ASTM D5193 D5193M-1993(2017) Standard Test Method for Coated Fabrics&x2014 Air Retention《涂层织物空气留持的标准试验方法》.pdf

《ASTM D5193 D5193M-1993(2017) Standard Test Method for Coated Fabrics&x2014 Air Retention《涂层织物空气留持的标准试验方法》.pdf》由会员分享，可在线阅读，更多相关《ASTM D5193 D5193M-1993(2017) Standard Test Method for Coated Fabrics&x2014 Air Retention《涂层织物空气留持的标准试验方法》.pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: D5193/D5193M 93 (Reapproved 2017)Standard Test Method forCoated FabricsAir Retention1This standard is issued under the fixed designation D5193/D5193M; the number immediately following the designation indicates theyear of original adoption or, in the case of revision, the year of last re

2、vision. A number in parentheses indicates the year of lastreapproval. A superscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This test method describes the determination of theretention of air by fabrics coated on one or both sides withrubber.1.2 The

3、 values stated in either SI units or inch-pound unitsare to be regarded separately as standard. The values stated ineach system may not be exact equivalents; therefore, eachsystem shall be used independently of the other. Combiningvalues from the two systems may result in non-conformancewith the sta

4、ndard.1.3 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety, health and environmental practices and deter-mine the applicability of regulatory limitations prior t

5、o use.1.4 This international standard was developed in accor-dance with internationally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of International Standards, Guides and Recom-mendations issued by the World Trade Organization TechnicalBarri

6、ers to Trade (TBT) Committee.2. Referenced Documents2.1 ASTM Standards:2D751 Test Methods for Coated Fabrics3. Summary of Test Method3.1 A membrane specimen of the material to be tested isplaced across a circular orifice in the measuring apparatus. Thebottom surface of the membrane is exposed to a s

7、ource of airat a specified pressure. The top surface of the specimen iscovered with water or soap solution. Absence of the appear-ance of air bubbles on the top surface of the material during aspecified exposure period indicates the lack of pin-holes, leaks,or other similar defects. The coated fabri

8、c is then acceptable foruse in the intended application. This procedure is limited tomembranes or coated fabrics having a thickness of less than 3mm 0.125 in.4. Significance and Use4.1 This test method describes a procedure for evaluatingrubberized fabrics that are used to manufacture pneumaticartic

9、les (that is, those that must retain air in order to performsatisfactorily in an intended application). Examples of sucharticles are emergency rafts, life preservers, marine recre-ational equipment, floats, pontons, and warning or detectiondevices, such as buoys or weather balloons.5. Apparatus5.1 T

10、he test apparatus shall consist of the assembly shownin Fig. 1.5.2 If preferred, wing nuts or toggle clamps may be substi-tuted to facilitate assembly and disassembly of the apparatus,as long as an air-tight seal is maintained during testing.6. Test Conditions6.1 Unless otherwise specified, the stan

11、dard conditions fortesting coated fabrics as cited in Test Methods D751 shall beused. All specimens and equipment shall be preconditioned for1 h prior to conducting the test.7. Time Lapse Between Vulcanization and Testing7.1 For all purposes, the minimum time between vulcaniza-tion and testing shall

12、 be 16 h.7.2 For nonproduct tests, the maximum time between vul-canization and testing shall be four weeks, and for evaluationsintended to be comparable, the tests, as far as possible, shouldbe carried out after the same time interval.7.3 For product tests, whenever possible, the time betweenvulcani

13、zation and testing should not exceed three months.8. Test Specimens8.1 Three circular test specimens, 330 6 3mm136 0.1in. in diameter, shall be accurately cut from the coated fabric.1This test method is under the jurisdiction of ASTM Committee D11 on Rubberand Rubber-like Materials and is the direct

14、 responsibility of Subcommittee D11.37on Coated Fabrics, Rubber Threads and Seals.Current edition approved Aug. 1, 2017. Published August 2017. Originallyapproved in 1991. Last previous edition approved in 2012 as D5193/D5193M 93(2012). DOI: 10.1520/D5193_D5193M-93R17.2For referenced ASTM standards,

15、 visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 1942

16、8-2959. United StatesThis international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for theDevelopment of International Standards, Guides and Recommendations issued by the World Trade Organization Techni

17、cal Barriers to Trade (TBT) Committee.1Holes conforming to the size and location of the bolts, asshown in Fig. 1, shall be punched around the perimeter of eachpiece.NOTE 1Specimen size is not critical. An apparatus which canaccommodate specimens having a diameter as small as 254 6 3mm106 0.1 in. is

18、acceptable. Report the specimen size used in 10.1.4.9. Procedure9.1 Position the specimen in the test apparatus by aligningthe punched holes with the projecting bolts and carefullypressing it into position in contact with the rubber gasket. If thefabric is coated on one side only, that side shall fa

19、ce down. Incases where the fabric is coated on both sides, the sidenormally exposed to the inflating air pressure shall be facedown. Place the upper section of the test assembly over thespecimen and tighten the bolts securely. Pour 1 to 2 mm 0.040to 0.080 in. of water, or preferably soap solution, o

20、nto theexposed surface of the specimen to ensure complete coveragethroughout the duration of the test. Gradually increase the airpressure until a level of 70 kPa 10 psi has been reached. Airbubbles initially appearing on the specimen surface, producedby air pressure during closure of the space betwe

21、en the clothand coating, shall be removed. Maintain the test pressure for atleast five, but preferably ten minutes and observe for theappearance of air bubbles. Failure is defined as the continuedappearance of surface air bubbles in any of the three specimenstested as taken from the sample of coated

22、 fabric beingevaluated.10. Report10.1 Report the following information:10.1.1 That the test was performed in accordance with TestMethod D5193/D5193M,10.1.2 Description of the material tested, including thethickness and type of coating,10.1.3 Temperature of the test,10.1.4 Diameter of the test specim

23、en, and10.1.5 Whether the material passed or failed the air reten-tion test.11. Precision and Bias11.1 No statement is made about either the precision or thebias of this test method. Results are reported on an individualpass/fail basis, thus no comparison with a standard referencematerial can be mad

24、e.12. Keywords12.1 air retention; coated fabrics; pneumatic end items.ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of a

25、ny such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are

26、invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not recei

27、ved a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of

28、 this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the Copyright Clearance Center, 222Rosewood Drive, Danvers, MA 01923, Tel: (978) 646-2600; http:/ 1 Air Retention Test ApparatusD5193/D5193M 93 (2017)2