FORD ESF-M3G156-A2-1992 TAPE GLASS CLOTH PRESSURE SENSITIVE THERMOSETTING ELECTRICAL 200 C (Shown on ESF-M3G156-A)《200℃电气用热固压敏玻璃布胶带 列于标准ESF-M3G156-A上》.pdf

《FORD ESF-M3G156-A2-1992 TAPE GLASS CLOTH PRESSURE SENSITIVE THERMOSETTING ELECTRICAL 200 C (Shown on ESF-M3G156-A)《200℃电气用热固压敏玻璃布胶带 列于标准ESF-M3G156-A上》.pdf》由会员分享，可在线阅读，更多相关《FORD ESF-M3G156-A2-1992 TAPE GLASS CLOTH PRESSURE SENSITIVE THERMOSETTING ELECTRICAL 200 C (Shown on ESF-M3G156-A)《200℃电气用热固压敏玻璃布胶带 列于标准ESF-M3G156-A上》.pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATIONMaterial Name Specification NumberDate Release No. Release/Revision1992 07 16 DF00E00107002194 Revised para 3.6 A. Vallabhanath1992 06 15 DF00E00107002176 Added -A2 & Updated A. Vallabhanath1988 09 15 167002-185-CF4S Released J. HuebnerWP 3948-a Page 1 of 3 TAPE, G

2、LASS CLOTH, PRESSURE SENSITIVE ESF-M3G156-ATHERMOSETTING, ELECTRICAL, 155 CTAPE, GLASS CLOTH, PRESSURE SENSITIVE ESF-M3G156-A2THERMOSETTING, ELECTRICAL, 200 C1. SCOPEThe mate rials defined by these specifications are glass cloth tapes withthermosetting, pressure sensitive adhesive.ESF-M3G156-A is ra

3、ted for continuous separation at 155 C.ESF-M3G156-A2 is rated for continuous operation at 200 C.2. APPLICATIONThese s pecifications were released originally for materials used in theignition coil and alternator.3. REQUIREMENTS3.1 STATISTICAL PROCESSSupplie rs must conform to the requirements of Ford

4、 Quality SystemStand ard Q-101. A mutually acceptable Control Plan as describedtherein is required for material/source approval. Appropriatestatist ical tools must be used to analyze process/product data sothat variation in the final product is continuously reduced.3.2 INFRARED SPECTROPHOTOMETRY AND

5、/OR THERMAL ANALYSISFord Motor Company, at its option, may conduct infrared and/ortherma l analysis of material/parts supplied to this specification.The IR spectra and thermograms established for i nitial approval shallconst itute the reference standard and shall be kept on file at thedesignated mat

6、erial laboratory. All samples sha ll produce IR spectraand thermograms that correspond to the reference standard when testedunder the same conditions.3.3 CONDITIONING AND TEST CONDITIONSAll test values indicated herein are based on ma terial conditioned ina control led atmosphere of 23 +/- 2 C and 5

7、0 +/- 5 % relativehumidity for not less than 24 h prior to testing and tested under thesame conditions unless otherwise specified.ENGINEERING MATERIAL SPECIFICATIONESF-M3G156-A ESF-M3G156-A2WP 3948-b Page 2 of 3 3.4 CONSTRUCTIONThese materials shall consist of a glass cloth, coated on one sidewith a

8、 noncorrosive thermosetting and pressure sensitive adhesive.3.4.1 Adhesive TypeESF-M3G156-A Rubber or AcrylicESF-M3G156-A2 Silicone3.5 THICKNESS 0.165 - 0.216 mm(ASTM D 1000)A A23.6 BREAKING STRENGTH, N/mm width, min 21 22(ASTM D 1000)Ultimate Elongation, %, min 3.0 5.0Test Me thod: This shall be me

9、asured coincidentally with breakingstrength.Ultimate Elongation = (L2 - L1)/L1 x 100Where: L1 = Original LengthL2 = Length at Break3.7 DIELECTRIC STRENGTH AT 23 +/- 2 C(ASTM D 1000)Total Thickness Reading, kV, min 1.5 3.03.8 ADHESION TO STEEL, N/m width, min 219 320(ASTM D 1000)3.9 ADHESION TO BACKI

10、NG, N/m width, min 120 200(ASTM D 1000)3.10 COPPER CORROSION(FLTM BU 106-01)No ev idence of the characteristic green color of cupric chlorideand/or the characteristic blue-black color of copper sulfide on thecopper plates.3.11 CHLORIDES, ppm, max 64 100(ASTM D 202)3.12 pH 6.5 - 7.5 6.5 - 7.5(ASTM D

11、202)ENGINEERING MATERIAL SPECIFICATIONESF-M3G156-A ESF-M3G156-A2WP 3948-b Page 3 of 3 3.13 THERMOSETTING VALUE, h, min 2 72(FLTM BU 107-01, 0.5 kg weight)3.14 SUPPLIERS RESPONSIBILITYAll materials supplied to this specification must be equivalent inal l characteristics to the material upon which app

12、roval wasoriginally granted.Pri or to making any change in the properties, composition,constr uction, color, processing or labeling of the materialorig inally approved under this specification, whether or not suchchange s affect the materials ability to meet the specificationrequir ements, the Suppl

13、ier shall notify Purchasing, Toxicology andthe affected Materials Engineering activity of the proposed changesand obtain the written approval of the Materials Engineeringactivity. Test data, t est samples and a new code identification areto be submitted with the request.Substance restrictions impose

14、d by law, regulations or Ford, apply tothe materials addressed by this document. The restrictions aredefined in Engineering Material Specification WS S-M99P9999-A1, unlessa different suffix (e.g., A2 or A3) is specified on the engineeringdocument for the application.4. APPROVAL OF MATERIALSMat erial

15、s defined by this specification must have prior approval by theresponsible Materials Engineeri ng activity. Suppliers desiring approval ofthe ir materials shall first obtain an expression of interest from theaffec ted Purchasing, Design and Materials Engineering activity. Uponrequest, the Supplier s

16、hall submit to the affected Materials Engineeringactivity a completed copy of their laboratory test reports, signed by aqualified and authorized representative of the test faci lity, demonstratingful l compliance with all the requirements of this specification (testresults, not nominal values), the

17、material designation a nd code number, andtes t specimens for Ford evaluation. Fords engineering approval of amateri al will be based on its performance to this specification and on anassessment of suitability for i ntended processes and/or applications. Uponapprov al, the material will be added to the Engineering Material ApprovedSource List.