ASTM D7236-2007(2013) 1875 Standard Test Method for Flash Point by Small Scale Closed Cup Tester (Ramp Method)《用小型闭杯试验器测定闪点的标准试验方法(斜坡法)》.pdf

《ASTM D7236-2007(2013) 1875 Standard Test Method for Flash Point by Small Scale Closed Cup Tester (Ramp Method)《用小型闭杯试验器测定闪点的标准试验方法(斜坡法)》.pdf》由会员分享，可在线阅读，更多相关《ASTM D7236-2007(2013) 1875 Standard Test Method for Flash Point by Small Scale Closed Cup Tester (Ramp Method)《用小型闭杯试验器测定闪点的标准试验方法(斜坡法)》.pdf（6页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: D7236 07 (Reapproved 2013)Standard Test Method forFlash Point by Small Scale Closed Cup Tester (RampMethod)1,2This standard is issued under the fixed designation D7236; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, t

2、he year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.INTRODUCTIONThis flash point test method is a dynamic test method and depends on a definite rate of temperatureincrease

3、 to control the precision of the test method. The rate of heating may not in all cases give theprecision quoted in the test method because of the low thermal conductivity of certain materials. Theuse of an equilibrium method such as Test Methods D3828, Method B improves the prediction offlammability

4、 for such materials, as the vapors above the test specimen and the test specimen are closerto thermal equilibrium.Flash point values are a function of the apparatus design, the condition of the apparatus used, andthe operational procedure carried out. Flash point can therefore only be defined in ter

5、ms of a standardtest method, and no general valid correlation can be guaranteed between results obtained by differenttest methods or with test apparatus different than that specified.1. Scope1.1 This test method covers the determination of the flashpoint of aviation turbine fuel, diesel fuel, kerosi

6、ne and relatedproducts in the temperature range of 40 to 135C by a smallscale closed cup apparatus.1.2 This test method is only applicable to homogeneousmaterials that are liquid at or near ambient temperature and attemperatures required to perform the test.1.3 This test method is not applicable to

7、liquids contami-nated by traces of highly volatile materials.1.4 This test method is a dynamic method and depends on adefinite rate of temperature increase. It is one of many flashpoint methods available, and every flash point test method,including this one, is an empirical one.1.5 If the users spec

8、ification requires a defined flash pointmethod, neither this test nor any other method should besubstituted for the prescribed method without obtaining com-parative data and an agreement from the specifier.1.6 The values stated in SI units are to be regarded asstandard. No other units of measurement

9、 are included in thisstandard.1.7 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitation

10、s prior to use. For specific hazardstatements, see Section 7 and the Material Safety Data Sheetfor the product being tested.2. Referenced Documents2.1 ASTM Standards:3D3828 Test Methods for Flash Point by Small Scale ClosedCup TesterD4057 Practice for Manual Sampling of Petroleum andPetroleum Produc

11、tsD4177 Practice for Automatic Sampling of Petroleum andPetroleum ProductsD6299 Practice for Applying Statistical Quality Assuranceand Control Charting Techniques to Evaluate AnalyticalMeasurement System PerformanceD6300 Practice for Determination of Precision and BiasData for Use in Test Methods fo

12、r Petroleum Products andLubricants1This test method is under the jurisdiction of ASTM Committee D02 onPetroleum Products, Liquid Fuels, and Lubricants and is the direct responsibility ofSubcommittee D02.08 on Volatility.Current edition approved Oct. 1, 2013. Published October 2013. Originallyapprove

13、d in 2006. Last previous edition approved in 2007 as D7236 07. DOI:10.1520/D7236-07R13.2This test method is being jointly developed and harmonized with the EnergyInstitute.3For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For An

14、nual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States1E300 Practice for Sampling Industrial Chemicals2.2 ISO Standards:4ISO Guide

15、 34 Quality Systems Guidelines for the Produc-tion of Reference MaterialsISO Guide 35 Certification of Reference MaterialGeneraland Statistical Principles3. Terminology3.1 Definitions:3.1.1 flash point, nlowest temperature corrected to apressure of 101.3 kPa, at which application of a test flamecaus

16、es the vapors of a test specimen of the sample to ignitemomentarily under the specified conditions of the test.3.2 Definitions of Terms Specific to This Standard:3.2.1 dynamic, adjthe condition where the vapor abovethe test specimen, and the test cup, are not in temperatureequilibrium at the time th

17、e test flame is applied.3.2.2 ramp method, nin flash point methods, method thathas a test temperature increase at a set rate.4. Summary of Test Method4.1 A 2 6 0.1 mL test specimen is introduced into the testcup that is then heated automatically at a constant rate of 2 60.5C/min. A gas test flame is

18、 directed through an openingshutter, in the test cup lid, at specified temperature intervalsuntil a flash is detected by the automatic flash detector. Theflash is reported as defined in 3.1.1.5. Significance and Use5.1 The flash point temperature is one measure of thetendency of the test specimen to

19、 form a flammable mixturewith air under controlled laboratory conditions. It is only oneof a number of properties that must be considered in assessingthe overall flammability hazard of a material.5.2 Flash point is used in shipping and safety regulations todefine flammable and combustible materials

20、and classify them.Consult the particular regulation involved for precise defini-tions of these classifications.5.3 This test method can be used to measure and describethe properties of materials in response to heat and a test flameunder controlled laboratory conditions and shall not be used todescri

21、be or appraise the fire hazard or fire risk of materialsunder actual fire conditions. However, results of this testmethod may be used as elements of a fire risk assessment, thattakes into account all of the factors that are pertinent to anassessment of the fire hazard of a particular end use.6. Appa

22、ratus6.1 Flash Point ApparatusThe apparatus consists of anelectrically heated test cup that is controlled automatically togive a temperature increase of 2.0 6 0.5C/min, a lid andshutter assembly, a pilot and test flame, an automatic flashdetector and a temperature display that displays and holds the

23、test temperature when a flash is detected. The key parts anddimensions are described in Annex A1 and illustrated in Fig.A1.1.6.2 Syringe, 2 mL, adjusted to deliver 2.00 6 0.1 mL.6.3 Barometer, accurate to 0.5 kPa. Barometers pre-corrected to give sea level readings, such as those used atweather stat

24、ions and airports, shall not be used.NOTE 1Automatic barometric correction in accordance with 12.2 maybe installed in the apparatus.6.4 Cooling Bath or Freezer, for cooling the samples, ifrequired, and capable of cooling the sample to at least 10Cbelow the expected flash point. If a freezer is used,

25、 it shall beof explosion-protected design.6.5 Draft Shield, a shield fitted at the back and on two sidesof the instrument, for use in circumstances where naturalprotection from drafts does not exist.NOTE 2A shield 350-mm high, 480-mm wide, and 240-mm deep, issuitable.7. Reagents and Materials7.1 Cle

26、aning SolventUse only noncorrosive solvents ca-pable of cleaning the test cup and lid assembly. Two commonlyused solvents are toluene and acetone. (WarningToluene,acetone and many solvents are flammable and a health hazard.Dispose of solvents and waste material in accordance withlocal regulations.)7

27、.2 Butane or Natural GasFor use as the pilot and testflame. (WarningButane and natural gases are flammableand a health hazard.)8. Sampling8.1 Obtain at least a 25 mL sample from a bulk test site inaccordance with Practices D4057, D4177, E300 or othercomparable sampling practices.8.2 Store samples in

28、 clean, tightly sealed containers atnormal room temperature (20 to 25C) or colder. Ensure thatthe container is 85 to 95 % full.8.3 Do not store samples for an extended period of time ingas permeable containers, such as plastic, because volatilematerial may diffuse through the walls of the container.

29、Samples in leaky containers are suspect and not a source ofvalid results.8.4 Erroneously high flash points can be obtained whenprecautions are not taken to avoid loss of volatile materials. Donot open containers unnecessarily. Do not make a transferunless the sample temperature is at least 10C below

30、 theexpected flash point. Where possible perform the flash point asthe first test on the sample.8.5 Samples containing dissolved or free water may bedehydrated with calcium chloride. Warming the sample ispermitted, but do not heat the sample above a temperature of10C below its expected flash point.

31、(WarningIf the sampleis expected of containing volatile components, the treatment asdescribed in 8.5 should be omitted.)8.6 Cool or adjust the temperature of the sample and itscontainer to at least 10C below the expected flash point before4Available from American National Standards Institute (ANSI),

32、 25 W. 43rd St.,4th Floor, New York, NY 10036.D7236 07 (2013)2opening to remove the test specimen. If an aliquot of theoriginal sample is to be stored prior to testing, ensure that thecontainer is filled to between 85 and 95 % of its capacity.Gently mix the subsample to ensure uniformity while mini-

33、mizing the possible loss of volatile components and light ends.NOTE 3Results of flash point tests may be affected if the samplevolume falls below 85 % of the containers capacity.9. Preparation of Apparatus9.1 Support the apparatus (Annex A1) on a level and steadysurface in a draft-free position (see

34、 Notes 4 and 5).NOTE 4A draft shield (6.5) is recommended to be used when naturalprotection from drafts does not exist.NOTE 5When testing materials that may produce toxic vapors, theapparatus may be located in a fume hood with an individual control of airflow, adjusted such that the toxic vapors can

35、 be withdrawn withoutcausing air currents around the test cup during the test.9.2 Clean the test cup, cover, and its accessories with anappropriate solvent (7.1) to remove traces of gum or residuefrom the previous test.NOTE 6Astream of clean dry air may be used to remove the last tracesof solvent us

36、ed.NOTE 7The filler orifice may be cleaned with a pipe cleaner.10. Verification of Apparatus10.1 Verify that the temperature measuring device is inaccordance with A1.7.10.2 Verify the performance of the apparatus at least onceper year by determining the flash point of a Certified ReferenceMaterial (

37、CRM) that has a certified flash point reasonably closeto the expected range of the samples to be tested. Examples ofmaterials that may be used to create CRMs are listed inAppendix X1. The flash point shall be determined using theprocedures stated in Section 11. Appendix X1 indicates typicallimits in

38、 Table X1.1 for a typical CRM and shows how tocalculate limits for an unlisted CRM.10.3 Once the performance of the apparatus has beenverified using a CRM, the flash point of Secondary WorkingStandards (SWS) can be determined along with their controllimits. These SWS can then be utilized for more fr

39、equentperformance checks. (See Appendix X1.)10.4 When the flash point obtained is not within the limitsstated in 10.2 or 10.3 check the condition and operation of theapparatus to ensure conformance to the details listed in AnnexA1, especially with regard to the action of the shutter, theposition and

40、 size of the test flame, the heating rate and thetemperature sensor readings. After any adjustment, repeat thetest in 10.2 or 10.3 using a fresh test specimen, with specialattention to the procedural details prescribed in the test method.11. Procedure11.1 Set the test cup temperature to 15 6 5C belo

41、w theexpected flash point temperature.11.2 When the test cup is at the required temperature, chargea clean and dry syringe (6.2), adjusted to a temperature at least10C below the expected flash point, witha2mLtestspecimen. Close the sample container immediately after with-drawal of the test specimen,

42、 to minimize any loss of volatilecomponents.11.3 Carefully transfer the syringe to the filler orifice anddischarge the test specimen into the test cup by fully depressingthe syringe plunger. Remove the syringe.11.4 Ignite the pilot and test flames. Adjust the test flame toconform to the size of the

43、4 mm gauge ring. Reset the flashdetector (A1.9). Start the test.NOTE 8The ignition of the test flame and control of the gas supplymay be automated on some instruments.11.5 The test cup is heated automatically at such a rate thatthe temperature, as indicated by the temperature sensor, in-creases by 1

44、.5 to 2.5C/min. The test flame is dipped into thetest cup, as the shutter is slowly and uniformly opened andclosed overa2to3-speriod, at 1C intervals for temperaturesup to and including 100C and thereafter every 2C fortemperatures over 100C.11.5.1 Observe the first two dips of the flame for continuo

45、usburning in the orifice. If a continuous luminous flame burns inthe orifice when the slide is opened and the test flame isintroduced, then the flash point lies considerably below the testtemperature. In such cases, discontinue the test and repeat thetest with a fresh test specimen using a lower exp

46、ected flashpoint.11.5.2 Application of the test flame may cause a blue halo oran enlarged flame prior to the actual flash point. This is not aflash and shall be ignored by the flash detector.11.6 Record the displayed and held temperature of thetemperature sensor when the application of the test flam

47、ecauses a flash to be automatically detected.11.7 Record the ambient barometric pressure using a barom-eter (6.3) in the vicinity of the apparatus at the time of the test.NOTE 9It is not considered necessary to correct the barometricpressure reading to 0C, although some barometers are designed to ma

48、kethis correction automatically.11.8 When the temperature at which the flash is observed isless than 10C or greater than 30C from the start temperatureof the test, the result is not valid. Repeat the test using a freshtest specimen adjusting the temperature of the first applicationof the test flame

49、until a valid determination is made.12. Calculation12.1 Barometric Pressure ConversionIf the barometricpressure reading is measured in a unit other than kilopascals,convert to kilopascals using one of the following equations:Reading in hPa 30.1 5 kPa (1)Reading in mbar 30.1 5 kPa (2)Reading in mmHg 30.1333 5 kPa (3)12.2 Correction of Detected Flash Point to Standard Atmo-spheric PressureCalculate the flash point corrected to astandard atmospheric pressure of 101.3 kPa, Tc, using thefollowing equation:Tc5 TD10.25 101.3 2 p! (4)where:TD= the d