FORD WSS-M4D827-B1-2013 ACRYLONITRILE BUTADIENE STYRENE (ABS) MOLDING COMPOUND MEDIUM HEAT RESISTANT INTERIOR TO BE USED WITH FORD WSS-M99P1111-A .pdf

《FORD WSS-M4D827-B1-2013 ACRYLONITRILE BUTADIENE STYRENE (ABS) MOLDING COMPOUND MEDIUM HEAT RESISTANT INTERIOR TO BE USED WITH FORD WSS-M99P1111-A .pdf》由会员分享，可在线阅读，更多相关《FORD WSS-M4D827-B1-2013 ACRYLONITRILE BUTADIENE STYRENE (ABS) MOLDING COMPOUND MEDIUM HEAT RESISTANT INTERIOR TO BE USED WITH FORD WSS-M99P1111-A .pdf（8页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions Rev. 2 2013 05 09 N Status Replaced by WSS-M4D827-C1 L. Soreide, NA 2012 05 04 Revised See Summary of Revisions A. Pan, APA 2011 05 13 Activated A. Pan, APA Controlled document at www.MATS Copyright 2013, Ford Global Technologies, LLC Page 1

2、of 8 ACRYLONITRILE BUTADIENE STYRENE (ABS) WSS-M4D827-B1 MOLDING COMPOUND, MEDIUM HEAT RESISTANT, INTERIOR NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is a molded in color, medium heat resistant injection molding compound based on acrylonitrile butadiene styrene

3、 (ABS) that has been UV stabilized for unpainted interior applications. 2. APPLICATION This specification was released originally for material used for visible interior body parts. 2.1 LIMITATIONS Material approved to this specification does not contain UV stabilizers for direct sunlight exposure in

4、 exterior applications. Therefore long term exposure to direct sunlight could cause chalking and loss of gloss. 3. REQUIREMENTS 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M9

5、9P1111-A). 3.1.1 Many 4D resin specifications prior to 2011, identified certain requirements with the symbol (s), which indicated that the mean and +/- 3 sigma values were to be reported. The specification minimum, maximum or range was established using 3 sigma data. For 2011 and beyond, refer to Ta

6、ble 1 for number of samples required for each test to establish specification limits. 3.1.2 This specification is based on virgin materials, however materials with recycled content as defined by WRS-M99P42-A1 (post-consumer and/or post industrial recyclates and repolymerised recycled materials) shou

7、ld be used whenever technically feasible. 3.1.3 The use of regrind is permitted, for economic / environmental reasons, with compliance as indicated in Ford Engineering CAD and Drafting Standard E-4. 3.1.4 Materials used in interior applications must meet the requirements outlined in WSS-M99P2222-C1/

8、Latest, Performance, Vehicle Interior Environment Quality Material/Component Requirements. Data must be included in material submission package. 3.1.5 Performance Criteria: Parts using this specification shall meet the appropriate performance specifications: All mold-in-color components using this m

9、aterial must comply with all the requirements of WSS-M15P4-F/Latest for interior applications. ENGINEERING MATERIAL SPECIFICATION WSS-M4D827-B1 Copyright 2013 Ford Global Technologies, LLC Page 2 of 8 3.2 SAMPLE PREPARATION Unless otherwise specified all tests shall be carried out on injection molde

10、d, one-end gated test specimens. The test specimens A and D shall be molded using molding conditions defined in ISO 2580-2. No annealing is allowed. See Tables 1 and 2 for the number of samples required. Specimens shall be as follows: Specimen A 150 minimum x 10 x 4.0 +/- 0.2 mm (ISO 527-2, Specimen

11、 Type 1A) Specimen B 355 x 100 x 2.0 +/- 0.1 mm (ISO 3795) Specimen C 145 x 60 x 3.2 +/- 0.2 mm Specimen D Center of Specimen A. 80 x 10 x 4.0 +/- 0.2 mm Specimen E 100 mm diameter x 3.2 mm Specimen F 80 mm diameter x 3.2 mm Specimen G 90 mm x 200 mm Specimen H 50 +/- 1 mm diameter x 3.2 +/- 0.2 mm

12、Specimen I 100 mm x 150 mm, min 3.3 APPEARANCE 3.3.1 Weathering Resistance Rating 4 min (FLTM BO 116-01, 601.6 kJ/m2 exposure Specimen C from smooth polished mold, ISO 105-A02 / AATCC Evaluation Procedure 1) After exposure the material shall show no fading or color change in excess of the specified

13、AATCC rating. In addition, there shall be no cracking, crazing or other deterioration. Use regional choice for initial approval and report the color house used. See Table 2 for additional color durability submission requirements. 3.4 MATERIAL PROPERTIES 3.4.1 Density 0.99 1.17 g/cm3 (ISO 1183, Metho

14、d A) 3.4.2 Tensile Strength at Yield 35 MPa min (ISO 527-1 At 23 +/- 2 C 18 kJ/m2 3.5.5.2 Impact Strength, Notched Izod; At -40 +/- 2 C 6.6 kJ/m2 4.3 MATERIAL IDENTIFICATION FOR RECYCLING PURPOSES ABS (ISO 1043/ 11469) ENGINEERING MATERIAL SPECIFICATION WSS-M4D827-B1 Copyright 2013 Ford Global Techn

15、ologies, LLC Page 7 of 8 Table 1: Minimum Sample Size Initial Approval New Manufacturing Location for Previously Approved Material Para. Test Minimum Lots Specimens per Lot Total Test Specimens Lots Specimens per lot Total Test Specimens 3.1 WSS-M99P1111-A 3.1.2 WSS-M99P2222-C1 Total Carbon, Hazardo

16、us Substances, Formaldehyde, Acraldehyde, Acetaldehyde (See below for odor and fogging) 1 1 1 per test 3.3.1 Weathering Resistance 1 1 1 3.4.1 Density 1 3 3 3.4.2 Tensile Strength at Yield* 3 5 15 1 5 5 3.4.3 Elongation at Yield* 3 5 15 1 5 5 3.4.4 Tensile Modulus 1 10 10 3.4.5 Flexural Modulus* 3 1

17、0 30 1 10 10 3.4.6 Impact Strength Notched Charpy (per condition)* 3 10 30 1 10 10 3.4.7 Heat Deflection Temperature* 3 2 6 1 2 2 3.4.8 Vicat Softening Temperature* 3 2 6 1 2 2 3.4.9 Heat Aged Properties 3.4.9.1 Tensile Strength at Yield Change 1 5 5 3.4.9.2 Impact Strength, Notched Charpy Change 1

18、10 10 3.4.10 Odor 1 9 9 3.4.11 Fogging Photometric 1 3 3 3.4.12 Fogging Gravimetric 1 3 3 3.4.13 Flammability 1 5 5 3.5.1 Melt Flow Rate 1 1 1 3.5.2 Coefficient of Linear Thermal Expansion (per condition) 1 3 3 3.5.3 Mold Shrinkage 1 5 5 3.5.4 Poissons Ratio 1 5 5 3.5.5 Impact Strength, Notched Izod

19、 (per condition) 1 10 10 3.5.6 Curves - FTIR - TGA - DSC - CLTE - Engineering Stress/Strain at 23 C 1 1 1 per test * For these requirements the 3 sigma value from the raw data is used to meet the requirements. ENGINEERING MATERIAL SPECIFICATION WSS-M4D827-B1 Copyright 2013 Ford Global Technologies,

20、LLC Page 8 of 8 Table 2: Minimum Color Property Testing 5. SUMMARY OF REVISIONS 2012 05 04 Deleted / EXTERIOR LIGHTING in specification title Deleted or non-direct sunlight exposure in exterior applications in specification scope Deleted and tail lamp housing in para 2. Application Reformatted para

21、3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS VIEQ specification WSS-M99P2222-B1 updated into WSS-M99P2222-C1 Deleted or as specified on the engineering document in para 3.1.4 Performance Criteria Fog number changed from 90 into 70 Impact Strength, Notched Charpy test method revised from ISO 17

22、9-1/2 into ISO 179-1/1eA Corrected remarks after table 1 from * For these requirements, the 3 Sigma value from the raw data is used to set the requirement max or min. into * For these requirements the 3 sigma value from the raw data is used to meet the requirements. Para. Test Method Lots Specimens

23、per Lot Total Test Specimens Color Test Direction 3.3.1 Weathering Resistance 1 1 1 Every color 3.4.2 Tensile Strength at Yield 1 5 5 As directed by Materials Engineering 3.4.5 Flexural Modulus 1 10 10 As directed by Materials Engineering 3.4.6 Impact Strength, Notched Charpy at 23 +/- 2 C 1 10 10 As directed by Materials Engineering 3.4.13 Flammability 1 5 5 Every color 3.4.10 Odor 1 9 9 As directed by Materials Engineering 3.4.12 Fogging Gravimetric 1 3 3 As directed by Materials Engineering