ASTM E2254-2009 Standard Test Method for Storage Modulus Calibration of Dynamic Mechanical Analyzers《动态机械分析器的储能模量的标准试验方法》.pdf

《ASTM E2254-2009 Standard Test Method for Storage Modulus Calibration of Dynamic Mechanical Analyzers《动态机械分析器的储能模量的标准试验方法》.pdf》由会员分享，可在线阅读，更多相关《ASTM E2254-2009 Standard Test Method for Storage Modulus Calibration of Dynamic Mechanical Analyzers《动态机械分析器的储能模量的标准试验方法》.pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: E2254 09Standard Test Method forStorage Modulus Calibration of Dynamic MechanicalAnalyzers1This standard is issued under the fixed designation E2254; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last rev

2、ision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This test method describes the calibration or perfor-mance confirmation for the storage modulus scale of a com-mercial or cust

3、om built dynamic mechanical analyzer (DMA)over the temperature range of -100 to 300 C using referencematerials in the range of 1 to 200 GPa.1.2 The values stated in SI units are to be regarded asstandard. No other units of measurement are included in thisstandard.1.3 This standard does not purport t

4、o address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:2E473 Ter

5、minology Relating to Thermal Analysis and Rhe-ologyE1142 Terminology Relating to Thermophysical Properties3. Terminology3.1 DefinitionsSpecific technical terms used in this testmethod are defined in Terminologies E473 and E1142.4. Summary of Test Method4.1 The storage modulus signal determined by a

6、dynamicmechanical analyzer for an elastic reference material is com-pared to the reported storage modulus for that referencematerial. A linear relationship is used to correlate the experi-mental storage modulus signal with the reported value of thereference material.4.2 The mode of deformation (for

7、example, tensile, flexure,compression, etc.) shall be reported.5. Significance and Use5.1 This test method calibrates or demonstrates conformityof a dynamic mechanical analyzer at an isothermal temperaturewithin the range of -100 to 300 C.5.2 Dynamic mechanical analysis experiments often usetemperat

8、ure ramps. This method does not address the effect ofthat change in temperature on the storage modulus.5.3 A calibration factor may be required to obtain correctedstorage modulus values.5.4 This method may be used in research and development,specification acceptance, and quality control or assurance

9、.6. Apparatus6.1 The essential instrumentation required to provide theminimum dynamic mechanical capability for this test methodincludes:6.1.1 Drive Motor, to apply force (or displacement) to thespecimen in a periodic manner. This motor may also be capableof providing static force or displacement on

10、 the specimen.6.1.2 Coupling Shaft, or other means to transmit the forcefrom the motor to the specimen.6.1.3 Clamping System(s), to fix the specimen between thedrive shaft and the stationary clamp(s).6.1.4 Position Sensor, to measure the change in position ofthe specimen during dynamic motion, or,6.

11、1.5 Force Sensor, to measure the force applied to thespecimen.6.1.6 Temperature Sensor, to provide an indication of thespecimen temperature to 6 1 C.6.1.7 Furnace, to provide controlled heating or cooling of aspecimen at a constant temperature or at a constant rate withinthe applicable temperature r

12、ange of -100 to +300 C.6.1.8 Temperature Controller, capable of executing a spe-cific temperature program by operating the furnace between-100 and +300 C.6.1.9 A Data Collection Device, to provide a means ofacquiring, storing and displaying measured or calculated sig-nals, or both. The minimum outpu

13、t signals required are storagemodulus, loss modulus, tangent delta, temperature and time.1This test method is under the jurisdiction ofASTM Committee E37 on ThermalMeasurements and is the direct responsibility of Subcommittee E37.10 on Funda-mental, Statistical and Mechanical Properties.Current edit

14、ion approved Sept. 1, 2009. Published January 2010. Originalapproved in 2003. Last previous edition approved in 2008 as E225408. DOI:10.1520/E2254-09.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStand

15、ards volume information, refer to the standards Document Summary page onthe ASTM website.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.6.2 Auxiliary instrumentation considered necessary in con-ducting this method near or below ambi

16、ent room temperature.6.2.1 Cooling capability to sustain a constant temperatureat or below ambient room temperature or to provide controlledcooling.6.3 Micrometer, calipers or other length measuring devicecapable of measuring length of 1.0 to 100 mm with a precisionof 6 0.01 mm.7. Reagents and Mater

17、ials7.1 A reference material of known storage modulus, formedto the shape suitable for characterization by the particulardynamic mechanical analyzer (see Table 1).NOTE 1The storage modulus of the calibration materials used in thisstandard is often similar to that of the construction materials of the

18、 testapparatus. Thus the examination of high modulus materials may result ininstrument compliance during testing. The test apparatus calibrationprocedure (see 9.1) should include a compliance correction. The user ofthis standard shall verify whether or not such compliance corrections areincluded pri

19、or to its use.8. Sampling8.1 Test specimens are typically prepared in the form of arectangular test bars or film strips.NOTE 2It is common practice to bevel or “break” edges of machinedparts. This practice shall not be followed in the preparation of testspecimens for this method. The measured storag

20、e modulus of such testspecimens reads low due to imperfect sample geometry.9. Calibration and Standardization9.1 Perform any storage modulus signal calibration proce-dures recommended by the manufacturer of the dynamicmechanical analyzer as described in the operations manual.10. Procedure10.1 Prepar

21、e the dynamic mechanical analyzer for operationunder the test conditions (for example, specimen clamps, purgegas, etc.) to be used for the characterization of the testspecimens. Unless otherwise indicated, the temperature condi-tion shall be isothermal between 20 and 22 C.10.2 Ensure that the storag

22、e modulus signal is less than 1MPa with no test specimen loaded and at an oscillation testfrequency of 1 Hz.NOTE 3Alternatively, a thin specimen of a low modulus material (forexample, a thin piece of paper) may be used. The dimensions of the testspecimen (see 10.3) shall be used rather than the true

23、 dimensions of thethin low modulus material.10.3 Measure and record the dimension of the test specimento a precision of 6 0.01 mm.10.4 Open the apparatus, place the reference material intothe specimen holder, and reassemble the apparatus. Equilibratethe reference material at the test conditions. Unl

24、ess otherwiseindicated, the test frequency shall be 1 Hz and the temperatureshall be isothermal between 2 and 23 C. Ensure that theapplied strain (or stress) amplitude is within the linear vis-coelastic regions of the sample typically less than 1 % strain.NOTE 4Typical specimen size is 50x9x1mm.Thes

25、pecimen shouldhave a length-to-thickenss ratio greater than 10-to-1.10.5 Record the storage modulus observed by the apparatusas Eo.10.6 Record the storage modulus of the reference materialfrom its certificate or from Table 1 as Es.10.7 Calculate and report the value of the slope (S) andpercent confo

26、rmity (C) of the measurement using Eq 2 and 3.11. Calculation11.1 For the purpose of this test method, it is assumed thatthe relationship between observed storage modulus (Eo) andthe reference storage modulus (Es) is linear and governed bythe slope (S)ofEq1.Es 5 Eo 3 S (1)11.2 By using the storage m

27、odulus values taken from 10.5and 10.6 calculate and report S using Eq 2 to four decimalplaces.S 5 Es / Eo (2)11.3 The percent conformity (C) (that is, the percent differ-ence between the experimental slope and unity) of the instru-ment storage modulus scale is calculated using the value of Sfrom 11.

28、2 and Eq 3.C 5 S 2 1.0000! 3 100 % (3)11.3.1 Conformity may be estimated to one significantfigure using the following criteria:11.3.1.1 If the value of S is between 0.9990 and 0.9999 orbetween 1.0001 and 1.0010, then the conformity is better than0.1 %.11.3.1.2 If the value of S is between 0.9900 and

29、 0.9990 orbetween 1.0010 and 1.0100, then conformity is better than 1 %.11.3.1.3 If the value of S is between 0.9000 and 0.9900 orbetween 1.0100 and 1.1000, then conformity is better than10 %.11.4 Report the value of S and the percent conformity, (C).11.5 Using the slope (S) from Eq 2, the observed

30、storagemodulus (Eo) can provide a corrected storage modulus (E)using Eq 4.TABLE 1 Reference Material ModulusA,B,CStorage Modulus, GPaTemperature,CCarbonSteelDMonelECopperFAluminum UHMWPE-198 207 185 121 77.9 . . .-101 201 182 116 75.8 . . .-46 198 180 114 74.5 . . .21 192 179 114 73.1 1.2693 191 179

31、 112 71.7 . . .149 189 178 112 70.3 . . .204 186 177 110 65.5 . . .260 182 175 . . . . . . . . .316 177 170 . . . . . . . . .AAmerican Society of Mechanical Engineers, New York, NY, B31.5a, Refrigera-tion Piping, page 45 (1992).BPerrys Chemical Engineers Handbook, R.H. Perry, D.W. Green, J.O. Mal-on

32、ey (eds.), 6th Edition, McGraw-Hill, New York, NY, page 6-92 (1984).CUltra High Molecular Weight Polyethylene Standard Reference Material SRM8456, National Institute of Standards and Technology, Gaithersburg, MD 20899(2000).D3.5 % Ni, 0.30 C.E67 % Ni, 30 % Cu.F99.90 % Cu, Alloy C12000, C12200.E2254

33、092E 5 Eo 3 S (4)12. Report12.1 The report shall include the following information:12.1.1 Details and description, including the manufacturerand instrument model number, where applicable, of the dy-namic mechanical analyzer. Also report the test mode, strainamplitude, and applied static load.12.1.1.

34、1 Whether or not the instrument calibration includescompliance correction.12.1.2 The value of S determined in 11.2, reported to at leastfour decimal places.12.1.3 The percent conformity (C), as determined in 11.3.12.1.4 The specific dated version of this method used.13. Precision and Bias13.1 An int

35、erlaboratory study is planned for 20092010 togenerate precision and bias information for this method.Anyone wishing to participate in this study may contact theE37 Staff Manager at ASTM Headquarters.13.2 Precision:13.2.1 The intralaboratory repeatability standard deviationfor S for a single instrume

36、nt using carbon steel and was foundto be 0.67 %.13.3 Bias:13.3.1 The measurement of conformity in this test method isa comparison of the calibration constant S with the theoreticalvalue of 1.0000 and provides an indication of bias.13.3.2 The intralaboratory conformity for C for a singleinstrument us

37、ing ultra high molecular weight polyethylenefollowing calibration with carbon steel was 4.0 %.14. Keywords14.1 calibration; conformity; dynamic mechanical analysis;storage modulusASTM International takes no position respecting the validity of any patent rights asserted in connection with any item me

38、ntionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committe

39、e and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeti

40、ng of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO

41、 Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM website (www.astm.org/COPYRIGHT/).E2254 093