1、Designation: G112 92 (Reapproved 2015)Standard Guide forConducting Exfoliation Corrosion Tests in Aluminum Alloys1This standard is issued under the fixed designation G112; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of

2、 last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This guide differs from the usualASTM standard in thatit does not address a specific test. Rather, it is an introduct

3、oryguide for new users of other standard exfoliation test methods,(see Terminology G15 for definition of exfoliation).1.2 This guide covers aspects of specimen preparation,exposure, inspection, and evaluation for conducting exfoliationtests on aluminum alloys in both laboratory accelerated envi-ronm

4、ents and in natural, outdoor atmospheres. The intent is toclarify any gaps in existent test methods.1.3 The values stated in SI units are to be regarded as thestandard. The inch-pound units given in parentheses are forinformation only.1.4 This standard does not purport to address all of thesafety co

5、ncerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:2G1 Practice for Preparing, Cleaning,

6、and Evaluating Corro-sion Test SpecimensG15 Terminology Relating to Corrosion and Corrosion Test-ing (Withdrawn 2010)3G34 Test Method for Exfoliation Corrosion Susceptibility in2XXX and 7XXX Series Aluminum Alloys (EXCO Test)G50 Practice for Conducting Atmospheric Corrosion Testson MetalsG66 Test Me

7、thod for Visual Assessment of ExfoliationCorrosion Susceptibility of 5XXX Series Aluminum Al-loys (ASSET Test)G85 Practice for Modified Salt Spray (Fog) TestingG92 Practice for Characterization of Atmospheric Test Sites2.2 ASTM Adjuncts:Illustrations of Appearance Classifications (6 glossy pho-tos)4

8、3. Terminology3.1 Definitions of Terms Specific to This Standard:3.1.1 panela flat, rectangular specimen normally takenwith the test surface parallel to the longitudinal and long-transverse dimensions of fabricated product. For thin sheet andextrusions, the thickness may be the full thickness of the

9、 part.3.1.2 samplea portion of a large piece, or an entire pieceout of a group of many pieces, that is submitted for evaluationand considered representative of the larger piece or population.For castings and forgings, this may be an extra portion orprolongation, or in the case of small parts, an ent

10、ire extra piecetaken from a specific lot.3.1.3 specimenthe actual test piece to be corrosion tested.Frequently this has a specific shape with prescribed dimen-sional tolerances and finishes.3.1.4 test planethe plane in the thickness of the samplethat is being tested. Generally this is the fabricated

11、 surface orsome specified interior plane. Interior planes typically used are:(a) T/10 = 10 % of the thickness removed, (this is representa-tive of a minimal machining cut to obtain a flat surface), (b)T/4 = quarter plane, 25 % of the thickness removed, and (c)T/2 = midplane, 50 % of the thickness re

12、moved.4. Significance and Use4.1 Although there are ASTM test methods for exfoliationtesting, they concentrate on specific procedures for test meth-odology itself. Existent test methods do not discuss materialvariables that can affect performance. Likewise they do notaddress the need to establish th

13、e suitability of an acceleratedtest for alloys never previously tested nor the need to correlateresults of accelerated tests with tests in outdoor atmospheresand with end use performance.4.2 This guide is a compilation of the experience of inves-tigators skilled in the art of conducting exfoliation

14、tests and1This guide is under the jurisdiction of ASTM Committee G01 on Corrosion ofMetals and is the direct responsibility of Subcommittee G01.05 on LaboratoryCorrosion Tests.Current edition approved Nov. 1, 2015. Published December 2015. Originallyapproved in 1992. Last previous edition approved i

15、n 2009 as G11292(2009). DOI:10.1520/G0112-92R15.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.3The last app

16、roved version of this historical standard is referenced onwww.astm.org.4Available from ASTM International Headquarters. Order Adjunct No.ADJG003402. Original adjunct produced in 1980.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States1ass

17、essing the degree and significance of the damage encoun-tered. The focus is on two general aspects: guides to techniquesthat will enhance the likelihood of obtaining reliableinformation, and tips and procedures to avoid pitfalls that couldlead to erroneous results and conclusions.4.3 The following t

18、hree areas of testing are considered: thetest materials starting with the “as-received” sample up throughfinal specimen preparation, the corrosion test procedures in-cluding choice of test, inspection periods, termination point,and rating procedures, and analyses of results and methods forreporting

19、them.4.4 This guide is not intended as a specific corrosion testprocedure by which to evaluate the resistance to exfoliation ofan aluminum alloy product.4.5 This guide is not intended as a basis for specifications,nor as a guide for material lot acceptance.5. Material5.1 Sample SizeMost exfoliation

20、tests do not require anyparticular specimen size, but when beginning a new investiga-tion it is best to obtain considerably more material than theminimum amount needed. About 50 to 100 % overage isrecommended. This avoids the need of procuring a secondsample, that may have a different response, to c

21、omplete anyconfirmatory retests or extensions to a specific program.5.2 Sample ReproducibilityThe specific location ofsamples in a mill product, and the number of samples to takeare beyond the scope of this guide. When testing largeproduction items, a typical procedure is to test at both ends(front

22、and rear), and to test at the side and at the mid-width ifthe product is 0.6 m (2 ft) or more in width. Thick productsshould be tested at various planes through the thickness.5.2.1 In addition, some assessment should be made of theuniformity of a large sample, or of numerous small samples.Typical qu

23、ick check methods would be to measure electricalconductivity or hardness. If the material variability has apattern, for example, a difference between front and rear of along extrusion, then this should be noted and the specimenssegregated accordingly. If the variability is random, thenmultiple test

24、specimens should be randomized.5.3 Sample MicrostructureThe directionality of the grainstructure of aluminum alloys will markedly affect the suscep-tibility to exfoliation. When a product shape and alloy arebeing tested for the first time, it is advisable to macroetch fullthickness by longitudinal a

25、nd by transverse slices to establishthe directionality and uniformity of the grain structure. Testpanels are normally positioned such that the test surface isparallel to the plane in the product with the most elongatedgrain structure. Complex shaped parts, such as certain extru-sions or die forgings

26、, may have several categories of grainstructures and grain flow that do not necessarily follow the partgeometry. Grain structure of such parts must be determined bymacroetching or from prior experience.5.3.1 For a given temper condition, unrecrystallized, pan-cake shaped grains, that are long and wi

27、de but relatively thin,are the most susceptible. Pancake shaped recrystallized grains,as in sheet, are the next most susceptible. This is followed bythe long, rod shaped grains found in extruded or rolled rod andbar with a symmetrical cross section, for example, circle,square, hex, or a rectangle wi

28、th the width not more than twicethe thickness. An equiaxed grain structure is the least suscep-tible to exfoliation, especially if the grain size is large. Oftenthe recrystallized surface layer on products such as extrusions,forgings, or sheet will not exfoliate, even though it corrodesintergranular

29、ly.5.4 Sample TemperWhen a large sample is obtained as astock item for use over a long time period, the extra materialshould be stored in a stable temper and at a low enoughtemperature so that no further precipitation will occur to alterthe starting condition of the metal. The unaged W temper of7XXX

30、 alloys is not stable and will continue to age harden atroom temperature. Room temperature storage of such materialshould be limited to a couple of months at most. Natural agingof these alloys can be retarded almost completely by storing thematerial in a freezer at 40C (40F) or colder. This factor i

31、sof even more importance in determination of mechanicalproperties than the investigation of corrosion resistance.6. Selection of an ASTM Test Method6.1 Selection of the appropriateASTM test method(s) to usewill depend primarily on the type of alloy and on the end useenvironment. When testing a new a

32、lloy or temper, a testmethod known to be applicable to the most similar commercialalloy is normally selected. The user is cautioned, however, thateven small changes in alloy chemistry, or changes in process-ing method (for example, rapid solidification processes) canmarkedly effect resistance of an

33、alloy and the appropriatenessof a test method. Normally exfoliation tests are conducted oningot metallurgy alloys, that tend to have the elongated grainstructure prone to exfoliate. The known alloy applicability ofthe ASTM test methods are listed below. Included are someobserved instances where a te

34、st method was found to beinappropriate, or at least produced results different than thoseobserved on the initial qualification alloys.6.1.1 It is advisable to initially employ more than onelaboratory test method and determine whether they agree; or ifnot, which method is the most discriminating. One

35、 procedurefor doing this is to apply different fabrication procedures to themetal that are known to generally affect resistance to exfolia-tion and determine which of the test methods best detectsdifferences in the corresponding resistance to exfoliation.Fabrication variables that often affect resis

36、tance to exfoliationare variable quench cooling rates, slow quenches being ad-verse; and variable amounts of aging, underaged, or peak agedconditions generally being more susceptible than overagedconditions (1).56.2 Test Method G66 Acidified Salt Solution ExfoliationTest (ASSET) is used for 5XXX all

37、oys containing 2.0 % ormore magnesium. The round robin qualification tests for thistest method were conducted on alloys 5086 (3.5 to 4.5 % Mg)5The boldface numbers in parentheses refer to a list of references at the end ofthis standard.G112 92 (2015)2and 5456 (4.7 to 5.5 % Mg). (2) However, Test Met

38、hod G66(ASSET) gives problem free exfoliation indications with all5XXX alloys.6.3 Test Method G34 Exfoliation Corrosion (EXCO) Test isintended for use with high strength 2XXX and 7XXX ingotmetallurgy alloys, a 96 h period being prescribed for the 2XXXalloys and a 48 h period for the 7XXX alloys.6.3.

39、1 For the 2XXX alloys, the round robin qualificationtests were conducted on alloys 2024 and 2124 in the T351 andT851 tempers. The appropriateness of the method has not beenfully established for all other 2XXX alloys. It has beenreported as being too aggressive and nonrepresentative ofperformance in

40、outdoor atmospheres for alloys 2219, 2419 and2519 in the T851 tempers (3) and for various Al-Li alloys inboth as-quenched and artificially aged tempers (1).6.3.2 For the 7XXX alloys the round robin qualificationtests were conducted on alloy 7075 in the T651, T7651, andT7351 tempers and alloy 7178 in

41、 the T651 and T7651 tempers.Experience has shown that the EXCO method can be used for7050 and 7150 alloys in the T651, T6151, T7451, T7651, andT7751 tempers, but the test is somewhat more aggressive onthese alloys (4). This method also was evaluated with copperfree alloys such as 7021-T6 and 7146-T6

42、, but generally anabbreviated exposure period of 16 to 24 h was used.6.3.3 Exposure of the powder metallurgy alloys 7090 and7091-T6 specimens to EXCO results in rapid dissolution andpowdering of the specimen, due to continuous drop of theextremely fine grains. Four years of exposure of the same part

43、sto seacoast atmosphere resulted only in mild general corrosionand no exfoliation (5).6.4 AnnexA2 of Practice G85 ModifiedASTMAceticAcidSalt Intermittent Spray Test, (MASTMAASIS) was developedusing alloys 2024, 2124, 7075, and 7178. This method usuallyis run in the wet bottom condition (some solutio

44、n and highhumidity always present). A dry bottom condition (no solutionpresent and gradually falling humidity during the purge andnon-spraying periods) has been recommended for 2XXXalloys.6.4.1 The test cabinets used to conduct the MASTMAASIStest, and the salt fog tests subsequently described in 6.5

45、 and6.6, are produced by several suppliers. The fog deliverysystems and cabinet geometry can differ and have graduallyevolved. Consequently some cabinet to cabinet variability intest results is inherent, due primarily to variation in spraytechniques and the relative humidity conditions during thenon

46、-spray portions of the cycle.6.4.2 There is no record of the MASTMAASIS environ-ment being unrealistically aggressive, causing exfoliation of amaterial that did not subsequently exfoliate in the seacoast. Assuch any occurrence of exfoliation in this test most likelyindicates susceptibility under som

47、e service conditions. Theconverse of this statement has not been observed.6.4.3 MASTMAASIS is not appropriate for 5XXX alloys,because it does not always detect exfoliation susceptibility inmaterials proven to be susceptible by other test methods.6.4.4 MASTMAASIS has been used with some success on6XX

48、X series alloys. However, in some cases it caused severeintergranular corrosion that could be confused with exfoliationcorrosion unless specimens are examined metallographically.6.5 Annex A3 of Practice G85 Seawater Acetic Acid Test(SWAAT) was developed using the same 5XXX, 2XXX, and7XXX alloys as m

49、entioned above for the ASSET and EXCOmethods (6).6.6 Practice G85 Annex A4 (SALT/SO2Spray Testing) wasdeveloped using the same, 2XXX and 7XXX alloys as men-tioned above for the EXCO method (7).6.7 Both the methods in Annex A3 and Annex A4 ofPractice G85 result in more gelatinous corrosion products thandoes Annex A2. This tends to increase pitting corrosion on thespecimens.Annex methodsA2,A3, andA4 in Practice G85 arenot equivalent, and the user should determine which methodbest suits the alloys and applications under investigation.7. Baseline Experience7.1 The best check