相关《ASTM B606-2002 Standard Specification for High-Strength Zinc-Coated (Galvanized) Steel Core Wire for Aluminum and Aluminum-Alloy Conductors Steel Reinforced《钢芯铝和铝合金导线用高强度镀锌(电镀)钢芯线的.pdf（4页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: B 606 02Standard Specification forHigh-Strength Zinc-Coated (Galvanized) Steel Core Wire forAluminum and Aluminum-Alloy Conductors, SteelReinforced1This standard is issued under the fixed designation B 606; the number immediately following the designation indicates the year oforiginal a

2、doption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon (e) indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification covers round, high-strength, zinc-coated (galvani

3、zed), steel core wire with Class A zinc coatingused for mechanical reinforcement in the manufacture ofspecial aluminum and aluminum-alloy conductors, steel rein-forced.1.2 This specification covers wire of diameter from 0.0500to 0.1900 in. inclusive.1.3 The values stated in inch-pound units or SI un

4、its are tobe regarded separately as standard. The values in each systemare not exact equivalents; therefore, each system shall be usedindependently of the other. Combining values from the twosystems may result in nonconformance with this specification.2. Referenced Documents2.1 The following documen

5、ts of the issue in effect on dateof material purchase form a part of this specification to theextent referenced herein.2.2 ASTM Standards:A 90/A 90M Test Method for Weight Mass of Coating onIron and Steel Articles with Zinc or Zinc-Alloy Coatings2A 370 Test Methods and Definitions for Mechanical Tes

6、tingof Steel Products3A 751 Test Methods, Practices, and Terminology forChemical Analysis of Steel Products3B 6 Specification for Zinc4B 193 Test Method for Resistivity of Electrical ConductorMaterials53. Terminology3.1 Definitions:3.1.1 lotunless otherwise specified in the contract ororder, a lot s

7、hall consist of all coils of wire of the samediameter and unit lengths submitted for inspection at the sametime.4. Ordering Information4.1 Orders for material under this specification shall includethe following information:4.1.1 Quantity of each size,4.1.2 Wire diameter in inches (Section 13),4.1.3

8、Certification, if required (Section 18),4.1.4 Test report, if required (Section 18), and4.1.5 Package size (Section 19).5. Materials and Manufacture5.1 The base metal shall be steel produced by the open-hearth, electric-furnace, or basic-oxygen process.5.2 The wire shall be cold drawn and coated wit

9、h zinc toproduce the desired properties.5.3 The slab zinc used for coating shall be high grade orbetter, conforming to Specification B 6.6. Chemical Composition6.1 The steel shall conform to the requirements prescribedin Table 1.TABLE 1 Chemical RequirementsElement Composition, %Carbon 0.50 to 0.88M

10、anganese 0.50 to 1.30Phosphorus, max 0.035Sulfur, max 0.045Silicon 0.10 to 0.356.2 Chemical analysis shall be conducted in accordancewith Test Methods, Practices, and Terminology A 751.1This specification is under the jurisdiction of ASTM Committee B01 onElectrical Conductors and is the direct respo

11、nsibility of Subcommittee B01.05 onConductors of Ferrous Metals.Current edition approved Oct. 10, 2002. Published October 2002. Originallypublished as B 606 75. Last previous edition B 606 98.2Annual Book of ASTM Standards, Vol 01.06.3Annual Book of ASTM Standards, Vol 01.03.4Annual Book of ASTM Sta

12、ndards, Vol 02.04.5Annual Book of ASTM Standards, Vol 02.03.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.7. Tensile Test7.1 The zinc-coated steel core wire shall conform to thetensile and elongation requirements prescribed in Tabl

13、e 2.7.2 Tensile tests shall be conducted in accordance with TestMethods and Definitions A 370, using the initial settings fordetermining stress at 1 % extension given in Table 3 of thisspecification.7.3 Test Specimens The test specimens shall be free ofbends or kinks other than the curvature resulti

14、ng from the usualcoiling operations. Any hand straightening necessary to permitinsertion of the specimen in the jaws of the testing machineshall be performed by drawing between wood blocks or bysome other equally satisfactory means.8. Wrap Test8.1 The material, as represented by the test specimens,

15、shallnot fracture when the galvanized wire is wrapped at a rate notexceeding 15 turns/min in a close helix of at least eight turnsaround a cylindrical mandrel with a diameter equal to threetimes the specified diameter of the wire under test, 6 5%.9. Coating Test9.1 The zinc-coated wire shall conform

16、 to the coatingrequirements prescribed in Table 4.TABLE 4 Zinc CoatingSpecified Diameter of Coated WireArea Density of ZincCoating, min of UncoatedWire Surfacein. mm oz/ft2g/m20.0500 to 0.0599 incl 1.270 to 1.521 incl 0.60 1830.0600 to 0.0749 incl 1.524 to 1.902 incl 0.65 1980.0750 to 0.0899 incl 1.

17、905 to 2.283 incl 0.70 2140.0900 to 0.1039 incl 2.286 to 2.639 incl 0.75 2290.1040 to 0.1199 incl 2.642 to 3.045 incl 0.80 2440.1200 to 0.1399 incl 3.048 to 3.553 incl 0.85 2590.1400 to 0.1799 incl 3.556 to 4.569 incl 0.90 2740.1800 to 0.1900 incl 4.572 to 4.823 incl 1.00 3059.2 The coating test sha

18、ll be conducted in accordance withTest Method A 90/A 90M.10. Adherence of Coating Test10.1 The zinc-coated wire shall be capable of beingwrapped in a close helix at a rate not exceeding 15 turns/minaround a cylindrical mandrel having a diameter as prescribed inTable 5, without cracking or flaking th

19、e zinc coating to such anextent that any zinc can be removed by rubbing with the barefingers.TABLE 5 Mandrel Size for Adherence TestSpecified Wire DiameterRatio ofMandrelDiameter toWire Diameterin. mm0.0500 to 0.0899, incl 1.270 to 2.283, incl 30.0900 to 0.1399, incl 2.286 to 3.553, incl 40.1400 to

20、0.1900, incl 3.556 to 4.823, incl 5NOTE 1Loosening or detachment during the adhesion test of super-ficial, small particles of zinc formed by mechanical polishing of thesurface of the zinc-coated wire shall not be considered cause for rejection.11. Joints11.1 No joints shall be made in the finished w

21、ire.11.2 Joints may be made at any stage of processing prior tofinal cold drawing, by the electric butt-weld or flash-weldingprocess.11.3 Welding equipment and procedure shall be such that itcan be demonstrated that the ultimate tensile strength of afinished wire specimen containing the welded secti

22、on shall benot less than 96 % of the specified minimum stress at 1 %extension.11.4 A welded section shall not be required to meet thestress at 1 % extension, and wrap tests.12. Density and Resistivity12.1 For the purpose of calculating mass per unit length,cross sections, and so forth, the density o

23、f galvanized steel wireat 20C shall be taken as 0.281 lb/in.3(7780 kg/m3).12.2 A maximum resistivity of galvanized steel wire is notguaranteed but a typical value of 0.19157 Vmm2/m may beused for calculating purposes. For conversion to other units ofconductivity or resistivity, refer to Test Method

24、B 193.13. Dimensions and Permissible Variations13.1 The specified diameter of the zinc-coated wire shall beexpressed in decimal fractions of an inch to four decimalplaces, or in millimetres to three decimal places.TABLE 2 Tensile RequirementsSpecified Diameter Stress at 1 % Extension, min Ultimate T

25、ensile Strength, min Elongation in 10 in. or250 mm, min %in. mm ksi MPa ksi MPa0.0500 to 0.0899, incl 1.270 to 2.283, incl 210 1450 235 1620 3.00.0900 to 0.1199, incl 2.286 to 3.045, incl 205 1410 230 1590 3.00.1200 to 0.1399, incl 3.048 to 3.553, incl 200 1380 225 1550 3.50.1400 to 0.1900, incl 3.5

26、56 to 4.823, incl 195 1340 220 1520 3.5TABLE 3 Initial Settings for Determining Stress at 1 % ExtensionSpecified Diameter Initial Stress Initial Setting of Extensometerin. mm ksi MPa in./in. or mm/mm0.0500 to 0.0899, incl 1.270 to 2.283, incl 14 97 0.0005 (0.05 % extension)0.0900 to 0.1199, incl 2.2

27、86 to 3.045, incl 28 193 0.0010 (0.10 % extension)0.1200 to 0.1900, incl 3.048 to 4.832, incl 42 290 0.0015 (0.15 % extension)B60602213.2 For diameter measurements and diameter tolerance,specified diameters shall be rounded to the closest 0.0005 in.(0.01 mm).13.3 The average of the largest and small

28、est diameterreadings, each to the nearest 0.001 in. (0.025 mm) taken at thesame cross section, shall not differ from the specified diameterby more than the tolerances shown in Table 6.14. Workmanship, Finish, and Appearance14.1 The zinc coating shall be reasonably smooth, continu-ous, of reasonably

29、uniform thickness, and free of imperfectionsnot consistent with good commercial practice.15. Number of Tests and Retests15.1 One test specimen shall be taken from each 5000 lb(2500 kg) or fraction thereof in the inspection lot.15.2 Each specimen shall be tested for compliance withSections 7, 8, 10,

30、and 13. At least half of the specimens shallbe tested for compliance with Section 9.15.3 Should one or more of the test specimens fail any ofthe tests specified, the nonconforming coil or coils may beremoved and the balance of the lot subjected to retests. Forretest purposes, two additional coils fo

31、r each 5000 lbs (2500kg) in the lot shall be sampled and tested for the property inwhich the original sample failed to comply.15.4 Should any of the retest specimens fail to meet theproperties specified, the lot represented by the test specimensshall be rejected.15.5 Instead of rejecting the entire

32、lot as provided in 15.4,the producer may test specimens from every coil in the lot forthe property in which failure occurred and reject only thenonconforming coils.16. Inspection16.1 Unless otherwise specified in the contract or purchaseorder, the manufacturer shall be responsible for the perfor-man

33、ce of all inspection and test requirements specified.16.2 All inspections and tests shall be made at the place ofmanufacture unless otherwise especially agreed upon betweenthe manufacturer and the purchaser at the time of the purchase.16.3 The manufacturer shall afford the inspector represent-ing th

34、e purchaser all reasonable manufacturers facilities tosatisfy him that the material is being furnished in accordancewith this specification.17. Rejection and Rehearing17.1 Material that fails to conform to the requirements ofthis specification shall be rejected. Rejection should be re-ported to the

35、producer or supplier promptly and in writing. Incase of dissatisfaction with the results of the test, the produceror supplier may make claim for a rehearing.18. Certification18.1 When specified in the purchase order or contract, aproducers or suppliers certification shall be furnished to thepurchase

36、r showing that the material was manufactured,sampled, tested and inspected in accordance with this specifi-cation and has been found to meet the requirements. Whenspecified in the purchase order or contract, a report of the testresults shall be furnished.19. Packaging and Package Marking19.1 The uni

37、t lengths shall be as specified in the contract ororder. Length tolerances shall be 62 % unless otherwisespecified by the purchaser.19.2 Package dimensions, kind of package (coils, reels, orreelless coils), and quantity of wire in each package shall beagreed upon between the manufacturer and the pur

38、chaser.19.3 A durable tag shall be securely attached to eachpackage showing the nominal wire diameter, length, approxi-mate weight, purchasers order number, and manufacturersname.19.4 The starting end shall be identified.19.5 In case there is more than one piece in a package, thelength and position

39、of each piece shall be shown on the tag.20. Keywords20.1 coated steel wire; high strength steel wire; steel corewire; steel wire; zinc-coated steel wireTABLE 6 Permissible Variations in Diameter of Zinc-Coated Steel WireNOTE 1It is recognized that the surface of zinc coatings, particularly those pro

40、duced by the hot-dip method of coating, are not perfectly smooth anddevoid of irregularities. If the tolerances shown in the table are rigidly applied to such irregularities that are inherent to the product, unjustified rejectionsof wire that would actually be satisfactory for use could occur. It is

41、 intended that these tolerances be used in gaging the wires where there is a minimumof such diameter irregularities due to galvanizing.Specified Diameter Permissible Variationin. mmin. mmPlus Minus Plus Minus0.0500 to 0.0749, incl 1.270 to 1.902, incl 0.0015 0.001 0.038 0.0250.0750 to 0.1199, incl 1

42、.905 to 3.045, incl 0.002 0.002 0.051 0.0510.1200 to 0.1399, incl 3.048 to 3.553, incl 0.003 0.002 0.076 0.0510.1400 to 0.1900, incl 3.556 to 4.823, incl 0.004 0.003 0.102 0.076B606023ASTM International takes no position respecting the validity of any patent rights asserted in connection with any it

43、em mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical com

44、mittee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a

45、meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Driv

46、e, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org).B606024