《ASTM A479 A479M-2018 Standard Specification for Stainless Steel Bars and Shapes for Use in Boilers and Other Pressure Vessels《锅炉和其他压力容器用不锈钢棒材和型材的标准规格》.pdf》由会员分享，可在线阅读，更多相关《ASTM A479 A479M-2018 Standard Specification for Stainless Steel Bars and Shapes for Use in Boilers and Other Pressure Vessels《锅炉和其他压力容器用不锈钢棒材和型材的标准规格》.pdf（12页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: A479/A479M 17A479/A479M 18 Used in USDOE-NE StandardsStandard Specification forStainless Steel Bars and Shapes for Use in Boilers andOther Pressure Vessels1This standard is issued under the fixed designation A479/A479M; the number immediately following the designation indicates the year

2、of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.A superscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the U.S. Depa

3、rtment of Defense.1. Scope*1.1 This specification2 covers hot- and cold-finished bars of stainless steel, including rounds, squares, and hexagons, andhot-rolled or extruded shapes such as angles, tees, and channels for use in boiler and pressure vessel construction.2NOTE 1There are standards coverin

4、g high nickel, chromium, austenitic corrosion, and heat-resisting alloy materials. These standards are under thejurisdiction of ASTM Subcommittee B02.07 and may be found in Annual Book of ASTM Standards, Vol 02.04.1.2 The values stated in either SI units or inch-pound units are to be regarded separa

5、tely as standard. The values stated in eachsystem may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from thetwo systems may result in non-conformance with the standard.1.3 Unless the order specifies the applicable “M” specification design

6、ation, the material shall be furnished to the inch-poundunits.1.4 This international standard was developed in accordance with internationally recognized principles on standardizationestablished in the Decision on Principles for the Development of International Standards, Guides and Recommendations

7、issuedby the World Trade Organization Technical Barriers to Trade (TBT) Committee.2. Referenced Documents2.1 ASTM Standards:3A262 Practices for Detecting Susceptibility to Intergranular Attack in Austenitic Stainless SteelsA370 Test Methods and Definitions for Mechanical Testing of Steel ProductsA48

8、4/A484M Specification for General Requirements for Stainless Steel Bars, Billets, and ForgingsA751 Test Methods, Practices, and Terminology for Chemical Analysis of Steel ProductsE112 Test Methods for Determining Average Grain SizeE527 Practice for Numbering Metals and Alloys in the Unified Numberin

9、g System (UNS)2.2 SAE Document:4SAE J 1086 Recommended Practice for Numbering Metals and Alloys3. General Requirements3.1 The following requirements for orders for material furnished under this specification shall conform to the applicablerequirements of the current edition of Specification A484/A48

10、4M.3.1.1 Definitions,3.1.2 General requirements for delivery,3.1.3 Ordering information,3.1.4 Process,3.1.5 Special tests,1 This specification is under the jurisdiction ofASTM Committee A01 on Steel, Stainless Steel and RelatedAlloysand is the direct responsibility of Subcommittee A01.17on Flat-Roll

11、ed and Wrought Stainless Steel.Current edition approved March 15, 2017Jan. 1, 2018. Published March 2017January 2018. Originally approved in 1962. Last previous edition approved in 20162017 asA479/A479M 16a.A479/A479M 17. DOI: 10.1520/A0479_A0479M-17.10.1520/A0479_A0479M-18.2 For ASME Boiler and Pre

12、ssure Vessel Code applications see related Specification SA-479/SA-479M in Section II of that Code.3 For referencedASTM standards, visit theASTM website, www.astm.org, or contactASTM Customer Service at serviceastm.org. For Annual Book of ASTM Standardsvolume information, refer to the standards Docu

13、ment Summary page on the ASTM website.4 Available from Society of Automotive Engineers (SAE), 400 Commonwealth Dr., Warrendale, PA 15096-0001, http:/www.sae.org.This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been

14、made to the previous version. Becauseit may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current versionof the standard as published by ASTM is to be considered the official document.*

15、A Summary of Changes section appears at the end of this standardCopyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States13.1.6 Heat treatment,3.1.7 Dimensions and permissible variations,3.1.8 Workmanship, finish, and appearance,3.1.9 Number of

16、 tests/test methods,3.1.10 Specimen preparation,3.1.11 Retreatment,3.1.12 Inspection,3.1.13 Rejection and rehearing,3.1.14 Material test report,3.1.15 Certification, and3.1.16 Packaging, marking, and loading.4. Other Requirements4.1 In addition to the requirements of this specification, all requirem

17、ents of the current editions of Specification A484/A484Mshall apply. Failure to comply with the general requirements of Specification A484/A484M constitutes nonconformance with thisspecification.5. Chemical Composition5.1 Chemical composition shall be reported to the purchaser, or his representative

18、, and shall conform to the requirementsspecified in Table 1.5.2 When a product analysis is performed or requested by the purchaser, the tolerance limits as described in SpecificationA484/A484M apply unless Supplementary Requirement S3 is invoked.5.3 Methods and practices relating to chemical analysi

19、s required by this specification shall be in accordance with Test Methods,Practices, and Terminology A751.6. Grain Size for Austenitic Grades6.1 All austenitic grades shall be tested for average grain size by Test Methods E112.6.2 The H grades shall conform to an average grain size as follows:6.2.1

20、ASTM No. 6 or coarser for Types 304H, 309H, 310H, and 316H,6.2.2 ASTM No. 7 or coarser for Types 321H, 347H, and 348H.6.3 For S32615, the grain size as determined in accordance with Test Methods E112, comparison method, Plate 11, shall be No.3 or finer.6.4 For N08810 and N08811, the average grain si

21、ze as determined in accordance with Test Methods E112 shall be No. 5 orcoarser.6.5 Supplementary Requirement S1 shall be invoked when nonH grade austenitic stainless steels are ordered for ASME Codeapplications for service above 1000F 540C.7. Mechanical Properties Requirements7.1 The material shall

22、conform to the mechanical property requirements specified in Table 2 for the grade ordered. At least oneroom-temperature test shall be performed by the manufacturer on a sample from at least one bar or shape from each lot of material.7.2 The yield strength shall be determined by the offset (0.2 %) m

23、ethod as prescribed in Test Methods and Definitions A370.7.3 Martensitic material supplied in the annealed condition shall be capable of meeting the hardened and tempered mechanicalproperties when heat treated.7.4 Hardness measurements, when required, shall be made at a location midway between the s

24、urface and the center of the crosssection.7.5 Martensitic grades shall be capable of meeting the hardness requirements after heat treating as specified in Table 3.8. Corrosion Testing8.1 Austenitic stainless steels solution annealed by the alternative method shall be tested and pass the intergranula

25、r corrosiontest requirements described in S2.8. Testing for Intermetallic Compounds8.1 When specified by the purchaser in the purchase order, the manufacturer shall test the austenitic or austenitic-ferritic(duplex) stainless steel material in its final condition in accordance with supplementary tes

26、t requirements S6.A479/A479M 182TABLE 1 Chemical RequirementsUNSDesigna-tionATypeComposition, %BCarbon Man-ganese Phos-phorus Sulfur Silicon Chromium Nickel Nitrogen Molyb-denum Other ElementsCAustenitic GradesN08020 Alloy 20 0.07 2.00 0.045 0.035 1.00 19.021.0 32.038.0 . . . 2.003.00 Cu 3.04.0;Cb 8

27、xC1.00N08020 Alloy 20 0.07 2.00 0.045 0.035 1.00 19.021.0 32.038.0 . . . 2.003.00 Cu 3.04.0;Cb 8xC1.00N08367 . . . 0.030 2.00 0.040 0.030 1.00 20.022.0 23.525.5 0.180.25 6.07.0 Cu 0.75N08367 . . . 0.030 2.00 0.040 0.030 1.00 20.022.0 23.525.5 0.180.25 6.07.0 Cu 0.75N08800 800 0.10 1.50 0.045 0.015 1

28、.00 19.023.0 30.035.0 . . . . . . FeK 39.5 min.Cu 0.75Al 0.150.60Ti 0.150.60N08810 800H 0.050.10 1.50 0.045 0.015 1.00 19.023.0 30.035.0 . . . . . . FeK 39.5 min.Cu 0.75Al 0.150.60Ti 0.150.60N08811 . . . 0.060.10 1.50 0.045 0.015 1.00 19.023.0 30.035.0 . . . . . . FeK 39.5 min.Cu 0.75AlL 0.250.60TiL

29、 0.250.60N08700 . . . 0.040 2.00 0.040 0.030 1.00 19.023.0 24.026.0 . . . 4.35.0 Cu 0.50;Cb 8xC0.40N08700 . . . 0.040 2.00 0.040 0.030 1.00 19.023.0 24.026.0 . . . 4.35.0 Cu 0.50;Cb 8xC0.40N08904 904L 0.020 2.00 0.045 0.035 1.00 19.023.0 23.028.0 0.10 4.05.0 Cu 1.02.0N08904 904L 0.020 2.00 0.045 0.0

30、35 1.00 19.023.0 23.028.0 0.10 4.05.0 Cu 1.02.0N08925 . . . 0.020 1.00 0.045 0.030 0.50 19.021.0 24.026.0 0.100.20 6.07.0 Cu 0.801.50N08926 . . . 0.020 2.00 0.030 0.010 0.50 19.021.0 24.026.0 0.150.25 6.07.0 Cu 0.501.50S20161 . . . 0.15 4.06.0 0.045 0.030 3.04.0 15.018.0 4.06.0 0.080.20 . . . . . .S

31、20161 . . . 0.15 4.06.0 0.045 0.030 3.04.0 15.018.0 4.06.0 0.080.20 . . . . . .S20910 XM-19 0.06 4.06.0 0.045 0.030 1.00 20.523.5 11.513.5 0.200.40 1.503.00 Cb 0.100.30;V 0.100.30S20910 XM-19 0.06 4.06.0 0.045 0.030 1.00 20.523.5 11.513.5 0.200.40 1.503.00 Cb 0.100.30;V 0.100.30S21600 XM-17 0.08 7.5

32、9.0 0.045 0.030 1.00 17.520.5 5.07.0 0.250.50 2.003.00 . . .S21600 XM-17 0.08 7.59.0 0.045 0.030 1.00 17.520.5 5.07.0 0.250.50 2.003.00 . . .S21603 XM-18 0.03 7.59.0 0.045 0.030 1.00 17.520.5 5.07.0 0.250.50 2.003.00 . . .S21603 XM-18 0.03 7.59.0 0.045 0.030 1.00 17.520.5 5.07.0 0.250.50 2.003.00 .

33、. .S21800S21904. . .XM-110.100.047.09.08.010.00.0600.0450.0300.0303.54.51.0016.018.019.021.58.09.05.57.50.080.180.150.40. . . . . .S21800S21904. . .XM-110.100.047.09.08.010.00.0600.0450.0300.0303.54.51.0016.018.019.021.58.09.05.57.50.080.180.150.40. . . . . .S24000 XM-29 0.08 11.514.5 0.060 0.030 1.

34、00 17.019.0 2.33.7 0.200.40 . . . . . .S24000 XM-29 0.08 11.514.5 0.060 0.030 1.00 17.019.0 2.33.7 0.200.40 . . . . . .S30200 302 0.15 2.00 0.045 0.030 1.00 17.019.0 8.010.0 0.10 . . . . . .S30200 302 0.15 2.00 0.045 0.030 1.00 17.019.0 8.010.0 0.10 . . . . . .S30400 304 0.08D 2.00 0.045 0.030 1.00

35、18.020.0 8.010.5 . . . . . . . . .S30400 304 0.08D 2.00 0.045 0.030 1.00 18.020.0 8.010.5 . . . . . . . . .S30403 304L 0.030 2.00 0.045 0.030 1.00 18.020.0 8.012.0 . . . . . . . . .S30403 304L 0.030 2.00 0.045 0.030 1.00 18.020.0 8.012.0 . . . . . . . . .S30409 304H 0.040.10 2.00 0.045 0.030 1.00 18

36、.020.0 8.010.5 . . . . . . . . .S30409 304H 0.040.10 2.00 0.045 0.030 1.00 18.020.0 8.010.5 . . . . . . . . .S30451 304N 0.08 2.00 0.045 0.030 1.00 18.020.0 8.012.0 0.100.16 . . . . . .S30451 304N 0.08 2.00 0.045 0.030 1.00 18.020.0 8.012.0 0.100.16 . . . . . .S30453 304LN 0.030 2.00 0.045 0.030 1.0

37、0 18.020.0 8.011.0 0.100.16 . . . . . .S30453 304LN 0.030 2.00 0.045 0.030 1.00 18.020.0 8.011.0 0.100.16 . . . . . .S30600 . . . 0.018 2.00 0.020 0.020 3.74.3 17.018.5 14.015.5 . . . 0.20 Cu 0.50S30600 . . . 0.018 2.00 0.020 0.020 3.74.3 17.018.5 14.015.5 . . . 0.20 Cu 0.50S30815 . . . 0.050.10 0.8

38、0 0.040 0.030 1.402.00 20.022.0 10.012.0 0.140.20 . . . Ce 0.030.08S30815 . . . 0.050.10 0.80 0.040 0.030 1.402.00 20.022.0 10.012.0 0.140.20 . . . Ce 0.030.08S30908 309S 0.08 2.00 0.045 0.030 1.00 22.024.0 12.015.0 . . . . . . . . .S30908 309S 0.08 2.00 0.045 0.030 1.00 22.024.0 12.015.0 . . . . .

39、. . . .S30909 309H 0.040.10 2.00 0.045 0.030 1.00 22.024.0 12.015.0 . . . . . . . . .S30909 309H 0.040.10 2.00 0.045 0.030 1.00 22.024.0 12.015.0 . . . . . . . . .S30940 309Cb 0.08 2.00 0.045 0.030 1.00 22.024.0 12.016.0 . . . . . . Cb 10C- 1.10S30940 309Cb 0.08 2.00 0.045 0.030 1.00 22.024.0 12.016

40、.0 . . . . . . Cb 10C- 1.10S30880 ER308E 0.08 1.002.50 0.030 0.030 0.250.60 19.522.0 9.011.0 . . . . . . . . .S30880 ER308E 0.08 1.002.50 0.030 0.030 0.250.60 19.522.0 9.011.0 . . . . . . . . .S31008 310S 0.08 2.00 0.045 0.030 1.00 24.026.0 19.022.0 . . . . . . . . .S31008 310S 0.08 2.00 0.045 0.030

41、 1.00 24.026.0 19.022.0 . . . . . . . . .S31009 310H 0.040.10 2.00 0.045 0.030 1.00 24.026.0 19.022.0 . . . . . . . . .S31009 310H 0.040.10 2.00 0.045 0.030 1.00 24.026.0 19.022.0 . . . . . . . . .A479/A479M 183TABLE 1 ContinuedUNSDesigna-tionATypeComposition, %BCarbon Man-ganese Phos-phorus Sulfur

42、Silicon Chromium Nickel Nitrogen Molyb-denum Other ElementsCS31010F . . . 0.030 5.506.50 0.030 0.0010 0.250.75 28.530.5 14.016.0 0.800.90 1.52.5 Al 0.05B 0.005S31040 310Cb 0.08 2.00 0.045 0.030 1.00 24.026.0 19.022.0 . . . . . . Cb 10C-1.10S31040 310Cb 0.08 2.00 0.045 0.030 1.00 24.026.0 19.022.0 .

43、. . . . . Cb 10C-1.10S31050 . . . 0.025 2.00 0.020 0.015 0.4 24.026.0 20.523.5 0.090.15 1.602.60 . . .S31254 . . . 0.020 1.00 0.030 0.010 0.80 19.520.5 17.518.5 0.180.25 6.06.5 Cu 0.501.00S31254 . . . 0.020 1.00 0.030 0.010 0.80 19.520.5 17.518.5 0.180.25 6.06.5 Cu 0.501.00S31266 . . . 0.030 2.004.0

44、0 0.035 0.020 1.00 23.025.0 21.024.0 0.350.60 5.26.2 Cu 1.002.50W 1.502.50S31266 . . . 0.030 2.004.00 0.035 0.020 1.00 23.025.0 21.024.0 0.350.60 5.26.2 Cu 1.002.50W 1.502.50S31600 316 0.08C 2.00 0.045 0.030 1.00 16.018.0 10.014.0 . . . 2.003.00 . . .S31600 316 0.08C 2.00 0.045 0.030 1.00 16.018.0 1

45、0.014.0 . . . 2.003.00 . . .S31603 316L 0.030 2.00 0.045 0.030 1.00 16.018.0 10.014.0 . . . 2.003.00 . . .S31603 316L 0.030 2.00 0.045 0.030 1.00 16.018.0 10.014.0 . . . 2.003.00 . . .S31609 316H 0.040.10 2.00 0.045 0.030 1.00 16.018.0 10.014.0 . . . 2.003.00 . . .S31609 316H 0.040.10 2.00 0.045 0.0

46、30 1.00 16.018.0 10.014.0 . . . 2.003.00 . . .S31635 316Ti 0.08 2.00 0.045 0.030 1.00 16.018.0 10.014.0 0.10 2.003.00 Ti 5(C+N)- 0.70S31635 316Ti 0.08 2.00 0.045 0.030 1.00 16.018.0 10.014.0 0.10 2.003.00 Ti 5(C+N)- 0.70S31640 316Cb 0.08 2.00 0.045 0.030 1.00 16.018.0 10.014.0 0.10 2.003.00 Cb 10C-

47、1.10S31640 316Cb 0.08 2.00 0.045 0.030 1.00 16.018.0 10.014.0 0.10 2.003.00 Cb 10C- 1.10S31651 316N 0.08 2.00 0.045 0.030 1.00 16.018.0 10.014.0 0.100.16 2.003.00 . . .S31651 316N 0.08 2.00 0.045 0.030 1.00 16.018.0 10.014.0 0.100.16 2.003.00 . . .S31653 316LN 0.030 2.00 0.045 0.030 1.00 16.018.0 10

48、.014.0 0.100.16 2.003.00 . . .S31653 316LN 0.030 2.00 0.045 0.030 1.00 16.018.0 10.014.0 0.100.16 2.003.00 . . .S31700 317 0.08 2.00 0.045 0.030 1.00 18.020.0 11.015.0 . . . 3.04.0 . . .S31700 317 0.08 2.00 0.045 0.030 1.00 18.020.0 11.015.0 . . . 3.04.0 . . .S31725 . . . 0.030 2.00 0.045 0.030 1.00 18.020.0 13.517.5 0.20 4.05.0 . . .S31725 . . . 0.030 2.00 0.045 0.030 1.00 18.020.0 13.517.5 0.20 4.05.0 . . .S31726 . . . 0.030 2.00 0.045 0.030 1.00 17.020.0 14.517.5 0.100.20 4.05.0 . . .S31726 . . . 0.030 2.00 0.045 0.030 1.00 17.020.0 14.517.5 0.10