FORD WSS-M5B280-C5-2008 PRIMER CLEANER GLASS TRANSPARENT TO BE USED WITH FORD WSS-M99P1111-A (Shown on FORD WSS-M5B280-C4)《玻璃用透明底漆 清洁剂 与标准FORD WSS-M99P1111-A一起使用 列于标准FORD WSS-M.pdf

《FORD WSS-M5B280-C5-2008 PRIMER CLEANER GLASS TRANSPARENT TO BE USED WITH FORD WSS-M99P1111-A (Shown on FORD WSS-M5B280-C4)《玻璃用透明底漆 清洁剂 与标准FORD WSS-M99P1111-A一起使用 列于标准FORD WSS-M.pdf》由会员分享，可在线阅读，更多相关《FORD WSS-M5B280-C5-2008 PRIMER CLEANER GLASS TRANSPARENT TO BE USED WITH FORD WSS-M99P1111-A (Shown on FORD WSS-M5B280-C4)《玻璃用透明底漆 清洁剂 与标准FORD WSS-M99P1111-A一起使用 列于标准FORD WSS-M.pdf（4页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2008 11 06 Revised Completely revised; Updated 2.1 and deleted Table 1 and Table 2, See summary of Revisions. Mukta Mehandru, FNA2007 04 19 Revised Inserted 2.1, 4.4.4, Table 1 and Table 2; Revised 4.4 M. Mehandru 1990 02 08 Released NB00E0017

2、9051000 K. King, E. R. Rezendes Printed copies are uncontrolled Copyright 2008, Ford Global Technologies, LLC Page 1 of 7 PRIMER, GLASS, SILANE, ONE STEP, UV DETECTABLE WSS-M5B280-C4 PRIMER/CLEANER, GLASS, TRANSPARENT WSS-M5B280-C5 1. SCOPE The materials defined by these specifications are glass cle

3、aners/adhesion promoters that deposit monomolecular films and also remove surface contaminates. 2. APPLICATION These specifications were released originally for materials used to clean and condition windshield glass prior to the application of adhesion promoting primer ( WSS-M2G314-B2). (These prime

4、rs should be applied by means of a brush, felt or other suitable applicator. WSS-M5B280-C4 is a one step glass primer. WSS-M25B280-C4 is not to be used as a one step glass primer with adhesive materials conforming to WSB-M2G316-B, and WSS-M2G316-B2/B3/B5. 2.1 MANUFACTURING PROCESS RECOMMENDATION The

5、se primers are moisture sensitive and require special handling for manual and automated process. Please contact supplier or the Material Engineering for current process standards. Approved suppliers are responsible for maintaining the accuracy and relevancy of these process parameters (in their Proc

6、ess Standard). Approved suppliers must submit any changes to these process parameters in a timely manner (within 30 days) for review and approval by Materials Engineering, Vehicle Operation, and Product Development Engineer. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material

7、 suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). ENGINEERING MATERIAL SPECIFICATION WSS-M5B280-C4/C5 Printed copies are uncontrolled Copyright 2008, Ford Global Technologies, LLC Page 2 of 4 3.2 COLOR WSS-M5B280-C4 Transparen

8、t Light Yellow WSS-M5B280-C5 Transparent Red/Any color but clear 3.2.1 Fluorescence on Glass Under Long-Wave UV Light This provision applies to WSS-M5B280-C4 primer. When the primer (within shelf life) is applied to glass, it will fluoresce when a BLAK-RAY Model B 100AP lamp or similar source illumi

9、nate the glass. The fluorescence is not a permanent feature of the primer after it is applied to the glass. 3.3 VISCOSITY, max (FLTM BI 111-01, No. 4, Ford Cup) WSS-M5B280-C4 29 - 44 s WSS-M5B280-C5 25 40 s 3.4 WEIGHT PER VOLUME (ASTM D 1475) The weight tolerance for any one supplier shall be +/- 0.

10、075 kg/L based on the weight of the original approved production sample (see para 4.3). 3.5 DRYING RATE, max WSS-M5B280-C4 30 minutes WSS-M5B280-C5 1 minute Test Method: Apply a 0.008 - 0.013 mm film of primer 25 mm wide to a 75 x 75 mm clean glass plate. To determine the primer drying rate, immedia

11、tely at rapid intervals, dab the primer film with a wad of absorbent cotton. Observe if any of the cotton fibers adhere to the primed surface. Record the drying rate, as the time elapsed from the initial primer application until the cotton fibers do not adhere to the primer. Note: The drying rate is

12、 longer for the C3 suffix material due to the type of solvent. C4 is a one step clear primer and thus has a different drying rate. Actual differences in drying rate as processed through the assembly plant are negligible. 3.9 STORAGE STABILITY Shall be stored at ambient room temperature below 35 C, a

13、way from all sources of heat such as ovens, direct sunlight etc. The material should not be stored outside. Under these storage conditions, the maximum shelf life of the material in unopened containers shall be six (4) months from date of receipt at Ford Motor Co. Material may not be used after the

14、expiration date unless the supplier has given written documentation to Materials Engineering and the affected Manufacturing Plant that the material conforms to requirements outlined in the material control plan. The supplier shall also indicate in the letter the number of additional days the materia

15、l will be usable. ENGINEERING MATERIAL SPECIFICATION WSS-M5B280-C4/C5 Printed copies are uncontrolled Copyright 2008, Ford Global Technologies, LLC Page 3 of 4 3.10 QUALITY The material shall be a smooth, homogenous mixture free from foreign materials and properties detrimental to normal production

16、operations. 3.11 NON-INTERCHANGEABILITY OF MATERIALS Only approved urethane adhesive WSB-M2G316-B, or WSS-M2G316-B2/B3/B4/B5, Glass Cleaner WSS-M5B280-C5, or WSS-M5B280-C4 Glass Primer WSS-M2G314-B2, Metal Primer WSB-M2G234-C/C2/C3 all from the same production source shall be used in conjunction wit

17、h one another. Note that WSS-M5B280-C4 must be used with WSS-M2G316-B4. 3.12 FUNCTIONAL APPROVAL Materials being evaluated for approval to this specification shall be subjected to a production trial. Functional trial results must be approved by the affected assembly operation and Design Engineering.

18、 Results shall be made available to Materials Engineering prior to material approval and release. 4. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. 4.1 FLASH POINT, Max. WSS-M5B280-C4 13 C (ASTM D 3278,

19、Setaflash Closed Cup) WSB-M5B280-C5, 13 C (ASTM D 3278, Setaflash Closed Cup) 4.2 FLAMMABILITY AND/OR TOXICITY These materials represent potential fire and/or health hazards. The Manufacturing Engineering Department shall notify both the Plant Security and the Safety Units of their presence in the P

20、lant to assure that proper fire and/or health precautions are provided. The location in which they are used or stored shall be included in the notifications. 4.3 WEIGHT PER VOLUME (ASTM D 816) Materials conforming to this specification and found satisfactory in production, range from 0.65 - 0.96 kg/

21、L. ENGINEERING MATERIAL SPECIFICATION WSS-M5B280-C4/C5 Printed copies are uncontrolled Copyright 2008, Ford Global Technologies, LLC Page 4 of 4 4.4 RELATED MATERIALS AND PROCEDURE 4.4.1 Glass Primer WSS-M2G314-B2 4.4.2 Metal Primer WSB-M2G234-C WSB-M2G234-C3 4.4.3 Urethane Adhesive WSS-M2G316-B2/B3

22、/B4/B5/B6 4.4.4 Performance Spec WSS-M11P57-A5 4.5 ODOR Shall be free form objectionable odors, both at “as received“ and application temperatures. 5.0 SUMMARY OF REVISIONS 2008 11 06 1. Added WSS-M5B280-C5 2. Revised Application to reflect the new specification for black out primer. 3. Revised Manufacturing Process Recommendation and deleted Tables 1, and 2. 4. Deleted Shear Adhesion Requirement. 5. Revised Storage Stability.