ASTM D5744-2013e1 8032 Standard Test Method for Laboratory Weathering of Solid Materials Using a Humidity Cell《采用湿度室的固体材料实验室老化的标准试验方法》.pdf

《ASTM D5744-2013e1 8032 Standard Test Method for Laboratory Weathering of Solid Materials Using a Humidity Cell《采用湿度室的固体材料实验室老化的标准试验方法》.pdf》由会员分享，可在线阅读，更多相关《ASTM D5744-2013e1 8032 Standard Test Method for Laboratory Weathering of Solid Materials Using a Humidity Cell《采用湿度室的固体材料实验室老化的标准试验方法》.pdf（23页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: D5744 131Standard Test Method forLaboratory Weathering of Solid Materials Using a HumidityCell1This standard is issued under the fixed designation D5744; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last

2、 revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1NOTEEditorially updated Research Report footnote information in Section 13 in December 2013.1. Scope1.1 This kinetic test method cove

3、rs a laboratory weatheringprocedure that (1) enhances reaction-product transport in theaqueous leach of a solid material sample of specified mass, and(2) measures rates of weathering-product mass release. Solubleweathering products are mobilized by a fixed-volume aqueousleach that is performed and c

4、ollected weekly. Leachate samplesare analyzed for pH, alkalinity/acidity, specific conductance,sulfate, and other selected analytes.1.1.1 This test method is intended for use to meet kinetictesting regulatory requirements for mining waste rock and oressized to pass a 6.3-mm (0.25-in.) Tyler screen.1

5、.1.2 Interlaboratory testing of this method has been con-fined to mine waste rock. Application of this test method tometallurgical-processing waste (for example, mill tailings) isoutside the scope of the test method.1.2 This test method is a modification of a laboratoryweathering procedure developed

6、 originally for miningwastes(1-3).2However, it may have useful application wher-ever gaseous oxidation coupled with aqueous leaching areimportant mechanisms for contaminant mobility.1.3 This test method calls for the weekly leaching of awell-characterized solid material sample (weighing at least1000

7、-g), with water of specified purity, and the collection andchemical characterization of the resulting leachate. Test dura-tion is determined by the users objectives of the test.1.4 As described, this test method may not be suitable forsome materials containing plastics, polymers, or refined met-als.

8、 These materials may be resistant to traditional particle sizereduction methods.1.5 Additionally, this test method has not been tested forapplicability to organic substances and volatile matter.1.6 This test method is not intended to provide leachatesthat are identical to the actual leachate produce

9、d from a solidmaterial in the field or to produce leachates to be used as thesole basis of engineering design.1.7 This test method is not intended to simulate site-specificleaching conditions. It has not been demonstrated to simulateactual disposal site leaching conditions. Furthermore, the test isn

10、ot designed to produce effluents that are in chemical equilib-rium with the solid phase sample.1.8 This test method is intended to describe the procedurefor performing the laboratory weathering of solid materials. Itdoes not describe all types of sampling and analytical require-ments that may be ass

11、ociated with its application.1.9 The values stated in SI units are to be regarded asstandard. No other units of measurement are included in thisstandard.1.9.1 ExceptionThe values given in parentheses are forinformation only.1.10 This standard does not purport to address all of thesafety concerns, if

12、 any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:3D75 Practice for Sampling AggregatesD276 Test M

13、ethods for Identification of Fibers in TextilesD420 Guide to Site Characterization for Engineering Designand Construction Purposes (Withdrawn 2011)41This test method is under the jurisdiction of ASTM Committee D34 on WasteManagement and is the direct responsibility of Subcommittee D34.01.04 on Waste

14、Leaching Techniques.Current edition approved Sept. 1, 2013. Published September 2013. Originallyapproved in 1996. Last previous edition approved in 2012 as D5744-12. DOI:10.1520/D5744-13E01.2The boldface numbers in parentheses refer to the list of references at the end ofthis standard.3For reference

15、d ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.4The last approved version of this historical standard is referenced onwww.

16、astm.org.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States1D653 Terminology Relating to Soil, Rock, and ContainedFluidsD737 Test Method for Air Permeability of Textile FabricsD1067 Test Methods for Acidity or Alkalinity of WaterD1125 Te

17、st Methods for Electrical Conductivity and Resis-tivity of WaterD1193 Specification for Reagent WaterD1293 Test Methods for pH of WaterD1498 Test Method for Oxidation-Reduction Potential ofWaterD2234/D2234M Practice for Collection of a Gross Sampleof CoalD3370 Practices for Sampling Water from Close

18、d ConduitsE276 Test Method for Particle Size or ScreenAnalysis at No.4 (4.75-mm) Sieve and Finer for Metal-Bearing Ores andRelated MaterialsE877 Practice for Sampling and Sample Preparation of IronOres and Related Materials for Determination of Chemi-cal Composition and Physical PropertiesE1915 Test

19、 Methods forAnalysis of Metal Bearing Ores andRelated Materials for Carbon, Sulfur, and Acid-BaseCharacteristicsE2242 Test Method for Column Percolation Extraction ofMine Rock by the Meteoric Water Mobility ProcedureD5744 Test Method for Laboratory Weathering of SolidMaterials Using a Humidity CellE

20、691 Practice for Conducting an Interlaboratory Study toDetermine the Precision of a Test Method3. Terminology3.1 Definitions:3.1.1 acid-producing potential, AP, nmaximum potentialfor a solid material sample to produce acidic effluent can bedetermined based on the total sulfur present in the sample.3

21、.1.1.1 DiscussionIt is assumed that this sulfur is presentas iron sulfides (for example, pyrite) 4). This assumption leadsto overestimation of the acid-producing potential of samplescontaining non-ferrous sulfide minerals such as galena (PbS) ornon-acid-producing sulfur-bearing minerals such as gyps

22、um(CaSO4). The AP is commonly converted to the amount ofcalcium carbonate required to neutralize the resulting amountof the acidic effluent produced by the oxidation of containediron sulfide minterals; it is expressed as the equivalent tonnesof calcium carbonate per 1000 tonnes of solid material (3)

23、. TheAPis, therefore, calculated by multiplying the percent of sulfurcontained in the material by a stoichiometric factor of 31.2 (5).3.1.2 interstitial water, nresidual water remaining in thesample pore spaces at the completion of the fixed-volumeweekly leach.3.1.3 leach, nweekly addition of water

24、to solid materialthat is performed either dropwise or by flooding for a specifiedtime period.3.1.4 loading, nmass of a chemical species, which is theproduct of the species concentration and the mass of theweekly leachate collected.3.1.5 mill tailings, nfinely ground ore processing waste(commonly pas

25、sing a 150-m 100-mesh screen) resultingfrom the mill processing of ore.3.1.6 neutralizing potential, NP, ncapacity of a solidmaterial sample to neutralize an acidic effluent while maintain-ing a drainage pH of at least 6.0. NP is expressed in terms oftonnes of calcium carbonate equivalent per 1000 t

26、onnes ofsolid material (3).3.1.6.1 DiscussionNP can be estimated using severaltechniques, including the following (1) determining the amountof calcium and magnesium carbonate in the sample; (2)digesting the solid material with an excess of standardized acidand back titrating with a standardized base

27、 to measure andconvert the residual acid to calcium carbonate equivalents (2,6); and (3) determining the carbonate carbon content in thesample (for example Test Method E1915 acid base classifica-tion).3.1.6.2 DiscussionThe AP and NP are specifically appli-cable to the determination of AP from mining

28、 wastes com-prised of iron-sulfide and carbonate minerals. These terms maybe applicable to any solid material containing iron-sulfide andcarbonate minerals.3.1.6.3 DiscussionCalcium plus magnesium carbonate de-termination generally provides a reasonably accurate NP quan-tification for samples in whi

29、ch carbonate minerals are present.Digestion and back-titration techniques generally overestimatethe capacity of mine waste samples to neutralize acid whilemaintaining drainage pH 6.0. These techniques can yieldnegative values if there is excess soluble acidity on the sample.Carbonate-carbon determin

30、ations will overestimate the capac-ity of mine-waste samples to neutralize acid if they containmetal carbonate minerals that are not net neutralizing (forexample, iron carbonates such as siderite FeCO3 (7).3.1.6.4 DiscussionAP and NP comprise most acid-baseclassifications and these two components ha

31、ve historicallybeen determined by several different analytical methods (7).However, only one acid-base classification is currently anASTM standard, Test Method E1915. Test Method E1915 useseither pyrolysis or chemical treatment of the mine-wastesample to speciate and quantify sulfide-sulfur and carb

32、onate-carbon concentrations, which are expressed as acid-generatingpotential (AGP) and acid neutralizing potential (ANP), respec-tively. Through this speciation, it provides a better estimate ofacid generation than historic AP determinations in whichnon-ferrous and non-acid-generating sulfur mineral

33、s are pres-ent (for example, galena PbSO4 and gypsum CaSO4,respectively.3.1.7 run-of-mine, adjusage in this test method refers toore and waste rock produced by excavation (with attendantvariable particle sizes) from open pit or underground miningoperations.3.1.8 waste rock, nrock produced by excavat

34、ion fromopen pit or underground mining operations that has an eco-nomic mineral content less than a specified economic cutoffvalue for metallurgical processing.4. Summary of Test Method4.1 This laboratory-weathering procedure is designed toenhance the mass release of acidity/alkalinity, metals, and

35、otherpertinent analytes from a sample of solid material weighing atleast 1000 g. This is done by providing conditions conducive toD5744 1312sample oxidation and then leaching the sample with a fixed-volume aqueous leach. Ratio of leach volume to sample massis0.5:1or1:1depending upon the efficiency o

36、f samplewetting and amount of effluent required for chemical analyses.The weekly effluent produced is characterized for dissolvedweathering products. This test method is performed on eachsample in a cylindrical cell. Multiple cells can be arranged inparallel. This configuration permits the simultane

37、ous testing ofmultiple splits of the same solid material sample, or of solidmaterial samples each characterized by different compositions.4.2 Two protocol options (Options A and B) comprise thetest procedure, and these options differ only in the way that theoxygen is supplied to samples in the indiv

38、idual humidity cells.Option A protocol calls for weekly cycles composed of threedays of dry air (less than 10 % relative humidity) and threedays of water-saturated air (approximately 95 % relative hu-midity) pumped up through the sample, followed by a leachwith water on Day 7. Option B protocol diff

39、ers from Option Ain that each cell is stored for six days under conditions ofcontrolled and relatively constant temperature and humidity,and oxygen is supplied to the sample by diffusion (and possiblyadvection) of ambient air rather than by pumping. Although atest duration as short as 20 weeks may b

40、e suitable for somesamples, more recent research indicates that a test durationwell beyond 20 weeks may be required depending upon theobjectives of the test (8,9).5. Significance and Use5.1 The laboratory weathering procedure will generate datathat can be used to: (1) determine whether a solid mater

41、ial willproduce an acidic, alkaline, or neutral effluent, (2) identifysolutes in the effluent that represent dissolved weatheringproducts formed during a specified period of time, (3) deter-mine the mass of solute release, and (4) determine the rate atwhich solutes are released (from the solids into

42、 the effluent)under the closely controlled conditions of the test.5.2 Data generated by the laboratory weathering procedurecan be used to address the following objectives: (1) determinethe variation of drainage quality as a function of compositionalvariations (for example, iron sulfide and calcium+m

43、agnesiumcarbonate contents) within individual mine-rock lithologies,(2) determine the amount of acid that can be neutralized by thesample while maintaining drainage pH 6.0 under the condi-tions of the test, (3) estimate mine-rock weathering rates to aidin predicting the environmental behavior of min

44、e rock, and (4)determine mine-rock weathering rates to aid in experimentaldesign of site-specific kinetic tests.5.3 The laboratory-weathering procedure provides condi-tions conducive to oxidation of solid material constituents andenhances the transport of weathering reaction products con-tained in t

45、he resulting weekly effluent. This is accomplished bycontrolling the exposure of the solid material sample to suchenvironmental parameters as reaction environment temperatureand application rate of water and oxygen.5.4 Because efficient removal of reaction products is vital totrack mineral dissoluti

46、on rates during the procedure, laboratoryleach volumes are large per unit mass of rock to promote therinsing of weathering-reaction products from the mine-rocksample.Acomparison of laboratory kinetic tests with field testshas shown that more reaction products from mineral dissolu-tion are consistent

47、ly released per unit weight and unit time inlaboratory weathering tests (9). For example, sulfate releaserates observed in laboratory tests of metal-mine rock have beenreported to be 3 to 8 times those for small-scale field test pilesof Duluth Complex rock (10), and from 2 to 20 times those forsmall

48、-scale field test piles of Archean greenstone rock (11).Agreater increase is anticipated when laboratory rates are com-pared with field rates measured from operational waste-rockpiles.5.5 Fundamental assumptions governing OptionsAand B ofthe procedure:5.5.1 Option AAn excess amount of air pumped upt

49、hrough the sample during the dry- and wet-air portions of theweekly cycle reduces the potential for oxidation reaction ratesbeing limited by low-oxygen concentrations. Weekly leacheswith low ionic strength water promote the removal of leachablemineral dissolution products produced from the previousweeks weathering cycle. The purpose of the three-day dry-airportion of the weekly cycle is to evaporate some of the waterthat remains in the pores of the sample after the weekly leachwithout totally drying out the sample. Consequently, samplesaturation is re