ASTM A515 A515M-2017 Standard Specification for Pressure Vessel Plates Carbon Steel for Intermediate- and Higher-Temperature Service《中温和高温服务用碳钢压力容器板的标准规格》.pdf

《ASTM A515 A515M-2017 Standard Specification for Pressure Vessel Plates Carbon Steel for Intermediate- and Higher-Temperature Service《中温和高温服务用碳钢压力容器板的标准规格》.pdf》由会员分享，可在线阅读，更多相关《ASTM A515 A515M-2017 Standard Specification for Pressure Vessel Plates Carbon Steel for Intermediate- and Higher-Temperature Service《中温和高温服务用碳钢压力容器板的标准规格》.pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: A515/A515M 17Standard Specification forPressure Vessel Plates, Carbon Steel, for Intermediate- andHigher-Temperature Service1This standard is issued under the fixed designation A515/A515M; the number immediately following the designation indicates the yearof original adoption or, in the

2、 case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.A superscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the U.S. Department of Defense.1. Scope*1.1

3、This specification2covers carbon-silicon steel platesprimarily for intermediate- and higher-temperature service inwelded boilers and other pressure vessels.1.2 Plates under this specification are available in threegrades having different strength levels as follows:Grade U.S. SI Tensile Strength, ksi

4、 MPa60 415 6080 41555065 450 6585 45058570 485 7090 4856201.3 The maximum thickness of plates is limited only by thecapacity of the composition to meet the specified mechanicalproperty requirements.1.4 For plates produced from coil and furnished withoutheat treatment or with stress relieving only, t

5、he additionalrequirements, including additional testing requirements and thereporting of additional test results, of Specification A20/A20Mapply.1.5 The values stated in either inch-pound units or SI unitsare to be regarded separately as standard. Within the text, theSI units are shown in brackets.

6、The values stated in eachsystem are not exact equivalents; therefore, each system mustbe used independently of the other. Combining values from thetwo systems may result in nonconformance with the specifi-cation.1.6 This international standard was developed in accor-dance with internationally recogn

7、ized principles on standard-ization established in the Decision on Principles for theDevelopment of International Standards, Guides and Recom-mendations issued by the World Trade Organization TechnicalBarriers to Trade (TBT) Committee.2. Referenced Documents2.1 ASTM Standards:3A20/A20M Specification

8、 for General Requirements for SteelPlates for Pressure VesselsA435/A435M Specification for Straight-Beam UltrasonicExamination of Steel PlatesA577/A577M Specification for Ultrasonic Angle-Beam Ex-amination of Steel PlatesA578/A578M Specification for Straight-Beam UltrasonicExamination of Rolled Stee

9、l Plates for Special Applica-tions3. General Requirements and Ordering Information3.1 Plates supplied to this product specification shall con-form to Specification A20/A20M. These requirements outlinethe testing and retesting methods and procedures, permissiblevariations in dimensions and mass, qual

10、ity and repair ofdefects, marking, loading, and ordering information.3.2 In addition to the basic requirements of thisspecification, certain supplementary requirements are availablewhere additional control, testing, or examination is required tomeet end use requirements. The purchaser is referred to

11、 thelisted supplementary requirements in this specification and tothe detailed requirements in Specification A20/A20M.3.3 If the requirements of this specification are in conflictwith the requirements of Specification A20/A20M, the require-ments of this specification shall prevail.3.4 Coils are excl

12、uded from qualification to this specifica-tion until they are processed into finished plates. Platesproduced from coil means plates that have been cut toindividual lengths from coil. The processor directly controls, oris responsible for, the operations involved in the processing ofcoils into finishe

13、d plates. Such operations include decoiling,leveling, cutting to length, testing, inspection, conditioning,heat treatment (if applicable), packaging, marking, loading forshipment, and certification.1This specification is under the jurisdiction of ASTM Committee A01 on Steel,Stainless Steel and Relat

14、ed Alloys and is the direct responsibility of SubcommitteeA01.11 on Steel Plates for Boilers and Pressure Vessels.Current edition approved Nov. 1, 2017. Published November 2017. Originallyapproved in 1964. Last previous edition approved in 2015 as A515/A515M 10(2015). DOI: 10.1520/A0515_A0515M-17.2F

15、or ASME Boiler and Pressure Vessel Code applications, see related Specifi-cation SA-515/SA-515M in Section II of that Code.3For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, re

16、fer to the standards Document Summary page onthe ASTM website.*A Summary of Changes section appears at the end of this standardCopyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United StatesThis international standard was developed in accordance with

17、 internationally recognized principles on standardization established in the Decision on Principles for theDevelopment of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.1NOTE 1For plates produced from coil and fu

18、rnished without heattreatment or with stress relieving only, three test results are reported foreach qualifying coil. Additional requirements regarding plate producedfrom coil are described in Specification A20/A20M.4. Materials and Manufacture4.1 Steelmaking PracticeThe steel shall be killed andmad

19、e to a coarse austenitic grain size practice.5. Heat Treatment5.1 Plates 2 in. 50 mm and under in thickness are normallysupplied in the as-rolled condition. The plates may be orderednormalized or stress relieved, or both.5.2 Plates over 2 in. 50 mm in thickness shall be normal-ized.6. Chemical Compo

20、sition6.1 The steel shall conform to the chemical requirementsgiven in Table 1 unless otherwise modified in accordance withSupplementary Requirement S17, Vacuum Carbon-DeoxidizedSteel, in Specification A20/A20M.7. Mechanical Properties7.1 Tension TestThe plates, as represented by the tensiontest spe

21、cimens, shall conform to the requirements given inTable 2.8. Keywords8.1 carbon steel; carbon steel plate; pressure containingparts; pressure vessel steels; steel plates for pressure vesselsTABLE 1 Chemical RequirementsElementsComposition, %Grade 60 Grade 415 Grade 65 Grade 450 Grade 70 Grade 485Car

22、bon, max:A, B1 in. 25 mm and under 0.24 0.28 0.31Over 1 to 2 in. 25 to 50 mm, incl 0.27 0.31 0.33Over 2 to 4 in. 50 to 100 mm, incl 0.29 0.33 0.35Over 4 to 8 in. 100 to 200 mm, incl 0.31 0.33 0.35Over 8 in. 200 mm 0.31 0.33 0.35Manganese,Bmax:Heat analysis 0.90 0.90 1.20Product analysis 0.98 0.98 1.

23、30Phosphorus, maxA0.025 0.025 0.025Sulfur, maxA0.025 0.025 0.025Silicon:Heat analysis 0.150.40 0.150.40 0.150.40Product analysis 0.130.45 0.130.45 0.130.45AApplies to both heat and product analyses.BFor each reduction of 0.01 percentage point below the specified maximum for carbon, an increase of 0.

24、06 percentage point above the specified maximum for manganeseis permitted, up to a maximum of 1.50 % by heat analysis and 1.60 % by product analysis.TABLE 2 Tensile RequirementsGrade60 415 65 450 70 485Tensile strength, ksi MPa 6080 415550 6585 450585 7090 485620Yield strength, min, ksi MPa 32 220 3

25、5 240 38 260Elongation in 8 in. 200 mm, min, %A21 19 17Elongation in 2 in. 50 mm, min, %A25 23 21ASee Specification A20/A20M for elongation adjustment.A515/A515M 172SUPPLEMENTARY REQUIREMENTSSupplementary requirements shall not apply unless specified in the purchase order.A list of standardized supp

26、lementary requirements for use at the option of the purchaser is includedin Specification A20/A20M. Those that are considered suitable for use with this specification are listedbelow by title.S1. Vacuum Treatment,S2. Product Analysis,S3. Simulated Post-Weld Heat Treatment of MechanicalTest Coupons,S

27、4.1 Additional Tension Test,S5. Charpy V-Notch Impact Test,S6. Drop-Weight Test (for Material 0.625 in. 16 mm andover in Thickness),S7. High-Temperature Tension Test,S8. Ultrasonic Examination in accordance with Specifica-tion A435/A435M,S9. Magnetic Particle Examination,S11. Ultrasonic Examination

28、in accordance with Specifica-tion A577/A577M,S12. Ultrasonic Examination in accordance with Specifica-tion A578/A578M, andS17. Vacuum Carbon-Deoxidized Steel.ADDITIONAL SUPPLEMENTARY REQUIREMENTSAlso listed below is an additional optional supplementary requirement suitable for this specification:S61

29、. Austenitic Grain SizeS61.1 The material shall have a carburized austenitic grainsize of 1 to 5.SUMMARY OF CHANGESCommittee A01 has identified the location of selected changes to this standard since the last issue(A515/A515M 10 (2015) that may impact the use of this standard. (Approved Nov. 1, 2017

30、.)(1) Revised 1.3 to remove thickness guidelines. (2) Added Section 8, Keywords.ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the val

31、idity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your com

32、ments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have

33、 not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple

34、copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the Copyright Clearance Center, 222Rosewood Drive, Danvers, MA 01923, Tel: (978) 646-2600; http:/ 173