FORD ESE-M8G164-A-2012 GASKET CELLULOSE SYNTHETIC RUBBER AND RESIN TO BE USED WITH FORD WSS-M99P1111-A .pdf

《FORD ESE-M8G164-A-2012 GASKET CELLULOSE SYNTHETIC RUBBER AND RESIN TO BE USED WITH FORD WSS-M99P1111-A .pdf》由会员分享，可在线阅读，更多相关《FORD ESE-M8G164-A-2012 GASKET CELLULOSE SYNTHETIC RUBBER AND RESIN TO BE USED WITH FORD WSS-M99P1111-A .pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATION Material Name Specification Number Date Para No. Revisions Rev 02 2012 05 07 N Status No usage or replacement N. Benipal, NA 1983 03 18 3.2 Was 67-77 kg/m3 , English units deleted CE3M-RD863100-E #69 1981 11 02 Released CE3L-RD863100-E Supp. #36 Page 1 of 3 GASKET

2、, CELLULOSE/SYNTHETIC RUBBER AND RESIN ESE-M8G164-A NOT TO BE USED FOR NEW DESIGN 1. SCOPE: The material defined by this specification is a moderate temperature heat insulating material composed of cellulose fibers, synthetic rubber and resins. This material is asbestos free. 2. APPLICATION: This sp

3、ecification was released originally for material used as a spacer gasket between the carburetor and intake manifold when the temperature will not exceed 150 C. 3. REQUIREMENTS: All tests shall be conducted in accordance with ASTM F 104, Type 3 material or SAE J 90 unless otherwise specified. Test sp

4、ecimens are to be selected from finished gaskets when practicable. Specimens used for fluid properties should not be cut or trimmed prior to exposure. 3.1 CONSTRUCTION The spacer-gasket consists of a cellulose board reinforced with an SBR rubber or NBR/phenolic resin binder, coated on all the outer

5、edges and sides with nitrile rubber and with all the bolt holes reinforced with phenolic bushing. The gasket is also coated with a release agent. 3.2 DENSITY, min 720 - 832 kg/m3 (Type 2) 3.3 COMPRESSIBILITY 8 - 20% (ASTM F 36, 34.5 MPa load) Recovery, min 50% 3.4 TENSILE STRENGTH, min 10.3 MPa 3.5

6、HEAT AGING (22 h at 150 C) Weight Change, % -2 to -8 Tensile Change, % 0 to -20 ENGINEERING MATERIAL SPECIFICATION ESE-M8G164-A Page 2 of 3 Test Method: Place 3 weight change samples 25 x 51 mm x sample thickness or any sample size which is practicable between 100 x 125 x 13 mm steel plates. Place i

7、n furnace set at 150 C for 22 h. Cool and test. 3.6 LIQUID IMMERSION ASTM ASTM Distilled 80% Fuel C (22 h at 23 +/- 2 C) Fuel C #3 Oil Water 2% EtOH Thickness Change, % 0 to +6 0 to +4 0 to +40 0 to +22 Weight Change, % +25 to +52 +10 to +36 0 to +40 +40 to +72 3.7 SURFACE COATING Minimum amount of

8、sticking and tearing with no evidence of corrosion . Metal Plates . Aluminum to Aluminum . Aluminum to Steel . Steel to Steel Test Method: A 15.9 mm I.D. x 38.1 mm O.D. test specimen is clamped between 2 discs of 13.5 mm I.D. x 51 mm O.D. metal plates (maximum thickness 1.57 mm) backed by 12.7 mm st

9、eel plates. A 12.7 mm steel bolt is inserted through the hole and a nut put on it. Tighten the bolt to 79 N.m. Heat the assembly to 149 +/- 3 C for 5 h. Remove and allow to cool to room temperature. The specimen shall come off the metal plates with a minimum of tearing and the metal plates must show

10、 no evidence of corrosion. 3.8 PHENOLIC BUSHINGS 3.8.1 Compressive Strength, min 69 MPa (ASTM D 695) 3.8.2 Deflection at 69 MPa, max 10% (ASTM D 695) 3.8.3 Removal Force From Gasket, min 378 N 3.8.4 Density, min 1394 kg/m3 (ASTM D 792) 3.9 INFRARED SPECTROPHOTOMETRY AND/OR THERMAL ANALYSIS Ford Moto

11、r Company, at its option, may conduct infrared and/or thermal analysis of material/parts supplied to this specification. The curves established for initial approval shall constitute the reference standard and shall be kept on file at Central Laboratory. All samples shall produce curves that correspo

12、nd to the reference standard when tested under the same conditions as those specified on the master curve. ENGINEERING MATERIAL SPECIFICATION ESE-M8G164-A Page 3 of 3 3.10 SUPPLIERS RESPONSIBILITY Material supplied to this specification must be equivalent to that originally approved. Changes in form

13、ulation or processing shall not be made without prior approval as described in Supplier Procedure I-A. 4. APPROVAL OF SUPPLIERS: Suppliers to this specification must be approved by the affected product engineering office. Procedure for gaining approval of a specific material to a new/existing ES-M specification is contained in Supplier Procedure I-A. Approved new suppliers will be added to the Engineering Materials Approved Source List.