ASTM E1522-1993(2008) Standard Specification for Autoclavable Protective Coatings on Laboratory Glassware《实验室玻璃器皿耐高压加热保护涂层的标准规范》.pdf

《ASTM E1522-1993(2008) Standard Specification for Autoclavable Protective Coatings on Laboratory Glassware《实验室玻璃器皿耐高压加热保护涂层的标准规范》.pdf》由会员分享，可在线阅读，更多相关《ASTM E1522-1993(2008) Standard Specification for Autoclavable Protective Coatings on Laboratory Glassware《实验室玻璃器皿耐高压加热保护涂层的标准规范》.pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: E 1522 93 (Reapproved 2008)Standard Specification forAutoclavable Protective Coatings on Laboratory Glassware1This standard is issued under the fixed designation E 1522; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision,

2、the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification covers the requirements for autocla-vable protective coatings on laboratory glassware u

3、p to andincluding the 4L size. These coatings will not prevent theescape of liquids from vessels under pressure.2. Chemical Resistance2.1 The physical resistance (see 3.1) of the coating shall beacceptable after continuous exposure for one hour to acids,(other than chromic), alcohols, bases, aliphat

4、ic hydrocarbons(except as noted below) and oxidizing agents at room tempera-ture. The intent of the coating is to allow enough time afterbreakage for proper disposal, not for continued use.2.2 The coating shall not be required to withstand exposureto aldehydes, esters, aromatic hydrocarbons, halogen

5、ated hy-drocarbons or ketones.3. Physical Resistance3.1 The thickness and character of the undamaged coatingshall be such that it will not permit the immediate total loss ofliquid at 15C to 70C from a protected stoppered or cappedcontainer filled to rated capacity when dropped from a heightof 40 in.

6、 onto a floor made of18 in. maximum vinyl tile overconcrete, but will prevent the escape of glass.4. Autoclavability4.1 The coating shall withstand 15 min autoclave cycles at121C and 15 psig, although some air pockets under thecoating and some other surface depressions may becomepermanent. Some mois

7、ture may be absorbed through thecoating during autoclaving and cause a slight clouding, but thisclouding must be removable by oven drying at not over 110C.Drying time will vary depending on size and configuration ofvessel.4.1.1 Coating life will vary depending on size and configu-ration of vessel an

8、d size and procedure of autoclave used. Alsoallow coating to clear and dry before repeating autoclave cycle.4.2 CAUTION: Loosen or remove all caps or closuresbefore autoclaving and allow autoclave pressure to return tozero before removing glassware to minimize the formation ofair pockets under the c

9、oating. Also allow coating to clear anddry before repeating autoclave cycle. Vacuum drying maydistort the coating.5. Temperature5.1 This coating should not be exposed to dry heat above110C or moist heat above 121C. However, prolonged expo-sure to either dry or wet heat will cause discoloration andem

10、brittlement. Discolored coatings may no longer be usable.Manufacturers should be consulted for specific applications.6. Microwaving6.1 Containers filled with aqueous solutions and having drycoatings (no obvious moisture under or on them) shall with-stand microwaving provided that the 110C temperatur

11、e limitis not exceeded. Wet coatings may develop steam pockets andcause the coatings to separate.6.1.1 Coating life will vary depending on size and configu-ration of vessel, temperature achieved and time at suchtemperature.6.2 CAUTION: Loosen or remove all caps or closuresbefore microwaving.7. Therm

12、al Combustion7.1 Combustion of various coatings will result in the releaseof certain chemicals. Combustion of PVC, for example, willresult in the release of the major combustion products ofcarbon dioxide, carbon monoxide, hydrogen chloride andwater. Provision should be made to deal appropriately wit

13、hsuch combustion products if combustion occurs.8. Flammability8.1 The coating shall not ignite and burn when exposed toopen flame, hot electric heating elements or other sources ofheat that are capable of initiating combustion.9. Color9.1 The coating may be clear or colored at the option of themanuf

14、acturer.10. Keywords10.1 coatings; glassware; laboratory; protective1This specification is under the jurisdiction of ASTM Committee E41 onLaboratory Apparatus and is the direct responsibility of Subcommittee E41.01 onApparatus.Current edition approved Nov. 1, 2008. Published January 2009. Originally

15、approved in 1993. Last previous edition approved in 2003 as E 152293 (2003).1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.ASTM International takes no position respecting the validity of any patent rights asserted in connection with

16、 any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible techni

17、cal committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideratio

18、n at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harb

19、or Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org).E 1522 93 (2008)2