SAE AMS 4172F-2013 Aluminum Alloy Extrusions 1 0Mg - 0 60Si - 0 28Cu - 0 20Cr (6061-T4511 or T4510) Solution Heat Treated and Stress Relieved by Stretching (UNS A96061)《1 0Mg 0 60S.pdf

《SAE AMS 4172F-2013 Aluminum Alloy Extrusions 1 0Mg - 0 60Si - 0 28Cu - 0 20Cr (6061-T4511 or T4510) Solution Heat Treated and Stress Relieved by Stretching (UNS A96061)《1 0Mg 0 60S.pdf》由会员分享，可在线阅读，更多相关《SAE AMS 4172F-2013 Aluminum Alloy Extrusions 1 0Mg - 0 60Si - 0 28Cu - 0 20Cr (6061-T4511 or T4510) Solution Heat Treated and Stress Relieved by Stretching (UNS A96061)《1 0Mg 0 60S.pdf（6页珍藏版）》请在麦多课文档分享上搜索。

1、_SAE Technical Standards Board Rules provide that: “This report is published by SAE to advance the state of technical and engineering sciences. The use of this report is entirely voluntary, and its applicability and suitability for any particular use, including any patent infringement arising theref

2、rom, is the sole responsibility of the user.”SAE reviews each technical report at least every five years at which time it may be reaffirmed, revised, or cancelled. SAE invites your written comments and suggestions.Copyright 2013 SAE InternationalAll rights reserved. No part of this publication may b

3、e reproduced, stored in a retrieval system or transmitted, in any form or by any means, electronic, mechanical, photocopying,recording, or otherwise, without the prior written permission of SAE.TO PLACE A DOCUMENT ORDER: Tel: 877-606-7323 (inside USA and Canada)Tel: +1 724-776-4970 (outside USA)Fax:

4、 724-776-0790Email: CustomerServicesae.orgSAE WEB ADDRESS: http:/www.sae.orgSAE values your input. To provide feedbackon this Technical Report, please visithttp:/www.sae.org/technical/standards/AMS4172FAEROSPACEMATERIALSPECIFICATIONAMS4172 REV. FIssued 1969-11Reaffirmed 2010-10Revised 2013-04Superse

5、ding AMS4172EAluminum Alloy, Extrusions1.0Mg - 0.60Si - 0.28Cu - 0.20Cr (6061-T4511 or T4510)Solution Heat Treated and Stress Relieved by Stretching(Composition similar to UNS A96061)RATIONALEAMS4172F has been revised to add provisions for billet types for tubing (1.1.1), provisions for T4510 temper

6、 material (3.2.2), provisions for press solution heat treatment (3.2.3), and revises Sampling and Testing (4.3.1) and Reports (4.4). 1. SCOPE1.1 FormThis specification covers an aluminum alloy in the form of extruded bars, rods, wire, profiles, and tubing.1.1.1 TubingTubing shall be additionally cla

7、ssified a follows:Type DescriptionI - Seamless tubing extruded from hollow billets using die and mandrelII - Tubing extruded from solid billets using porthole or spider die or similar toolingWhen no Type is specified, Type I shall apply.1.2 ApplicationThese products have been used typically for part

8、s requiring moderate strength, especially where such parts require brazing or welding and where distortion during machining must be minimized, but usage is not limited to such applications.2. APPLICABLE DOCUMENTSThe issue of the following documents in effect on the date of the purchase order forms a

9、 part of this specification to the extent specified herein. The supplier may work to a subsequent revision of a document unless a specific document issue is specified. When the referenced document has been cancelled and no superseding document has been specified, the last published issue of that doc

10、ument shall apply.SAE AMS4172F Page 2 of 62.1 SAE PublicationsAvailable from SAE, 400 Commonwealth Drive, Warrendale, PA 15096-0001 or www.sae.org.AMS2355 Quality Assurance, Sampling and Testing, Aluminum Alloys and Magnesium Alloy, Wrought Products (Except Forging Stock), and Rolled, Forged, or Fla

11、sh Welded RingsAMS2772 Heat Treatment of Aluminum Alloy Raw MaterialsAS1990 Aluminum Alloy Tempers2.2 ASTM PublicationsAvailable from ASTM International, 100 Barr Harbor Drive, P.O. Box C700, West Conshohocken, PA 19428-2959, Tel: 610-832-9585, www.astm.org.ASTM B 594 Ultrasonic Inspection of Alumin

12、um-Alloy Wrought Products for Aerospace ApplicationsASTM B 660 Packaging/Packing of Aluminum and Magnesium ProductsASTM B 666/B 666M Identification Marking of Aluminum and Magnesium ProductsASTM B 807/B 807M Extrusion Press Solution Heat Treatment for Aluminum Alloys2.3 ANSI PublicationsAvailable fr

13、om American National Standards Institute, 25 West 43rd Street, New York, NY 10036-8002, Tel: 212-642-4900, www.ansi.org.ANSI H35.2 Dimensional Tolerances for Aluminum Mill ProductsANSI H35.2M Dimensional Tolerances for Aluminum Mill Products (Metric)3. TECHNICAL REQUIREMENTS3.1 CompositionShall conf

14、orm to the percentages by weight shown in Table 1, determined in accordance with AMS2355.TABLE 1 - COMPOSITIONElement min maxSiliconIronCopperManganeseMagnesiumChromiumZincTitaniumOther ElementsOther ElementsAluminum0.40-0.15-0.80.04-remainder0.80.70.400.151.20.350.250.150.050.15SAE AMS4172F Page 3

15、of 63.2 ConditionMaterial shall be produced in one of the following tempers. If no temper is specifed, Temper T4511 shall be supplied.3.2.1 Temper T4511Solution heat treated and stress relieved by stretching to produce a nominal permanent set of 1-1/2%, but not less than 1% nor more than 3%.3.2.1.1

16、Extrusions may receive minor straightening, after stretching, of an amount necessary to meet the requirements of 3.5.3.2.1.2 Extrusions shall be supplied with the as-extruded surface finish; light polishing to remove minor surface imperfections is permissible provided such imperfections can be remov

17、ed within specified dimensional tolerances.3.2.2 Temper T4510Solution heat treated and stress relieved by stretching to produce a nominal permanent set of 1-1/2%, but not less than 1% nor more that 3%.3.2.2.1 Extrusions shall receive no additional straightening or stretching to meet requirements of

18、3.53.2.2.2 Extrusions shall be supplied with the as-extruded surface finish; light polishing to remove minor surface imperfections is permissible provided such imperfections can be removed within specified dimensionaltolerances.3.2.3 Heat Treatment shall be classified as follows:Class Description1 F

19、urnace solution heat treated in accordance with AMS2772.2 Extruded and press solution heat treated in accordance with ASTM B807/B807M.If no Class is specified, either Class may be provided.3.2.43.3 PropertiesExtrusions shall conform to the following requirements, determined in accordance with AMS235

20、5:3.3.1 As Solution Heat Treated and Stress Relieved3.3.1.1 Tensile PropertiesShall be as shown in Table 2.TABLE 2 - MINIMUM TENSILE PROPERTIESProperty ValueTensile Strength 26.0 ksi (179 MPa)Yield Strength at 0.2% Offset 16.0 ksi (110 MPa)Elongation in 2 Inches (50.8 mm) or 4D 16%SAE AMS4172F Page

21、4 of 63.3.2 Response to Heat TreatmentExtrusions, precipitation heat treated in accordance with AMS2772 to the T62 temper (See AS1990), shall have the following properties:3.3.2.1 Tensile PropertiesShall be as shown in Table 3.TABLE 3A - MINIMUM TENSILE PROPERTIES, INCH/POUND UNITSNominal Diameter o

22、rLeast Thickness(Bars, Rods, Wire, Shapes) orNominal Wall Thickness(Tubing), InchesTensileStrengthksiYield Strengthat 0.2% OffsetksiElongation in2 Inches or 4D%Up to 0.250, excl Up to 0.250 and over38.038.035.035.0810TABLE 3B - MINIMUM TENSILE PROPERTIES, SI UNITSNominal Diameter orLeast Thickness(B

23、ars, Rods, Wire, Shapes) orNominal Wall Thickness(Tubing), MillimetersTensileStrengthMPaYield Strengthat 0.2% OffsetMPaElongation in50.8 mm or 4D%Up to 6.35, exclUp to 6.35 and over2622622412418103.4 QualityExtrusions, as received by purchaser, shall be uniform in quality and condition, sound, and f

24、ree from foreign materials and from imperfections detrimental to usage of the extrusions.3.4.1 When specified by purchaser, extrusions shall be subjected to ultrasonic inspection in accordance with ASTM B594. Standards for acceptance shall be as agreed upon by purchaser and vendor.3.5 TolerancesShal

25、l conform to all applicable requirements of ANSI H35.2 or ANSI H35.2M.4. QUALITY ASSURANCE PROVISIONS4.1 Responsibility for InspectionThe vendor of extrusions shall supply all samples for vendors tests and shall be responsible for the performance of all required tests. Purchaser reserves the right t

26、o sample and to perform any confirmatory testing deemed necessary to ensure that the extrusions conform to specified requirements.4.2 Classification of Tests4.2.1 Acceptance TestsComposition (3.1), tensile properties (3.3.1.1 and 3.3.2.1), ultrasonic inspection (3.4.1) when specified, and tolerances

27、 (3.5) are acceptance tests and, except for composition, shall be performed on each inspection lot.SAE AMS4172F Page 5 of 64.3 Sampling and TestingShall be in accordance with AMS2355.4.3.1 Additional Sampling and Testing of Material Press Solution Heat TreatedCompliance with the requirements of Tabl

28、e 2 shall be determined by hardness tests followed by tension tests performed on samples from the two softest extrusions in the inspection lot. The method of hardness testing shall be left to the discretion of the producer.4.4 ReportsThe vendor of extrusions shall furnish with each shipment, a repor

29、t stating that the extrusions conform to the chemical composition and tolerances, results of ultrasonic inspection (when specified) and stating that the product conforms to the other acceptance tests. This report shall include the purchase order number, inspection lot number, AMS4172F, size or secti

30、on identification number, extrusion type, class of heat treatment, and quantity. The report shall also include the producer, the product form and the mill produced size.4.5 Resampling and RetestingShall be in accordance with AMS2355.5. PREPARATION FOR DELIVERY5.1 IdentificationShall be in accordance

31、 with ASTM B 666/B 666M.5.2 PackagingExtrusions shall be prepared for shipment in accordance with ASTM B 660 and in compliance with applicable rules and regulations pertaining to the handling, packaging, and transportation of the extrusions to ensure carrier acceptance and safe delivery.6. ACKNOWLED

32、GMENTA vendor shall mention this specification number and its revision letter in all quotations and when acknowledging purchase orders.7. REJECTIONSExtrusions not conforming to this specification, or to modifications authorized by purchaser, will be subject to rejection.8. NOTES8.1 A change bar (|)

33、located in the left margin is for the convenience of the user in locating areas where technical revisions, not editorial changes, have been made to the previous issue of this document. An (R) symbol to the left of the document title indicates a complete revision of the document, including technical

34、revisions. Change bars and (R) are not used in original publications, nor in documents that contain editorial changes only.8.2 Hardness should be not lower than 55 HB/10/500 or 60 HB/10/1000, determined in accordance with ASTM E 10. Hardness has been used to verity that product is properly processed

35、, but an “out-of-range hardness number” is not always indicative of product with “out-of-specification tensile strength”. Further analysis including material composition verification, heat treat process parameter review, and/or tensile property measurement on product with out-of-range hardness may b

36、e necessary.SAE AMS4172F Page 6 of 68.3 Terms used in AMS are clarified in ARP1917.8.4 Dimensions and properties in inch/pound units and the Fahrenheit temperatures are primary; dimensions and properties in SI units and the Celsius temperatures are shown as the approximate equivalents of the primary

37、 units and are presented only for information.8.5 Purchase documents should specify not less than the following:AMS4172FForm and size or section identification number of extrusions desiredQuantity of extrusions desiredUltrasonic inspection acceptance standards, when specified (See 3.4.1).Whether Typ

38、e II tubing is required (Where no type is specified, Type I shall apply)Whether Temper T4510 extrusions are requiredWhether Class 1 or Class 2 solution heat treatment is required.8.6 Similar SpecificationsASTM B 221 and ASTM B 221M are listed for information only and shall not be construed as acceptable alternates unless all requirements of this AMS are met.PREPARED BY AMS COMMITTEE “D“