ASTM F2581-2012 Standard Specification for Wrought Nitrogen Strengthened 11Manganese-17Chromium-3Molybdenum Low-Nickel Stainless Steel Alloy Bar and Wire for Surgical Implants (UNS.pdf

《ASTM F2581-2012 Standard Specification for Wrought Nitrogen Strengthened 11Manganese-17Chromium-3Molybdenum Low-Nickel Stainless Steel Alloy Bar and Wire for Surgical Implants (UNS.pdf》由会员分享，可在线阅读，更多相关《ASTM F2581-2012 Standard Specification for Wrought Nitrogen Strengthened 11Manganese-17Chromium-3Molybdenum Low-Nickel Stainless Steel Alloy Bar and Wire for Surgical Implants (UNS.pdf（6页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: F2581 12Standard Specification forWrought Nitrogen Strengthened 11Manganese-17Chromium-3Molybdenum Low-Nickel Stainless Steel Alloy Bar and Wirefor Surgical Implants (UNS S29225)1This standard is issued under the fixed designation F2581; the number immediately following the designation

2、indicates the year oforiginal adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope*1.1 This specification covers the chemica

3、l, mechanical, andmetallurgical requirements for wrought nitrogen strengthened11manganese-17chromium-3molybdenum low-nickel stainlesssteel alloy bar and wire for surgical implants.1.2 The values stated in either SI units or inch-pound unitsare to be regarded separately as standard. The values stated

4、 ineach system may not be exact equivalents; therefore, eachsystem shall be used independently of the other. Combiningvalues from the two systems may result in non-conformancewith the standard.1.3 This standard does not purport to address all of thesafety concerns, if any, associated with its use. I

5、t is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:2A262 Practices for Detecting Susceptibility to IntergranularAttack in Austeniti

6、c Stainless SteelsA484/A484M Specification for General Requirements forStainless Steel Bars, Billets, and ForgingsA555/A555M Specification for General Requirements forStainless Steel Wire and Wire RodsA751 Test Methods, Practices, and Terminology for Chemi-cal Analysis of Steel ProductsE8/E8M Test M

7、ethods for Tension Testing of Metallic Ma-terialsE10 Test Method for Brinell Hardness of Metallic MaterialsE18 Test Methods for Rockwell Hardness of Metallic Ma-terialsE29 Practice for Using Significant Digits in Test Data toDetermine Conformance with SpecificationsE45 Test Methods for Determining t

8、he Inclusion Content ofSteelE112 Test Methods for Determining Average Grain SizeE354 Test Methods for Chemical Analysis of High-Temperature, Electrical, Magnetic, and Other Similar Iron,Nickel, and Cobalt AlloysE407 Practice for Microetching Metals and AlloysF138 Specification for Wrought 18Chromium

9、-14Nickel-2.5Molybdenum Stainless Steel Bar and Wire for SurgicalImplants (UNS S31673)F746 Test Method for Pitting or Crevice Corrosion ofMetallic Surgical Implant MaterialsF748 Practice for Selecting Generic Biological Test Methodsfor Materials and DevicesF1314 Specification for Wrought Nitrogen St

10、rengthened 22Chromium 13 Nickel 5 Manganese 2.5 MolybdenumStainless Steel Alloy Bar and Wire for Surgical Implants(UNS S20910)F1586 Specification for Wrought Nitrogen Strengthened21Chromium10Nickel3Manganese2.5Molybdenum Stainless Steel Alloy Bar for SurgicalImplants (UNS S31675)IEEE/ASTM SI 10 Amer

11、ican National Standard for MetricPractice2.2 Aerospace Material Specification:3AMS 2248 Chemical Check Analysis Limits, Corrosion andHeat Resistant Steels and Alloys, Maraging and OtherHighly-Alloyed Steels, and Iron AlloysAMS 2630 Inspection, Ultrasonic Product over 0.5 Inch(12.7 mm) Thick2.3 ISO S

12、tandard:4ISO 6892 Metallic Materials Tensile Testing at AmbientTemperature1This specification is under the jurisdiction of ASTM Committee F04 onMedical and Surgical Materials and Devices and is the direct responsibility ofSubcommittee F04.12 on Metallurgical Materials.Current edition approved Oct. 1

13、, 2012. Published October 2012. Originallyapproved in 2007. Last previous edition approved in 2007 as F2581 07. DOI:10.1520/F2581-12.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume infor

14、mation, refer to the standards Document Summary page onthe ASTM website.3Available from Society of Automotive Engineers (SAE), 400 CommonwealthDr., Warrendale, PA 15096-0001, http:/www.sae.org.4Available from American National Standards Institute (ANSI), 25 W. 43rd St.,4th Floor, New York, NY 10036,

15、 http:/www.ansi.org.*A Summary of Changes section appears at the end of this standardCopyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States1ISO 9001 Quality Management SystemsRequirements3. Terminology3.1 Definitions of Terms Specific to Thi

16、s Standard:3.1.1 barround, rectangular, or other complex shapedproduct delivered straightened and cut to defined lengths, witha maximum cross-sectional area of 16 in.2103 cm2.3.1.2 fine wirewire with diameter or major dimension lessthan 0.063 in. 1.6 mm.3.1.3 forging barbar as described in 3.1.1 use

17、d for pro-duction of forgings, may be furnished in the hot-rolled anddescaled condition.3.1.4 lotthe total number of mill products produced fromthe same melt heat under the same conditions at essentially thesame time.3.1.5 wirerounds, rectangular, or other complex shapedproduct produced and delivere

18、d in coils.4. Ordering Information4.1 Inquiries and orders for material under this specificationshall include the following information:4.1.1 Quantity;4.1.2 ASTM designation and date of issue;4.1.3 Mechanical properties;4.1.4 Form;4.1.5 Applicable dimensions including size, thickness,width, and leng

19、th (exact, random, or multiples) or drawingnumber;4.1.6 TolerancesUnless otherwise specified by thepurchaser, tolerances must meet the requirements of Specifi-cations A484/A484M and A555/A555M, as applicable;4.1.7 Condition (see 5.1);4.1.8 Finish (see 5.2);4.1.9 Special tests, if any; and4.1.10 Othe

20、r requirements.5. Materials and Manufacture5.1 ConditionBar and wire shall be furnished, asspecified, in the annealed or cold-worked condition. Bar usedfor the production of forgings may be furnished in the hotworked and descaled condition, as agreed upon between thepurchaser and supplier.5.2 Finish

21、Types of finish available in bar and wire arecold-drawn, pickled, ground, ground and polished, shaved, oras specified by the purchaser.6. Chemical Requirements6.1 The suppliers heat analysis shall conform to the chemi-cal requirements prescribed in Table 1. The supplier shall notship material that i

22、s outside the limits specified in Table 1.6.1.1 Requirements for the major and minor elementalconstituents are listed in Table 1. Also listed are importantresidual elements.Analysis for elements not listed in Table 1 isnot required to verify compliance with this specification.6.1.2 Methods and pract

23、ices relating to chemical analysisrequired by this specification shall be in accordance with TestMethods A751.6.1.3 For reference purposes, Test Methods E354 shallapply.6.2 Product AnalysisThe product analysis is either for thepurpose of verifying the composition of a heat or lot or todetermine vari

24、ations in the composition within the heat.6.2.1 Acceptance or rejection of a heat or lot of materialmay be made by the purchaser on the basis of this productanalysis.6.2.2 Product analysis tolerances do not broaden the speci-fied heat analysis requirements but cover variations betweenlaboratories in

25、 the measurement of chemical content. Productanalysis limits shall be as specified in Table 2.7. Metallurgical Requirements7.1 The material shall contain no delta ferrite, chi, or sigmaphases when it is examined metallographically at 100 mag-nification in accordance with Practice E407.7.2 The microc

26、leanliness of the steel, as determined by TestMethod E45, MethodA, on representative billet or bar samplesfrom the heat shall not exceed the following:InclusionTypeA (Sulphide) B (Alumina) C (Silicate)D (Globularoxide)Thin 1.5 1.5 1.5 1.5Heavy 1.0 1.0 1.0 1.0TABLE 1 Chemical CompositionElement Compo

27、sition, % (mass/mass)Carbon 0.15 to 0.25Manganese 9.50 to 12.50Phosphorus 0.020 maxSulfur 0.010 maxSilicon 0.2 to 0.6Chromium 16.50 to 18.00Nickel 0.05 maxMolybdenum 2.70 to 3.70Nitrogen 0.45 to 0.55Copper 0.25 maxIron balanceAAApproximately equal to the difference of 100 % and the sum percentage of

28、 theother specified elements. The percentage of iron difference is not required to bereported.TABLE 2 Product Analysis TolerancesAElementPermissible VariationUnder the MinimumLimit or Over theMaximum Limit, % (mass/mass)BCarbon 0.01ManganeseC0.20Phosphorus 0.005Sulfur 0.005Silicon 0.05Chromium 0.25N

29、ickel 0.03Molybdenum 0.05NitrogenC0.05Copper 0.03ARefer to AMS 2248 for chemical check analysis limits (except nitrogen).BFor elements in which only a maximum percentage is indicated, the “underminimum limit” is not applicable.CThe specified range for this element is not covered by AMS 2248 and has

30、beenestablished through industrial practice.F2581 1228. Mechanical Properties8.1 Tensile Properties:8.1.1 Tensile properties shall be determined in accordancewith Test Methods E8/E8M.8.1.2 The mechanical properties of test specimens shallconform to the requirements specified in Table 3.8.1.3 The lev

31、el of mechanical properties for material inother conditions shall be specified in the purchase order.8.2 Hardness:8.2.1 Hardness values shall be determined in accordancewith Test Method E10 or Test Methods E18.8.2.2 When desired, hardness limits may be specified by thepurchaser. Hardness determinati

32、ons shall be made on a productcross section, midway between the center and surface, if thecross section is adequate.8.3 Number of Tests:8.3.1 Perform tension testing per Test Methods E8/E8M.Should any of the test specimens not meet the specifiedrequirements, test two additional test pieces represent

33、ative ofthe same lot, in the same manner, for each failed test piece. Thelot shall be considered in compliance only if all additional testpieces meet the specified requirements.8.3.2 Tensile test results for which any specimen fracturesoutside the gauge length shall be considered acceptable, if both

34、the elongation and reduction of area meet the minimumrequirements specified. Refer to subsections 7.11.4 and 7.11.5of Test Methods E8/E8M. If either the elongation or reductionof area is less than the minimum requirement, discard the testand retest. Retest one specimen for each specimen that did not

35、meet the minimum requirements.9. Ultrasonic Inspection9.1 All centerless ground or peeled and polished round bar 0.375 in. 9.5 mm in nominal diameter shall be ultrasoni-cally inspected at final diameter according toAMS 2630, ClassA1. Equivalent test methods may be substituted when agreedupon by the

36、purchaser and supplier.NOTE 1AMS 2630 specifies a minimum size limit of 0.50 in. 12.7mm. F04.12 subcommittee has intentionally specified the use of AMS2630 below 0.50 in. 12.7 mm based on the experience of users andproducers on the committee. There is disagreement in the industry as towhether AMS 26

37、32, which does apply to sizes under 0.50 in. 12.7 mm,applies to solid round bar.10. Dimensions and Permissible Variations10.1 Units of Measure:10.1.1 SelectionThis specification requires that the pur-chaser selects the units (SI or inch-pound) to be used forproduct certification. In the absence of a

38、 stated selection ofunits on the purchase order, this selection may be expressed bythe purchaser in several alternate forms listed in order ofprecedence.10.1.1.1 If the purchaser and supplier have a history ofusing specific units, these units shall continue to be certifieduntil expressly changed by

39、the purchaser.10.1.1.2 In the absence of historic precedence, if the unitsused to define the product on the purchasers purchase order(PO), specification, and engineering drawing are consistent,these units shall be used by the supplier for product certifica-tion.10.1.1.3 If the purchasers selection o

40、f units is unclear, theunits of measure shall be agreed upon between the purchaserand supplier.10.1.2 Conversion of UnitsIf the suppliers test equipmentdoes not report in the selected units, the test equipment unitsmay be converted to the selected units for certification pur-poses. Accurate arithmet

41、ic conversion and proper use ofsignificant digits should be observed when performing thisconversion. IEEE/ASTM SI 10 provides guidelines for the useof SI units. Annex A of that standard provides conversiontables and Annex B provides rules for conversion and signifi-cance.11. Special Tests11.1 Bar an

42、d wire conforming to this specification shall becapable of passing the intergranular corrosion susceptibilitytest in accordance with Practice E of Practices A262.11.2 Bar and wire conforming to this specification shallhave a homogeneous microstructure with an average grain sizeof ASTM No. 5 or finer

43、 when measured in accordance withTest Methods E112.11.2.1 It is preferred that samples for grain size determina-tion be selected after the hot working operation or after thefinal annealing operation prior to the final cold workingoperation.11.2.2 If grain size samples are selected after a final cold

44、working, specimens shall be tested according to Test MethodsE112 or as agreed upon between the supplier and purchaser.11.3 Any other special requirements shall be specified bythe purchaser.12. Significance and Numerical Limits12.1 The following applies to all specified numerical limitsin this specif

45、ication. To determine conformance to these limits,an observed or calculated value shall be rounded to the nearestunit in the last right hand digit used in expressing thespecification limit, in accordance with rounding method ofPractice E29.TABLE 3 Mechanical RequirementsConditionUltimateTensileStren

46、gthmin, psi MPaYieldStrength(0.2 %offset),min, psiMPaElongationAmin, %Reductionin Area min,%Annealed 120 00082770 00048240 50Cold Worked 160 0001103120 00082712 .AElongation of material 0.063 in. 1.6 mm or greater in diameter (D) or width (W)shall be measured using a gauge length of 2 in. or 4D or 4

47、W. The gauge lengthshall be reported with the test results. The method for determining elongation ofmaterial under 0.063 in. 1.6 mm in diameter or thickness may be negotiated.Alternatively, a gauge length corresponding to ISO 6892 may be used whenagreed upon between supplier and purchaser (5.65 So1/

48、2, where Sois theoriginal cross sectional area of the gauge length).F2581 12313. Certification13.1 Certification shall be provided by the supplier that thematerial meets the requirements of this specification. A reportof the test results shall be furnished at the time of shipment.14. Quality Program

49、 Requirements14.1 The bar and wire producer and any processors shallmaintain a quality program such as that which is defined in ISO9001 or a similar quality program.15. Keywords15.1 low-nickel; manganese; metals (for surgical implants);nitrogen strengthened; stainless steel; surgical applicationsAPPENDIXES(Nonmandatory Information)X1. RATIONALEX1.1 The purpose of this specification is to characterize thecomposition and properties of wrought low nickel, nitrogenstrengthened 11manganese-17chromium-3molybdenum barand wire to