ASTM D6509-2000 Standard Specification for Atactic Polypropylene (APP) Modified Bituminous Base Sheet Materials Using Glass Fiber Reinforcements《用玻璃纤维加筋法测定无规立构聚丙烯改良沥青基薄板材的标准规范》.pdf

《ASTM D6509-2000 Standard Specification for Atactic Polypropylene (APP) Modified Bituminous Base Sheet Materials Using Glass Fiber Reinforcements《用玻璃纤维加筋法测定无规立构聚丙烯改良沥青基薄板材的标准规范》.pdf》由会员分享，可在线阅读，更多相关《ASTM D6509-2000 Standard Specification for Atactic Polypropylene (APP) Modified Bituminous Base Sheet Materials Using Glass Fiber Reinforcements《用玻璃纤维加筋法测定无规立构聚丙烯改良沥青基薄板材的标准规范》.pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: D 6509 00Standard Specification forAtactic Polypropylene (APP) Modified Bituminous BaseSheet Materials Using Glass Fiber Reinforcements1This standard is issued under the fixed designation D 6509; the number immediately following the designation indicates the year oforiginal adoption or,

2、 in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon (e) indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification covers prefabricated modified bitumi-nous sheet materials wi

3、th glass fiber reinforcement, which useatactic polypropylene (APP) as the primary modifier and whichare intended for use as a base sheet in the fabrication ofmultiple ply roofing and waterproofing membranes.1.2 This is a material specification only. Issues regarding thesuitability of specific roof c

4、onstructions or application tech-niques are beyond the scope of this specification.1.3 The specified tests and property limits used to charac-terize the sheet materials covered by this specification areintended to establish minimum properties. In-place roof systemdesign criteria, such as fire resist

5、ance, field strength, impact/puncture resistance, material compatibility, uplift resistance,the need for field applied coatings, and others, are factorsbeyond the scope of this material specification.1.4 The values stated in SI units are to be regarded as thestandard. Inch-pound units are given in p

6、arentheses for infor-mation only.1.5 The following precautionary statement pertains only tothe test method portion, Section 8, of this specification. Thisstandard does not purport to address all of the safety concerns,if any, associated with its use. It is the responsibility of the userof this stand

7、ard to establish appropriate safety and healthpractices and determine the applicability of regulatory limita-tions prior to use.2. Referenced Documents2.1 ASTM Standards:D 1079 Terminology Relating to Roofing, Waterproofing,and Bituminous MaterialsD 5147 Test Methods for Sampling and Testing Modifie

8、dBituminous Sheet Material2D 5636 Test Method for Low Temperature Unrolling of Feltor Sheet Roofing and Waterproofing Materials23. Terminology3.1 DefinitionsFor definitions of terms used in this speci-fication, refer to Terminology D 1079.4. Materials and Manufacture4.1 In the manufacturing process,

9、 the reinforcement isimpregnated and coated on both sides in an APP-modifiedbituminous coating. The APP-modified bituminous coatingmay be compounded with a mineral stabilizer.4.2 The base sheet may be surfaced with mineral matter toprevent sticking in the roll. The reverse side may be coveredwith a

10、thin polyolefin film or with other surfacing that will notinterfere with adhesion or bonding of the sheet during appli-cation.5. Physical Properties5.1 The sheet shall conform to the minimum physicalproperties described in Table 1.5.2 The finished product shall not crack or be so sticky as tocause t

11、earing or other material damage upon being unrolled atany product temperature between 4 and 60C (40 and140F).6. Dimensions, Mass, and Permissible Variations6.1 The finished product shall conform to the followingdimensions and variations:6.1.1 The width of the roll shall be as agreed upon betweenthe

12、purchaser and the supplier and shall not vary more than1%.6.1.2 The area of the roll shall be no less than as agreedupon between the purchaser and the supplier.6.1.3 The selvage width shall be within 6 mm (14 in.) of thenominal selvage width and shall be not less than 76 mm (3 in.)in width from the

13、edge of the sheet.6.2 The mass and thickness of the finished product shall beas prescribed in Table 2.7. Workmanship, Finish and Appearance7.1 The finished product shall be uniformly impregnatedand coated with atactic polypropylene (APP)-modified bitu-men. It shall be free of visible defects, such a

14、s holes, ragged oruntrue edges, breaks, cracks, tears, and protrusions.7.2 When unrolled on a smooth plane, the sheet shall bestraight and true so that the lap will mate with an adjacentsheet, within the tolerance for the lap without wrinkles,buckles, or fishmouths.1This specification is under the j

15、urisdiction of ASTM Committee D-8 onRoofing, Waterproofing and Bituminous Materials and is the direct responsibility ofSubcommittee D08.04 on Felts and Fabrics.Current edition approved Jan. 10, 2000. Published March 2000.2Annual Book of ASTM Standards, Vol 04.04.1Copyright ASTM, 100 Barr Harbor Driv

16、e, West Conshohocken, PA 19428-2959, United States.8. Sampling and Test Methods8.1 Sample the material and determine the properties de-scribed in this specification in accordance with Test MethodsD 5147 unless otherwise indicated.8.2 High Temperature StabilitySample the material anddetermine the hig

17、h temperature stability in accordance withTest Methods D 5147 and as described herein. Report thehighest test temperature at which flowing, dripping, or dropformation does not occur. Materials shall be permitted to betested in 5.5C (10F) increments.8.3 Low Temperature UnrollingSample the material an

18、ddetermine the low temperature unrolling in accordance withTest Method D 5636 and as described herein. Report the lowesttest temperature at which none of the specimens show crackingor surface rupture. The temperature, at or below which theproduct must pass, is stated in Table 1.9. Inspection9.1 Insp

19、ectionInspection shall be in accordance with thisspecification.9.2 Inspection AlternativesAlternative inspection require-ments shall be determined by and as agreed upon between thepurchaser and the supplier.10. Rejection and Resubmittal10.1 Failure to ConformFailure to conform to any of therequireme

20、nts as stated in this specification constitutes groundsfor rejection.10.2 Rejection RedressThe supplier shall have the right toinspect the rejected materials. The supplier and the purchasershall agree to the quantity of rolls deemed unacceptable. Thesupplier shall then have the right to submit the s

21、ame number ofnew rolls as replacements.11. Packaging and Package Marking11.1 Unless otherwise agreed upon by the purchaser andsupplier, each product package shall be marked plainly with thesuppliers name, the product brand, the ASTM designation, thenet coverage, and the type of bitumen if not eviden

22、t in the labelname of the product.11.2 The rolls shall be wrapped or banded securely in amanner that completely encircles the roll and will preventslipping or unrolling.11.3 No roll shall contain more than two pieces and no morethan 3 % of the rolls in any lot shall contain two pieces. If a rollcont

23、ains a manufacturing splice, the splice shall be markedclearly.12. Keywords12.1 atactic polypropylene (APP); glass fiber; modifiedbituminous sheet; peak load; polyolefin film; reinforcementTABLE 1 Physical Properties of Atactic Polypropylene (APP)-Modified Bituminous Base Sheet Materials Using Glass

24、 FiberReinforcementsNOTE 1The properties in this table are “as manufactured” unlessotherwise noted.PropertyPeak load at 18 6 2C (0 6 3.6F)MD and XMD, kN/m, (lbf/in.) min12.2 (70)Elongation at 18 6 2C (0 6 3.6F)MD and XMD, at peak load, % min1Peak load at 23 6 2C (73.46 3.6F)MD and XMD, before and af

25、ter heatconditioning, kN/m (lbf/in.), min 8.8 (50)Elongation at 23 6 2C (73.463.6F) MD and XMD, before and af-ter heat conditioning, at peak load, %min 2Tear strength at 23 6 3C (73.4 63.6F), N (lbf), min 311 (70)Low temperature, flexibility, beforeand after heat conditioning, C (F),max 0 (+32)Dimen

26、sional stability, % change max 0.2Compound stability, C (F) min 110 (230)Water absorption, % max 3.2Moisture content, % max 1Low temperature unrolling, C (F),max 5 (41)TABLE 2 Dimensions and Mass of Atactic Polypropylene (APP)-Modified Bituminous Base Sheet Materials Using Glass FiberReinforcementsN

27、OTE 1The properties in this table are “as manufactured” unlessotherwise noted.PropertyThickness, min, mm (mils) 1.8 (70)Net mass per unit area, min,g/m2(lbs/100 ft2)1952 (40)Bottom side coating thickness, min,mm (mils)0.76 (30)D 65092The American Society for Testing and Materials takes no position r

28、especting the validity of any patent rights asserted in connectionwith any item mentioned in this standard. Users of this standard are expressly advised that determination of the validity of any suchpatent rights, and the risk of infringement of such rights, are entirely their own responsibility.Thi

29、s standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM Head

30、quarters. Your comments will receive careful consideration at a meeting of the responsibletechnical committee, which you may attend. If you feel that your comments have not received a fair hearing you should make yourviews known to the ASTM Committee on Standards, at the address shown below.This sta

31、ndard is copyrighted by ASTM, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the above address or at610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website (www.astm.org).D 65093