FORD ESB-M99D43-A-2009 POLYPROPYLENE 50% WOOD FIBER FILLED - EXTRUDED COMPOSITE TO BE USED WITH FORD WSS-M99P1111-A 《50%木纤维填充的聚丙烯(PP)挤压复合材料 与标准FORD WSS-M99P1111-A一起使用 [使用 FORD .pdf

《FORD ESB-M99D43-A-2009 POLYPROPYLENE 50% WOOD FIBER FILLED - EXTRUDED COMPOSITE TO BE USED WITH FORD WSS-M99P1111-A 《50%木纤维填充的聚丙烯(PP)挤压复合材料 与标准FORD WSS-M99P1111-A一起使用 [使用 FORD .pdf》由会员分享，可在线阅读，更多相关《FORD ESB-M99D43-A-2009 POLYPROPYLENE 50% WOOD FIBER FILLED - EXTRUDED COMPOSITE TO BE USED WITH FORD WSS-M99P1111-A 《50%木纤维填充的聚丙烯(PP)挤压复合材料 与标准FORD WSS-M99P1111-A一起使用 [使用 FORD .pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2009 01 22 A - N-STATUS A Replaced by ESB-M99D43-B L. Sinclair, FNA 2006 11 15 Revised Inserted 3.0; Deleted 3.1, 3.17, 3.21 & 4 1982 01 22 Released Released ESB-M99D43-A EM1-6000-79 Printed copies are uncontrolled Copyright 2009, Ford Global

2、Technologies, LLC Page 1 of 3 POLYPROPYLENE, 50% WOOD FIBER FILLED- NOT TO BE USED FOR NEW DESIGN ESB-M99D43-A EXTRUDED COMPOSITE ESB-M99D43-B 1. SCOPE The material defined by these specifications is an extruded grade of wood fiber filled polypropylene for vacuum or match metal die molding. 2. APPLI

3、CATION ESB-M99D43-A was released originally for material used as a molded package tray foundation in the 1983 Escort/Lynx carlines. ESB-M99D43-B was released originally for material used as a molded trunkliner foundation in the 1986 Taurus/Sable. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCT

4、ION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 THICKNESS As specified on engineering drawings 3.3 COMPOSITION The composition is primarily wood fiber and polypropylene with a talc filler and a smal

5、l amount of polyethylene as a carrier for the carbon black. The composition shall be the same as originally approved as determined under para 3.17. 3.4 ASH CONTENT 6 +/- 4% (ASTM D 586) 3.5 DENSITY 1.03 +/- 0.08 g/cm3(SAE J315, Avg. of 3) 3.6 WATER ABSORPTION, max 2% (SAE J 315, 24 h immersion, avg.

6、 of 3) 3.7 WARPAGE, max (SAE J 315, avg. of 3 tests, % change from original) . After 24 h H20 immersion 2% . 24 h H20 immersion followed 5% by 24 h at 88 C (measure at 88 C) ENGINEERING MATERIAL SPECIFICATION ESB-M99D43-AESB-M9D43-BPrinted copies are uncontrolled Copyright 2009, Ford Global Technolo

7、gies, LLC Page 2 of 3 3.8 DIMENSIONAL STABILITY, max (SAE J 315, Methods B and/or C, avg. of 3) After 24 h H20 0.1% After 24 h H20 followed by 24 h at 88 C 0.2% After 24 h at 88 C only (measure at 88 C) 0.5% 3.9 FLEXURAL STRENGTH (ASTM D 790, avg. of 5) MD 49.9 +/- 11.6 MPa AMD 40.0 +/- 11.0 MPa 3.1

8、0 FLEXURAL MODULUS OF ELASTICITY, TANGENT (ASTM D 790, avg. of 5) MD 3.93 +/- 0.78 GPa AMD 2.81 +/- 0.69 GPa 3.11 TENSILE STRENGTH (ASTM D 638, avg. of 5) MD 21.7 +/- 4.3 MPa AMD 15.7 +/- 2.9 MPa 3.12 TENSILE ELONGATION AT BREAK (ASTM D 638, avg. of 5) MD 1.9 +/- 0.7% AMD 1.7 +/- 0.9% 3.13 TENSILE M

9、ODULUS OF ELASTICITY (YOUNGS) (ASTM D 638, avg. of 5) MD 3.4 +/- 0.9 GPa AMD 2.8 +/- 0.8 GPa 3.14 HARDNESS, ROCKWELL “R“ 92 +/- 8 (ASTM D785, avg. of 5) 3.15 DEFLECTION TEMPERATURE, min (ASTM D 648, 13 mm sample width) At 455 kPa At 1820 kPa MD 115 C 80 C AMD 115 C 70 C 3.16 HEAT AGING - LONG TERM N

10、o more than 30% loss in (88 +/- 3 C for 1000 h) tensile strength ENGINEERING MATERIAL SPECIFICATION ESB-M99D43-AESB-M9D43-BPrinted copies are uncontrolled Copyright 2009, Ford Global Technologies, LLC Page 3 of 3 3.18 ESB-M99D43-A FLAMMABILITY In order to comply with Federal Motor Vehicle Safety Sta

11、ndard No. 302, the material portions of components and composites shall not burn, or transmit a flame across its surface, at a rate of more than 101 mm per minute. To demonstrate compliance, the sample size and method of testing shall be in accordance with FLTM BN 024-02. 3.19 ESB-M99D43-B FLAMMABIL

12、ITY, max 101 mm/min (FLTM BN 024-02, without lot sampling plan) In addition, the test specimen shall not exhibit any flashing or sudden flaming on either surface in excess of the above max value. 3.20 FLAMMABILITY TEST PROGRAM Materials, portions of components, and composites governed by this specif

13、ication must also comply with the requirements of ES-D3AB-11014-AA. 5. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of these specifications. 5.1 IMPACT STRENGTH, IZOD, MIN (ASTM D 256) Notched Unnotched MD 29 J/m 71 J/m AMD

14、20 J/m 44 J/m 5.2 A suitable film may be laminated to one or both sides of the extruded product to facilitate bonding. 5.3 Small holes occurring in formed parts made of this material may be repaired by filling in with molten, unbacked polypropylene fiber (ESB-M3H36-A, ESB-M3H48-B, or equivalent). The appearance of the trimmed side of the part shall not be affected. In addition, the repair shall not adversely affect the material properties of this specification.