ASTM A1017 A1017M-2007 Standard Specification for Pressure Vessel Plates Alloy Steel Chromium-Molybdenum-Tungsten《铬钼钨合金钢制压力容器板的标准规范》.pdf

《ASTM A1017 A1017M-2007 Standard Specification for Pressure Vessel Plates Alloy Steel Chromium-Molybdenum-Tungsten《铬钼钨合金钢制压力容器板的标准规范》.pdf》由会员分享，可在线阅读，更多相关《ASTM A1017 A1017M-2007 Standard Specification for Pressure Vessel Plates Alloy Steel Chromium-Molybdenum-Tungsten《铬钼钨合金钢制压力容器板的标准规范》.pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: A 1017/A 1017M 07Standard Specification forPressure Vessel Plates, Alloy Steel, Chromium-Molybdenum-Tungsten1This standard is issued under the fixed designation A 1017/A 1017M; the number immediately following the designation indicates theyear of original adoption or, in the case of rev

2、ision, the year of last revision. A number in parentheses indicates the year of lastreapproval. A superscript epsilon (e) indicates an editorial change since the last revision or reapproval.1. Scope*1.1 This specification covers Chromium-Molybdenum-Tungsten alloy steel plates intended primarily for

3、weldedboilers and pressure vessels designed for elevated temperatureservice.1.2 Plates are available under this specification in threegrades having different alloy contents as follows:GradeNominalChromiumContent, %NominalMolybdenumContent, %NominalTungstenContent, %23 2.25 0.20 1.60911 9.00 1.00 1.0

4、0122 12.00 0.40 2.001.3 The maximum thickness of plates is limited only by thecapacity of the composition to meet the specified mechanicalproperty requirements.1.4 The specification is expressed in both inch-pound unitsand in SI units. However, unless the order specifies theapplicable “M” specificat

5、ion designation (SI units), the mate-rial shall be furnished to inch-pound units.1.5 The values stated in either inch-pound units or SI unitsare to be regarded separately as standard. Within the text, theSI units are shown in brackets. The values stated in eachsystem are not exact equivalents; there

6、fore, each system mustbe used independently of the other.2. Referenced Documents2.1 ASTM Standards:2A 20/A 20M Specification for General Requirements forSteel Plates for Pressure VesselsA 435/A 435M Specification for Straight-Beam UltrasonicExamination of Steel PlatesA 577/A 577M Specification for U

7、ltrasonic Angle-BeamExamination of Steel Plates3. General Requirements3.1 Material supplied to this material specification shallconform to Specification A 20/A 20M. Such requirementsoutline the testing and retesting methods and procedures,permissible variations in dimensions and weight mass, qual-it

8、y and repair of defects, marking, loading, and so forth.3.2 Specification A 20/A 20M also establishes the rules forthe ordering information that should be complied with whenpurchasing material to this specification.3.3 In addition to the basic requirements of this specifica-tion, certain supplementa

9、ry requirements are available whenadditional control, testing, or examination is required to meetend use requirements. The purchaser is referred to the listedsupplementary requirements in this specification and to thedetailed requirements in Specification A 20/A 20M.3.4 If the requirements of this s

10、pecification are in conflictwith the requirements of Specification A 20/A 20M, the re-quirements of this specification shall prevail.4. Materials and Manufacture4.1 Steelmaking PracticeThe steel shall be killed.5. Heat Treatment5.1 Except as allowed by 5.2 and 5.3, all plates shall benormalized at 1

11、900 to 1975F 1040 to 1080C. Plates forGrades 23 and 122 shall be tempered at 1350 to 1470F 730to 800C. Grade 911 plates shall be tempered at 1365 to1435F 740 to 780C.5.2 If permitted by the purchaser, plates for Grades 23 and122 may be austenitized at 1900 to 1975F 1040 to 1080C,subjected to acceler

12、ated cooling from the austenitizing tem-perature by air blasting or liquid quenching, and then temperedat 1350 to 1470F 730 to 800C.5.3 Plates ordered without the heat treatment required byeither 5.1 or 5.2 shall be furnished in either the stress-relievedor annealed condition, and the purchaser shal

13、l be responsiblefor the heat treatment of such plates to conform to either 5.1 or5.2.1This specification is under the jurisdiction of ASTM Committee A01 on Steel,Stainless Steel and Related Alloys and is the direct responsibility of SubcommitteeA01.11 on Steel Plates for Boilers and Pressure Vessels

14、.Current edition approved March 1, 2007. Published March 2007. Originallyapproved in 2001. Last previous edition approved in 2006 asA 1017/A 1017M 06.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStand

15、ards volume information, refer to the standards Document Summary page onthe ASTM website.1*A Summary of Changes section appears at the end of this standard.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.6. Chemical Composition6.1 The

16、 steel shall conform to the requirements for chemicalcomposition given in Table 1.7. Mechanical Properties7.1 Tension Test:7.1.1 The material as represented by the tension test speci-mens shall conform to the applicable requirements given inTable 2.7.2 Hardness Test:7.2.1 Grade 23 plates shall have

17、a hardness not exceeding220 HB 97HRB.7.2.2 Grade 122 plates shall have a hardness not exceeding250 HB 25HRC.8. Marking8.1 In addition to the marking required in SpecificationA 20/A 20M, each plate shall be legibly stamped or stenciled,dependent upon the ordered thickness, with the letter “N” fornorm

18、alized and tempered, “Q” for accelerated cooled andtempered, “S” for stress relieved, or “A” for annealed, which-ever is applicable.TABLE 1 Chemical RequirementsNOTEWhere “.”appears in this table there is no requirement.Element Composition %Grade 23 Grade 911 Grade 122CarbonHeat Analysis 0.040.10 0.

19、090.13 0.070.14Product Analysis 0.030.10 0.080.14 0.050.17ManganeseHeat Analysis 0.100.60 0.300.60 0.70 max.Product Analysis 0.090.66 0.250.66 0.77 max.Phosphorus, max.Heat Analysis 0.030 0.020 0.020Product Analysis 0.030 0.025 0.025Sulfur, max.Heat Analysis 0.010 0.010 0.010Product Analysis 0.012 0

20、.012 0.012SiliconHeat Analysis 0.50 max. 0.100.50 0.50 max.Product Analysis 0.50 max. 0.080.56 0.56 max.ChromiumHeat Analysis 1.902.60 8.59.5 10.011.5Product Analysis 1.782.72 8.49.7 9.911.6MolybdenumHeat Analysis 0.050.30 0.901.10 0.250.60Product Analysis 0.040.35 0.851.15 0.200.65Nickel, max.Heat

21、Analysis . . . 0.40 0.50Product Analysis . . . 0.43 0.54VanadiumHeat Analysis 0.200.30 0.180.25 0.150.30Product Analysis 0.180.33 0.160.27 0.130.32ColumbiumHeat Analysis 0.020.08 0.060.10 0.040.10Product Analysis 0.020.10 0.050.11 0.030.11BoronHeat Analysis 0.00050.006 0.00030.006 0.005 max.Product

22、Analysis 0.00040.007 0.00020.007 0.006 max.NitrogenHeat Analysis 0.030 max. 0.040.09 0.040.10Product Analysis 0.030 max. 0.0350.095 0.030.11Aluminum, max.Heat Analysis 0.03A0.02 0.02Product Analysis 0.04A0.02 0.02TungstenHeat Analysis 1.451.75 0.901.10 1.502.50Product Analysis 1.401.80 0.851.15 1.40

23、2.60CopperHeat Analysis . . . . . . 0.301.70Product Analysis . . . . . . 0.201.80Titanium, maxHeat Analysis . . . 0.01 0.01Product Analysis . . . 0.01 0.01Zirconium, maxHeat Analysis . . . 0.01 0.01Product Analysis . . . 0.01 0.01AAcid Soluble AluminumTABLE 2 Tensile RequirementsGrade 23 Grade 911 G

24、rade 122Tensile Strength, ksi MPa 74 to 100510 to 69090 to 120620 to 840 90 620 min.Yield Strength ksi MPa min 58 400 64 440 58 400Elongation in 2 in. % min 20 18 20A 1017/A 1017M 0729. Keywords9.1 alloy steel; alloy steel plate; pressure containing parts;pressure vessel steels; steel plates; steel

25、plates for pressurevesselsSUPPLEMENTARY REQUIREMENTSSupplementary requirements shall not apply unless specified in the order. A list of standardizedsupplementary requirements for use at the option of the purchaser is included in SpecificationA 20/A 20M. Several of those considered suitable for use w

26、ith this specification are listed below bytitle. Other tests may be performed by agreement between the supplier and the purchaser.S1 Vacuum TreatmentS2 Product AnalysisS3 Simulated post-weld heat treatment of mechanical testcouponsS4.1 Additional Tension TestS5 Charpy V-notch impact testS6 Drop Weig

27、ht Test (for Material 0.625 in. 16 mm andOver in Thickness)S7 High-Temperature Tension TestS8 Ultrasonic Examination in accordance with SpecificationA 435/A 435MS9 Magnetic Particle ExaminationS11 Ultrasonic Examination in accordance with Specifica-tion A 577/A 577MS12 Ultrasonic Examination in acco

28、rdance with Specifica-tion A 578/A 578MS17 Vacuum Carbon Deoxidized SteelSUMMARY OF CHANGESCommittee A01 has identified the location of selected changes to this standard since the last issue(A 1017/A 1017M 06) that may impact the use of this standard. (Approved March 1, 2007)(1) Revised chemistry of

29、 grade 122 in Table 1 to reduce Crmaximum.Committee A01 has identified the location of selected changes to this standard since the last issue (A 1017/A 1017M 05) thatmay impact the use of this standard. (Approved March 1, 2006)(1) Revised chemistry of grades 911 and 122 in Table 1.ASTM International

30、 takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their ow

31、n responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be ad

32、dressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, a

33、t the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org).A 1017/A 1017M 073