ASTM D6164-2005 Standard Specification for Styrene Butadiene Styrene (SBS) Modified Bituminous Sheet Materials Using Polyester Reinforcements《聚合物增强的苯乙烯丁二烯苯乙烯(SBS)改良沥青层材料的标准规范》.pdf

《ASTM D6164-2005 Standard Specification for Styrene Butadiene Styrene (SBS) Modified Bituminous Sheet Materials Using Polyester Reinforcements《聚合物增强的苯乙烯丁二烯苯乙烯(SBS)改良沥青层材料的标准规范》.pdf》由会员分享，可在线阅读，更多相关《ASTM D6164-2005 Standard Specification for Styrene Butadiene Styrene (SBS) Modified Bituminous Sheet Materials Using Polyester Reinforcements《聚合物增强的苯乙烯丁二烯苯乙烯(SBS)改良沥青层材料的标准规范》.pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: D 6164 05Standard Specification forStyrene Butadiene Styrene (SBS) Modified BituminousSheet Materials Using Polyester Reinforcements1This standard is issued under the fixed designation D 6164; the number immediately following the designation indicates the year oforiginal adoption or, in

2、 the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon (e) indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification covers prefabricated modified bitumi-nous sheet materials reinf

3、orced with polyester fabric as theprimary reinforcement, (see Note 1) with or without granules,which use styrene butadiene styrene (SBS) thermoplasticelastomer as the primary modifier and are intended for use inthe fabrication of multiple ply roofing and waterproofingmembranes.NOTE 1Many modified bi

4、tuminous sheets are currently marketedwith polyester mat reinforced with glass yarns to improve processing inthe manufacture of the finished modified bitumen product and to reducedistortions that may be introduced during production. These glass yarnsare typically a small percentage of the reinforcem

5、ent and do not contributeto the physical properties of the finished product so much as to make theseproducts be classified by D 6162.1.2 This specification is intended as a material specificationonly. Issues regarding the suitability of the specific roofconstructions or application techniques are be

6、yond this scope.1.3 The specified tests and property limits used to charac-terize the sheet materials are intended to establish minimumproperties. In-place roof system design criteria, such as fireresistance, field strength, impact/puncture resistance, materialcompatibility, uplift resistance, and o

7、thers, are factors beyondthe scope of this material specification.1.4 The values stated in SI units are to be regarded as thestandard. The values given in parentheses are for informationonly.2. Referenced Documents2.1 ASTM Standards:2D 1079 Terminology Relating to Roofing, Waterproofing,and Bitumino

8、us MaterialsD 5147 Test Methods for Sampling and Testing ModifiedBituminous Sheet MaterialD 6162 Specification for Styrene Butadiene Styrene (SBS)Modified Bituminous Sheet Materials Using a Combina-tion of Polyester and Glass Fiber Reinforcements3. Terminology3.1 DefinitionsFor definitions of terms

9、used in this speci-fication, refer to Terminology D 1079:3.1.1 elongation at 5 % of maximum load, nthe elonga-tion measured on the load-elongation curve at which point theload has dropped to 5 % of its maximum value.4. Classification4.1 Modified bituminous sheet materials reinforced withpolyester fa

10、bric, Type I and Type II, are covered by thisspecification.4.2 The following grades are used to describe the materialsurfacing:4.2.1 Grade GGranule Surfaced.4.2.2 Grade SSmooth Surfaced.5. Material and Manufacture5.1 In the process of manufacture, the reinforcement issaturated with asphalt or modifi

11、ed asphalt and is impregnatedand coated on both sides with an SBS modified bituminouscoating. The SBS modified bituminous coating shall be per-mitted to be compounded with a mineral stabilizer.5.2 The Grade G sheet is surfaced on the weather side withmineral granules, except for any selvage. To prev

12、ent sticking inthe roll, the reverse side and any selvage shall be permitted tobe covered with a fine mineral surfacing or any other surfacingthat will not interfere with adhesion or bonding of the lapduring application.5.3 Sheet material intended for application by heat welding(torching) shall meet

13、 the minimum bottom coating requirementfound in Table 1.1This specification is under the jurisdiction of ASTM Committee D08 onRoofing and Waterproofing and is the direct responsibility of Subcommittee D08.04on Felts and Fabrics.Current edition approved Oct. 1, 2005. Published October 2005. Originall

14、yapproved in 1997. Last previous edition approved in 2000 as D 6164 00.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe AST

15、M website.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.6. Physical Properties6.1 The sheet shall conform to the minimum physicalproperties prescribed in Table 2.6.2 The finished product shall not crack nor be so sticky asto cause

16、tearing or other material damage upon being unrolledat any product temperature between 4 and 60C (40 and140F).7. Dimensions, Mass, and Permissible Variations7.1 The finished product shall conform to the followingdimensions and variations:7.1.1 The width of the roll shall be as agreed between thepurc

17、haser and the seller and shall not vary more than 1 %.7.1.2 The area of the roll shall be no less than as agreedbetween the purchaser and the seller.7.1.3 The selvage width shall be within 6.4 mm (14 in.) ofthe nominal selvage width and shall be not less than 76.2 mm(3 in.) in width without a laying

18、 line and 63.5 mm (2.5 in.) inwidth if the sheet has a laying line. If a laying line is provided,the line must not be less than 76.2 mm (3 in.) from the edge ofthe sheet.7.2 The mass and thickness of the finished product shall beas prescribed in Table 1.8. Workmanship, Finish, and Appearance8.1 The

19、finished product shall be coated completely in acontinuous, unbroken film and shall be free of such defects asholes, tears, cracks, wrinkles, or permanent deformations,blisters, ragged or untrue edges, and areas of uncoated rein-forcement.8.2 The surface of the weather side shall be uniform infinish

20、 and texture.8.3 For Grade G material, the mineral granules shall bedistributed uniformly over the entire surface in an even layerexcluding any selvage, shall be embedded firmly in the SBSmodified bituminous coating, and the line of demarcationbetween the granule-surfaced portion of the weather side

21、 andany selvage shall be straight and parallel to the edges of thesheet.8.4 When unrolled on a smooth plane, the sheet shall bestraight and true so that the lap will mate with the adjacentsheet within the tolerance for the lap without wrinkles, buckles,or fishmouths.9. Sampling and Test Methods9.1 S

22、ample the material and determine the properties de-scribed in this specification in accordance with Test MethodsD 5147, unless otherwise indicated.9.2 Elongation at 5 % of Maximum LoadSample thematerial and determine the elongation at 23 6 2C (73.4 63.6F) in accordance with Test Methods D 5147 (Sect

23、ion 6)and as defined in 3.1.1.10. Inspection10.1 InspectionInspection shall be in accordance with therequirements of this specification.10.2 Inspection AlternativesAlternative inspection re-quirements shall be determined by and as agreed upon betweenthe purchaser and supplier.11. Rejection and Resub

24、mittal11.1 Failure to ConformFailure to conform to any of therequirements as stated in this specification constitutes groundsfor rejection.11.2 Rejection RedressThe supplier shall have the right toinspect the rejected materials. The supplier and the purchasershall agree to the quantity of rolls deem

25、ed unacceptable. Thesupplier shall then have the right to submit the same number ofnew rolls as replacement.TABLE 1 Dimensions and Masses of SBS Modified BituminousSheet Materials Using Polyester ReinforcementsDescription Type I Type IIThickness, min, mm (mils),Grade S 2.2 (85) 2.9 (115)Grade G 3.3

26、(130) 3.3 (130)Net mass/unit area, min, g/m2(lbs/100 ft2)Grade S 2636 (54) 3417 (70)Grade G 3661 (75) 4394 (90)Bottom coating thickness, heat weldingapplication products, min, mm (mils)Grade S 1.0 (40) 1.0 (40)Grade G 1.0 (40) 1.0 (40)TABLE 2 Physical Properties of SBS Modified Bituminous SheetMater

27、ials Using Polyester ReinforcementsAPropertyType 1Grade: G and SType IIGrade: G and SMaximum load at 18 6 2C (0 63.6F), MD and XMD, min, before andafter heat conditioning, kN/m (lbf/in.) 12.3 (70) 17.5 (100)Elongation at 18 6 2C (0 6 3.6F),MD and XMD, min, at maximum load,before and after heat condi

28、tioning, (%) 20 20Maximum load at 23 6 2C (73.4 63.6F), MD and XMD, min, before andafter heat conditioning, kN/m (lbf/in.) 8.8 (50) 12.3 (70)Elongation at 23 6 2C (73.4 6 3.6F),MD and XMD, min, at maximum load,before and after heat conditioning, (%) 35 50Elongation at 5 % of maximum load23 6 2C (73.

29、4 6 3.6F), MD andXMD, min, before and after heatconditioning, (%) 38 60Tear strength at 23 6 2C(73.4 6 3.6F), min, lbf (N) 246 (55) 311 (70)Low temperature flexibility, max, beforeand after heat conditioning, C (F) 18 (0) 18 (0)Dimensional stability, max, (%) 1 1Compound stability at 102C (215F) no

30、failures no failuresGranule embedment, g, (max)(Grade G only) 2 2AThe properties in this table are “as manufactured” unless otherwise noted.D616405212. Packaging and Package Marking12.1 The finished material shall be furnished as rolls. Therolls shall be wrapped securely to prevent shifting of mater

31、ialand to permit normal handling. If a roll contains a manufac-turing splice, the splice shall be marked clearly; no roll shallcontain more than one splice or two pieces.12.2 Unless otherwise agreed upon by the supplier andpurchaser, each product package shall be marked plainly withthe suppliers nam

32、e, the product name, the ASTM designationincluding type and grade, the net coverage, and the type ofbitumen if not evident in the label name of the product.13. Keywords13.1 modified bituminous sheet; polyester reinforcement;styrene butadiene styrene (SBS); thermoplastic elastomerASTM International t

33、akes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own

34、responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addr

35、essed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at

36、the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org).D6164053