ASTM F1859-2014e1 Standard Specification for Rubber Sheet Floor Covering Without Backing《不带衬垫的橡胶板底层的标准规格》.pdf

《ASTM F1859-2014e1 Standard Specification for Rubber Sheet Floor Covering Without Backing《不带衬垫的橡胶板底层的标准规格》.pdf》由会员分享，可在线阅读，更多相关《ASTM F1859-2014e1 Standard Specification for Rubber Sheet Floor Covering Without Backing《不带衬垫的橡胶板底层的标准规格》.pdf（4页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: F1859 141Standard Specification forRubber Sheet Floor Covering Without Backing1This standard is issued under the fixed designation F1859; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last revision. A num

2、ber in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1NOTEReference to Test Method F1515 in Table 1 was removed editorially in April 2016.1. Scope1.1 This specification covers the requirements for the co

3、m-pound and physical characteristics of rubber sheet floor cov-ering without backing.1.2 The values stated in inch-pound units are to be regardedas standard. The values given in parentheses are mathematicalconversions to SI units that are provided for information onlyand are not considered standard.

4、1.3 The following precautionary statement pertains only tothe test method portion, Section 10, of this specification: Thisstandard does not purport to address all the safety concerns, ifany, associated with its use. It is the responsibility of the userof this standard to establish appropriate safety

5、 and healthpractices and determine the applicability of regulatory limita-tions prior to use.2. Referenced Documents2.1 The following documents of the issue in effect on thedate of the material purchase form a part of this specification tothe extent referenced herein:2.2 ASTM Standards:2D412 Test Me

6、thods for Vulcanized Rubber and Thermoplas-tic ElastomersTensionD883 Terminology Relating to PlasticsD1566 Terminology Relating to RubberD2240 Test Method for Rubber PropertyDurometer Hard-nessF141 Terminology Relating to Resilient Floor CoveringsF386 Test Method for Thickness of Resilient Flooring

7、Ma-terials Having Flat SurfacesF410 Test Method for Wear Layer Thickness of ResilientFloor Coverings by Optical MeasurementF710 Practice for Preparing Concrete Floors to ReceiveResilient FlooringF925 Test Method for Resistance to Chemicals of ResilientFlooringF970 Test Method for Static Load LimitF1

8、482 Practice for Installation and Preparation of PanelType Underlayments to Receive Resilient FlooringF1514 Test Method for Measuring Heat Stability of ResilientFlooring by Color ChangeF1515 Test Method for Measuring Light Stability of Resil-ient Flooring by Color Change2.3 ANSI Standard:ANSI/ASQC Z

9、1.4 Sampling Procedures and Tables for In-spection by Attributes33. Terminology3.1 DefinitionsFor definitions of other terms used in thisstandard, see Terminology F141.4. Classification4.1 Rubber sheet floor covering covered by this specifica-tion shall conform to the following types:4.1.1 Type IHom

10、ogeneous rubber sheet floor covering,4.1.2 Type IIHeterogeneous (Layered) rubber sheet floorcovering.4.2 The above may have either smooth, embossed, ormolded pattern surfaces.4.3 These products shall not contain asbestos.5. Ordering Information5.1 Purchasers shall state whether this specification is

11、 to beused, select the preferred options permitted herein and includethe following information in the invitation to bid or purchaseorder:5.1.1 Title, number, and date of this specification,5.1.2 Type, color, and surface (see Section 4 and Section 6),1This specification is under the jurisdiction of A

12、STM Committee F06 onResilient Floor Coverings and is the direct responsibility of Subcommittee F06.80on Specifications.Current edition approved Nov. 1, 2014. Published December 2014. Originallyapproved in 1998. Last previous edition approved in 2012 as F1859-12. DOI:10.1520/F1859-14.2For referenced

13、ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.3Available from American National Standards Institute (ANSI), 25 W. 43rd St.,

14、4th Floor, New York, NY 10036, http:/www.ansi.org.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States15.1.3 Quantity, in square feet, square yards, or squaremetres,5.1.4 Thickness required. (see Section 8),5.1.5 Overall thickness, if mold

15、ed pattern sheet flooring isspecified (see 8.1),5.1.6 Width required (see 8.4),5.1.7 Length required (see 8.5),5.1.8 Resistance to chemicals, (see 7.4),5.1.9 Lot information, if other than as specified in ANSI/ASQC Z1.4 (see 10.1 and 11.1),5.1.10 Sampling, if other than as specified in ANSI/ASQCZ1.4

16、 (see 10.1 and 11.1),5.1.11 Statement requesting certification, if certification ofcompliance is required (see 12.1),5.1.12 Packing requirements, if other than as specified (see14.1),5.1.13 Palletization, if required,5.1.14 Marking required, if other than specified (see 13.1),and5.1.15 Other require

17、ments.6. Materials and Manufacture6.1 MaterialThe polymeric binder of the rubber sheetfloor covering shall satisfy the definition of rubber in Termi-nology D1566, and have been vulcanized, as defined inTerminology D1566 (under vulcanization), such that it be-comes thermoset as defined in Terminology

18、 D883. The rubbersheet flooring made from this compound shall be resistant toneutral pH cleaners.6.2 Color, Pattern, and Wear Layer SurfaceThe color,pattern, and wear layer surface, as applicable, shall be asspecified in the contract or order (see 5.1).NOTE 1The colors and patterns that are availabl

19、e are indicated inindividual manufacturers current catalogs. As manufactured, colors mayvary somewhat in hue or shade from the catalog.NOTE 2Where color match is a concern, samples from the manufac-turer shall be obtained to verify color acceptability.6.3 Homogeneous Rubber Sheet Floor CoveringThe s

20、ur-face coloring or mottling shall be uniform throughout the entirethickness of the rubber sheet floor covering.6.4 Heterogeneous (Layered) Rubber Sheet FloorCoveringThe surface coloring or mottling need not extendthrough the entire thickness of the rubber sheet floor covering,but must extend throug

21、hout the entire thickness of the wearlayer.6.4.1 The wear layer must have a minimum thickness of0.040 in. (1.0 mm) when measured in accordance with TestMethod F410.6.4.2 The appearance of the rubber sheet floor covering,after removing 0.020 in. (0.51 mm) of the wear layer thickness,shall compare fav

22、orably in appearance with the rubber sheetfloorings original appearance. The removal of the wear layermay be accomplished by any suitable method.7. Performance Requirements7.1 HardnessThe rubber sheet floor covering shall have adurometer hardness of not less than 85 (Shore, Type A) whentested in acc

23、ordance with Test Method D2240.7.2 Modulus at 10 % ElongationWhen tested in accor-dance with Test Method D412 at a rate of 6 in. (152.4mm)/min, using a 1 in. (25.4 mm) by 5 in. (127 mm) gagelength rectangular specimen, the modulus shall not be less than300 psi (2.07 MPa). For molded pattern rubber s

24、heet floorcovering, the raised pattern shall be removed by any suitablemethod.7.3 Static Load LimitWhen tested in accordance with TestMethod F970, with an applied load of 250 lb (113.4 kg), theresidual indentation shall not be greater than 0.005 in. (0.127mm).7.4 Resistance to ChemicalsWhen tested i

25、n accordancewith Test Method F925, the rubber sheet floor covering shallhave no more than a slight change in surface dulling, surfaceattack, or staining when exposed to the following chemicals:7.4.1 White vinegar (5 % acetic acid),7.4.2 Rubbing alcohol (70 % isopropyl alcohol),7.4.3 Sodium hydroxide

26、 solution (5 % NaOH),7.4.4 Hydrochloric acid solution (5 % HCl),7.4.5 Sulfuric acid solution (5 % H2SO4),7.4.6 Household ammonia solution (5 % NH4OH),7.4.7 Household bleach (5.25 % NaOCl),NOTE 3These basic chemicals are representative of those likely to befound in domestic, commercial, and instituti

27、onal use. Many proprietarycompounds contain one or more of these basic chemicals. Should theflooring for an unusual application need to be resistant to a specificchemical, this additional requirement should become part of the procure-ment document (see 5.1.8).NOTE 4Since standard SBR rubber flooring

28、 is not recommended forinstallation where the product will be exposed to animal fats, vegetableoils, and petroleum-based reagents, mineral oil, olive oil, kerosene, andgasoline have been removed from the standard chemical list to eliminateany confusion regarding product selection.7.5 Resistance to H

29、eatWhen tested in accordance to TestMethod F1514, the color change of the rubber sheet floorcovering shall have an average E not greater than 8.0 afterseven days exposure to 158F (70C). The specimen surfaceshall be wiped with a clean, white cotton cloth prior to takingthe initial and post test condi

30、tioned period color readings toremove any wax bloom or other contaminants which mayaffect the accuracy of the color readings.7.6 Resistance to LightExisting Q-UV and Xenon-arc testmethods used to test rubber floor tiles, rubber sheets and rubberstair treads resulted in extremely high failure rates w

31、hich arenot typical in everyday use of these products.8. Dimensions, Mass, and Permissible Variations8.1 Overall ThicknessMolded pattern rubber sheet floorcovering shall be measured for overall thickness at the thickestcross-sectional area of the flooring. The thickness of themolded pattern shall be

32、 uniform throughout the flooring.8.2 Base ThicknessMolded pattern rubber sheet floorcovering base thickness shall be measured at the thinnestcross-sectional area of the flooring. The thinnest cross-sectional area shall be uniform throughout the flooring.8.3 ThicknessThe thickness of the rubber sheet

33、 floorcovering shall be as specified in the contract or order (see5.1.4). An average tolerance, obtained from five individualF1859 1412measurements, of 60.006 in. (60.15 mm) from the specifiedthickness shall be permitted in the base thickness alone or incombination with the overall thickness, when m

34、easured inaccordance with Test Method F386. The difference between thefive individual measurements can not be greater than 0.008 in.(0.2 mm). In the case of molded pattern rubber sheet floorcovering, overall thickness and base thickness shall be re-ported.8.4 WidthThe width shall be as specified in

35、the contract ororder (see 5.1.6). The net width (gross width less selvages)shall not be less than as marked on the label or package whenmeasured in accordance with 8.6.8.5 LengthThe length of the roll shall be as specified inthe contract or order (see 5.1.7). The sheet length shall not beless than a

36、s marked on the label or package when measured inaccordance with 8.6. Each roll shall be in one piece, except thatless than 20 % of the rolls in any one shipment may consist ofnot more than two pieces, the shortest length shall not be lessthan 5 linear yards (4.57 m), or as agreed upon by the purcha

37、serand seller. Such rolls shall be clearly marked.8.6 Length and Width MeasurementsMeasurements shallbe made with a calibrated 100 ft (30 m) steel tape graduated atintervals of116 in. or 1 mm. The roll shall be extended to itsfull length on a flat surface and all creases and bucklesremoved, insofar

38、as practical, without applying stresses thatcause any significant stretching. Measurements of length shallbe rounded to the nearest inch or 10 mm. Net width shall bemeasured to the nearest116 in. or 1 mm at not less than tenlocations uniformly distributed along the length of each roll,and the result

39、s averaged.9. Workmanship, Finish, and Appearance9.1 The rubber sheet floor covering furnished in accordancewith this specification shall be an acceptable match to approvedsamples in color, pattern, and appearance. The product shall befree of defects, which adversely affect performance or appear-anc

40、e. Such defects include: blemishes, spots, lines,indentations, blisters, and delamination.9.2 Unless otherwise specified in the contract or order (see5.1), the back or bonding surface of the rubber sheet floorcovering shall be buffed, roughened, ribbed, grooved, orotherwise modified to improve the a

41、dhesive bond of the rubbersheet floor covering, but in no case shall the thickness of theflooring be decreased to the extent that any depression orgroove on the bonding surface be perceptible, under anycircumstances, on the exposed surface.10. Sampling for Test10.1 Sampling for testing physical char

42、acteristics listed inTable 1 shall be done in accordance with the provisions setforth in ANSI/ASQC Z1.4. The inspection level shall bespecial inspection level S-1, as noted in Table I ofANSI/ASQCZ1.4, and the acceptable quality level (AQL) shall be 6.5defects per hundred units as noted in Table II-(

43、A) of ANSI/ASQC Z1.4 or as otherwise specified in 10.2. The lot size shallbe expressed in units. A unit represents a single, manufactured,inventoried, finished roll.10.1.1 Samples shall be obtained in the required length fromthe outside end of the roll and shall encompass the total widthof the mater

44、ial.10.2 Sampling for testing physical characteristics listed inTable 1 shall be agreed upon by the purchaser and themanufacturer as part of the procurement document.11. Inspection11.1 Sampling for inspection of the rubber sheet floorcovering for defects that would adversely affect performance(see 9

45、.1) shall be done in accordance with the provisions setforth in ANSI/ASQC Z1.4. The inspection level shall be LevelI as noted in Table I of ANSI/ASQC Z1.4 with an acceptablequality level (AQL) of 6.5 defects per hundred as noted inTable II(A) of ANSI/ASQC Z1.4or as otherwise specified in11.2. The lo

46、t size shall be expressed in units. A unit representsa single, manufactured, inventoried, finished roll.11.2 Inspection of the rubber sheet floor covering for defectsthat would adversely affect performance (see 9.1) shall beagreed upon by the purchaser and the manufacturer as part ofthe procurement

47、documents.12. Certification12.1 When specified in the purchase order or contract (see5.1.11), a manufacturers certification and any other documentsrequired to substantiate certification shall be furnished to thepurchaser that the product was manufactured to meet thisspecification.TABLE 1 Characteris

48、tics and TestsCharacteristic Requirement ASTM Test Method ReferenceComposition of Material Certificate of Compliance 6.1Wear Layer Thickness min 0.040 in. (1.0 mm) F410 6.4.1Hardness min 85 Shore A D2240 7.1Modulus at 10 % Elonga-tionmin 300 psi (2.07 MPa) D412 7.2Static Load Limit #0.005 in. (0.127

49、 mm) F970 7.3Resistance to Chemicals No more than a slightchange in surface dulling,surface attack, or staining.F925 7.4Resistance to Heat Ave. E not greater than 8.0 F1514 7.5Average Thickness 0.006 in. (0.15 mm) F386 8.3Width Not less than as specified Section 88.4Length Not less than as specified Section 5F1859 141313. Product Marking13.1 Unless otherwise specified in 5.1, the rubber sheet floorcovering shall be marked with the name of the material asdefined by the contract or order under which the shipment ismade, the pattern number, wi