ASTM B606 B606M-2008(2016) Standard Specification for High-Strength Zinc-Coated (Galvanized) Steel Core Wire for Aluminum and Aluminum-Alloy Conductors Steel Reinforced《铝和铝合金导体和钢筋用.pdf

《ASTM B606 B606M-2008(2016) Standard Specification for High-Strength Zinc-Coated (Galvanized) Steel Core Wire for Aluminum and Aluminum-Alloy Conductors Steel Reinforced《铝和铝合金导体和钢筋用.pdf》由会员分享，可在线阅读，更多相关《ASTM B606 B606M-2008(2016) Standard Specification for High-Strength Zinc-Coated (Galvanized) Steel Core Wire for Aluminum and Aluminum-Alloy Conductors Steel Reinforced《铝和铝合金导体和钢筋用.pdf（4页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: B606/B606M 08 (Reapproved 2016)Standard Specification forHigh-Strength Zinc-Coated (Galvanized) Steel Core Wire forAluminum and Aluminum-Alloy Conductors, SteelReinforced1This standard is issued under the fixed designation B606/B606M; the number immediately following the designation ind

2、icates the yearof original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.A superscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification covers round, high-str

3、ength, zinc-coated (galvanized), steel core wire with Class A zinc coating(GA3) for use in overhead electrical conductors.1.2 This specification covers wire of diameter from 0.0500to 0.1900 in. inclusive or 1.27 to 4.82 mm inclusive.1.3 The values stated in either SI units or inch-pound unitsare to

4、be regarded separately as standard. The values stated ineach system may not be exact equivalents; therefore, eachsystem shall be used independently of the other. Combiningvalues from the two systems may result in non-conformancewith the standard.2. Referenced Documents2.1 The following documents of

5、the issue in effect on dateof material purchase form a part of this specification to theextent referenced herein.2.2 ASTM Standards:2A90/A90M Test Method for Weight Mass of Coating onIron and Steel Articles with Zinc or Zinc-Alloy CoatingsA370 Test Methods and Definitions for Mechanical Testingof St

6、eel ProductsA751 Test Methods, Practices, and Terminology for Chemi-cal Analysis of Steel ProductsB6 Specification for ZincB193 Test Method for Resistivity of Electrical ConductorMaterialsE29 Practice for Using Significant Digits in Test Data toDetermine Conformance with Specifications3. Terminology

7、3.1 Definitions:3.1.1 lotunless otherwise specified in the contract ororder, a lot shall consist of all coils of wire of the samediameter and unit lengths submitted for inspection at the sametime.3.1.2 Product CodeDefines product coating type, coatingclass and strength grade. This specification cove

8、rs only HighStrength Class A Zinc Coated products and identified asproduct code GA3.4. Ordering Information4.1 Orders for material under this specification shall includethe following information:4.1.1 Quantity of each size,4.1.2 Wire diameter in inches or millimeters (Section 13),4.1.3 Certification

9、, if required (Section 18),4.1.4 Test report, if required (Section 18), and4.1.5 Package size (Section 19).4.1.6 Order Example: Five multiple lengths of 12 000 ft.each, 0.1327 in. GA3 wire, packaged onto wooden non-returnable reels, with certified test report.4.1.7 Product Code (see paragraph 3.1.2)

10、.5. Materials and Manufacture5.1 The base metal shall be steel produced by the open-hearth, electric-furnace, or basic-oxygen process.5.2 The wire shall be cold drawn and coated with zinc toproduce the desired properties.5.3 The slab zinc used for coating shall be high grade orbetter, conforming to

11、Specification B6.6. Chemical Composition6.1 The steel shall conform to the requirements prescribedin Table 1.6.2 Chemical analysis shall be conducted in accordancewith Test Methods, Practices, and Terminology A751.1This specification is under the jurisdiction of ASTM Committee B01 onElectrical Condu

12、ctors and is the direct responsibility of Subcommittee B01.05 onConductors of Ferrous Metals.Current edition approved Oct. 1, 2016. Published October 2016. Originallyapproved in 1975. Last previous edition approved in 2008 as B606/B606M 081.DOI: 10.1520/B0606_B0606M-08R16.2For referenced ASTM standa

13、rds, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA

14、19428-2959. United States17. Tensile Test7.1 The zinc-coated steel core wire shall conform to thetensile and elongation requirements prescribed in Table 2 orTable 3.7.2 Tensile tests shall be conducted in accordance with TestMethods and Definitions A370, using the initial settings fordetermining str

15、ess at 1 % extension given in Table 4 or Table5 of this specification.7.3 Test SpecimensThe test specimens shall be free ofbends or kinks other than the curvature resulting from the usualcoiling operations. Any hand straightening necessary to permitinsertion of the specimen in the jaws of the testin

16、g machineshall be performed by drawing between wood blocks or bysome other equally satisfactory means.8. Wrap Test8.1 The material, as represented by the test specimens, shallnot fracture when the galvanized wire is wrapped at a rate notexceeding 15 turns/min in a close helix of at least eight turns

17、around a cylindrical mandrel with a diameter equal to threetimes the specified diameter of the wire under test, 65%.9. Coating Test9.1 The zinc-coated wire shall conform to the coatingrequirements prescribed in Table 6 or Table 7.9.2 The coating test shall be conducted in accordance withTest Method

18、A90/A90M.10. Adherence of Coating Test10.1 The zinc-coated wire shall be capable of beingwrapped in a close helix at a rate not exceeding 15 turns/minaround a cylindrical mandrel having a diameter as prescribed inTable 8 or Table 9, without cracking or flaking the zinc coatingto such an extent that

19、any zinc can be removed by rubbing withthe bare fingers.NOTE 1Loosening or detachment during the adhesion test ofsuperficial, small particles of zinc formed by mechanical polishing of thesurface of the coated wire shall not be considered cause for rejection.11. Joints11.1 No joints shall be made in

20、the finished wire.11.2 Joints may be made at any stage of processing prior tofinal cold drawing, by the electric butt-weld or flash-weldingprocess.11.3 Welding equipment and procedure shall be such that itcan be demonstrated that the ultimate tensile strength of afinished wire specimen containing th

21、e welded section shall benot less than 96 % of the specified minimum stress at 1 %extension.11.4 A welded section shall not be required to meet thestress at 1 % extension, elongation, and wrap tests.12. Density and Resistivity12.1 For the purpose of calculating mass per unit length,cross sections, a

22、nd so forth, the density of galvanized steel wireat 20C shall be taken as 0.281 lb/in.37780 kg/m3.12.2 A maximum resistivity of galvanized steel wire is notguaranteed but a typical value of 0.19157 mm2/m may beused for calculating purposes. For conversion to other units ofconductivity or resistivity

23、, refer to Test Method B193.13. Dimensions and Permissible Variations13.1 The specified diameter of the zinc-coated wire shall beexpressed in decimal fractions of an inch to four decimalplaces, or in millimeters to two decimal places.13.2 To determine the applicable tolerance range from Table10 or T

24、able 11, round the specified diameter to the nearest0.001 in. 0.01 mm, in accordance with the rounding methodof Practice E29.13.3 Measure the largest and smallest diameter taken at thesame cross section rounded to the nearest 0.001 in. 0.01 mmin accordance with the rounding method of Practice E29.Ca

25、lculate the average of the two measurements. The calculatedvalue shall not differ from the specified diameter by more thanthe applicable tolerance range shown in Table 10 or Table 11.14. Workmanship, Finish, and Appearance14.1 The zinc coating shall be reasonably smooth,continuous, of reasonably uni

26、form thickness, and free ofimperfections not consistent with good commercial practice.15. Number of Tests and Retests15.1 One test specimen shall be taken from each 5000 lb2500 kg or fraction thereof in the inspection lot.15.2 Each specimen shall be tested for compliance withSections 7, 8, 10, and 1

27、3. At least half of the specimens shallbe tested for compliance with Section 9.15.3 Should one or more of the test specimens fail any ofthe tests specified, the nonconforming coil or coils may beTABLE 1 Chemical RequirementsElement Composition, %Carbon 0.50 to 0.88Manganese 0.50 to 1.30Phosphorus, m

28、ax 0.035Sulfur, max 0.045Silicon 0.10 to 0.35TABLE 2 Tensile RequirementsSpecified Diameter Stress at 1 % Extension, min Ultimate Tensile Strength, min Elongation in 10 in.,min %in. kpsi kpsi0.0500 to 0.0899, incl 210 235 3.00.0900 to 0.1199, incl 205 230 3.00.1200 to 0.1399, incl 200 225 3.50.1400

29、to 0.1900, incl 195 220 3.5B606/B606M 08 (2016)2removed and the balance of the lot subjected to retests. Forretest purposes, two additional coils for each 5000 lbs 2500kg in the lot shall be sampled and tested for the property inwhich the original sample failed to comply.15.4 Should any of the retes

30、t specimens fail to meet theproperties specified, the lot represented by the test specimensshall be rejected.15.5 Instead of rejecting the entire lot as provided in 15.4,the producer may test specimens from every coil in the lot forthe property in which failure occurred and reject only thenonconform

31、ing coils.16. Inspection16.1 Unless otherwise specified in the contract or purchaseorder, the manufacturer shall be responsible for the perfor-mance of all inspection and test requirements specified.16.2 All inspections and tests shall be made at the place ofmanufacture unless otherwise especially a

32、greed upon betweenthe manufacturer and the purchaser at the time of the purchase.16.3 The manufacturer shall afford the inspector represent-ing the purchaser all reasonable manufacturers facilities tosatisfy him that the material is being furnished in accordancewith this specification.TABLE 3 Tensil

33、e Requirements MetricSpecified Diameter Stress at 1 % Extension, min Ultimate Tensile Strength, min Elongation in 250 mm,min %mm MPa MPa1.27 to 2.28, incl 1450 1620 3.02.29 to 3.04, incl 1410 1590 3.03.05 to 3.55, incl 1380 1550 3.53.56 to 4.82, incl 1340 1520 3.5TABLE 4 Initial Settings for Determi

34、ning Stress at 1 % ExtensionSpecified Diameter Initial StressInitial Settingof Extensometerin. kpsi in./in.0.0500 to 0.0899, incl 15 0.0005(0.05 %extension)0.0900 to 0.1199, incl 30 0.0010(0.10 %extension)0.1200 to 0.1900, incl 46 0.0015(0.15 %extension)TABLE 5 Initial Settings for Determining Stres

35、s at 1 % ExtensionMetricSpecified Diameter Initial StressInitial Setting ofExtensometermm MPa mm/mm1.27 to 2.28, incl 110 0.0005 (0.05 %extension)2.29 to 3.04, incl 210 0.0010 (0.10 %extension)3.05 to 4.82, incl 320 0.0015 (0.15 %extension)TABLE 6 Zinc CoatingSpecified Diameter of Coated Wire, in.Ar

36、ea Density of Coating, min,of Uncoated Wire Surface, oz/ft2Class A0.0500 to 0.0599, incl 0.600.0600 to 0.0749, incl 0.650.0750 to 0.0899, incl 0.700.0900 to 0.1039, incl 0.750.1040 to 0.1199, incl 0.800.1200 to 0.1399, incl 0.850.1400 to 0.1799, incl 0.900.1800 to 0.1900, incl 1.00TABLE 7 Zinc Coati

37、ng MetricSpecified Diameter of Coated WireArea Density of Coating,min, of Uncoated WireSurface, g/m2mm Class A1.27 to 1.52, incl 1831.53 to 1.90, incl 1981.91 to 2.28, incl 2142.29 to 2.64, incl 2292.65 to 3.04, incl 2443.05 to 3.55, incl 2593.56 to 4.57, incl 2744.58 to 4.82, incl 305TABLE 8 Mandre

38、l Size for Adherence TestSpecified Wire DiameterRatio ofMandrelDiameter toWire Diameterin.0.0500 to 0.0899, incl 30.0900 to 0.1399, incl 40.1400 to 0.1900, incl 5TABLE 9 Mandrel Size for Adherence Test MetricSpecified Wire DiameterRatio ofMandrelDiameter toWire Diametermm1.27 to 2.28, incl 32.29 to

39、3.04, incl 43.05 to 4.82, incl 5B606/B606M 08 (2016)317. Rejection and Rehearing17.1 Material that fails to conform to the requirements ofthis specification shall be rejected. Rejection should be re-ported to the producer or supplier promptly and in writing. Incase of dissatisfaction with the result

40、s of the test, the produceror supplier may make claim for a rehearing.18. Certification18.1 When specified in the purchase order or contract, aproducers or suppliers certification shall be furnished to thepurchaser showing that the material was manufactured,sampled, tested and inspected in accordanc

41、e with this specifi-cation and has been found to meet the requirements. Whenspecified in the purchase order or contract, a report of the testresults shall be furnished.19. Packaging and Package Marking19.1 The unit lengths shall be as specified in the contract ororder. Length tolerances shall be 62

42、% unless otherwisespecified by the purchaser (See Explanatory Note 1).19.2 Package dimensions, kind of package (coils, reels, orreelless coils), and quantity of wire in each package shall beagreed upon between the manufacturer and the purchaser.19.3 A durable tag shall be securely attached to eachpa

43、ckage showing the nominal wire diameter, length, approxi-mate weight, purchasers order number, and manufacturersname.19.4 The starting end shall be identified.19.5 In case there is more than one piece in a package, thelength and position of each piece shall be shown on the tag.20. Keywords20.1 coate

44、d steel wire; high strength steel wire; steel corewire; steel wire; zinc-coated steel wireEXPLANATORY NOTESNOTE 1Steel wire cannot be produced to exact specified lengths.Since welding of steel wires for use in electrical conductors is notaccepted, the random lengths of wire that result from normal p

45、roductioncan result in otherwise good product being rejected and scrapped. In orderto reduce cost, the purchaser and manufacturer should, at the time ofpurchase, have an agreed upon method to permit the acceptance of oddlengths of steel wire.Atypical agreement would be to permit lengths otherthan th

46、e specified length for up to 5 % of the purchased quantity with anysingle piece being not less than 50 % of the specified length.ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard ar

47、e expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not

48、revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which yo

49、u may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Per