FORD WSS-M2G401-B6-2007 ADHESIVES CYANOACRYLATE (CA) - TO BE USED WITH FORD WSS-M99P1111-A (SHOWN ON FORD WSS-M2G401-B1)《氰基丙烯酸酯（CA）胶粘剂 与标准FORD WSS-M99P1111-A一起使用 列于标准FORD WSS-M.pdf

《FORD WSS-M2G401-B6-2007 ADHESIVES CYANOACRYLATE (CA) - TO BE USED WITH FORD WSS-M99P1111-A (SHOWN ON FORD WSS-M2G401-B1)《氰基丙烯酸酯（CA）胶粘剂 与标准FORD WSS-M99P1111-A一起使用 列于标准FORD WSS-M.pdf》由会员分享，可在线阅读，更多相关《FORD WSS-M2G401-B6-2007 ADHESIVES CYANOACRYLATE (CA) - TO BE USED WITH FORD WSS-M99P1111-A (SHOWN ON FORD WSS-M2G401-B1)《氰基丙烯酸酯（CA）胶粘剂 与标准FORD WSS-M99P1111-A一起使用 列于标准FORD WSS-M.pdf（9页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2007 04 20 Activated G. Kowalski Printed copies are uncontrolled Copyright 2007, Ford Global Technologies, LLC Page 1 of 9 ADHESIVES, CYANOACRYLATE, (CA) WSS-M2G401-B1/B10 1. SCOPE The materials defined by these specifications are a series of

2、solventless, room temperature curing cyanoacrylate adhesives. 2. APPLICATION These specifications were released originally for single component industrial quality adhesives formulated for bonding all metals, most rubbers and many plastics. See attached strategy table for details. LIMITATIONS: Surfac

3、es must be clean, free of oil and debris prior to application. When mixed substrates are used, material selection should be based on maximum bond strength of weakest bond to substrate. I.E. Substrates: EPDM Rubber on Steel. The adhesive bond strength of steel is superior to EPDM Rubber. Therefore, t

4、he material selection should be based on maximum bond strength of the adhesive to EPDM Rubber. B1 Toughened ethyl cyanoacrylate low viscosity adhesive for general filling use, with a 90 second fixturing time. For parts that encounter shock, vibration, or thermal cycling. B2 Thermally resistant ethyl

5、 cyanoacrylate high viscosity adhesive for porous surfaces, with a 360 second fixturing time. Material is thermally resistant up to 121 C. Typical applications: speaker assemblies, automotive components, electrical equipment, oil filters, and disk drives. B3 Thermally resistant ethyl cyanoacrylate g

6、el adhesive for porous surfaces, with a 30 second fixturing time. This is a heat resistant (-53 to 121 C) instant adhesive for vertical or overhead surface applications. B4 Thermally resistant ethyl cyanoacrylate gel adhesive, with a 30 second fixturing time. This is a thermal resistant/thermal cycl

7、ing resistant (-53 to 121 C) instant adhesive for vertical or overhead surfaces . B5 Surface insensitive ethyl cyanoacrylate gel adhesive for porous surfaces, with a 15 second fixturing time. General purpose no-run material that can be applied to vertical surfaces. I ideal use for porous absorbent o

8、r acidic surfaces. B6 Toughened ethyl cyanoacrylate medium viscosity adhesive for clear gap filling, with a 30 second fixturing time. An adhesive formulated for excellent impact and peel strength in gap filling applications. Material bonds well to rubber. Typically used where slower fixture speeds a

9、re required or parts are subjected to shock and vibration. ENGINEERING MATERIAL SPECIFICATIONWSS-M2G401-B1/B10 Printed copies are uncontrolled Copyright 2007, Ford Global Technologies, LLC Page 2 of 9 B7 Low odor/low bloom alkoxy cyanoacrylate gel adhesive for porous surfaces, with a 90 second fixtu

10、ring time. Used where adhesive run-off or drips must be avoided such as glass, vertical, or overhead surfaces. B8 Low odor/low bloom alkoxy cyanoacrylate low viscosity adhesive for close fitting parts, with a 50 second fixturing time. Used for appearance sensitive assemblies such as glass or plastic

11、. B9 Surface insensitive ethyl cyanoacrylate low viscosity adhesive for general purpose applications, with a 5 - 15 second fixturing time Used for bonding porous, absorbent, dry, or acidic surfaces such as: leather, fabric, plastic, and rubber. B10 Surface insensitive ethyl cyanoacrylate low viscosi

12、ty adhesive for general purpose applications, with a 5-15 second fixturing time Used for bonding to vertical or overhead surfaces, porous, absorbent, dry, or acidic surfaces such as: leather, fabric, plastic, and rubber. 3. REQUIREMENTS 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material sup

13、pliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 CONTROL ITEMS Control items must be run on every lot of material, control of these items must be represented in the PFMEA and control plan. After the review and sign-off of the

14、 control documents (PFMEA, CP, and SPC data) for a significant number of lots, the frequency of the testing can be reduced as agreed upon by the Materials Engineering representative. Periodic review of the data is necessary to determine if the process has shifted, retesting of para 4.0 parameters ma

15、y be requested by Materials Engineering if a significant shift has occurred. 3.2.1 Lot to Lot Testing on B1 materials 3.2.1.1 Viscosity, mPas 100 - 200 (BS 5350 Part B8 Physica cone and plate, cone MK22, shear rate 1000s-125 + 0.5 C) 3.2.1.2 Tensile Strength, N/mm2, min 1.8 (ASTM D 1414-03, DIN 5350

16、4 30 sec. RTC, Buna N rubber cord stock TS105) 3.2.1.3 Tensile Shear Heat Aging, N/mm2, min 1.8 (ASTM D 1002-05, ASTM D 3163 ISO 4587, DIN EN1465. Grit blast steel lap shears TS101 Pre-condition lap shears at 70 +/-5% RH for 1 hour. Clamp and cure test specimens at 70 +/- 5% RH) 3.2.1.4 Appearance B

17、lack liquid (ASTM E 284-05) ENGINEERING MATERIAL SPECIFICATIONWSS-M2G401-B1/B10 Printed copies are uncontrolled Copyright 2007, Ford Global Technologies, LLC Page 3 of 9 3.2.2 Lot to Lot Testing on B2 materials 3.2.2.1 Viscosity, mPas 5,000 16,000 (ASTM D 1084, 20 rpm Brookfield HBT, spindle, 3, 25

18、+/- 0.5 C. Perform tests after holding sample 24 hrs at 25 +/- 0.5 C, Run spindle at100 RPM for one minute before making reading) 3.2.2.2 Tensile Shear Hot Strength, N/mm2, min 4.1 (ASTM D 1002-05, ASTM D 3163, ISO 4587, DIN EN 1465. Grit Blast steel lap shears TS101, degreased. Pre-condition lap sh

19、ears at 70 +/- 5% RH for 1 hour) 3.2.2.3 Tensile Shear, Heat Resistance, N/mm2, min 18.6 (ASTM D 1002-05, ASTM D 3163, ISO 4587, DIN EN 1465. Grit blasted steel lap shears TS101, degreased. Pre-condition lap shears at 70 +/- 5% RH for 1 hour. Cure test specimens at 70 +/- 5% RH) 3.2.2.4 Tensile Shea

20、r Al/Al lap shears, N/mm2, min 7.0 (ASTM D 1002-05, ASTM D 3163, ISO 4587, DIN EN 1465. Aluminum lap shears TS021, as received) 3.2.2.5 Tensile Shear 48 hr RTC, N/mm2, min 13.8 (ASTM D 1002-05, ASTM D 3163 ISO 4587, DIN EN1465. Grit blast steel lap shears TS101, degreased. Pre-condition lap shears a

21、t 70 +/- 5% RH for 1 hour. Cure test specimens at 70 +/- 5% RH) 3.2.2.6 Appearance Black liquid (ASTM E 284-05) 3.2.3 Lot to Lot Testing on B3 materials 3.2.3.1 Viscosity, mPas 10,000 to 60,000 (ASTM D 1084, 20 rpm Brookfield RVT, spindle TC, helipath at 25 +/- 0.5 C) 3.2.3.2 Tensile Shear Hot Stren

22、gth, N/mm2, min 5.6 (ASTM D 1002-05, ASTM D 3163, ISO 4587, DIN EN 1465. Grit Blasted steel lap shears TS101) 3.2.3.3 Appearance Colorless to (ASTM E 284-05) slightly pale ENGINEERING MATERIAL SPECIFICATIONWSS-M2G401-B1/B10 Printed copies are uncontrolled Copyright 2007, Ford Global Technologies, LL

23、C Page 4 of 9 3.2.4 Lot to Lot Testing on B4 materials 3.2.4.1 Viscosity, mPas 18,000 to 45,000 (ASTM D 1084, 20 rpm Brookfield RVT, spindle TC, Helipath at 25 +/- 0.5 C) 3.2.4.2 Tensile Shear Heat Resistance, N/mm2, min 9.0 (ASTM D 1002-05, ASTM D 3163, ISO 4587, DIN EN 1465. Grit Blast steel lap s

24、hears TS101) 3.2.4.3 Appearance Transparent, (ASTM E 284-05) colorless gel 3.2.5 Lot to Lot Testing on B5 materials 3.2.5.1 Viscosity, mPas 18,000 to 40,000 (ASTM D 1084, 20 rpm, Brookfield RVT, spindle TC, helipath. Perform tests after holding sample 48 hrs at 25 +/- 0.5 C) 3.2.5.2 Viscosity, mPas

25、100,000 to 300,000 (ASTM D 1084, 2.5 rpm, Brookfield RVT, spindle TC, helipath. Perform tests after holding sample 48 hours at 25 +/- 0.5 C) 3.2.5.3 Viscosity, mPas 100 to 300 (BS EN ISO 3219, on down curve Casson, Physica MC 100 cone and plate, cone MK22. Equivalent rheometers/cones may be used at

26、25 +/- 0.5 C) 3.2.5.4 Tensile Strength, N/mm2, min 6.0 (ASTM D 1414-03, DIN 53504 10 sec RTC, Buna N rubber) 3.2.5.5 Appearance Clear to slightly (ASTM E 284-05) cloudy gel 3.2.6 Lot to Lot Testing on B6 materials 3.2.6.1 Viscosity, mPas 4,000 to 8,000 (ASTM D 1084, 20 rpm Brookfield RVT, spindle TC

27、, Helipath, at 25 +/- 0.5 C) 3.2.6.2 Tensile Shear Hot Strength, N/mm2, min 8.3 (ASTM D 1002-05, ASTM D 3163, ISO 4587, DIN EN 1465. Grit blasted steel lap shears TS101) ENGINEERING MATERIAL SPECIFICATIONWSS-M2G401-B1/B10 Printed copies are uncontrolled Copyright 2007, Ford Global Technologies, LLC

28、Page 5 of 9 3.2.6.3 Appearance Water white to (ASTM E 284-05) slightly cloudy gel 3.2.7 Lot to Lot Testing on B7 materials 3.2.7.1 Viscosity, mPas 10,000 to 26,000 (ASTM D 1084, 20 rpm Brookfield RVT, spindle TC, Helipath, at 25 +/- 0.5 C) 3.2.7.2 Tensile Shear 24 hrs RTC, 0 gap, N/mm2, min 9.7 (AST

29、M D 1002-05, ASTM D 3163, ISO 4587, DIN EN 1465. Grit blasted steel lap shears TS101. Pre-condition lap shears at 70 +/- 5% RH for 1 hour. Clamp and cure test specimens at 70 +/- 5% RH) 3.2.7.3 Appearance Transparent, (ASTM E 284-05) colorless to light cloudy gel 3.2.8 Lot to Lot Testing on B8 mater

30、ials 3.2.8.1 Viscosity, mPas 25 to 55 (BS 5350 Part B8, 3000s-1, Physica cone plate, viscosity, 25 +/- 0.5 C. Age in natural 20g CA bottle or approved equivalent) 3.2.8.2 Tensile Strength, N/mm2, min 4.5 (ASTM D 1414-03, DIN 53504, 10 sec RTC, Buna N rubber cord stock TS105) 3.2.8.3 Appearance Trans

31、parent, (ASTM E 284-05) colorless to straw colored liquid 3.2.9 Lot to Lot Testing on B9 materials 3.2.9.1 Viscosity, mPas 70 to 130 (BS 5350 Part B8, 3000s-1, Physica cone & plate, cone MK22 300s-1, at 25 +/-0.5 C) 3.2.9.2 Tensile Strength, N/mm2, min 6.0 (ASTM D 1414-03, DIN 53504, 10 sec RTC, Bun

32、a N rubber cord stock TS105) 3.2.9.3 Appearance Transparent, (ASTM E 284-05) colorless to straw colored liquid ENGINEERING MATERIAL SPECIFICATIONWSS-M2G401-B1/B10 Printed copies are uncontrolled Copyright 2007, Ford Global Technologies, LLC Page 6 of 9 3.2.10 Lot to Lot Testing on B10 materials 3.2.

33、10.1 Viscosity, mPas 50,000 200,000 (BS 5350 Part B8, 1s-1, Physica MC100 cone and plate, cone MK22. Equivalent rheometers/ cones may be used. (Ref. STM740 for details) 3.2.10.2 Viscosity, mPas 3,500 10,000 (BS 5350 Part B8, 20s-1, Physica MC100 cone and plate, cone MK22. Equivalent rheometers/ cone

34、s may be used. (Ref. STM740 for details) 3.2.10.3 Tensile Strength, N/mm2, min 6.0 (ASTM D 1414-03, DIN 53504, 30 sec. RTC, Buna N rubber. Pre-condition specimens at 70 +/- 5% RH for one hour. Record specimen lot number) 3.2.10.4 Appearance Clear to slightly (ASTM E 284-05) cloudy gel 4. MATERIAL PR

35、OPERTIES Material properties items must be determined from a lot of material where the manufacturing process is under statistical control. Once these parameters are established no annual recertification is necessary unless the process has shifted. A materials engineering representative may request i

36、ndividual retests on an “as needed“ basis. The information below is provided for clarification and assistance in meeting the requirements of these specifications. 4.1 SHEAR STRENGTH, Original Properties, PSI (ASTM D 1002) Averaged Data for Various Cyanoacrylate Adhesives on Aluminum Substrates050010

37、 0 0150 0200025003000B1 B2 B3 B4 B5 B6 B7 B8 B9 B10Recommended products above lineAveraged Shear Strength Data for Various Cyanoacrylate Adhesives on Steel Substrates010 0 02000300040005000B1 B2 B3 B4 B5 B6 B7 B8 B9 B10Recommended products above lineENGINEERING MATERIAL SPECIFICATIONWSS-M2G401-B1/B1

38、0 Printed copies are uncontrolled Copyright 2007, Ford Global Technologies, LLC Page 7 of 9 Averaged Shear Strength at Peak of Various Cyanoacrylate Adhesives on Unfilled Poypropylene05010 0150200B1 B2 B3 B4 B5 B6 B7 B8 B9 B10Recommended products above lineAveraged Shear Strength at Peak of Various

39、Cyanoacrylate Adhesives on 30% Glass Filled Polypropylene010 0200300400B1 B2 B3 B4 B5 B6 B7 B8 B9 B10Recommended products above lineAveraged Shear Strength at Peak Values for Various Cyanoacrylate Adhesives on 40% Talc Filled Polypropylene010 0200300400500B1 B2 B3 B4 B5 B6 B7 B8 B9 B10Recommended pr

40、oducts above lineAveraged Shear Strength Data for Various Cyanoacrylate Adhe s ive s on EPDM Rubbe r02040608010 012 0B1 B2 B3 B4 B5 B6 B7 B8 B9 B10Recommended products above lineENGINEERING MATERIAL SPECIFICATIONWSS-M2G401-B1/B10 Printed copies are uncontrolled Copyright 2007, Ford Global Technologi

41、es, LLC Page 8 of 9 4.2 SHEAR STRENGTH AFTER THERMAL CYCLING, % change, max (ASTM D 1002) Thermal Cycle Aging Effect on Various Cyanoacrylate Adhesives Substrate: Steel on Steel-100.00-50.000.0050.00100.00B1 B2 B3 B4 B5 B6 B7 B8 B9 B10ShearStrength(%Change)4.3 SHEAR STRENGTH AFTER HUMIDITY AGING, %

42、Change, max (ASTM D 1002, 12 weeks at 40 C/95% Relative Humidity) Effect on Shear Strength of Various Cyanoacrylate Adhesives Aged at 40C/95% Relative Humidity Substrates: Steel on Steel-120.00-80.00-40.000.0040.0080.00120.00B1 B2 B3 B4 B5 B6 B7 B8 B9 B10ShearStrength(%Change)6 WEEKS12 WEEKS4.4 SHEA

43、R STRENGTH AFTER HEAT AGING, % Change, max (ASTM D 1002, 12 weeks at 80 C) Heat Aged Effect on Shear Strength of Various Cyanoacrylate Adhesives Aged at 80C Substrate: Steel on Steel-150.00-100.00-50.000.0050.00100.00B1 B2 B3 B4 B5 B6 B7 B8 B9 B10ShearStrength(%Change)6 w eeks12 w eksENGINEERING MATERIAL SPECIFICATIONWSS-M2G401-B1/B10 Printed copies are uncontrolled Copyright 2007, Ford Global Technologies, LLC Page 9 of 9 4.5 SHELF LIFE 12 months from date of manufacture when stored in sealed unopened containers out of direct sunlight at a temperature of 4 +/- 2 C. ATTACHMENT