ASTM F1860-2014 Standard Specification for Rubber Sheet Floor Covering With Backing《有背衬的橡胶薄板楼面覆盖层的标准规格》.pdf

《ASTM F1860-2014 Standard Specification for Rubber Sheet Floor Covering With Backing《有背衬的橡胶薄板楼面覆盖层的标准规格》.pdf》由会员分享，可在线阅读，更多相关《ASTM F1860-2014 Standard Specification for Rubber Sheet Floor Covering With Backing《有背衬的橡胶薄板楼面覆盖层的标准规格》.pdf（5页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: F1860 12F1860 14Standard Specification forRubber Sheet Floor Covering With Backing1This standard is issued under the fixed designation F1860; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last revision. A

2、 number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification covers the requirements for the compound and physical characteristics of rubber sheet floor coveringhaving a rubber

3、 wear layer with backing. Products may also contain intermediate layers.1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematicalconversions to SI units that are provided for information only and are not considered standard.1.3 The fol

4、lowing precautionary statement pertains only to the test method portion, Section 10, of this specification: Thisstandard does not purport to address all the safety concerns, if any, associated with its use. It is the responsibility of the user ofthis standard to establish appropriate safety and heal

5、th practices and determine the applicability of regulatory limitations priorto use.2. Referenced Documents2.1 The following documents if the issue in effect on the date of the material purchase form a part of this specification to theextent referenced herein:2.2 ASTM Standards:2D412 Test Methods for

6、 Vulcanized Rubber and Thermoplastic ElastomersTensionD883 Terminology Relating to PlasticsD1566 Terminology Relating to RubberD2240 Test Method for Rubber PropertyDurometer HardnessF141 Terminology Relating to Resilient Floor CoveringsF387 Test Method for Measuring Thickness of Resilient Floor Cove

7、ring With Foam LayerF410 Test Method for Wear Layer Thickness of Resilient Floor Coverings by Optical MeasurementF710 Practice for Preparing Concrete Floors to Receive Resilient FlooringF925 Test Method for Resistance to Chemicals of Resilient FlooringF970 Test Method for Static Load LimitF1482 Prac

8、tice for Installation and Preparation of Panel Type Underlayments to Receive Resilient FlooringF1514 Test Method for Measuring Heat Stability of Resilient Flooring by Color ChangeF1515 Test Method for Measuring Light Stability of Resilient Flooring by Color Change2.3 ANSI Standards:ANSI/ASQC Z1.4 Sa

9、mpling Procedures and Tables for Inspection by Attributes33. Terminology3.1 DefinitionsFor definitions of other terms used in this standard, see Terminology F141.4. Classification4.1 TypesRubber sheet floor covering covered by this specification shall conform to the following types:4.1.1 Type IHomog

10、eneous1 This specification is under the jurisdiction of ASTM Committee F06 on Resilient Floor Coveringsand is the direct responsibility of Subcommittee F06.80 onSpecifications.Current edition approved May 1, 2012Nov. 1, 2014. Published May 2012December 2014. Originally approved in 1998. Last previou

11、s edition approved in 20102012 asF1860-10.-12. DOI: 10.1520/F1860-12.10.1520/F1860-14.2 For referencedASTM standards, visit theASTM website, www.astm.org, or contactASTM Customer Service at serviceastm.org. For Annual Book of ASTM Standardsvolume information, refer to the standards Document Summary

12、page on the ASTM website.3 Available from American National Standards Institute (ANSI), 25 W. 43rd St., 4th Floor, New York, NY 10036, http:/www.ansi.org.This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to

13、 the previous version. Becauseit may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current versionof the standard as published by ASTM is to be considered the official document.Copyrigh

14、t ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States14.1.2 Type IIHeterogeneous4.2 GradesRubber sheet floor covering shall be one of the following grades:4.2.1 Grade 1Fibrous backing4.2.2 Grade 2Foamed rubber backing4.3 The above may have either s

15、mooth, embossed, or molded pattern surfaces.4.4 These products shall not contain asbestos.5. Ordering Information5.1 Purchasers shall state whether this specification is to be used, select the preferred options permitted herein and include thefollowing information in the invitation to bid or purchas

16、e order:5.1.1 Title, number, and date of this specification,5.1.2 Type, color, and surface (see Section 4 and Section 6),5.1.3 Quantity, in square feet, square yards, or square metres,5.1.4 Thickness required. (see 8.3),5.1.5 Overall thickness, if molded pattern flooring is specified (see 8.1),5.1.6

17、 Width required (see 8.4),5.1.7 Length required (see 8.5),5.1.8 Resistance to chemicals, (see 7.4),5.1.9 Lot information, if other than as specified in AANSI/ASQC Z1.4. (see 10.1 and 11.1),5.1.10 Sampling, if other than as specified in ANSI/ASQC Z1.4 (see 10.1 and 11.1),5.1.11 Statement requesting c

18、ertification, if certification of compliance is required (see 12.1),5.1.12 Packing requirements, if other than as specified (see 14.1),5.1.13 Palletization, if required,5.1.14 Marking required, if other than specified (see 13.1), and5.1.15 Other requirements.6. Materials and Manufacture6.1 Homogeneo

19、us Rubber Sheet Floor CoveringThe product shall consist of a wear layer and backing. The surface coloringor mottling shall be uniform throughout the entire thickness of the wear layer. The backing shall be fibrous or foamed rubber andthoroughly bonded to the wear layer so as not to delaminate under

20、normal use.6.2 Heterogeneous (Layered) Rubber Sheet Floor CoveringThe product shall consist of a wear layer, intermediate layer(s),and a backing. The surface coloring or mottling shall be uniform throughout the entire thickness of the wear layer, but need notextend through the intermediate layer(s).

21、 The backing shall be fibrous or foamed rubber. The wear layer, intermediate layer(s) andbacking shall be thoroughly bonded so as not to delaminate under normal use.6.3 Wear Layer:6.3.1 The polymeric binder of the wear layer shall satisfy the definition of rubber in Terminology D1566, and have beenv

22、ulcanized, as defined in Terminology D1566 (under vulcanization), such that it becomes thermoset as defined in TerminologyD883. The wear layer made from this compound shall be resistant to neutral pH cleaners.6.3.2 The wear layer must have a minimum thickness of 0.040 in. (1.0 mm) when measured in a

23、ccordance with Test MethodF410.6.3.3 The appearance of the rubber sheet floor covering after removing 0.020 in. (0.51 mm) of the wear layer thickness, shallcompare favorably in appearance with the sheet floorings original appearance. The removal of the wear layer may beaccomplished by any suitable m

24、ethod.6.3.4 The wear layer may have a smooth, embossed, or molded pattern surface.6.4 Intermediate LayersThe layer(s) may consist of, but not be limited to, rubber, foamed rubber, or other materials, whichare intended to improve the performance characteristics of the product.6.5 BackingsThe composit

25、ion of the backings shall be fibrous or foamed rubber and may contain other ingredients providedthe resultant backing is suitable for installation on floors above-, on-, or below-grade when installed according to manufacturersinstallation recommendations.6.6 Color, Pattern, and Wearing SurfaceThe co

26、lor, pattern, and wear layer surface, as applicable, shall be as specified in thecontract or order (see 5.1).NOTE 1The colors and patterns that are available are indicated in individual manufacturers current catalogs. As manufactured, colors may varysomewhat in hue or shade from the catalog.NOTE 2Wh

27、ere color match is a concern, samples from the manufacturer shall be obtained to verify color acceptability.F1860 1427. Performance Requirements7.1 HardnessThe rubber sheet floor covering shall have a durometer hardness of not less than 85 (Shore, TypeA) when testedin accordance with Test Method D22

28、40. The backing material shall be removed prior to testing and may be accomplished by anysuitable method.7.2 Modulus at 10 % ElongationWhen tested in accordance with Test Method D412 at a rate of 6 in. (152.4 mm)/min, usinga 1 in. (25.4 mm) by 5 in. (127 mm) gage length rectangular specimen, the mod

29、ulus shall not be less than 300 psi (2.07 MPa).For molded pattern rubber sheet floor covering, the raised pattern shall be removed by any suitable method. Prior to testing, thebacking material shall be removed and may be accomplished by any suitable method.7.3 Static Load LimitWhen tested in accorda

30、nce with Test Method F970, with an applied load of 250 lb (113.4 kg), theresidual indentation shall not be greater than 0.005 in. (0.127 mm).7.4 Resistance to ChemicalsWhen tested in accordance with Test Method F925, the rubber sheet floor covering shall have nomore than a slight change in surface d

31、ulling, surface attack, or staining when exposed to the flowing chemicals:7.4.1 White vinegar (5 % acetic acid),7.4.2 Rubbing alcohol (70 % isopropyl alcohol),7.4.3 Sodium hydroxide solution (5 % NaOH),7.4.4 Hydrochloric acid solution (5 % HCl),7.4.5 Sulfuric acid solution (5 % H2SO4),7.4.6 Househol

32、d ammonia solution (5 % NH4OH),7.4.7 Household bleach solution (5.25 % NaOCl),NOTE 3These basic chemicals are representative of those likely to be found in domestic, commercial, and institutional use. Many proprietarycompounds contain one or more of these basic chemicals. Should the flooring for an

33、unusual application need to be resistant to a specific chemical, thisadditional requirement should become part of the procurement document, (see 5.1.8).NOTE 4Since standard SBR rubber flooring is not recoommended for installation where the product will be exposed to animal fats, vegetable oils,and p

34、etroleum-based reagents, mineral oil, olive oil, kerosene, and gasoline have been removed from the standard chemical list to eliminate any confusionregarding product selection.7.5 Resistance to HeatWhen tested in accordance to Test Method F1514, the color change of the rubber sheet floor coveringsha

35、ll have an average E not greater than 8.0 after seven days exposure to 158F (70C). The specimen surface shall be wipedwith a clean, white cotton cloth prior to taking the initial and post test conditioned period color readings to remove any wax bloomor other contaminants which may affect the accurac

36、y of the color readings.7.6 Resistance to LightWhen tested in accordance to Test MethodExisting Q-UV and Xenon-arc test methods used F1515, thecolor change of the rubber sheet floor covering shall have an average to test rubber floor tiles, rubber sheets and rubber stairEnot greater than 8.0 after 3

37、00 h of exposure to light, simulated by a properly fitted xenon-arc radiant energy source.treads resultedin extremely high failure rates which are not typical in everyday use of these products.8. Dimensions, Mass, and Permissible Variations8.1 Overall ThicknessMolded pattern rubber sheet floor cover

38、ing shall be measured for overall thickness at the thickest crosssectional area of the flooring. The thickness of the molded pattern shall be uniform throughout the flooring.8.2 Base ThicknessMolded pattern rubber sheet floor covering base thickness shall be measured at the thinnest cross sectionala

39、rea of the flooring. The thinnest cross sectional area shall be uniform throughout the flooring.8.3 ThicknessThe thickness of the rubber sheet floor covering shall be as specified in the contract or order (see 5.1.4). Anaverage tolerance, based on five individual measurements, of60.008 in. (60.2 mm)

40、 from the specified thickness shall be permittedin the base thickness alone or in combination with the overall thickness, when measured in accordance with Test Method F387.The difference between the five individual measurements can not be greater than 0.010 in. (0.25 mm) from the nominal thickness.I

41、n the case of molded pattern rubber sheet floor covering, overall thickness and base thickness shall be reported.8.4 WidthThe width shall be as specified in the contract or order (see 5.1.6). The net width (gross width less selvages) shallnot be less than as marked on the label or package when measu

42、red in accordance with 8.6.8.5 LengthThe length of the roll shall be as specified in the contract or order (see 5.1.7). The sheet length shall not be lessthan as marked on the label or package when measured in accordance with 8.6. Each roll shall be in one piece, except that lessthan 20 % of the rol

43、ls in any one shipment may consist of not more than two pieces, the shortest length shall not be less than 5linear yards (4.57 m), or as agreed upon by the purchaser and seller. Such rolls shall be clearly marked.8.6 Length and Width MeasurementsMeasurements shall be made with a calibrated 100 ft (3

44、0 m) steel tape graduated atintervals of 116 in. or 1 mm. The roll shall be extended to its full length on a flat surface and all creases and buckles removed,insofar as practical, without applying stresses that cause any significant stretching. Measurements of length shall be rounded to thenearest i

45、nch or 10 mm. Net width shall be measured to the nearest 116 in. or 1 mm at not less than ten locations uniformlydistributed along the length of each roll, and the results averaged.F1860 1439. Workmanship, Finish, and Appearance9.1 The rubber sheet floor covering furnished in accordance with this sp

46、ecification shall be an acceptable match to approvedsamples in color, pattern, and appearance. The product shall be free of defects, that adversely affect performance or appearance.Such defects include: blemishes, spots, lines, indentations, blisters, and delamination.10. Sampling for Test10.1 Sampl

47、ing for testing physical characteristics listed in Table 1 shall be done in accordance with the provisions set forth inANSI/ASQC Z1.4. The inspection level shall be special inspection level S-1, as noted in Table I of ANSI/ASQC Z1.4, and theacceptable quality level (AQL) shall be 6.5 defects per hun

48、dred units as noted in Table II-(A) ofANSI/ASQC Z1.4 or as otherwisespecified in 10.2. The lot size shall be expressed in units. A unit represents a single, manufactured, inventoried, finished roll.10.1.1 Samples shall be obtained in the required length from the outside end of the roll and shall enc

49、ompass the total width ofthe material.10.2 Sampling for testing physical characteristics listed in Table 1 shall be agreed upon by the purchaser and the manufactureras part of the procurement document.11. Inspection11.1 Sampling for inspection of the rubber sheet floor covering for defects that would adversely affect performance (see 9.1)shall be done in accordance with the provisions set forth in ANSI/ASQC Z1.4. The inspection level shall be Level I as noted inTable I of ANSI/ASQC Z1.4 with an acceptable quality level (AQL) of 6.5 defects p