ASTM D5034-2009(2013) Standard Test Method for Breaking Strength and Elongation of Textile Fabrics (Grab Test)《纺织品的拉伸和撕裂强度的标准试验方法(织物抓样强力试验)》.pdf

《ASTM D5034-2009(2013) Standard Test Method for Breaking Strength and Elongation of Textile Fabrics (Grab Test)《纺织品的拉伸和撕裂强度的标准试验方法(织物抓样强力试验)》.pdf》由会员分享，可在线阅读，更多相关《ASTM D5034-2009(2013) Standard Test Method for Breaking Strength and Elongation of Textile Fabrics (Grab Test)《纺织品的拉伸和撕裂强度的标准试验方法(织物抓样强力试验)》.pdf（8页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: D5034 09 (Reapproved 2013)Standard Test Method forBreaking Strength and Elongation of Textile Fabrics (GrabTest)1This standard is issued under the fixed designation D5034; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision

2、, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Department of Defense.1. Scope1.1 This test method covers

3、 the grab and modified grab testprocedures for determining the breaking strength and elonga-tion of most textile fabrics. Provisions are made for wet testing.1.1.1 The grab test procedure is applicable to woven,nonwoven, and felted fabrics, while the modified grab testprocedure is used primarily for

4、 woven fabrics.1.2 This test method is not recommended for glass fabrics,or for knitted fabrics and other textile fabrics which have highstretch (more than 11 %).NOTE 1For the determination of the breaking force and elongation oftextile fabrics using the raveled strip test procedure and the cut stri

5、p testprocedure, refer to Test Method D5035.1.3 This test method provides the values in both inch-poundunits and SI units. Inch-pound units is the technically correctname for the customary units used in the United States. SI unitsis the technically correct name for the system of metric unitsknown as

6、 the International System of Units. The values statedin either acceptable metric units or in other units shall beregarded separately as standard. The values stated in eachsystem may not be exact equivalents; therefore, each systemmust be used independently of the other, without combining inany way.1

7、.4 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2. Referenced Do

8、cuments2.1 ASTM Standards:2D76 Specification for Tensile Testing Machines for TextilesD123 Terminology Relating to TextilesD629 Test Methods for Quantitative Analysis of TextilesD1059 Test Method for Yarn Number Based on Short-Length Specimens (Withdrawn 2010)3D1776 Practice for Conditioning and Tes

9、ting TextilesD5035 Test Method for Breaking Force and Elongation ofTextile Fabrics (Strip Method)D4848 Terminology Related to Force, Deformation andRelated Properties of TextilesD4849 Terminology Related to Yarns and FibersD4850 Terminology Relating to Fabrics and Fabric TestMethods3. Terminology3.1

10、 For definition of textile terms used in this test method:breaking force, breaking load, elongation, extension, tensiletest, refer to Terminology D4848.3.2 For definitions of textile terms used in this test method:constant-rate-of-extension (CRE tensile testing machine,constant-rate-of-load (CRL) te

11、nsile testing machine, constant-rate-of-traverse (CRT) tensile testing machine, refer to Termi-nology D4849.3.3 For definitions of textile terms used in this test method:grab test in fabric testing, and modified grab test in fabrictesting refer to Terminology D4850.3.4 For all other textile terms us

12、ed in this test method, referto Terminology D123.4. Summary of Test Method4.1 A 100-mm (4.0-in.) wide specimen is mounted centrallyin clamps of a tensile testing machine and a force applied until1This test method is under the jurisdiction of ASTM Committee D13 on Textilesand is the direct responsibi

13、lity of Subcommittee D13.60 on Fabric Test Methods,Specific.Current edition approved July 1, 2013. Published September 2013. ReplacesGrab Testing sections of Test Method D1682 90. Originally approved in 1990.Last previous edition approved in 2009 as D503409. DOI: 10.1520/D5034-09R13.2For referenced

14、ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.3The last approved version of this historical standard is referenced onwww.as

15、tm.org.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States1the specimen breaks. Values for the breaking force and theelongation of the test specimen are obtained from machinescales, dials, autographic recording charts, or a computerinterf

16、aced with the testing machine.4.2 This test method describes procedures for carrying outfabric grab tensile tests using two types of specimens and threealternative types of testing machines. For reporting, use thefollowing identification system of specific specimen and ma-chine combinations.4.2.1 Ty

17、pe of specimen:4.2.1.1 GGrab4.2.1.2 MGModified grab4.2.2 Type of tensile testing machine:4.2.2.1 EConstant-rate-of-extension (CRE)4.2.2.2 LConstant-rate-of-load (CRL)4.2.2.3 TConstant-rate-of -traverse (CRT)4.2.3 Possible combinations can be identified as follows:Test SpecimenType of TesterConstant-

18、Rate-of-ExtensionConstant-Rate-of-LoadConstant-Rate-of-TraverseGrab G-E G-L G-TModified Grab MG-E MG-L MG-TFor example, Test Method D5034, G-E refers to a grab test carried out on aconstant rate-of-extension tensile testing machine.5. Significance and Use5.1 The grab test procedure in this test meth

19、od for thedetermination of breaking force and elongation is consideredsatisfactory for acceptance testing of commercial shipments ofmost woven or nonwoven textile fabrics, and the modified grabtest procedure is considered satisfactory for acceptance testingof commercial shipments of most woven texti

20、le fabrics, sincethe procedures have been used extensively in the trade foracceptance testing.5.1.1 In case of disagreement arising from differences inreported test values when using this test method for acceptancetesting of commercial shipments, the purchaser and the sup-plier should conduct compar

21、ative tests to determine if there isa statistical bias between their laboratories. Competent statis-tical assistance is recommended for the investigation of bias.As a minimum, the two parties should take a group of testspecimens which are as homogeneous as possible and whichare from a lot of materia

22、l of the type in question. The testspecimens should then be randomly assigned in equal numbersto each laboratory for testing. The average results from the twolaboratories should be compared using Students t-test forunpaired data and an acceptable probability level chosen by thetwo parties before tes

23、ting is begun. If a bias is found, either itscause must be found and corrected, or the purchaser and thesupplier must agree to interpret future test results in light of theknown bias.5.2 This test method is not recommended for knitted fabricsbecause of their high stretch.5.3 Some modification of tec

24、hnique may be necessary forany fabric having a strength in excess of 200-N/cm (1140-lb/in.) width. Special precautionary measures are provided for usewhen necessary for strong fabrics.5.4 All of the procedures are applicable for testing fabricseither conditioned or wet.5.5 Comparison of results from

25、 tensile testing machinesoperating on different principles is not recommended. Whendifferent types of machines are used for comparison testing,constant-time-to-break at 20 6 3 s is the established way ofproducing data. Even then the data may differ significantly.5.6 Although a constant-rate-of-exten

26、sion is preferred inthese procedures, in cases of dispute, unless there is agreementto the contrary between the purchaser and the supplier, aconstant-time-to-break (20 6 3 s) is to be used.5.7 The grab test procedure is applicable to the determina-tion of the effective strength of the fabric; that i

27、s, the strengthof the yarns in a specific width together with the fabricassistance from the adjacent yarns. The breaking force deter-mined by the grab procedure is not a reflection of the strengthof the yarns actually gripped between clamps and cannot beused for direct comparison with yarn strength

28、determinations.Grab test specimens require much less time to prepare althoughthey require more fabric per specimen. There is no simplerelationship between grab tests and strip tests since the amountof fabric assistance depends on the type of fabric and construc-tion variables.5.8 The modified grab t

29、est procedure is applicable to thedetermination of the breaking force of fabrics with construc-tions in which the application of tensile stress on raveled stripspecimens produces further unraveling. This test method isparticularly applicable to high-strength fabrics.6. Apparatus, Reagents, and Mater

30、ials6.1 Tensile Testing Machine, of the CRE, CRL, or CRT typeconforming to Specification D76, with respect to forceindication, working range, capacity, and elongation indicator,and designed for operation at a speed of 300 6 10 mm/min (126 0.5 in./min); or, a variable speed drive, change gears, orint

31、erchangeable weights as required to obtain the 20 6 3-stime-to-break (see 5.5 and 5.6).Metric Equivalentsin. 1 2mm 25 50FIG. 1 Schematic Illustration of Jaw Faces for Modified GrabTestD5034 09 (2013)26.2 Clamps and Jaw FacesEach jaw face shall be smooth,flat, and with a metallic, or other agreed upo

32、n, gripping surface.The faces shall be parallel and have matching centers withrespect to one another in the same clamp and to the corre-sponding jaw face of the other clamp.6.2.1 For grab tests, each clamp shall have a front (or top)jaw face measuring 25 6 1 mm (1.0 6 0.02 in.) perpendicularto the d

33、irection of the application of the force, and not less than25 nor more than 50 mm (1.0 nor more than 2.0 in.) parallel tothe direction of the application of the force (Note 2). The back,or bottom, jaw face of each clamp shall be at least as large asits mate. Use of a larger face for the second jaw r

34、educes theproblem of front and back jaw face misalignment.NOTE 2Front (or top) faces measuring 25 by 50 mm (1.0 by 2.0 in.)will not necessarily give the same value as 25 by 25-mm (1.0 by 1.0-in.)faces. For many materials, the former are preferable because of the largergripping area which tends to re

35、duce slippage. While both sizes of grippingsurface are permitted, the face sizes used must be the same for all samplesin the test and must be recorded in the report.6.2.2 For modified grab tests, the top (or front) jaw facesshall measure 25 by 50 mm (1.0 by 2.0 in.) or more, with thelonger dimension

36、 parallel to the direction of load application.The bottom (or back) jaw faces shall measure 50 by 50 mm(2.0 by 2.0 in.) or more. (See Fig. 1.)6.3 Metal Clamp, auxiliary, 170 g (6 oz) with at least100-mm (4.0-in.) width anvils.6.4 Distilled Water, for wet testing.6.5 Nonionic Wetting Agent, for wet t

37、esting.6.6 Container, for wetting out specimens.6.7 Standard Fabrics4, for use in verification of apparatus.(See Annex A1.)6.8 Pins, stainless-steel, 10-mm (38-in.) diameter by 125mm (5 in.) long. Two are required if used.7. Sampling7.1 Lot SampleTake a lot sample as directed in theapplicable materi

38、al specification. In the absence of such aspecification, randomly take rolls or pieces that constitute thelot sample using the following schedule:Number of Rolls, Pieces in Lot,InclusiveNumber of Rolls or Pieces in LotSample1to3 all4to24 425 to 50 5over 50 10 % to a maximum of 10 rolls orpiecesNOTE

39、3An adequate specification or other agreement between thepurchaser and the supplier requires taking into account the variabilitybetween rolls of fabric and between specimens from a swatch from a rollof fabric to provide a sampling plan with a meaningful producers risk,consumers risk, acceptable qual

40、ity level, and limiting quality level.7.2 Laboratory SampleFrom each roll or piece of fabrictaken from the lot sample, cut at least one laboratory samplethe full width of the fabric and1m(1yd)along the selvage(machine direction).NOTE 4Results obtained on small hand samples (swatches) can onlybe cons

41、idered as representative of the sample swatch and cannot beassumed to be representative of the fabric piece from which the handsample (swatch) was taken.7.3 Test SpecimensFrom each laboratory sample, take fivespecimens from the warp (machine) direction and eight speci-mens from the filling (cross) d

42、irection (if tested) for eachtesting condition.7.3.1 Testing conditions include the following:7.3.1.1 Warp or Machine DirectionStandard conditionsfor testing textiles.7.3.1.2 Warp or Machine DirectionWet at 21C (70F).7.3.1.3 Filling or Cross DirectionStandard conditions fortesting textiles.7.3.1.4 F

43、illing or Cross DirectionWet at 21C (70F).7.3.2 When using the constant-time-to-break technique andunfamiliar fabrics, prepare two or three extra specimens toestablish the proper rate of loading (or speed for testing).8. Conditioning8.1 For Conditioned Testing:8.1.1 If the samples have a higher mois

44、ture content than themoisture present when at equilibrium in the standard atmo-sphere for testing textiles, precondition as directed in PracticeD1776.8.1.2 Bring samples to moisture equilibrium in the standardatmosphere for testing textiles as directed in Practice D1776.Equilibrium is considered to

45、have been reached when theincrease in mass of the specimen in successive weighings madeat intervals of not less than 2 h does not exceed 0.1 % of themass of the specimen.NOTE 5It is recognized that in practice, materials are frequently notweighed to determine when moisture equilibrium has been reach

46、ed. Whileconditioning for a fixed time cannot be accepted in cases of dispute, it maybe sufficient in routine testing to expose the material to the standardatmosphere for testing textiles for a reasonable period of time before thespecimens are tested. As a guide the following conditioning periods ar

47、esuggested:FiberMinimum Condi-tioning Period, h5Animal Fibers (for example, wool, and regenerated proteins) 8Vegetable Fibers (for example, cotton) 6Viscose 8Acetate 4Fibers having a regain less than 5 % at 65 % relativehumidity28.2 For Wet Testing:8.2.1 Specimens to be tested in the wet condition s

48、hall beimmersed in water at room temperature until thoroughly wetted(Note 6). To thoroughly wet a specimen, it may be necessary toadd not more than 0.05 % of a nonionic wetting agent to thewater. A test of any wet specimen shall be completed withintwo minutes after its removal from the water.NOTE 6T

49、he material has been thoroughly wet out when it has been4Apparatus and accessories are commercially available.5These periods are approximate and apply only to fabrics, spread out in singlethickness, and exposed to freely moving air in the standard atmosphere for testingtextiles. Heavy or coated fabrics may require conditioning periods longer than thosesuggested. If a fabric contains more than one fiber, it should be conditioned for theperiod required by the fiber component which requires the most time (for example,8 h for a wool and acetate blend).D50