FORD WSB-M4A177-A-2012 WIRE SILICON BRONZE BRAZING TO BE USED WITH FORD WSS-M99P1111-A .pdf

《FORD WSB-M4A177-A-2012 WIRE SILICON BRONZE BRAZING TO BE USED WITH FORD WSS-M99P1111-A .pdf》由会员分享，可在线阅读，更多相关《FORD WSB-M4A177-A-2012 WIRE SILICON BRONZE BRAZING TO BE USED WITH FORD WSS-M99P1111-A .pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions Rev. 4 2012 09 12 Revised Editorial comment added A. Wexler, NA 2012 06 27 Re-activated Still used for purchase A. Wedepohl, NA 1990 06 28 NB00E10040016003 Released R Moore NAAO, N. Riley EAO Controlled document at www.MATS Copyright 2012, Fo

2、rd Global Technologies, Inc. Page 1 of 2 WIRE, SILICON BRONZE, BRAZING WSB-M4A177-A 1. SCOPE The material defined by this specification is a silicon bronze (copper silicon) brazing wire. 2. APPLICATION This specification was released originally for material used as a consumable electrode in combinat

3、ion with inert gas shielding with argon, helium, or mixtures of the two. The specification number is released as a part number for Ford purchasing to obtain braze wire. 3. REQUIREMENTS 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Compan

4、ys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 CHEMICAL COMPOSITION (Inductively coupled plasma emission spectroscopy) Weight percent Lead 0.02 max Iron 0.50 max Tin 0.2 max Zinc 0.4 max Aluminum 0.01 max Manganese 0.5 - 1.5 Silicon 2.8 - 3.0 Other 0.50 max Phosphorus 0.05 m

5、ax Copper Remainder Total other 0.50 Materials meeting these requirements comply with the composition requirements in: AWS A 5.7 ER CuSi-A ISO 24373 - Cu 6560 (CuSi3Mn1) Note: The limits listed above are derived from the more restrictive standard (AWS or ISO) for each element. The only Ford specific

6、 requirement is the lowering of the allowable silicon content from 4 to 3% to improve paint adhesion and corrosion performance of the weld area on painted parts. Reduced silicon content also promotes lower porosity in laser brazed joints. ENGINEERING MATERIAL SPECIFICATION WSB-M4A177-A Copyright 201

7、2, Ford Global Technologies, Inc. Page 2 of 2 3.3 SURFACE FINISH Wire furnished to this specification shall have a smooth finish, free from compounds or other materials detrimental to quality brazing and/or brazing equipment. 3.4 PERFORMANCE This specification is a material specification only and do

8、es not cover the application specific performance requirements given in engineering specifications for the welding process, engineering drawings or manufacturing control plans. Performance requirements and appropriate validation tests will be agreed and approved by the responsible product design and

9、 manufacturing engineering activities. 4. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. Contact for questions concerning Engineering Material Specifications. 4.1 These brazing wires should have a nomin

10、al diameter random wound and/or precision wound (level layer), as specified on the purchase order. 5. SUMMARY OF REVISIONS 2012 09 12 Added comment about lower porosity in laser brazed joints to 3.2. 2012 06 27 Re-activated, as specification was still used by Purchasing. Moved Size requirement to General Info. Revised composition limits to include both AWS and ISO limits. 2012 03 13 In-activated specification. No Ford replacement