ASTM A582A582M-12(2017) Standard Specification for Free-Machining Stainless Steel Bars.pdf

《ASTM A582A582M-12(2017) Standard Specification for Free-Machining Stainless Steel Bars.pdf》由会员分享，可在线阅读，更多相关《ASTM A582A582M-12(2017) Standard Specification for Free-Machining Stainless Steel Bars.pdf（4页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: A582/A582M 12 (Reapproved 2017)Standard Specification forFree-Machining Stainless Steel Bars1This standard is issued under the fixed designation A582/A582M; the number immediately following the designation indicates the yearof original adoption or, in the case of revision, the year of l

2、ast revision. A number in parentheses indicates the year of last reapproval.A superscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the U.S. Department of Defense.1. Scope1.1 This specification covers hot-fin

3、ished or cold-finishedbars, except bars for forging (Note 1), suitable for machiningprocesses. It includes rounds, squares, and hexagons in themore commonly used types of stainless free-machining steelsdesigned especially for optimum machinability and for generalcorrosion and high-temperature servic

4、e. Stainless steel barsother than the free-machining types are covered in a separatespecification (Note 2).1.2 This specification is expressed in both inch-pound unitsand in SI units; however, unless the purchase order or contractspecifies the applicable M specification designation (SI units),the in

5、ch-pound units shall apply. The values stated in eitherinch-pound units or SI (metric) units are to be regardedseparately as standard: within the text and tables, the SI unitsare shown in brackets. The values stated in each system maynot be exact equivalents: therefore, each system shall be usedinde

6、pendently of the other. Combining values from the twosystems may result in nonconformance with the specification.NOTE 1For bars for reforging, see Specification A314.NOTE 2For non-free machining stainless bars, see SpecificationA276.2. Referenced Documents2.1 ASTM Standards:2A276 Specification for S

7、tainless Steel Bars and ShapesA314 Specification for Stainless Steel Billets and Bars forForgingA370 Test Methods and Definitions for Mechanical Testingof Steel ProductsA484/A484M Specification for General Requirements forStainless Steel Bars, Billets, and ForgingsA751 Test Methods, Practices, and T

8、erminology for Chemi-cal Analysis of Steel ProductsA959 Guide for Specifying Harmonized Standard GradeCompositions for Wrought Stainless SteelsE527 Practice for Numbering Metals and Alloys in theUnified Numbering System (UNS)2.2 SAE Document:3SAE J 1086 Recommended Practice for Numbering Metalsand A

9、lloys33. Ordering Information3.1 It is the responsibility of the purchaser to specify allrequirements that are necessary for product ordered under thisspecification. Such requirements to be considered include, butare not limited to, the following:3.1.1 Quantity (weight or number of pieces),3.1.2 Typ

10、e (alloy) or UNS designation (Table 1),3.1.3 Form (bars, angles, and so forth),3.1.4 Condition (Table 2),3.1.5 Finish (5.1),3.1.6 Applicable dimensions, including size, thickness,width, and length,3.1.7 Cross section (round, square, and so forth),3.1.8 ASTM designation (Specification A582/A582M) and

11、approval date,3.1.9 Preparation for delivery, and3.1.10 Marking requirements.NOTE 3Atypical ordering description is as follows: 5000 lb 2000 kgType 416 bars, annealed and centerless ground, 112 in. 40 mm round, 10to 12 ft 3 to 4 m in length, ASTM Specification A582/A582Mdated.4. General Requirements

12、4.1 Product furnished to this specification shall conform tothe requirements of Specification A484/A484M, including anysupplementary requirements indicated in the purchase order orcontract. Failure to comply with the general requirements ofSpecification A484/A484M constitutes nonconformance withthis

13、 specification.1This specification is under the jurisdiction of ASTM Committee A01 on Steel,Stainless Steel and Related Alloysand is the direct responsibility of SubcommitteeA01.17 on Flat-Rolled and Wrought Stainless Steel.Current edition approved March 15, 2017. Published March 2017. Originallyapp

14、roved in 1967. Last previous edition approved in 2012 as A582/A582M 121.DOI: 10.1520/A0582_A0582M-12R17.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standard

15、s Document Summary page onthe ASTM website.3Available from Society of Automotive Engineers (SAE), 400 CommonwealthDr., Warrendale, PA 15096-0001.*A Summary of Changes section appears at the end of this standardCopyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19

16、428-2959. United StatesThis international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for theDevelopment of International Standards, Guides and Recommendations issued by the World Trade Organization Tech

17、nical Barriers to Trade (TBT) Committee.15. Materials and Manufacture5.1 Bars may be furnished either hot finished or coldfinished, suitable for machining processes, in one of theconditions listed in Table 2.6. Chemical Requirements6.1 The chemical composition shall conform to the require-ments spec

18、ified in Table 1.6.2 Methods and practices relating to chemical analysisrequired by this specification shall be in accordance with TestMethods, Practices, and Terminology A751.7. Hardness Requirement7.1 The product shall conform to the hardness requirementslisted in Table 3 for Brinell Hardness Numb

19、er (HBW).7.2 At least one hardness test shall be made midwaybetween surface and center on each lot to determine that thematerial conforms to Table 3.7.2.1 Hardness testing shall be performed in accordancewith Test Methods and Definitions A370.7.2.2 For sizes below 1 in. 25 mm cross section, thehardn

20、ess value may be determined by tensile test and conver-sion to hardness in accordance with Test Methods and Defini-tions A370.8. Certification8.1 Certificate of ComplianceWhen specified in the pur-chase order or contract, the producer or supplier shall furnish acertificate of compliance stating that

21、 the product wasmanufactured, sampled, tested, and inspected in accordanceTABLE 1 Chemical RequirementsUNSDesig-nationATypeBChemical Composition, %CarbonCManga-neseCPhos-phorus,CSulfurCSilicon,maxChromium NickelMolyb-denumSeleniumOtherElementsAusteniticS20300 XM-1D0.08 5.06.5 0.04 0.180.35 1.00 16.0

22、018.0 5.06.5 . . . . . . Cu1.752.25S30300 303 0.15 2.00 0.20 0.15min1.00 17.019.0 8.010.0 . . . . . . . . .S30310 XM-5D0.15 2.54.5 0.20 0.25min1.00 17.019.0 7.010.0 . . . . . . . . .S30323 303Se 0.15 2.00 0.20 0.06 1.00 17.019.0 8.010.0 . . . 0.15min.S30345 XM-2D0.15 2.00 0.05 0.110.16 1.00 17.019.0

23、 8.010.0 0.400.60 . . . Al0.601.00MartensiticS41600 416 0.15 1.25 0.06 0.15min1.00 12.014.0 . . . . . . . . . . . .S41610 XM-6D0.15 1.502.50 0.06 0.15min1.00 12.014.0 . . . . . . . . . . . .S41623 416Se 0.15 1.25 0.06 0.06 1.00 12.014.0 . . . . . . 0.15min.S42020 420F 0.300.40 1.25 0.06 0.15min1.00

24、12.014.0 0.50E. . Cu0.60ES42023 420FSe 0.200.40 1.25 0.06 0.06 1.00 12.014.0 0.50E. . . 0.15minCu0.60ES44020 440F 0.951.20 1.25 0.06 0.15min1.00 16.018.0 0.50E. . Cu0.60ES44023 440FSe 0.951.20 1.25 0.06 0.06 1.00 16.018.0 0.50E. . . 0.15minCu0.60EFerriticS18200 XM-34D0.08 2.50 0.04 0.15min1.00 17.51

25、9.5 . . . 1.502.50 . . . . . .S18235 . . . 0.025 0.50 0.030 0.150.35 1.00 17.518.5 1.00 2.002.50 . . . Ti0.301.00N0.025C+N0.035S41603 . . . 0.08 1.25 0.06 0.15min1.00 12.0-14.0. . . .S43020 430F 0.12 1.25 0.06 0.15min1.00 16.018.0 . . . . . . . . . . . .S43023 430FSe 0.12 1.25 0.06 0.06 1.00 16.018.

26、0 . . . . . . 0.15min.ADesignation established in accordance with Practice E527 and SAE J 1086, Recommended Practice for Numbering Metals and Alloys (UNS).BUnless otherwise indicated, a grade designation originally assigned by the American Iron and Steel Institute (AISI).CMaximum unless otherwise no

27、ted.DNaming system originated by ASTM.EAt manufacturers option, reported only when intentionally added.A582/A582M 12 (2017)2with this specification (including year date) and any otherrequirements designated in the purchase order or contract, andhas been found to meet such requirements.8.2 Test Repor

28、tsWhen specified in the purchase order orcontract. A certified report of the test results shall be furnishedat time of shipment. The report shall include the ASTMspecification designation, year date, and revision, if any.9. Keywords9.1 austenitic stainless steel; ferritic stainless steel; free-machi

29、ning stainless steel; martensitic stainless steel; stainlesssteel barsAPPENDIX(Nonmandatory Information)X1. CROSS REFERENCEX1.1 This table is intended to assist the user when Specifi-cation A582/A 582M is referenced in a government procure-ment. It shows the types of steels in Specification A582/A 5

30、82M replacing the steels formerly specified in QQ-S-764B.X1.1 Cross ReferenceUNS DesignationAQQ-S-764BSpecification A582,TypeS20300 203EZ XM-1S30300 303 303S30310 303 Plus X XM-5S30323 303Se 303SeS30345 303Ma XM-2S41600 416 416S41610 416 Plus X XM-6S41623 416Se 416SeS42020 420F 420FS42023 420FSe 420

31、FSeS43020 430F 430FS43023 430FSe 430FSeADesignation established in accordance with Practice E527 and SAE J 1086, Recommended Practice for Numbering Metals and Alloys (UNS).TABLE 2 ConditionType Condition A(Annealed)Condition T(IntermediateTemper)Condition H(Hard Temper)XM-1 A . . .303 A . .XM-5 A .

32、.303Se A . . . . . .XM-2 A . .416 A T HXM-6 A T H416Se A T H420F A . . . . . .420FSe A . . . . . .440F A . . . . . .440FSe A . . . . . .XM-34 A . .S18235 A . . . . . .S41603 A . . . . . .430F A . . . . . .430FSe A . . . . . .TABLE 3 Mechanical Test RequirementsTypes Condition BrinellHardnessA(HBW)Al

33、l (except 440F, 440FSe and S18235) A 262 max416, 416Se, 420FSe, and XM-6 T 248 to 302416, 416Se, and XM-6 H 293 to 352440 F and 440FSe A 285 maxS18235 A 207 maxASizes below approximately 1 in. 25 mm cross section may be tensile tested andconverted to hardness per Test Methods and Definitions A370.A5

34、82/A582M 12 (2017)3ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement

35、of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for

36、 additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known

37、to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM a

38、t the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the Copyright Clearance Center, 222Rosewood Drive, Danvers, MA 01923, Tel: (978) 646-2600; http:/ 12 (2017)4