DLA MIL-DTL-32373 D-2011 PLUG MACHINE THREAD MAGNETIC DRAIN [Superseded DLA MS35844 REV D CANC NOTICE 5 DLA MS35844 REV D VALID NOTICE 4 DLA MS35844 REV D NOTICE 3 DLA MS35844 REV .pdf

《DLA MIL-DTL-32373 D-2011 PLUG MACHINE THREAD MAGNETIC DRAIN [Superseded DLA MS35844 REV D CANC NOTICE 5 DLA MS35844 REV D VALID NOTICE 4 DLA MS35844 REV D NOTICE 3 DLA MS35844 REV .pdf》由会员分享，可在线阅读，更多相关《DLA MIL-DTL-32373 D-2011 PLUG MACHINE THREAD MAGNETIC DRAIN [Superseded DLA MS35844 REV D CANC NOTICE 5 DLA MS35844 REV D VALID NOTICE 4 DLA MS35844 REV D NOTICE 3 DLA MS35844 REV .pdf（9页珍藏版）》请在麦多课文档分享上搜索。

1、Comments, suggestions, or questions on this document should be addressed to Defense Logistics Agency Aviation VEB, 8000 Jefferson Davis Highway, Richmond, VA 23297-5616, or e-mailed to STDZNMGTdla.mil. Since contact information can change, you may want to verify the currency of this address informat

2、ion using the ASSIST database at https:/assist.daps.dla.mil/. AMSC N/A FSC 5365 INCH-POUND MIL-DTL-32373 27 January 2011 SUPERSEDING MS35844D 23 February 1978 DETAIL SPECIFICATION PLUG, MACHINE THREAD, MAGNETIC: DRAIN This specification is approved for use by all Departments and Agencies of the Depa

3、rtment of Defense. 1. SCOPE 1.1 Scope. This specification covers two types of machine thread magnetic drain plugs used to seal engine oil lubrication systems and to capture ferrous contaminants in engine oil. 1.2 Classification. The machine thread magnetic drain plugs are of the following types as s

4、pecified below: Type I - External hexagonal (hex) head Type II - External hex head with 3/4-inch square drive 1.3 Part or identifying number (PIN). The PIN to be used for drain plugs acquired to this specification is created as follows (see 6.2): MS 35844 - XXX X Example of reference part number: MS

5、35844-83A Protective finish: A - Zinc B - Cadmium, when required by the contract (see 6.2) C - Anodized Dash number (see tables I and II) Specification number MS prefix (retaining MS part number) Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-DT

6、L-32373 2 2. APPLICABLE DOCUMENTS 2.1 General. The documents listed in this section are specified in sections 3 and 4 of this specification. This section does not include documents cited in other sections of this specification or recommended for additional information or as examples. While every eff

7、ort has been made to ensure the completeness of this list, document users are cautioned that they must meet all specified requirements of the documents cited in sections 3 and 4 of this specification, whether or not they are listed. 2.2 Government documents. 2.2.1 Specification and standards. The fo

8、llowing specification and standards form a part of this document to the extent specified herein. Unless otherwise specified, the issues of these documents are those cited in the solicitation or contract. FEDERAL STANDARD FED-STD-H28 - Screw-Thread Standards for Federal Services DEPARTMENT OF DEFENSE

9、 SPECIFICATION MIL-A-8625 - Anodic Coatings for Aluminum and Aluminum Alloys DEPARTMENT OF DEFENSE STANDARD MIL-STD-130 - Identification Marking of U.S. Military Property (Copies of these documents are available online at https:/assist.daps.dla.mil/ or from the Standardization Document Order Desk, 7

10、00 Robbins Avenue, Building 4D, Philadelphia, PA 19111-5094.) 2.3 Non-government publications. The following documents form a part of this document to the extent specified herein. Unless otherwise specified, the issues of these documents are those cited in the solicitation or contract. AMERICAN SOCI

11、ETY FOR QUALITY ASQ Z1.4 - Sampling Procedures and Tables for Inspection by Attributes (Copies of this document are available online at http:/www.asq.org or from the American Society for Quality, 600 North Plankinton Avenue, Milwaukee, WI 53023.) Provided by IHSNot for ResaleNo reproduction or netwo

12、rking permitted without license from IHS-,-,-MIL-DTL-32373 3 AMERICAN SOCIETY OF MECHANICAL ENGINEERS ASME B46.1 - Surface Texture (Surface Roughness, Waviness, and Lay) (Copies of this document are available online at http:/www.asme.org or from the American Society of Mechanical Engineers, Three Pa

13、rk Avenue, New York, NY 10016-5990.) ASTM INTERNATIONAL ASTM A29/A29M - Standard Specification for Steel Bars, Carbon and Alloy, Hot-Wrought, General Requirements for ASTM A47/A47M - Standard Specification for Ferritic Malleable Iron Castings ASTM A108 - Standard Specification for Steel Bar, Carbon

14、and Alloy, Cold-Finished ASTM B211 - Standard Specification for Aluminum and Aluminum-Alloy Bar, Rod, and Wire ASTM B633 - Standard Specification for Electrodeposited Coatings of Zinc on Iron and Steel (Copies of these documents are available online at http:/www.astm.org or from ASTM International,

15、100 Barr Harbor Drive, P.O. Box C700, West Conshohocken, PA 19428-2959.) INTERNATIONAL MAGNETICS ASSOCIATION MMPA 0100 - Standard Specification for Permanent Magnet Materials (Copies of this document are available online at http:/www.intl-magnetics.org or from the International Magnetics Association

16、, 8 South Michigan Avenue, Suite 1000, Chicago, IL 60603-3452.) SAE INTERNATIONAL SAE AMS-QQ-P-416 - Plating, Cadmium (Electrodeposited) SAE AS35769 - Gasket, Metallic, Encased, Annular, Copper SAE J532 - Automotive Straight Thread Filler and Drain Plugs (Copies of these documents are available onli

17、ne at http:/www.sae.org or from SAE International, 400 Commonwealth Drive, Warrendale, PA 15096-0001.) 2.4 Order of precedence. Unless otherwise noted herein or in the contract, in the event of a conflict between the text of this document and the references cited herein, the text of this document ta

18、kes precedence. Nothing in this document, however, supersedes applicable laws and regulations unless a specific exemption has been obtained. Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-DTL-32373 4 3. REQUIREMENTS 3.1 Materials. 3.1.1 Machine

19、thread drain plug body. Materials used in the manufacture of the machine thread drain plug body shall be as specified in 3.1.1.1 through 3.1.1.3. 3.1.1.1 Carbon steel. Carbon steel shall conform to compositional grade designations 1011 through 1025 in accordance with ASTM A29/A29M. Dimensional requi

20、rements for steel stock shall conform to ASTM A108. 3.1.1.2 Aluminum alloy. Aluminum alloy shall conform to chemical composition 2011, temper T3, or composition 2017, temper T4, in accordance with ASTM B211. 3.1.1.3 Malleable iron. Malleable iron shall conform to grade 32510 in accordance with ASTM

21、A47/A47M. 3.1.2 Protective finishes. 3.1.2.1 Carbon steel and malleable iron. Drain plugs produced from carbon steel or malleable iron shall be one of the following: a. Zinc plated in accordance with ASTM B633, class Fe/Zn 13, type II. b. When required by contract (see 6.2), cadmium plated in accord

22、ance with SAE AMS-QQ-P-416, type II, class 2; class 3 cadmium plating is permissible for thread sizes of 1/2-inch or less. 3.1.2.2 Aluminum alloys. Drain plugs produced from aluminum alloys shall be anodized using type IC or IIB coatings in accordance with MIL-A-8625. 3.1.3 Magnet types. Magnets sha

23、ll be of the permanent magnet type and materials shall be of the Alnico 5 or the ceramic type conforming to MMPA 0100. 3.2 Dimensions. Dimensions shall conform to those shown in figure 1 and tables I and II. Dimensions and features not described herein shall be in accordance with SAE J532. 3.3 Magne

24、ts. 3.3.1 Magnetic lift. Magnets shall lift a minimum of 6 ounces of soft steel after being installed into the drain plug (see 4.4.2.1). 3.3.2 Temperature. Magnets shall be firmly retained in the drain plug at temperatures up to 500 F (260 C) (see 4.4.2.2). 3.4 Threads. Threads shall be in accordanc

25、e with FED-STD-H28 (see tables I and II). Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-DTL-32373 5 NOTES: 1. All dimensions are in inches. Dimensions are shown in tables I and II. Unless otherwise specified, tolerances are 0.010 on machined su

26、rfaces. 2. All machined surfaces shall have a surface texture not greater than 125 micrometers (m) from the nominal; and all unmachined surfaces shall have a surface texture not greater than 500 m from the nominal in accordance with ASME B46.1. 3. Across-corner dimensions of the hexagonal heads shal

27、l be a minimum of 1.092 times larger than the nominal across-flats width of the hexagonal heads (dimension “L“). 4. The maximum magnet diameter shall be not less than 0.100 less than the thread pitch diameter. FIGURE 1. Machine thread magnetic drain plugs. TABLE I. Type I machine thread magnetic dra

28、in plug dash numbers. MS dash number (steel) MS dash number (aluminum) “A“ thread size “B“ “L“ (nominal) “M“ Gasket dash number1-1 -2 3/8-24 UNF-2A 0.31 0.625 0.50 6 -49 -50 1/2-20 UNF-2A 0.34 0.750 0.53 9 -3 -4 5/8-18 UNF-2A 0.38 0.875 0.62 11 -83 -84 3/4-16 UNF-2A 0.38 1.000 0.62 15 -5 -6 7/8-14 U

29、NF-2A 0.41 1.125 0.66 18 -99 -100 7/8-18 UNS-2A 0.41 1.125 0.66 18 -111 -112 1-18 UNS-2A 0.44 1.250 0.75 21 -7 -8 1-1/4-12 UNF-2A 0.47 1.500 0.78 31 -133 -134 1-1/4-18 UNEF-2A 0.47 1.500 0.78 31 -149 -150 1-1/2-18 UNEF-2A 0.50 1.750 0.88 48 1 In accordance with SAE AS35769 (see 3.5). Provided by IHS

30、Not for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-DTL-32373 6 TABLE II. Type II machine thread magnetic drain plug dash numbers. MS dash number (iron) MS dash number (aluminum) “A“ thread size “B“ “H“ flange diameter “L“ (nominal) “M“ Gasket dash number1-9 -10 2-

31、12 UN-2A 0.56 2.25 1.500 1.37 55 -167 -168 2-16 UN-2A 0.56 2.25 1.500 1.37 55 -11 -12 3-12 UN-2A 0.56 3.25 1.500 1.37 76 1 In accordance with SAE AS35769 (see 3.5). 3.5 Gaskets. Gaskets shall conform to SAE AS35769 and shall be appropriately sized to the drain plug (see tables I and II). 3.6 Marking

32、s. Markings shall consist of the MS part number (see 1.3) and the manufacturer commercial and government entity (CAGE) code in accordance with MIL-STD-130 (see figure 1). 3.7 Recycled, recovered, or environmentally preferable materials. Recycled, recovered, or environmentally preferable materials sh

33、ould be used to the maximum extent possible, provided that the material meets or exceeds the operational and maintenance requirements, and promotes economically advantageous life cycle costs. 4. VERIFICATION 4.1 Classification of tests. All inspections required herein for the testing of drain plugs

34、are classified as conformance tests and shall be conducted in accordance with the sampling techniques and methods of testing specified herein. 4.2 Sampling for inspection. A random sample of drain plugs for visual inspection and testing shall be selected from each lot in accordance with ASQ Z1.4, in

35、spection level 2. The acceptance quality limit (AQL) shall as specified in the contract (see 6.2). 4.3 Lot. A lot shall consist of drain plugs of the same type, materials, and construction produced continuously by one machine or one series of progressive processing machines. 4.3.1 Rejection. The fai

36、lure of any specimen shall be cause for rejection of the lot represented by the sample. 4.3.2 Certified test report. If specified (see 6.2), the manufacturer shall furnish a certified test report showing that the manufacturers product satisfactorily conforms to this specification. The test report sh

37、all include, as a minimum, actual results of the tests specified herein. 4.4 Tests. Unless otherwise specified, all tests described herein shall be conducted at ambient room temperature. Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-DTL-32373 7

38、 4.4.1 Examination of product. All drain plug samples shall be examined for conformance to the requirements as shown in table III. TABLE III. Conformance test requirements. Test requirement Requirementparagraph Requirement standard Materials Machine thread magnetic drain plug Carbon steel - composit

39、ion - stock dimensions Aluminum alloy Malleable iron Protective finish Zinc plating (steel or iron) Cadmium plating (steel or iron) Anodization (aluminum alloy) Magnets 3.1.1.1 3.1.1.1 3.1.1.2 3.1.1.3 3.1.2.1 3.1.2.1 3.1.2.2 3.1.3 ASTM A29/A29M ASTM A108 ASTM B211 ASTM A47/A47M ASTM B633 SAE AMS-QQ-

40、P-416 MIL-A-8625 MMPA 0100 Dimensions Machine tolerances Surface texture 3.2 3.2 3.2 Figure 1, tables I and II Figure 1 ASME B46.1 Plug threads 3.4 FED-STD-H28 Gasket 3.5 SAE AS35769 4.4.1.1 Rejects. Failure of any sample to meet the stated requirements shall be cause for rejection of the entire lot

41、. 4.4.2 Magnets. Machine thread drain plugs with installed magnets shall be tested as described in 4.4.2.1 and 4.4.2.2. 4.4.2.1 Magnet lift. Using a drain plug with magnet installed, lift a solid piece of soft steel weighing not less than six ounces. Apply the magnet to the steel piece and manually

42、raise the drain plug so that only the magnet lifts the steel piece. Hold the drain plug and steel in a suspended position for not less than five seconds. Failure of the magnet to hold the steel piece in suspension for five seconds shall be cause for rejection (see 3.3.1). 4.4.2.1.1 Rejects. Samples

43、failing the magnet retention test shall result in rejection of the entire lot. 4.4.2.2 Magnet retention. Using an oven with thermostat control, heat the sample drain plug with installed magnet to 500 F (260 C). Once the test sample is at temperature, remove the sample from the oven using tongs and i

44、nsulated gloves (Warning: The test sample will be very hot.). Use pliers to grasp and apply light torque to the magnet to verify that the magnet is firmly affixed to the drain plug. Do not overtorque. Failure of the magnet to remain firmly retained in the drain plug at temperature shall be cause for

45、 rejection (see 3.3.2). Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-DTL-32373 8 4.4.2.2.1 Rejects. Samples failing the magnet temperature test shall result in rejection of the entire lot. 5. PACKAGING 5.1 Packaging. For acquisition purposes,

46、the packaging requirements shall be as specified in the contract or order (see 6.2). When packaging of materiel is to be performed by DoD or in-house contractor personnel, these personnel need to contact the responsible packaging activity to ascertain packaging requirements. Packaging requirements a

47、re maintained by the Inventory Control Points packaging activities within the Military Service or Defense Agency, or within the military services system commands. Packaging data retrieval is available from the managing Military Departments or Defense Agencys automated packaging files, CD-ROM product

48、s, or by contacting the responsible packaging activity. 6. NOTES (This section contains information of a general or explanatory nature that may be helpful, but is not mandatory.) 6.1 Intended use. The machine thread magnetic drain plugs covered by this specification are intended for use in engine oi

49、l lubrication systems as a means to seal and access the engine oil reservoir and to magnetically attract and capture ferrous contaminants in the engine oil that could result in accelerated engine wear. 6.1.1 Type I. Type I machine thread magnetic drain plugs feature an external hexagonal head that provides the surfaces against which torque is applied when loosening or tig