ASTM F877-2011a Standard Specification for Crosslinked Polyethylene (PEX) Hot- and Cold-Water Distribution Systems《交联聚乙烯(PEX)冷热水分配系统的标准规格》.pdf

《ASTM F877-2011a Standard Specification for Crosslinked Polyethylene (PEX) Hot- and Cold-Water Distribution Systems《交联聚乙烯(PEX)冷热水分配系统的标准规格》.pdf》由会员分享，可在线阅读，更多相关《ASTM F877-2011a Standard Specification for Crosslinked Polyethylene (PEX) Hot- and Cold-Water Distribution Systems《交联聚乙烯(PEX)冷热水分配系统的标准规格》.pdf（7页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: F877 11aAn American National StandardStandard Specification forCrosslinked Polyethylene (PEX) Hot- and Cold-WaterDistribution Systems1This standard is issued under the fixed designation F877; the number immediately following the designation indicates the year of originaladoption or, in

2、the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A superscriptepsilon () indicates an editorial change since the last revision or reapproval.1. Scope*1.1 This specification covers requirements, test methods,and marking requirements for s

3、ystem components when testedwith nominal SDR9 crosslinked polyethylene tubing as asystem. Systems are intended for 100 psi (0.69 MPa) waterservice up to and including a maximum working temperatureof 180F (82C). Requirements and test methods are includedfor materials, workmanship, dimensions and tole

4、rances, burstpressure, sustained pressure, excessive temperature and pres-sure, and thermo-cycling tests. The components covered bythis specification are intended for use in residential andcommercial, hot and cold, potable water distribution systems orother applications such as municipal water servi

5、ce lines,radiant panel heating systems, hydronic baseboard heatingsystems, snow and ice melting systems, and building servicespipe.1.2 The text of this specification references notes, footnotes,and appendixes which provide explanatory material. Thesenotes and footnotes (excluding those in tables and

6、 figures) shallnot be considered as requirements of the specification.1.3 The values stated in inch-pound units are to be regardedas the standard. The values stated in parentheses are providedfor information only.NOTE 1Suggested hydrostatic design stresses and hydrostatic pres-sure ratings for tubin

7、g and fittings are listed in Appendix X1. Design,assembly, and installation considerations are discussed in Appendix X2.An optional performance qualification and an in-plant quality controlprogram are recommended in Appendix X3.1.4 The following safety hazards caveat pertains only to thetest method

8、portion, Section 7, of this specification: Thisstandard does not purport to address all of the safety concerns,if any, associated with its use. It is the responsibility of the userof this standard to establish appropriate safety and healthpractices and determine the applicability of regulatory limit

9、a-tions prior to use.2. Referenced Documents2.1 ASTM Standards:2D618 Practice for Conditioning Plastics for TestingD1598 Test Method for Time-to-Failure of Plastic PipeUnder Constant Internal PressureD1599 Test Method for Resistance to Short-Time HydraulicPressure of Plastic Pipe, Tubing, and Fittin

10、gsD1600 Terminology for Abbreviated Terms Relating toPlasticsD1898 Practice for Sampling of Plastics3D2749 Symbols for Dimensions of Plastic Pipe FittingsD2837 Test Method for Obtaining Hydrostatic Design Basisfor Thermoplastic Pipe Materials or Pressure Design Basisfor Thermoplastic Pipe ProductsD3

11、140 Practice For Flaring Polyolefin Pipe and Tubing3F412 Terminology Relating to Plastic Piping SystemsF876 Specification for Crosslinked Polyethylene (PEX)TubingF1960 Specification for Cold Expansion Fittings with PEXReinforcing Rings for Use with Cross-linked Polyethylene(PEX) TubingF1961 Specific

12、ation for Metal Mechanical Cold Flare Com-pression Fittings with Disc Spring for Crosslinked Poly-ethylene (PEX) TubingF1807 Specification for Metal Insert Fittings Utilizing aCopper Crimp Ring for SDR9 Cross-linked Polyethylene(PEX) Tubing and SDR9 Polyethylene of Raised Tempera-ture (PE-RT) Tubing

13、F1865 Specification for Mechanical Cold Expansion InsertFitting With Compression Sleeve for Cross-linked Polyeth-ylene (PEX) TubingF2080 Specification for Cold-Expansion Fittings WithMetal Compression-Sleeves for Cross-Linked Polyethyl-ene (PEX) Pipe1This specification is under the jurisdiction of A

14、STM Committee F17 on PlasticPiping Systems and is the direct responsibility of Subcommittee F17.61 on Water.Current edition approved Aug. 1, 2011. Published August 2011. Originallyapproved in 1984. Last previous approved 2011 as F877 11. DOI: 10.1520/F0877-11A.2For referenced ASTM standards, visit t

15、he ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.3Withdrawn. The last approved version of this historical standard is referencedon www.astm.org.1*A S

16、ummary of Changes section appears at the end of this standard.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.F2159 Specification for Plastic Insert Fittings Utilizing aCopper Crimp Ring for SDR9 Cross-linked Polyethylene(PEX) Tubing

17、and SDR9 Polyethylene of Raised Tempera-ture (PE-RT) TubingF2434 Specification for Metal Insert Fittings Utilizing aCopper Crimp Ring for SDR9 Cross-linked Polyethylene(PEX) Tubing and SDR9 Cross-linked Polyethylene/Aluminum/Cross-linked Polyethylene (PEX-AL-PEX)TubingF2735 Specification for Plastic

18、 Insert Fittings For SDR9Cross-linked Polyethylene (PEX) and Polyethylene ofRaised Temperature (PE-RT) TubingF2854 Specification for Push-Fit Crosslinked Polyethylene(PEX) Mechanical Fittings for Crosslinked Polyethylene(PEX) Tubing2.2 ANSI Standards:B 36.10 Welded and Seamless Wrought Steel Pipe4Z

19、17.1 Preferred Numbers42.3 AWWA Standard:Manual M-11, Steel Pipe Design and Installation52.4 Federal Standard:Fed Std. No. 123 Marking for Shipment (Civil Agencies)62.5 Military Standard:MIL-STD-129 Marking for Shipment and Storage62.6 NSF Standard:NSF/ANSI Standard No. 14 for Plastic Piping Compone

20、ntsand Related Materials7NSF/ANSI Standard No. 61 for Drinking Water SystemComponents-Health Effects73. Terminology3.1 The terminology used in this specification is in accor-dance with Terminology F412, Terminology D1600, and Sym-bols D2749, unless otherwise specified. The abbreviation forcrosslinke

21、d polyethylene is PEX. Plastic tubing denotes aparticular diameter schedule of plastic pipe in which outsidediameter of the tubing is equal to the nominal size plus18 in.Plastic pipe outside diameter schedule conforms to ANSIB 36.10.3.2 Definitions of Terms Specific to This Standard:3.2.1 crosslinke

22、d polyethylene plasticsplastics preparedby crosslinking (curing) polyethylene compounds.3.2.2 fittingan appurtenance such as coupling, elbow ortee used to connect tubing or as an accessory to tubing.3.2.3 standard dimension ratio (SDR)a selected series ofnumbers in which the average outside diameter

23、 to minimumwall thickness dimension ratios are constant for all sizes oftubing in each standard dimension ratio, and which are theANSI Z 17.1 Preferred Number Series R 10 modified by +1.3.2.4 manifoldan appurtenance that has at least one inletand multiple outlets.3.2.5 system componentsfittings and

24、manifolds.4. Materials4.1 General PEX systems shall use crosslinked polyeth-ylene tubing as described in Specification F876.4.2 Fitting and manifold materials shall meet the applicablerequirements as described in Specifications F1807, F1865,F1960, F1961, F2080, F2159, F2434, F2735,orF2854.4.3 Certif

25、icationPEX tubing and system components,used for the distribution of potable water, shall be productsapproved for that service by the regulatory bodies having suchjurisdiction. These products shall be tested for that service bya nationally recognized and accredited testing laboratory andshall bear t

26、he certification mark of the testing agency.5. Classification5.1 FittingsThis specification classifies fittings includingmanifolds, intended for use in systems with PEX tubing, by amaximum continuous use temperature that shall be 180F(82C) and by nominal sizes from18 in. through 6 in. on thebasis of

27、 resistance to burst pressure, hydrostatic sustainedpressure, excessive temperature pressure capability, and bythermocycling. Fittings shall be compatible with tubing madeto the requirements of Specification F876.6. Requirements6.1 WorkmanshipFittings shall be made from materialsthat are homogeneous

28、 throughout and free of visible cracks,holes, foreign inclusions, or other defects. All sealing surfacesshall be smooth and free of foreign material. The walls offittings and manifolds shall be free of cracks, holes, blisters,voids, foreign inclusions, or other defects that are visible to thenaked e

29、ye and may affect fitting integrity.6.2 Dimensions and Tolerances:6.2.1 The dimensions and tolerances of fittings shall meetthe specific requirements contained in Specifications F1807,F1865, F1960, F1961, F2080, F2159, F2434, and F2735 orother recognized specification.6.2.2 Fittings shall be compati

30、ble with tubing made to therequirements of Specification F876.6.3 Corrosion ResistanceFittings shall be made frommaterials that are generally regarded as corrosion resistant.6.3.1 Compliance with this specification requires that fit-tings contained in Specifications F1807, F1865, F1960, F1961,F2080,

31、 F2159, F2434, and F2735, and F2854 must meet thePerformance and Test Method requirements of F877.6.4 Hydrostatic Burst:6.4.1 Tubing and fittings (tested as assemblies) assembledusing the manufacturers instructions shall meet the minimumhydrostatic burst requirements shown in Table 1 when tested ina

32、ccordance with 7.6.6.4.2 Manifolds with integral shut-offs (valves) shall betested with all ports in the full-open or unrestricted position.6.4.2.1 If the manifold has more than one connection size,the test pressure selected from Table 1 shall be based upon thelargest nominal PEX connection.4Availab

33、le from American National Standards Institute (ANSI), 25 W. 43rd St.,4th Floor, New York, NY 10036, http:/www.ansi.org.5Available from American Water Works Association (AWWA), 6666 W. QuincyAve., Denver, CO 80235, http:/www.awwa.org.6Available from Standardization Documents Order Desk, DODSSP, Bldg.

34、 4,Section D, 700 Robbins Ave., Philadelphia, PA 19111-5098, http:/dodssp.daps.dla.mil.7Available from NSF International, P.O. Box 130140, 789 N. Dixboro Rd., AnnArbor, MI 48113-0140, http:/www.nsf.org.F877 11a26.5 Hydrostatic Sustained Pressure Strength6.5.1 Tubing and fittings (tested as assemblie

35、s) shall meetthe minimum hydrostatic sustained pressure strength require-ments shown in Table 2 when tested in accordance with 7.4.6.5.1.1 Manifolds with integral shut-off (valves) shall betested with all ports in the full-open or unrestricted position.6.6 Thermocycling:6.6.1 Fittings, assembled usi

36、ng the manufacturers instruc-tions, shall not leak after completion of 1000 cycles betweenthe temperatures of 60F (16C) and 180F (82C) when testedin accordance with 7.5.6.6.1.1 Manifolds with integral shut-offs (valves) shall betested with all ports in the full open or unrestricted position.6.7 Exce

37、ssive TemperaturePressure Capability:6.7.1 GeneralIn the event of a water heating systemmalfunction, PEX tubing and system components shall haveadequate strength to accommodate short-term conditions, 48 hof 210F (99C), 150 psi (1034 kPa) until repairs can be made.6.7.2 Excessive Temperature Hydrosta

38、tic SustainedPressureTubing and system components, when tested asassemblies, shall not fail as defined in Test Method D1598 inless than 30 days (720 h) when tested in accordance with 7.7.6.7.2.1 Manifolds with integral shut-offs (valves) shall betested with all ports in the full open or unrestricted

39、 position.NOTE 2Tests applicable to assemblies and bends (6.4, 6.5, 6.6, and6.7) are intended to be performance qualification tests and not testsrequired of each fitting.7. Test Methods7.1 ConditioningThe test specimens should be condi-tioned at 70 to 77F (23 6 2C) and 50 6 5 % relativehumidity for

40、not less than 40 h prior to test in accordance withPractice D618, for those tests where conditioning is required.7.2 Test ConditionsConduct the tests in the standardlaboratory atmosphere of 70 to 77F (23 6 2C) and 50 6 5%relative humidity, unless otherwise specified in the test meth-ods or in this s

41、pecification.7.3 SamplingA sufficient quantity of tubing and systemcomponents, as agreed upon by the purchaser and the seller,shall be selected and tested to determine conformance with thisspecification (see Practice D1898). In the case of no prioragreement, random samples selected by the testing la

42、boratoryshall be deemed adequate.7.4 Hydrostatic Sustained Pressure Determine in accor-dance with Test Method D1598, except for the following:7.4.1 Test at least six joints, from randomly selected speci-mens assembled per the manufacturers instructions with atleast 5-pipe diameters between joints.7.

43、4.2 Test temperature shall be 180 6 4F (82 6 2C).7.4.3 The external test environment shall be air or water.7.4.4 Fill the specimens with water at a temperature of atleast 120F (50C).7.5 Thermocycling:7.5.1 Summary of Test MethodThis test method describesa pass-fail test for thermally cycling PEX tub

44、ing and systemcomponent assemblies over a critical temperature range for aselected number of cycles while subjected to a nominal internalpressure. This test method provides a measure of resistance tofailure due to the combined effects of differential thermalexpansion and creep for PEX tubing and fit

45、tings intended forcontinuous use up to and including 180F (82C).7.5.2 ApparatusA nitrogen or air source capable of main-taining a nominal internal pressure of 100 6 10 psi (0.69 60.069 MPa) on the specimens is required. The immersionsystem shall consist of two water reservoirs controlled at 60 64F (

46、166 2C) and 180 6 4F (82 6 2C). The specimen shallbe cycled from one reservoir to the other or the hot and coldwater shall be alternately cycled over the test specimensautomatically and returned to the proper reservoirs.NOTE 3Automatic cycling may be accomplished by pumping fromeach reservoir, throu

47、gh a delivery system having timer-actuated valves, toa specimen water trough having synchronized, timer-actuated returndrains. Any automatic apparatus shall provide for complete immersion ofthe test specimen in the trough.7.5.3 Sampling and Specimen Preparation Select at leastsix joints from randoml

48、y selected specimens assembled per themanufacturers instructions. Close the specimen assembly withany suitable end closures that allow “free-end” mounting andwill not leak under the thermocycling conditions, and connectthe specimen assembly to the pressure source.7.5.4 ProcedurePressurize the specim

49、en assembly withnitrogen or air to 100 6 10 psi (0.69 6 0.069 MPa) . Immersein 60 6 4F (16 6 2C) water to determine if there are anyinitial leaks. All leaks shall be eliminated before the thermo-cycling test is started. Thermally cycle the specimen assemblyeither manually or automatically and under an internal pressureof 100 6 10 psi (0.696 0.069 MPa), alternately between 60 64F (16 6 2C) and 180 6 4F (82 6 2C) by means ofimmersion in water using the following test cycle:TABLE 1 Burst Pressure Requirements forSDR9 PEX T