《NAVY MIL-T-22260-1963 TAPES PRESSURE-SENSITIVE ADHESIVE ELECTRICAL HIGH TEMPERATURE INSULATION POLYTETRAFLUOROETHYLENE [Superseded By NAVY MIL-I-23594 C CANC NOTICE 1 NAVY MIL-I-23-23.pdf》由会员分享，可在线阅读，更多相关《NAVY MIL-T-22260-1963 TAPES PRESSURE-SENSITIVE ADHESIVE ELECTRICAL HIGH TEMPERATURE INSULATION POLYTETRAFLUOROETHYLENE [Superseded By NAVY MIL-I-23594 C CANC NOTICE 1 NAVY MIL-I-23-23.pdf（11页珍藏版）》请在麦多课文档分享上搜索。

1、MIL-T-222b0 9999906 1083703 419 M % MIL-T-22260 (Wep) I Iday 1961 MILITARY STECIFICATION TAPE, INSULATING, ELECTRICAL, PRESSUXE SETJSI T I vk: ETCHXD POLY TIJTRATL UOROE THYLENE This specification has been approved by the Bureau of Naval Weapons, Department of the Navy. 1. SCOPE 1.1 This specificati

2、on describes the requirements for the procurement of one type of pressure-sensitive, adhesive, etched polytetrafluoroethylene insulation tape intended for use in the construction of electrical and elec- tronic equipment where it is necessary to impregnate wfth insulation varnish after application of

3、 tape insulation. 2. APPLICABLE DOCUMENTS 2.1 The following specifications, standards, and publications, or such portion thereof as may be designated herein, of the issue in effect on the date of invitation for bids, forms a part of this specification. SPECIFICATIONS FEDERAL L-P-406 Plastics, Organi

4、c; General Specifications, Test Methods MILITARY MIL-P-17555 STANJIARDS FEDERAL FED- STD- 17 5 Preparation for Delivery of Electronic Equipment; Miscellaneous Electric Equipment (Except Rotating Electrical Equipment) and Associated Repair Parts Adhesive, Methods of Testing 1 FSC 597 O .- Provided by

5、 IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-T-22260 9999906 1083704 355 aL-T-22260 (Wep) PUBLICATIONS tBIJREAU OF NAVAL WEAPONS NAVORD OP 400 General Instructions for the Design, Manufac- ture, and Inspection of Naval Ordnance Equip- i ment (Copies of s

6、pecifications, standards, drawings, and publications re- quested by contractors in connection with specific procurement functions should be obtained from the procuring activity or as directed by the con- tracting officer.) 2.2 Other publications. - The following documents form a part of this Unless

7、otherwise indicated, the issue in effect on date of specification. invitation for bids shall apply. AMERICAN SOCIETY FOR TESTING MATERIALS D624- 54 D747 - 50 aa 2 - 54 ASTM- Al 67 Methods of Tests for Tear Resistance of Vulcanized Rubber Methods of Tests for Stiffness in Flexure of Plastics Methods

8、of Tests or Tensile Properties of Thin Plastic Sheets and Films (Tentative) Corrosion-Resisting Chromium-Nickel Steel Plate, Sheet, and Strip, Type 302 or 304 (Application for copies should be addressed to the American Society for Testing Materials, 1916 Race Street, Philadelphia 3, Pennsylvania.) 3

9、. REQUIREMENTS 3.1 General requirements. 3.1.1 Pre-production samples. - Unless otherwise specified in the con- tract or order, pre-production samples of the tape shall be manufactured by the methods and procedures proposed for the production lot. shall be tested ao specified in section 4 herein and

10、 are for the purpose of determining that the production items meet the requirements of this specif- ication and the design. These samples See 4.1.2. 3.1.2 Materials. 3.1.2.1 Backing. - The backing material shall be a high grade polytetra- fluoroethylene, etched or prepared so that conventional adhes

11、ive or plastic insulation varnish6 will adhere to it. rosive material, unsightly defects, dirt, lumps, and irregularitieq. 2 The backing shall be free from cor- : Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-T-22260 H 9999906 LO83705 291 W MIL

12、-T-22260 (Wep) 3.1.2.2 Adhesive. - The adhesive shall be pressure-sensitive and shall not require heat, moisture, or other specific preparation prior to applica- tion. The adhesive shall be non-corrosive and thermosetting or heat-curing. 3.1.2.3 Rolls. - The tape shall be furnished in lengths of 18,

13、 36, 60, and 72 yards per roll, unless otherwise specified. Where the tape is re- quired for machine taping, the overall diameter of the roll and the mandrel diameter of the cylinder core shall be specified by the contract or purchase order; when the tape is applied by hand, it shall be put up in ro

14、lls over a core diameter of three inches, unless otherwise specified. 3.1.3 Gages. - The contractor shall provide himself with whatever gages are necessary and adequate to ensure that the material to which this speci- fication applies will meet the dimensional requirements of the specifica- tim. If

15、so stipulated in the contract, order, or requisition, the Govern- ment will furnish drawings of pertinent Navy Final Inspection Gages for guid- ance in the design of the contractors inspection gages. cedure shall not relieve the contractor of, his responsibility in the design and manufacture of such

16、 gages as may be required for the satisfactory ful- fillment of the contract requirements, but is intended to facilitate accept- ance of all components and assemblies by Navy Final Inspection Gages. However, such pro- 3.1.4 Requests for deviation. - Requests for deviation from this spec- ification,

17、applicable drawings, specifications, publications, materials, and processes specified herein shall be as set forth in NAVORD OP 400. 3.1.5 Conflicting requirements. - Conflicting requirements arising be- tween this specification and any specification, publication, or drawing listed herein shall be r

18、eferred in writing to the procuring agency or ap- pointed agent for interpretation, clarification, and resolution (or correc- tion). 3.2 Performance requirements and product characteristics. - The tape shall meet the following performance requirements and product characteris- tics : 3.2.1 Width and

19、thickness. - The tape shall be furnished in standard widths and thicknesses shown in Table I, and shall be tested for width and thickness as specified in 4.5.4.1. 3 3 Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-T-222b0 W 99999Ob LO8370b 128 =

20、 MIL-T-22260 (Wep) TABLE I Width in Tolerance in Overall Thickness To 1 eranc e Inches Inches In Inches (All Widths) In Inches (+) 114 112 5/8 3 I4 1 1-1/4 1-112 .O3 .O3 .O3 .O3 .O3 .O3 .O3 .O035 .O045 .o055 .O065 . O005 .O005 ,0006 .o01 , 3.2.2 Specific gravity. - The specific gravity of the tape s

21、hall aver- age at least 2.1, when tested as in 4.5.4.2. 3.2.3 Tensile strength. - The tensile strength of the tape shall aver- age at least 2500 pounds per square inch in both the machine and transverse directions, when tested as in 4.5.4.3. 3.2.4 than 150 percent in both the machine and transverse

22、directions, when tested as in 4.5.4.4. Elongation. - The elongation of the tape shall average no more 3.2.5 Tear strength. - The tear strength of the tape shall average no less than 400 pounds per inch, when tested as in 4.5.4.5. 3.2.6 Stiffness at 77 degrees F. - Stiffness shall average at least 40

23、,000 pounds per square inch, when tested as in 4.5.4.6. 3.2.7 Water absorption. - Water absorption shall be zero percent, whe tested as in 4.5.4.7. 3.2.8 Flammability. - The tape shall be non-flammable, when tested a in 4.5.4.8. 3.2.9 Resistance to weathering. - The tape shall show no cracking, craz

24、ing, or other degradation, when tested as in 4.5.4.9. 3.2.10 Adhesion. - The tape shall have a minimum average adhesion value of 10 ounces, when tested as in 4.5.4.10. 4 -.- Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-T-222b0 999990b 1083707

25、Ob4 BEL-T-22260 (Wep) 3.2.11 Dielectric constant. - Dielectric constant shall average at least 2.0 at 1000 cycles, when tested as in 4.5.4.11. 3.2.12 Power factor. - Power factor shall average at least 0.0003 at 60 to 100,000,000 cycles, when tested as in 4.5.4.12. 3.2.13 Volume resistivity. - Volum

26、e resistivity shall be a minimum average value of megohms, when tested as in 4.5.4.13. 3.2.14 Surface resistivity. - Surface resi tivity, at 100 percent R.H., shall have a mini.num average value of 3.6 by 10 8 megohms, when tested as in 4.5.4.14. 3.2.15 Dielectric strength, short time. - Short time

27、dielectric strength shall have a minimum average value of 2500 volts per mil, when tested as in 4.5.4.15. 3.2.16 as in 4.5.4.16. Surface arc resistance. - The tape shall not track, when tested 3.3 Workmanship. - The workmanship shall conform to the best commercial practices. form coating, and the fi

28、nished tape shall contain no bare spots or lumps. The adhesive shall be applied to the backing in a smooth, uni- 4. QUALITY ASSURANCE PROVISIONS 4.1 Government inspection. - The Government inspector will make such inspections as are necessary to determine that the tape is in accordance with the requ

29、irements of the contract and specifications. Unless otherwise specified, these inspections will be conducted in accordance with instruc- tions contained in NAVORD OP 400. 4.1.1 Sampling. - Unless otherwise specified by the contract or pur- chase order, and when applicable, the sampling plans and pro

30、cedures used by the Government inspector in the determination of the acceptability of products submitted by a supplier for Government inspection shall be in accordance with 4.1.2 and 4.1.4. 4.1.2 Pre-production sample. - Unless otherwise specified for each con- tract or order, a representative sampl

31、e of five rolls shall be manufactured by the methods and procedures proposed for the production lot. These shall be submitted to the Government inspector for pre-production tests at an activity designated by the Bureau of Naval Weapons, for purposes of deter- mining compliance with the requirements

32、of the contract and specifications. Further production of the item by the contractor prior to approval of the contracting activity or the completion of tests on the pre-production sam- ples shall be at the contractors risk. Pre-production samples accepted will be applied as part of the quantity spec

33、ified by the contract or order, but shall not be used in any equipment manufacfured for the Government. 5 Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-T-222b0 7999706 1083708 TTO MIL-T-22260 (Wep) 4.1.3 Lot size. - As applied to Government ins

34、pection of units of pro- duct, the term “lot“ shall mean “inspection lot“; i.e., a collection of units of product submitted by a supplier for Government inspection. Unless otherwise determined by the Government inspector, each shipment of units of product shall be a separate “inspection lot“ and may

35、 differ from the quan- tity specified in the order or contract. Where a shipment consists of less than 60 units, the Government inspector may select and combine several ship- ments into one “inspection lot.“ In any event, all units of a single “in- spection lot“ shall be made to the same design, wit

36、h the same material and manufacturing techniques, and shall be part of one continuous production run. 4.1.4 periodic production samples. - The Government inspector shall randomly select from each production lot a number of units equal to 10 per- cent of the lot size, but not less than 6 nor more tha

37、n 40 units. Unless otherwise specified in the contract or purchase order, these units shall be submitted to a Bureau of Naval Weapons assigned activity to determine com- pliance of the samples with the requirements of the contract, specifications, and drawings. specifications and withstands the test

38、s specified in 4.5. tion samples accepted will be applied as part of the quantity specified by the contract or order, but shall not be used in any equipment manufactured for the Government. The tape shall be considered satisfactory if it meets all Periodic produc- 4.2 Contractors inspection. - Contr

39、actors inspection shall be conduct- ed in accordance with provisions of “Inspections by Contractor“, as contain- ed in NAVORD OP 400. 4.3 Classification of tests. - Inspection and testing of the tape shall be classified, as follows: 4.3.1 Pre-production and periodic production tests. - Pre-productio

40、n and periodic production tests shall be accomplished on samples selected as specified in 4.1.2 and 4.1.4 which are representative of the production of the tape after the award of the contract, to determine that the production meets the requirements of this specification. These tests are detailed in

41、 4.5. Acceptance shall be based on no defects in the sample. the sample to comply with these requirements will result in the rejection of the lot or the cessation of production, as determined by the procuring activity . Failure of 4.3.2 Tests after delivery. - Unless otherwise specified in the con-

42、tract, the Government reserves the right to conduct any or all of the tests specified herein, as deemed necessary, after receipt of the tape. Any de- fects discovered during or after these tests due to the contractors fail- .Ure to comply with the specifications for this material shall be corrected

43、by the contractor at no expense to the Goverment, provided the contractor is notified of such defects within the guarantee period of the contract. 6 I , - Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-T-22260 9999906 LOB3709 937 i MIL-T-22260 (

44、Wep) 4.4 Test equipment. 4.4.1 Testing machine. - The testing machine shall be similar to that described in method 1041 of PED-STD-175, with at least a 10-inch jaw sep- aration, a preferable working range of O to 10 pounds, with readings in 0.1 pound increments or less, and with a pulling clamp spee

45、d of 12 plus or minus 0.5 inches per minute. 4.4.2 Steel strip. - A cold-rolled, corrosion resisting steel strip (ASTM Standard Designation A167, Type 302 or 304) 1/16 inch by 2 inches by 5 inches, finished to a surface roughness of not more than 20 nor less than 10 microinches, as measured by a sur

46、findicator or equivalent surface measur- ing device, shall provide a rigid base for testing adhesion of tape. Strips shall be polished lengthwise and measurements taken crosswise. Quarter- inch scribe marks shall be placed on one edge of the strips at 1/2-inch in- t erva1 s. 4.4.3 Roller. - The stee

47、l roller required shall be 3.25 inches plus or minus 0.1 inch in diameter by li75 plus or minus 0.5 inches in width, shall be covered with rubber approximately 1/4 inch thick, and shall have a duro- meter hardness of 80 plus or minus 5. The weight of the complete assembly, which is controlled by the

48、 original diameter of the steel roller, shall be 4.5 plus or minus 0.1 pound. 4.5 Pre-production and periodic production tests. 4.5.1 The contractor or Government inspector shall conduct pre-pro- duction and periodic production tests as specified in 4.3.1 to assure that the upper or movable member s

49、hall consist of a foot having a flat steel face measuring 1/4 inch in diameter and so arranged as to move with its face parallel to the face of the anvil at all times. The movable member shall be of such weight and shall be so attached to the oper- ating rod of the micrometer that three ounces of dead weight shall be ap- plied to all samples being measured. Measurements shall be made at random in lengths of not less than three feet on each roll of tape, and