ASTM D6779-2012 3750 Standard Classification System for and Basis of Specification for Polyamide Molding and Extrusion Materials (PA)《聚酰胺模制和挤压材料(PA)规格基础的标准分类系统》.pdf

《ASTM D6779-2012 3750 Standard Classification System for and Basis of Specification for Polyamide Molding and Extrusion Materials (PA)《聚酰胺模制和挤压材料(PA)规格基础的标准分类系统》.pdf》由会员分享，可在线阅读，更多相关《ASTM D6779-2012 3750 Standard Classification System for and Basis of Specification for Polyamide Molding and Extrusion Materials (PA)《聚酰胺模制和挤压材料(PA)规格基础的标准分类系统》.pdf（14页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: D6779 12Standard Classification System for and Basis of Specification forPolyamide Molding and Extrusion Materials (PA)1This standard is issued under the fixed designation D6779; the number immediately following the designation indicates the year oforiginal adoption or, in the case of r

2、evision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope*1.1 This classification system covers polyamide materialssuitable for molding and extrusion. Some of

3、 these composi-tions are also suitable for application from solution.1.2 The properties included in this classification system arethose required to identify the compositions covered. Otherrequirements necessary to identify particular characteristicsimportant to specialized applications are to be spe

4、cified byusing suffixes as given in Section 5.1.3 This classification system and subsequent line callout(specification) are intended to provide a means of calling outplastic materials used in the fabrication of end items or parts.It is not intended for the selection of materials. Materialselection c

5、an be made by those having expertise in the plasticfield after careful consideration of the design and the perfor-mance required of the part, the environment to which it will beexposed, the fabrication process to be employed, the costsinvolved, and the inherent properties of the material other thant

6、hose covered by this classification system.1.4 The values stated in SI units are to be regarded asstandard. No other units of measurement are included in thisstandard.1.5 The following precautionary caveat pertains only to thetest methods portion, Section 11, of this classification system.This stand

7、ard does not purport to address all of the safetyconcerns, if any, associated with its use. It is the responsibilityof the user of this standard to establish appropriate safety andhealth practices and determine the applicability of regulatoryrequirements prior to use.NOTE 1This classification system

8、 is similar to ISO 1874-1/-2,although the technical content is significantly different.2. Referenced Documents2.1 ASTM Standards:2D257 Test Methods for DC Resistance or Conductance ofInsulating MaterialsD789 Test Methods for Determination of Solution Viscosi-ties of Polyamide (PA)D792 Test Methods f

9、or Density and Specific Gravity (Rela-tive Density) of Plastics by DisplacementD883 Terminology Relating to PlasticsD1600 Terminology for Abbreviated Terms Relating toPlasticsD3892 Practice for Packaging/Packing of PlasticsD4000 Classification System for Specifying Plastic Materi-alsD5740 Guide for

10、Writing Material Standards in the Classi-fication FormatD6260 Test Method for Gravimetric Determination of Car-bon Black in Nylon Materials (PA)3D7209 Guide for Waste Reduction, Resource Recovery, andUse of Recycled Polymeric Materials and ProductsE29 Practice for Using Significant Digits in Test Da

11、ta toDetermine Conformance with Specifications2.2 IEC/ISO Standards:4IEC 60243-1 Electrical Strength of Insulating MaterialsTest MethodsPart 1: Tests at Power FrequenciesIEC 60250 Recommended Methods for the Determinationof the Permittivity and Dielectric Dissipation Factor ofElectrical Insulating M

12、aterials at Power, Audio and RadioFrequencies Including Metre WavelengthsISO 75-1 PlasticsDetermination of Temperature of De-flection Under LoadPart 1: General Test MethodsISO 75-2 PlasticsDetermination of Temperature of De-flection Under LoadPart 2: Plastic and EboniteISO 179-1 PlasticsDeterminatio

13、n of Charpy ImpactStrengthPart 1: Non-instrumented Impact TestISO 294-1 PlasticsInjection Moulding of Test Specimensof Thermoplastic MaterialsPart 1: General Principles,Multipurpose-Test Specimens and BarsISO 307 Determination of Viscosity Number of PolyamidesIn Dilute SolutionsISO 527-1 PlasticsDet

14、ermination of Tensile PropertiesPart 1: General Principles1This classification system is under the jurisdiction ofASTM Committee D20 onPlastics and is the direct responsibility of Subcommittee D20.15 on ThermoplasticMaterials.Current edition approved April 1, 2012. Published April 2012. Originallyap

15、proved in 2002. Last previous edition approved in 2011 as D6779 - 11. DOI:10.1520/D6779-12.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Su

16、mmary page onthe ASTM website.3Withdrawn. The last approved version of this historical standard is referencedon www.astm.org.4Available from American National Standards Institute (ANSI), 25 W. 43rd St.,4th Floor, New York, NY 10036, http:/www.ansi.org.1*A Summary of Changes section appears at the en

17、d of this standard.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.ISO 527-2 PlasticsDetermination of Tensile PropertiesPart 2: Testing ConditionsISO 1183 PlasticsMethods for Determining the Densityand Relative Density of Non-Cellular

18、 PlasticsISO 1874-1 PlasticsPolyamide (PA) Homopolymers andCopolymers for Moulding and ExtrusionPart 1: Desig-nationISO 1874-2.2 PlasticsPolyamide (PA) Homopolymersand Copolymers for Moulding and ExtrusionPart 2:Preparation of Test Specimens and Determination ofPropertiesISO 3167 Plastics, Multipurp

19、ose Test SpecimensISO 3451-4 PlasticsDetermination of AshPart 4: Poly-amidesISO 11357-1 PlasticsDifferential ScanningCalorimetryPart 1: General PrinciplesISO 11357-3 PlasticsDifferential ScanningCalorimetryPart 3: Determination of Temperature andEnthalpy of Melting and CrystallizationISO 15512 Plast

20、icsDetermination of Water Content3. Terminology3.1 The terminology used in this classification system is inaccordance with Terminologies D883 and D1600.4. Classification4.1 Polyamide materials are classified into groups in accor-dance with their composition. These groups are subdivided intoclasses a

21、nd grades as shown in the Basic Property Table (TablePA).NOTE 2An example of this classification system for unreinforcedpolyamide is given as follows: The designation PA0123 indicates thefollowing:PA = polyamide as found in Terminology D1600,01 (group) = polyamide 66,2 (class) = heat stabilized, and

22、3 (grade) = with a minimum viscosity number of 210 andthe requirements given in Table PA.4.1.1 Grades of reinforced or filled versions, or both, of thebasic materials are identified by a single letter that indicates thereinforcement or filler used and two digits, in multiples of 5,that indicate the

23、nominal quantity in percent by weight. Thus,a letter designation G for glass reinforced and 35 for percent orreinforcement, G35, specifies a material with a nominal glasslevel of 35 %. The reinforcement letter designations andassociated tolerance levels are shown as follows:Symbol MaterialTolerance(

24、Based on the Total Mass)C carbon- and graphite-fiber-reinforced 62%G glass-reinforced 62%L lubricants (such as PTFE, graphite,silicone, and molybdenum disulfide)Depends upon material andprocessto be specified.M mineral-reinforced 62%R combinations of reinforcements orfillers, or both63%NOTE 3An exam

25、ple of this classification system for reinforcedpolyamide is given as follows: The designation PA012G35 indicates thefollowing:PA = polyamide as found in Terminology D1600,01 (group) = polyamide 66,2 (class) = heat stabilized, andG35 (grade) = nominal 35 % glass with the requirementsgiven in Table P

26、A.NOTE 4This part of the classification system uses percent of rein-forcements or additives, or both, in the callout of the modified basicmaterial. The types and percentages of reinforcements and additives aresometimes shown on the suppliers technical data sheet. If necessary,additional control of t

27、hese reinforcements and additives can be accom-plished by use of the suffix part of the system (see Section 5).NOTE 5Materials containing reinforcements or fillers, or both, atnominal levels not in multiples of 5 are included in the nearest PA gradedesignation. For example, a material with a nominal

28、 glass fiber level of33 % is included with Grade G35 as shown in Note 4.NOTE 6Ash content of filled or reinforced materials is determinedusing Test Method ISO 3451-4.4.2 Variations of polyamide materials that are not in TablePA are classified in accordance with Tables PA and A or B.Table PA is used

29、to specify the group of polyamide and TableA or B is used to specify property requirements.4.2.1 Specific requirements for variations of polyamidematerials shall be shown by a six-character designator. Thedesignation will consist of the letter “A” or “B” and the fivedigits comprising the cell number

30、s for the property require-ments in the order as they appear in Tables A and B.4.2.1.1 Although the values listed are necessary to includethe range of properties available in existing materials, notevery possible combination of the properties exists or can beobtained.4.2.2 When the grade of the basi

31、c material is not known, isnot important or does not meet the Table PA requirements, theuse of “0” grade classification shall be used for reinforcedmaterials in this classification system.NOTE 7An example of this classification system for a reinforcedpolyamide material is given as follows. The desig

32、nationPA0110G30A42270 would indicate the following material requirements:PA0110 = Polyamide 66, from Table PA,G30 = Glass reinforced at 30 % nominal,A = Table A property requirements,4 = Tensile strength, 140 MPa, min,2 = Tensile modulus, 4500 MPa, min,2 = Charpy impact, 5.0 kJ/m2, min,7 = Deflectio

33、n temperature at 1.8 MPa, 200C, min,and0 = Unspecified.If no properties are specified, the designation would bePA0110G30A00000.NOTE 8When a grade of polyamide is not fully identified by astandard callout, it is possible to specify all table properties by the use ofan addition of Classification D4000

34、 suffixes. Suffix values will overridethe PA table values. An example of an unreinforced polyamide material isgiven as follows: PA0212KN023. This example is a general purpose, lowviscosity PA6 material where K denotes tensile properties, N denotestensile modulus with ISO 527 as the test method, and

35、023 denotes a valueof 2300 MPa. This value for tensile modulus overrides the normal tablevalue. This example can be applied to replace all table values, that is,tensile stress, notched Charpy impact, and heat deflection temperature.D6779 1224.3 To facilitate the specification of special materials wh

36、erethe basic property table does not reflect the properties required,Table B has been incorporated into this classification system.This table will be used in a manner similar to Table A.NOTE 9Pigmented or colored polyamides can differ significantlyfrom the natural polymers in mechanical properties d

37、epending on thechoice of colorants and concentrations. The main property affected isductility, as illustrated by a reduction in Charpy impact and elongationvalues. In a typical white pigmented polyamide, elongation losses of up to50 % and Charpy impact losses of up to 30 % are common. To specifyprop

38、erty requirements of pigmented materials, use Table B.NOTE 10An example of a special material using this classificationsystem is as follows: The designation PA0220B54220 would indicate thefollowing material requirements from Table B:PA0220 = Polyamide 6, heat stabilized, from Table PA,B = Table B pr

39、operty requirements,5 = Tensile strength, 70 MPa, min,4 = Tensile modulus, 2400 MPa, min,2 = Charpy impact, 4.0 kJ/m2, min,2 = Deflection temperature at 1.8 MPa, 55C, min,and0 = unspecified.TABLE PA Requirements for Polyamides Dry-as-MoldedA,BGroup Description Class Description Grade DescriptionCVis

40、cosityNumber,ISO 307,min, mL/gDensity,DISO 1183g/cm3TensileStrength,ISO 527-1andISO 527-2,MPa, minTensileModulus,EISO 527-1andISO 527-2,MPa, minCharpyImpactResistance,ISO 179/1eA, kJ/m2,minDeflectionTemperature,FISO 75-1andISO 75-2,at 1.8 MPa,C, min01 PA66 1 General-purpose1 135 1.13 to 1.15 70 2300

41、 3.3 602 165 1.13 to 1.15 70 2300 3.3 603 210 1.13 to 1.15 70 2300 3.3 604 270 1.13 to 1.15 70 2300 3.3 605 recycled 115 1.13 to 1.15 70 2300 3.3 606 recycled 135 1.13 to 1.15 70 2300 3.3 607 115 1.13 to 1.15 70 2300 3.3 60G15 15 % glass . . . 1.20 to 1.26 100 4000 3.0 215G20 20 % glass . . . 1.25 t

42、o 1.33 115 5000 4.0 220G25 25 % glass . . . 1.29 to 1.37 140 6000 5.0 225G35 35 % glass . . . 1.35 to 1.45 170 8000 7.0 235G40 40 % glass . . . 1.42 to 1.52 175 9000 8.0 235G45 45 % glass . . . 1.45 to 1.55 180 10 000 9.0 240G50 50 % glass . . . 1.51 to 1.61 190 11 000 10.0 245M40 40 % mineral . . .

43、 1.45 to 1.55 80 5000 2.0 1000 other2 Heat-stabilized1 135 1.13 to 1.15 70 2300 3.0 602 165 1.13 to 1.15 70 2300 3.0 603 210 1.13 to 1.15 70 2300 3.0 604 270 1.13 to 1.15 70 2300 3.0 605 recycled 115 1.13 to 1.15 70 2300 3.0 606 recycled 135 1.13 to 1.15 70 2300 3.0 60G15 15 % glass . . . 1.20 to 1.

44、26 100 4000 3.0 220G25 25 % glass . . . 1.29 to 1.37 140 6000 5.0 225G30 30 % glass . . . 1.32 to 1.42 160 7000 6.0 230G35 35 % glass . . . 1.35 to 1.45 170 8000 7.0 235G40 40 % glass . . . 1.43 to 1.53 175 9000 8.0 235G45 45 % glass . . . 1.45 to 1.55 180 10 000 9.0 240G50 50 % glass . . . 1.51 to

45、1.61 190 11 000 10.0 245M40 40 % mineral . . . 1.45 to 1.55 80 5000 2.0 100R20 20 % filler . . . 1.23 to 1.31 70 3200 1.5 . . .R40 40 % filler . . . 1.43 to 1.53 100 5500 2.5 2000 other3 Nucleated 1 135 1.13 to 1.15 80 2500 2.8 602 165 1.13 to 1.15 80 2500 2.8 603 210 1.13 to 1.15 80 2500 2.8 604 27

46、0 1.13 to 1.15 80 2500 2.8 605 recycled 115 1.13 to 1.15 80 2500 2.8 606 recycled 135 1.13 to 1.15 80 2500 2.8 600 other4 Nucleated,heat-stabilized1 Requirements the same as corresponding grades under Group 01, Class 323450 other5 Impact-modified1 . . . 1.06 to 1.12 52 1700 9.0 502 recycled . . . 1.

47、06 to 1.12 50 1600 8.0 50G15 15 % glass . . . 1.15 to 1.23 85 3000 6.0 210G35 35 % glass . . . 1.31 to 1.41 110 5500 6.0 225D6779 123TABLE PA Requirements for Polyamides Dry-as-MoldedA,BGroup Description Class Description Grade DescriptionCViscosityNumber,ISO 307,min, mL/gDensity,DISO 1183g/cm3Tensi

48、leStrength,ISO 527-1andISO 527-2,MPa, minTensileModulus,EISO 527-1andISO 527-2,MPa, minCharpyImpactResistance,ISO 179/1eA, kJ/m2,minDeflectionTemperature,FISO 75-1andISO 75-2,at 1.8 MPa,C, min0 other6 Impact-modified,heat-stabilized1 . . . 1.08 to 1.12 52 1700 9.0 502 recycled . . . 1.08 to 1.12 50

49、1600 8.0 50G15 15 % glass . . . 1.15 to 1.23 85 3000 6.0 210G35 35 % glass . . . 1.31 to 1.41 110 5500 6.0 225M40 40 % mineral . . . 1.45 to 1.55 75 4500 4.0 . . .R35 35 % filler . . . 1.38 to 1.48 80 5500 3.0 2000 other7 Toughened 1 . . . 1.06 to 1.10 42 1500 40 452 recycled . . . 1.05 to 1.11 40 1300 35 45G15 15 % glass . . . 1.15 to 1.23 70 2800 9.0 180G35 35 % glass . . . 1.28 to 1.38 110 5500 11 2200 other8 Tough-ened,heat-stabilized1 . . . 1.06 to 1.10 42 1500 40 452 recycled . . . 1.05 to 1.11 40 1300 35 45G15 15 % glass . . . 1.15 t