ASTM D4005-1992(2009) Standard Test Method for Plastic-Coated Fabrics&8212 Completeness of Fusion of PVC Dispersion Coatings《塑料涂覆织物&8212 聚氯乙烯(PVC)弥散涂层的溶解度的标准试验方法》.pdf

《ASTM D4005-1992(2009) Standard Test Method for Plastic-Coated Fabrics&8212 Completeness of Fusion of PVC Dispersion Coatings《塑料涂覆织物&8212 聚氯乙烯(PVC)弥散涂层的溶解度的标准试验方法》.pdf》由会员分享，可在线阅读，更多相关《ASTM D4005-1992(2009) Standard Test Method for Plastic-Coated Fabrics&8212 Completeness of Fusion of PVC Dispersion Coatings《塑料涂覆织物&8212 聚氯乙烯(PVC)弥散涂层的溶解度的标准试验方法》.pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: D4005 92 (Reapproved 2009)Standard Test Method forPlastic-Coated FabricsCompleteness of Fusion of PVCDispersion Coatings1This standard is issued under the fixed designation D4005; the number immediately following the designation indicates the year oforiginal adoption or, in the case of

2、revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This test method describes a simple procedure to deter-mine the completeness of fusion of poly(v

3、inyl chloride) (PVC)dispersion coatings on fabric. This test applies primarily tocoatings with a mechanical bond and does not include tiecoating.1.2 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this stand

4、ard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2. Summary of Test Method2.1 Specimens of the PVC-coated fabric are examined forsurface cracks or breaks, followed by immersion in acetone.Subequent appearance of additio

5、nal cracking indicates thatfusion is incomplete.3. Significance and Use3.1 Poly(vinyl chloride) (PVC) is applied to coated fabricsas a dispersion of PVC particles in a liquid vehicle. During theprocessing of the fabric the PVC is fused or melted to producea uniform film on the fabric. This test meas

6、ures whether thePVC is converted, fused, or melted to produce a homogeneousfilm.3.2 This conversion process is a melting of the crystallitestructures in the polymer particles followed by solution of themolten polymer in the plasticizing vehicle. Fusion is importantin the production of PVC-coated fab

7、rics.4. Apparatus and Reagents4.1 Glass Beaker, 500-mL.4.2 Acetone.4.3 Glass Rods, 5-mm diameter.4.4 Metal Clips.5. Sampling5.1 Select a sample of coated fabric to adequately representthe roll or lot under consideration.5.2 Cut three 20 by 40-mm test specimens to be tested, onein the middle and the

8、others from the sides at least 200 mmfrom the edges of the roll of fabric.5.3 Remove the PVC coating from the fabric of the testspecimens by peeling carefully.6. Procedure6.1 Carefully examine each specimen for cracks on thesurface or breaks (cracks completely through the film) andrecord size, frequ

9、ency, and location.6.2 Wrap each specimen around a glass rod with the coatingunder test outward. Secure the assembly with a metal clamp.6.3 Immerse the test specimens in acetone at 23 6 2C for15 min. Remove and examine visually. Determine whethercracks or breaks have appeared.7. Report7.1 Report the

10、 following information:7.1.1 Description of the material and date manufactured,7.1.2 Date tested,7.1.3 If any cracks or breaks have appeared, report thatfusion is incomplete, and7.1.4 Report the observation of each test specimen sepa-rately.8. Precision and Bias8.1 This test is essentially a “pass-f

11、ail” test and does notassess a quantitatively measured test characteristic. Due to thisno precision and bias data are reported.9. Keywords9.1 coated fabrics; fusion; PVC1This test method is under the jurisdiction of ASTM Committee D11 on Rubberand is the direct responsibility of Subcommittee D11.37

12、on Coated Fabrics, RubberThreads and Seals.Current edition approved Sept. 1, 2009. Published March 2010. Originallyapproved in 1981. Last previous edition approved in 2005 as D4005 92 (2005).DOI: 10.1520/D4005-92R09.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken

13、, PA 19428-2959, United States.ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof i

14、nfringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this sta

15、ndard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your

16、views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM website (www.astm.org/COPYRIGHT/).D4005 92 (2009)2