ASTM D4103-2017 Standard Practice for Preparation of Substrate Surfaces for Coefficient of Friction Testing《磨擦系数测试用基物表面的制备》.pdf

《ASTM D4103-2017 Standard Practice for Preparation of Substrate Surfaces for Coefficient of Friction Testing《磨擦系数测试用基物表面的制备》.pdf》由会员分享，可在线阅读，更多相关《ASTM D4103-2017 Standard Practice for Preparation of Substrate Surfaces for Coefficient of Friction Testing《磨擦系数测试用基物表面的制备》.pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: D4103 17Standard Practice forPreparation of Substrate Surfaces for Coefficient of FrictionTesting1This standard is issued under the fixed designation D4103; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of l

2、ast revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This practice covers procedures for the preparation ofOVCT (Official Vinyl Composition Tile) and wood panels forsubsequ

3、ent use in tests to measure the coefficient of friction.1.2 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bilit

4、y of regulatory limitations prior to use.1.3 This international standard was developed in accor-dance with internationally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of International Standards, Guides and Recom-mendations issued by the Worl

5、d Trade Organization TechnicalBarriers to Trade (TBT) Committee.2. Referenced Documents2.1 ASTM Standards:2D1436 Test Methods for Application of Emulsion FloorPolishes to Substrates for Testing Purposes3. Significance and Use3.1 The reliability of any of the practices using panelsprepared by these p

6、rocedures may be dependent upon themanner and care in which the test panels are prepared. Havingthese practices in a single procedure eliminates the necessityfor covering these details in all of the practices wherein thepanels are used.4. Test Panels (OVCT)4.1 Preparation of OVCT for Testing Emulsio

7、n FloorPolishesFor interlaboratory and specification testing, tiles ofOVCT shall be used.3The tiles are prepared for use as follows:4.1.1 Thoroughly scrub all tiles using No. 00 steel wool andany suitable aqueous type wax remover or stripper. Scrub hardto help smooth out high and low spots on the ti

8、le. Rinse wellwith clear water, towel dry, and air dry for 15 to 30 min in arack that allows air to reach both sides of the tile.4.1.2 Apply two coats of any suitable floor polish using anymethod as prescribed in Section 5. Allow to dry 2 h betweencoats and a minimum of an overnight dry (15 to 16 h)

9、 after thesecond coat.4.1.3 The next day, strip off all the polish from the tilesfollowing the procedure used in 4.1.1.4.1.4 Repeat the coating (4.1.2) and stripping (4.1.1) opera-tions four more times. A total of ten coats of polish will thenhave been applied and removed.NOTE 1These tiles may be us

10、ed and reused for testing many timesafter having been prepared once in accordance with 4.1.1 4.1.4. Tilesshould be discarded when they show excessive wear or when erraticresults are obtained when used with testing devices. At least 25 tests canbe run before this will be noticed.4.1.5 When scrubbing

11、the tiles it is often found that theybecome distorted and are no longer flat. Any of the devicesused for measuring coefficient of friction will give poorreproducibility if the tiles are not flat. Therefore, it is recom-mended that the tiles be flattened prior to coating for a test. Thefollowing proc

12、edure is suggested:4.1.5.1 Strip the tiles of any previous polish using theprocedure given in 4.1.1. (If the procedures 4.1.1 4.1.4 havebeen followed exactly, this should not be necessary.) Rinsewell with clear water, towel dry, and air dry for 15 to 30 minin a rack that allows air to reach both sid

13、es of the tile.1This practice is under the jurisdiction of ASTM Committee D21 on Polishesand is the direct responsibility of Subcommittee D21.06 on Slip Resistance.Current edition approved March 1, 2017. Published April 2017. Originallyapproved in 1982. Last previous edition approved in 2016 as D410

14、3 90 (2016).DOI: 10.1520/D4103-17.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.3OVCT tile may be obtained

15、through Armstrong Flooring from various homeimprovement stores. The following Armstrong tile substrates have been found toperform adequately for this test method: Armstrong Excelon Feature Tile: Black(56790), http:/ ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-

16、2959. United StatesThis international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for theDevelopment of International Standards, Guides and Recommendations issued by the World Trade Organization Technica

17、l Barriers to Trade (TBT) Committee.14.1.5.2 Pile the tiles face to face and back to back on a pieceof glass slightly larger than the tiles.4.1.5.3 Place the tiles on the glass in an oven at 105 to 115F(40.6 to 46.1C) for 2 to 212 h.4.1.5.4 Remove the entire pile from the oven and let cool,still on

18、the glass, at least overnight (15 to 16 h) at roomtemperature (approximately 73F (22.8C).4.1.5.5 The tiles are now ready for coating with the testpolishes.5. Application of Test Polish5.1 Apply one coat of the emulsion polish to be tested, usingany of the five methods described in Method D1436. Afte

19、rcoating, place the tile in a vertical position. If at the end of 10min there is a bead of polish at the bottom of the tile, wipe itoff and allow the tile to dry in this vertical position for2hatstandard conditions. (See Section 3 of Test Method D1436.)5.1.1 Reverse the tile, top to bottom (rotate t

20、ile 180) andapply a second coat in accordance with Test Method D1436 asthe first. This rotation will equalize the film thickness. Allowthe second coat to dry 18 to 24 h at standard conditions (seeSection 3 of Test Method D1436) before testing.5.2 Regardless of the method used for coating test tile,

21、onlyone method shall be used if a series of tests are being run on asingle polish or a group of polishes.5.3 If there is insufficient polish available to apply two coatsas recommended in 5.1, only one coat may be applied. If aseries of tests is being run, the same number of coats shall beused for al

22、l tests in the series.6. Test Panels (Wood)6.1 Preparation of Wood Panels for Testing Solvent-Based(liquid or paste) PolishesFor interlaboratory and specifica-tion testing, 9 by 9 by38 in. (229 by 229 by 9.5 mm) blocks oflaminated oak shall be used.6.1.1 Thoroughly clean blocks with mineral spirits

23、to re-move wax (new blocks usually have a factory coating of wax).Follow with a mineral spirits rinse to insure removal of allresidual wax. Allow at least 30 min prior to coating for alltraces of the mineral spirits to evaporate. Panels may be usedover and over again providing they are stored proper

24、ly. Blocksnot stored properly may warp. Warped panels will not givereproducible results if used for subsequent coefficient offriction testing. Care should be taken to store blocks in a flatposition and use only flat blocks for testing.7. Application of Test Polish7.1 Using a small amount of the test

25、 polish on a clean cottoncloth (about3gon4ply3by3in.(76by76mm), apply aneven coat of the test polish to a clean panel and allow to dryprior to buffing (one hour should be sufficient). Buff the driedpolish with a clean, dry cloth using moderate pressure, tomaximum shine.7.1.1 After buffing, apply a s

26、econd coat of polish, allow todry, and again buff to maximum shine.7.2 When polished to maximum shine, the blocks are nowready for subsequent testing.8. Keywords8.1 coefficient of testing; polishesASTM International takes no position respecting the validity of any patent rights asserted in connectio

27、n with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible

28、technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consid

29、eration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Bar

30、r Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the Copyright Clearance Center, 222Rosewood Drive, Danvers, MA 01923, Tel: (978) 646-2600; http:/ 172