ASTM F628-2012 Standard Specification for Acrylonitrile-Butadiene-Styrene (ABS) Schedule 40 Plastic Drain Waste and Vent Pipe With a Cellular Core《带有多孔芯的40号表丙烯腈-丁二烯-苯乙烯 (ABS) 塑料排水管.pdf

《ASTM F628-2012 Standard Specification for Acrylonitrile-Butadiene-Styrene (ABS) Schedule 40 Plastic Drain Waste and Vent Pipe With a Cellular Core《带有多孔芯的40号表丙烯腈-丁二烯-苯乙烯 (ABS) 塑料排水管.pdf》由会员分享，可在线阅读，更多相关《ASTM F628-2012 Standard Specification for Acrylonitrile-Butadiene-Styrene (ABS) Schedule 40 Plastic Drain Waste and Vent Pipe With a Cellular Core《带有多孔芯的40号表丙烯腈-丁二烯-苯乙烯 (ABS) 塑料排水管.pdf（12页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: F628 08F628 12 An American National StandardStandard Specification forAcrylonitrile-Butadiene-Styrene (ABS) Schedule 40 PlasticDrain, Waste, and Vent Pipe With a Cellular Core1This standard is issued under the fixed designation F628; the number immediately following the designation indi

2、cates the year of originaladoption or, in the case of revision, the year of last revision.Anumber in parentheses indicates the year of last reapproval.Asuperscriptepsilon () indicates an editorial change since the last revision or reapproval.1. Scope*1.1 This specification covers coextruded acryloni

3、trile-butadiene-styrene (ABS) plastic drain, waste, and vent pipe made toSchedule 40 iron pipe sizes (IPS) and produced by the coextrusion process with concentric inner and outer solid ABS layers andthe core consisting of closed-cell cellular ABS. Plastic which does not meet the material requirement

4、s specified in Section 5 isexcluded from single layer and all coextruded layers.1.2 Fittings suitable for use with pipe meeting the requirements of this specification are given in Annex A1. Fittings meetingthe requirement of Specification D2661 are also acceptable.1.3 Acrylonitrile-butadiene-styrene

5、 plastic which does not meet the definitions of virgin ABS plastic as given in 3.2.4 isexcluded, as performance of plastic other than those defined as virgin was not determined. ABS rework plastic which meets therequirements of rework plastic as given in 5.3 is acceptable.1.4 Reprocessed plastic or

6、recycled plastic as defined in Terminology D883 is excluded.1.5 Recommendations for storage, joining, and installation are provided in Appendixes X1, X2, and X3, respectively.1.6 The text of this specification references notes, footnotes, and appendixes which provide explanatory material. These note

7、sand footnotes (excluding those in tables and figures) shall not be considered as requirements of the specification.1.7 The values stated in inch-pound units are to be regarded as the standard. The values given in parentheses are for informationonly.2. Referenced Documents2.1 ASTM Standards:2D618 Pr

8、actice for Conditioning Plastics for TestingD883 Terminology Relating to PlasticsD1600 Terminology for Abbreviated Terms Relating to PlasticsD1898 Practice for Sampling of Plastics (Withdrawn 1998)3D2122 Test Method for Determining Dimensions of Thermoplastic Pipe and FittingsD2235 Specification for

9、 Solvent Cement for Acrylonitrile-Butadiene-Styrene (ABS) Plastic Pipe and FittingsD2321 Practice for Underground Installation of Thermoplastic Pipe for Sewers and Other Gravity-Flow ApplicationsD2412 Test Method for Determination of External Loading Characteristics of Plastic Pipe by Parallel-Plate

10、 LoadingD2444 Test Method for Determination of the Impact Resistance of Thermoplastic Pipe and Fittings by Means of a Tup (FallingWeight)D2661 Specification for Acrylonitrile-Butadiene-Styrene (ABS) Schedule 40 Plastic Drain, Waste, and Vent Pipe and FittingsD3311 Specification for Drain, Waste, and

11、 Vent (DWV) Plastic Fittings PatternsD3965 Classification System and Basis for Specifications for Rigid Acrylonitrile-Butadiene-Styrene (ABS) Materials for Pipeand FittingsD5360 Practice for Design and Construction of Bituminous Surface TreatmentsE105 Practice for Probability Sampling of Materials1

12、This specification is under the jurisdiction of ASTM Committee F17 on Plastic Piping Systems and is the direct responsibility of Subcommittee F17.63 on DWV.Current edition approved May 1, 2008Nov. 15, 2012. Published May 2008January 2013. Originally approved in 1979. Last previous edition approved i

13、n 20062008 asF628 06F628 08.1.DOI:10.1520/F0628-08.10.1520/F0628-12.2 For referencedASTM standards, visit theASTM website, www.astm.org, or contactASTM Customer Service at serviceastm.org. For Annual Book of ASTM Standardsvolume information, refer to the standards Document Summary page on the ASTM w

14、ebsite.3 The last approved version of this historical standard is referenced on www.astm.org.This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Becauseit may not be technically possi

15、ble to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current versionof the standard as published by ASTM is to be considered the official document.*A Summary of Changes section appears at the end of this standardCopy

16、right ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States1E1508 Guide for Quantitative Analysis by Energy-Dispersive SpectroscopyE122 Practice for Calculating Sample Size to Estimate, With Specified Precision, the Average for a Characteristic of a

17、Lot orProcessF402 Practice for Safe Handling of Solvent Cements, Primers, and Cleaners Used for Joining Thermoplastic Pipe and FittingsF412 Terminology Relating to Plastic Piping SystemsF1498 Specification for Taper Pipe Threads 60 for Thermoplastic Pipe and Fittings2.2 Federal Standard:Fed. Std. No

18、. 123 Marking for Shipment (Civil Agencies)42.3 Military Standard:MIL-STD-129 Marking for Shipment and Storage43. Terminology3.1 Definitions:3.1.1 Definitions are in accordance with Terminology F412, and abbreviations are in accordance with Terminology D1600,unless otherwise specified. The abbreviat

19、ion for acrylonitrile-butadiene-styrene plastic is ABS.3.1.2 cellular plastica plastic containing numerous cells, intentionally introduced, interconnecting or not, distributedthroughout the mass.3.1.3 closed-cell cellular plasticcellular plastic in which almost all the cells are noninterconnecting.3

20、.1.4 coextruded pipepipe consisting of two or more concentric layers of material bonded together in processing by anycombination of temperature, pressure, grafting, crosslinking, or adhesion.3.1.5 coextrusiona process whereby two or more heated or unheated plastic material streams forced through one

21、 or moreshaping orifice(s) become one continuously formed piece.3.1.6 room temperaturea temperature in the range from 68 to 85 6 3.6F (20 to 30 6 2C).3.2 Definitions of Terms Specific to This Standard:3.2.1 lota lot shall consist of all pipe produced, of one size, from one extrusion line, during one

22、 designated 24-h period.3.2.2 recycled plastica plastic prepared from discarded articles that have been cleaned and reground.3.2.3 reprocessed plastica thermoplastic prepared from usually melt processed scrap or reject parts by a plastics processor,or from nonstandard or nonuniform virgin material.3

23、.2.4 virgin ABS plasticplastic in the form of pellets, granules, powder, floc, or liquid that has not been subjected to use orprocessing other than that required for its initial manufacture.4. Classification4.1 Pipe produced in accordance with this specification is intended to provide pipe suitable

24、for the drainage and venting ofsewage and certain other non-hazardous liquid wastes.NOTE 1Before installing pipe for waste disposal use, the approval of the cognizant building code authority should be obtained as conditions notcommonly found in normal use may be encountered and temperatures in exces

25、s of 180F (82C) may be encountered.NOTE 2This specification does not include requirements for pipe intended to be used to vent combustion gases.5. Materials5.1 Material SpecificationVirginABS plastic shall conform to the requirements prescribed in Specification D3965 with a cellclassification of 4-2

26、-2-2-2. The color and form of the material shall be as agreed upon between the seller and the purchaser inaccordance with Specification D3965.5.2 The ABS plastic shall conform to the following requirements:5.2.1 Acrylonitrile-Butadiene-Styrene (ABS) PlasticPlastic shall contain a minimum of 15 % acr

27、ylonitrile, 6 % butadiene, and15 % styrene or substituted styrene, or both, of polymers or blends of polymers.5.2.2 ABS plastic shall contain no more than 10 % of other monomeric or polymeric components plus other necessarycompounding ingredients.5.3 Rework MaterialThe manufacturer shall use only hi

28、s own clean rework pipe material conforming with these cell classrequirements. Use it only in the core layer. The pipe produced shall meet all the requirements of this specification.6. Requirements6.1 GeneralThe pipe and fittings should be homogeneous throughout and free of visible cracks, holes, fo

29、reign inclusions, orother injurious defects. The pipe shall be as uniform as commercially practicable in color, opacity, density, and other physicalproperties.4 Available from Standardization Documents Order Desk, DODSSP, Bldg. 4, Section D, 700 Robbins Ave., Philadelphia, PA 19111-5098, http:/www.d

30、odssp.daps.mil.F628 1226.1.1 The requirements in this section are intended only for use as quality control tests, not as simulated service tests.6.2 Dimension and Tolerance:6.2.1 Outside DiameterThe outside diameter and tolerances shall meet the requirements of Table 1 when measured inaccordance wit

31、h Test Method D2122. The tolerances for out-of-roundness shall apply to pipe prior to shipment.6.2.2 Wall ThicknessThe wall thickness and tolerances shall meet the requirements of Table 2 when measured in accordancewith Test Method D2122.6.2.3 LengthThe pipe shall be in either 10 or 20-ft (3.05 or 6

32、.1-m) lengths, unless otherwise specified. The allowable toleranceon length shall be +12, 0 in. (+12, 0 mm).6.3 Performance Requirements:6.3.1 Pipe StiffnessThe minimum pipe stiffness values at 5 % deflection when measured in accordance with Test MethodD2412, shall equal or exceed the values in Tabl

33、e 3. The rate of crosshead motion shall be 0.20 to 0.25 in./min (5.1 to 6.3 mm/min).Three specimens shall be tested. If all three meet this requirement, the sample meets this requirement. If one or two fail, additionaltesting shall be conducted in accordance with 6.3.1.1. If all three fail, the samp

34、le does not meet the requirement.6.3.1.1 Pipe Stiffness and Lower Confidence LimitIn the event that one or two of the specimens tested in 6.3.1 fail to meetthe minimum requirement, the average pipe stiffness of eleven specimens shall meet or exceed the minimum requirement givenin Table 3. The 99 % l

35、ower confidence limit (LCL) shall be within 15 % of the average value. The LCL shall be calculated usingthe Students “t” distribution, with N-1 degrees of freedom, where N is the number of specimens. The critical t value shall be usedto at least three significant digits. Alternatively, if the LCL ex

36、ceeds the minimum pipe stiffness requirement in Table 3, but is notwithin 15 % of the average, the sample meets the requirements of the Pipe Stiffness testing. The eleven specimens include the threetested under 6.3.1, and an additional eight with rotation by 35, as specified in Test Method D2412, co

37、ntinuing throughout theremaining specimens.6.3.1.2 The LCL based on testing eleven specimens is calculated as follows:LCL5avg PS!2$2.76std. dev.!/=N!%where:avg PS!5(PSi!#/11! (1)std. dev.!5F(PS2 2(PS! 2 /NN 21 G1/2N 511.6.3.1.3 The 15 % requirement is calculated as follows:avg2LCL!/avg!3100#15%NOTE

38、3For quality control testing, a single specimen may be used with the thinnest wall at the top.NOTE 4The 5 % deflection criterion, which was arbitrarily selected for testing convenience, should not be considered as a limitation with respect toin-use deflection. The engineer is responsible for establi

39、shing the acceptable deflection limit.NOTE 5The strength and load-carrying capabilities of plastic pipe are measured and reported as pipe stiffness, which is determined in accordancewith Test Method D2412. The term “crush strength” is not applicable to plastic piping because the values obtained can

40、be significantly different,depending on the bedding, loading, or testing technique used, and the term derives from rigid pipe and refers to its ultimate strength at rupture.6.3.2 Pipe FlatteningThere shall be no evidence of rupture when pipe is deflected 25 % of the initial inside diameter whenteste

41、d in accordance with Test Method D2412. Three specimens shall be tested; all shall meet the requirements. Failure shall bea crack or break extending entirely through the pipe wall visible to the unaided eye.6.3.3 Impact StrengthThe minimum impact resistance, when tested at the time of manufacture, s

42、hall comply with Table 4.Testin accordance with Test Method D2444 using Tup A and Holder B. Use 12lb (5 kg) tup for testing pipe sizes 4 in. and smallerand a 20lb (10kg) tup for sizes larger than 4 in.TABLE 1 Outside Diameters and Tolerances for ABS Schedule 40 Plastic Drain, Waste, and Vent Pipe Pr

43、oduced by the CoextrusionProcess with Concentric Inner and Outer Solid ABS-Layers and the Core Consisting of Closed-Cell Cellular ABSNominal Pipe Size,in.Outside DiameterAverage, in. (mm) Tolerance on Average,in. (mm)Out-of-Roundness MaximumDiameter Minus MinimumDiameter, in. (mm)A114 1.660 (42.16)

44、+0.010, 0.000 (+0.25, 0.00) 0.024 (0.60)112 1.900 (48.26) +0.010, 0.000 (+0.25, 0.00) 0.024 (0.60)2 2.375 (60.32) +0.010, 0.000 (+0.25, 0.00) 0.024 (0.60)3 3.500 (88.90) +0.015, 0.000 (+0.38, 0.00) 0.030 (0.76)4 4.500 (114.30) +0.015, 0.000 (+0.38, 0.00) 0.100 (2.54)6 6.625 (168.28) +0.011, 0.011 (+

45、0.28, 0.28) 0.100 (2.54)A Measured at time of manufacturing.F628 1236.3.3.1 Test 10 specimens. When 9 or 10 specimens pass, accept the lot. When 2 or more specimens fail, test 10 additionalspecimens.When 17 of 20 specimens tested pass, accept the lot.When 4 or more of 20 specimens fail, test 20 addi

46、tional specimens.When 32 of 40 specimens pass, accept the lot. When 9 or more of 40 specimens fail, the lot does not meet the requirements ofthis specification.6.3.3.2 Failure of the test specimen shall be shattering or any crack or break extending entirely through the pipe wall and visibleto the un

47、aided eye.6.3.4 BondThe bond between layers shall be strong and uniform. It shall not be possible to separate any two layers with aprobe or point of a knife blade so that the layers separate cleanly, or so the probe or knife blade moves freely between the layers;nor shall separation of bond occur be

48、tween layers during testing performed under the requirements of this specification.6.3.5 Pigments or Screening AgentsThe ABS compound used in the outer layer shall contain pigments or screening agentsto provide protection against UV radiation.6.4 Other Requirements:6.4.1 InspectionInspection shall b

49、e made prior to installation of all pipe. Pipe that does not meet the requirements of 6.1 shallbe returned to the seller.6.4.2 JoiningCoextruded ABS Schedule 40 drain, waste, and vent pipe with a cellular core are joined using molded fittingsmeeting the requirements of Specifications D2661 and D3311 or the requirements for fittings listed in the Annex of thisspecification.TABLE 2 Wall Thickness and Tolerance for ABS Schedule 40Plastic Drain, Waste, and Vent Pipe Produced by the CoextrusionProcess with Concent