ASTM E1320-2010 Standard Reference Radiographs for Titanium Castings《钛铸件用标准参考射线照片》.pdf

《ASTM E1320-2010 Standard Reference Radiographs for Titanium Castings《钛铸件用标准参考射线照片》.pdf》由会员分享，可在线阅读，更多相关《ASTM E1320-2010 Standard Reference Radiographs for Titanium Castings《钛铸件用标准参考射线照片》.pdf（4页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: E1320 10Standard Reference Radiographs forTitanium Castings1This standard is issued under the fixed designation E1320; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last revision. A number in parentheses

2、indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Department of Defense.1. Scope1.1 The reference radiographs provided in the adjunct to thisstandard are reprod

3、uctions of original radiographs and aresupplied as a means for establishing some of the categories andseverity levels of discontinuities in titanium castings that maybe revealed by radiographic examination. Use of this standardfor the specification or grading of castings requires procure-ment of the

4、 adjunct reference radiographs which illustrate thediscontinuity types and severity levels. They should be used inaccordance with contractual specifications.NOTE 1The original radiographs produced for Volume I were takenwith X-rays in the range of 110 KV to 220 KV. The original radiographsproduced f

5、or Volume II were taken with X-rays in the range of 200 K to340 KV.1.2 These film reference radiographs are not intended toillustrate the types and degrees of discontinuities found intitanium castings when performing digital radiography. Ifperforming digital radiography of titanium castings, refer t

6、oDigital Reference Image Standard E2669.1.3 These reference radiographs consist of two volumes.Volume I, described in Table 1, is applicable to a wall thicknessof up to 1 in. (0 to 25.4 mm). Volume II, described in Table 2,is applicable to a wall thickness of over 1 in. to 2 in. (25.4 mmto 50.8 mm).

7、 The standard may be used, where there is no otherapplicable standard, for other thicknesses for which agreementhas been reached between purchaser and manufacturer.NOTE 2The reference radiographs are not impacted by this revision.There have been no revisions to the adjunct reference radiographs sinc

8、eoriginal issue. The adjunct reference radiographs of any issue remain validand may be used to this standard.1.4 The plates produced to serve for use in this standardwere purposely cast to exhibit the desired discontinuity. Theplates were cast using different processes as shown in Table 1and Table 2

9、. Hot isostatic pressing was not used on any of theplates.1.5 The values stated in inch-pound units are to be regardedas the standard. The values given in parentheses are mathemati-cal conversions to SI units that are provided for informationonly and are not considered standard.1.6 This standard doe

10、s not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2. Referenced Documents2.1 ASTM Stan

11、dards:2E94 Guide for Radiographic ExaminationE1316 Terminology for Nondestructive ExaminationsE2669 Digital Reference Images for Titanium Castings2.2 ASTM Adjuncts:Reference Radiographs for the Inspection of Titanium Cast-ingsVolume I, applicable up to 1 in. (25.4 mm)3,4Volume II, applicable over 1

12、in. to 2 in. (25.4 mm to 50.8mm)4,53. Terminology3.1 DefinitionsFor definitions of terms used in this stan-dard, see Terminology E1316.4. Significance and Use4.1 These reference radiographs are designed so that accep-tance standards, which may be developed for particular re-quirements, can be specif

13、ied in terms of these radiographs. Theradiographs are of castings that were produced under condi-tions designed to produce the discontinuities. The reference1This standard is under the jurisdiction of ASTM Committee E07 on Nonde-structive Testing and is the direct responsibility of Subcommittee E07.

14、02 onReference Radiological Images.Current edition approved Sept. 1, 2010. Published September 2010. Originallyapproved in 1990. Last previous edition approved in 2005 as E1320 - 05. DOI:10.1520/E1320-10.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Se

15、rvice at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.3Available from ASTM International Headquarters. Order Reference Radio-graph No. RRE132001.4Volumes I and II are available from ASTM International Headquarte

16、rs as a set.Order Reference Radiographs RRE1320CS.5Available from ASTM International Headquarters. Order Reference Radio-graph No. RRE132002.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.radiographs are intended to be used for cast

17、ing thicknessranges in accordance with Table 1 and Table 2.5. Description of Discontinuities5.1 This section is provided to aid in the identification andclassification of discontinuities. It briefly describes the radio-graphic appearance of those discontinuities in the referenceradiograph adjuncts a

18、nd indicates their probable cause intitanium. The radiographic appearance of different discontinui-ties can at times be very similar. Therefore, care should alwaysbe taken during the process of identification. In extreme casesother methods of identification, either nondestructive or de-structive, ma

19、y need to be employed to obtain positive identi-fication.5.1.1 GasGas in its various forms is usually caused by thereaction of molten titanium with the mold or residual materialleft in the mold. Gas tends to migrate to the upper portions ofthe casting. The formation of clustered or scattered gas hol

20、esresults from the generation of larger amounts of gas than asingle gas hole. Whether the larger amount of gas spreads outor is confined to a small area is dependent upon a number offactors including casting process, reaction area, solidificationrate, wall thickness, and geometry.5.1.1.1 Gas holeA s

21、pherical void formed through therelease and subsequent entrapment of gas during solidification.A gas hole will appear as a dark round spot on the radiograph.5.1.1.2 Clustered gas holesAclosely nested group of darkround voids concentrated within a self-defined boundary area.5.1.1.3 Scattered gas hole

22、sMultiple voids appearing asdark round spots on the radiograph. They are randomly spreadthroughout a part or area of a part to a lesser concentration thanclustered gas holes but with the potential to degrade the castingthrough their interaction which precludes their evaluation on anindividual basis.

23、5.1.2 ShrinkageWhile at times the appearance of shrink-age in titanium may be radiographically similar to shrinkage insteel, the faster solidification rate of titanium has a dramaticeffect on the conditions under which each shrinkage type willoccur in titanium. Other factors which influence the form

24、ationof shrinkage are wall thickness and thickness transition gradi-ents, gate size and orientation, mold design, casting configu-ration, metal/mold temperature, and pouring rate and method.All the types of shrinkage described in 5.1.2.1 through 5.1.2.3have a degree of overlap. However, each is most

25、 likely to occurunder a specific set of conditions primarily influenced by metalfeed, section thickness and cooling rate.5.1.2.1 Scattered shrinkageAppears on a radiograph asdark fine lacy or filamentary voids of varying densities. Thesevoids are usually uniformly spread throughout the area of theca

26、sting where shrinkage is occurring and are relatively shallow.Scattered shrinkage cavities are most common in wall thick-nesses ranging from18 in. to34 in. (3.175 mm to 19.05 mm)TABLE 1 VOLUME I0 to 1 in.Discontinuity Casting Process AlloyPlateThickness, in.Applicable CastingThickness, in.Gas hole C

27、entrifugal ram graphite Ti 6AL 4V N/A up to 1Clustered holes Centrifugal precision Ti 6AL 4V14 up to38Clustered holes Centrifugal precision Ti 6AL 4V12 over38 to58Clustered holes Centrifugal precision Ti 6AL 4V34 over58 to 1Scattered gas holes Top pour lost wax Ti 6AL 4V14 up to38Scattered gas holes

28、 Top pour lost wax Ti 6AL 4V12 over38 to58Scattered gas holes Top pour lost wax Ti 6AL 4V34 over58 to 1Shrinkage cavity Centrifugal ram graphite Ti 6AL 4V12 over14 to58Shrinkage cavity Centrifugal ram graphite Ti 6AL 4V34 over58 to 1Scattered shrinkage cavity Top pour lost wax Ti 6AL 4V14 up to38Sca

29、ttered shrinkage cavity Top pour lost wax Ti 6AL 4V12 over38 to58Scattered shrinkage cavity Top pour lost wax Ti 6AL 4V34 over58 to 1Centerline shrinkage Centrifugal ram graphite Ti 6AL 4V14 up to38Centerline shrinkage Centrifugal ram graphite Ti 6AL 4V12 over38 to58Centerline shrinkage Centrifugal

30、ram graphite Ti 6AL 4V34 over58 to 1Less dense inclusions Varied Ti 6AL 4V N/A up to 1More dense inclusions Varied Ti 6AL 4V N/A up to 1NOTE 11 in. = 25.4 mm.TABLE 2 VOLUME IIOver 1 in. to 2 in.Discontinuity Casting Process AlloyPlateThickness, in.Applicable CastingThickness, in.Gas hole Centrifugal

31、 ram graphite Ti 6AL 4V 114 over 1 to 2Clustered gas holes Centrifugal ram graphite Ti 6AL 4V 114 to 134 over 1 to 2Scattered gas holes Centrifugal ram graphite Ti 6AL 4V 114 over 1 to 112Scattered gas holes Centrifugal ram graphite Ti 6AL 4V 134 over 112 to 2Shrinkage cavity Centrifugal ram graphit

32、e Ti 6AL 4V 114 over 1 to 112Shrinkage cavity Centrifugal ram graphite Ti 6AL 4V 134 over 112 to 2Centerline shrinkage Centrifugal ram graphite Ti 6AL 4V 114 over 1 to 112Centerline shrinkage Centrifugal ram graphite Ti 6AL 4V 134 over 112 to 2NOTE 11 in. = 25.4 mm.E1320 102being more prevalent in t

33、he thinner sections of the range.Scattered shrinkage cavities are caused by varying coolingrates in the same area of a casting that can result fromdifferences in wall thickness or other factors.5.1.2.2 Centerline shrinkageCharacterized by a more dis-crete dark indication than scattered shrinkage. Th

34、e indicationhas definite borders consisting of a lacy network of varyingdensity or a network of interconnected elongated voids. Cen-terline shrinkage is located primarily in the center of thematerial cross section with a tendency to orient toward gates orrisers. It is more common in thickness over14

35、 in. (6.35 mm).5.1.2.3 Shrinkage cavityAppears as a dark void withsmooth sides taking an appearance very similar to a gas hole.A shrinkage cavity, particularly in thicker wall sections, isusually larger than a single gas hole would be. The cavity isformed during the cooling process due to a lack of

36、feedingmetal. The cavity compensates for the rapid solidificationtaking place at the surface of the casting, thereby forming thecavity in the center area of the wall. Shrinkage cavity has adefinite tendency to occur near hot spots where walls are12 in.(12.7 mm) thick or more.5.1.3 Less dense inclusi

37、onsAppear as dark indications ina variety of shapes and sizes on a radiograph. Inclusions maybe found in groups or appear singularly. Less dense inclusionscan be caused by contaminants in the molten titanium, residualmaterials left on the surface of the mold, or broken pieces ofthe mold becoming ent

38、rapped during solidification.5.1.4 More dense inclusionsAppear as light indications ina variety of shapes and sizes on a radiograph. More denseinclusions can be caused by contaminants introduced in thesame manner as less dense inclusions, or tungsten introducedduring weld repairs.6. Method of Prepar

39、ation6.1 The original radiographs used to prepare the adjunctreference radiographs were produced on high contrast, finegrained film. The radiographs were made with a penetrametersensitivity as determined by ASTM penetrameters (see GuideE94) of 2-2T. The reproductions of the original radiographshave

40、been made with a desired density within the range of 2.0to 2.25. They have retained substantially the contrast of theoriginal radiographs.6.2 In selecting the individual reference radiographs, theaim was to obtain a graduated series for each type ofdiscontinuity. It is not intended that like numbere

41、d levels orclasses on the different reference radiograph pages be consid-ered to cause equal degradation in the ultimate performance, orserviceability, or both, of any particular casting.6.2.1 The criteria used to select the individual radiographsrepresenting each severity level were based on the si

42、ze, shape,spacing, alignment, and radiographic density of the disconti-nuities present.6.3 In some cases, plates other than the thickness indicatedon the reference radiographs were utilized to complete indi-vidual severity levels.6.4 For the discontinuity classifications of gas hole, lessdense inclu

43、sions, and more dense inclusions, only one series ofeight gradations is displayed for each. These gradations areintended to be used over the entire thickness range applicableto the volume. Therefore, careful consideration should be takenwhen specifying allowable severity levels for the thicker walls

44、izes.6.5 Film DeteriorationRadiographic films are subject towear and tear from handling and use. The extent to which theimage deteriorates over time is a function of storage condi-tions, care in handling and amount of use. Reference radio-graph films are no exception and may exhibit a loss in imageq

45、uality over time. The radiographs should therefore be peri-odically examined for signs of wear and tear, includingscratches, abrasions, stains, and so forth. Any reference radio-graphs which show signs of excessive wear and tear whichcould influence the interpretation and use of the radiographsshoul

46、d be replaced.7. Basis for Application7.1 The reference radiographs may be applied as acceptancestandards tailored to the end use of the product. Application ofthese reference radiographs as acceptance standards should bebased on the intended use of the product and the followingconsiderations:7.1.1

47、An area of like size to that of the reference radiographshall be the unit area by which the production radiograph isevaluated, and any such area shall meet the requirements asdefined for acceptability.7.1.2 Any combination or portion of these reference radio-graphs may be used as is relevant to the

48、particular application.Different grades or acceptance limits may be specified for eachdiscontinuity type. Further, different grades may be specifiedfor various regions or zones of the component.7.1.3 Special consideration may be required where morethan one discontinuity type is present in the same a

49、rea. Anymodification of the acceptance criteria required on the basis ofmultiple discontinuity types must be specified.7.1.4 Production radiographs containing shrinkage, gas, orinclusions may be rated by the overall condition with regard tosize, number, and distribution. These factors should be consid-ered in balance.7.1.5 As a minimum, the acceptance criteria should containinformation addressing: zoning of the part (if applicable),acceptance severity level for each discontinuity type, and thespecific area to which