1、A.C.N. 006 893 232Holden LimitedEngineering DepartmentMATERIAL SPECIFICATIONNUMBERSHEETRELEASEREVISION:HN 19701 of 3February, 1988NAME: ADHESIVE CYANOACRYLATE - BLACKTHIS DOCUMENT MUST NOT BE REPRODUCED. IF USED IN RELATION TOTHE COMPANYS PRODUCTS THE RECIPIENT IS RESPONSIBLE TOCONFIRM THE DOCUMENT

2、ISSUE DATE IS STILL VALID.FORM : I:LABRTORYFORMSTDMATSPEC.DOC1. SCOPEA single component, solvent free modified cyanoacrylate ester with a 2-5minutes fixturing time. This adhesive offers temperature and environmentalresistance over other cyanoacrylate adhesives. The material bonds to a widevariety of

3、 metals, plastics and rubbers.2. GENERALCured material shall be insoluble and resist water, humidity and other chemicalsused in the assembly of automotive products. The cured material produces abond that provides improved resistance to peel and cleavage loading.3. PROPERTIES AND TEST REQUIREMENTS3.1

4、 Liquid Adhesive3.1.l Colour - opaque black.3.3.3 Specific gravity - 1.1 nominal.3.1.3 Usable viscosity - 200 to 2,200 cP.3.1.4 Flash point (ASTM D92) - 80C min.3.1.5 Soluble in - MEK Aceton, Nitromethane3.2 Cured Adhesive3.2.l Melting point - 165 C3.2.2 Hardness - 82 SHORE D3.2.3 Cure time - 48 hou

5、rs max.3.2.4 Service temperature range - -54 to 104 C3.2.5 Soluble in - Dimethyl Formanide, Nitromethane3.3 Bond Properties. Tensile Shear Strength. Steel/Steel mPa min.(ASTM D 1002).3.3.1 48 hours room temperature cure - 13.83.3.2 Hot strength - 24 hour RTCThen 24 hour at 121 C and tested at 121 C

6、- 6.93.3.3 Heat ageing, 24 hour RTC then 24 hours 121 C tested atroom temperature - 20.6.3.3.4 Humidity resistance 48 hours RTC then 100 hours at 38 C and100% humidity - 13.8.A.C.N. 006 893 232Holden LimitedEngineering DepartmentMATERIAL SPECIFICATIONNUMBERSHEETRELEASEREVISION:HN 19702 of 3February,

7、 1988NAME: ADHESIVE CYANOACRYLATE - BLACKTHIS DOCUMENT MUST NOT BE REPRODUCED. IF USED IN RELATION TOTHE COMPANYS PRODUCTS THE RECIPIENT IS RESPONSIBLE TOCONFIRM THE DOCUMENT ISSUE DATE IS STILL VALID.FORM : I:LABRTORYFORMSTDMATSPEC.DOC3. PROPERTIES AND TEST REQUIREMENTS3.4 180 peal strength. Steel/

8、steel N/m min.25 mm x 200 mm x .125 mm steel foil 24 hour RTC then 4 hours at 121 C,tested at room temperature - 3,450.3.5 Storage stability - four months minimum from time of receipt when storedunder refrigerated conditions (4 C).4. APPROVAL )CERTIFICATION )- Refer clauses A, B, C and G, HN 1000.IN

9、SPECTION AND REJECTION )A.C.N. 006 893 232Holden LimitedEngineering DepartmentMATERIAL SPECIFICATIONNUMBERSHEETRELEASEREVISION:HN 19703 of 3February, 1988NAME: ADHESIVE CYANOACRYLATE - BLACKTHIS DOCUMENT MUST NOT BE REPRODUCED. IF USED IN RELATION TOTHE COMPANYS PRODUCTS THE RECIPIENT IS RESPONSIBLE TOCONFIRM THE DOCUMENT ISSUE DATE IS STILL VALID.FORM : I:LABRTORYFORMSTDMATSPEC.DOCAPPROVED MATERIALS APPROVED SUPPLIERSBLACK MAX LOCTITE AUST.