ASTM D3440-2001(2007) Standard Guide for Preparing Specifications for Water-Emulsion Floor Polishes《水乳化地板擦亮剂制备规格》.pdf

《ASTM D3440-2001(2007) Standard Guide for Preparing Specifications for Water-Emulsion Floor Polishes《水乳化地板擦亮剂制备规格》.pdf》由会员分享，可在线阅读，更多相关《ASTM D3440-2001(2007) Standard Guide for Preparing Specifications for Water-Emulsion Floor Polishes《水乳化地板擦亮剂制备规格》.pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: D 3440 01 (Reapproved 2007)Standard Guide forPreparing Specifications for Water-Emulsion Floor Polishes1This standard is issued under the fixed designation D 3440; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the ye

2、ar of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon (e) indicates an editorial change since the last revision or reapproval.1. Scope1.1 This guide covers preparing specifications for water-emulsion floor polishes on all nonwood floors and for seal

3、edwood floors.1.2 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2

4、. Referenced Documents2.1 ASTM Standards:2D 1288 Method of Test for Total Ash and Silica in Water-Emulsion Polishes2D 1290 Test Method for Sediment in Water-Emulsion Pol-ishes by CentrifugeD 1455 Test Method for 60 Specular Gloss of EmulsionFloor PolishD 1791 Test Method for Accelerated Aging of Liq

5、uidWater-Emulsion Floor PolishesD 1792 Test Method for Long-Term Removability Proper-ties of Emulsion Floor PolishesD 1793 Test Method for Water Spotting of Emulsion FloorPolishesD 2047 Test Method for Static Coefficient of Friction ofPolish-Coated Flooring Surfaces as Measured by theJames MachineD

6、2048 Test Method for Powdering of Floor Polish FilmsD 2825 Terminology Relating to Polishes and Related Ma-terialsD 2834 Test Method for Nonvolatile Matter (Total Solids)in Water-Emulsion Floor Polishes, Solvent-Based FloorPolishes, and Polymer-Emulsion Floor PolishesD 3052 Practice for Rating Water

7、-Emulsion Floor PolishesD 3153 Test Method for Recoatability of Water-EmulsionFloor PolishesD 3206 Test Method for Soil Resistance of Floor PolishesD 3207 Test Method for Detergent Resistance of FloorPolish FilmsD 3210 Test Method for Comparing Colors of Films fromWater-Emulsion Floor PolishesE70 Te

8、st Method for pH of Aqueous Solutions With theGlass Electrode2.2 Federal Standards:3Federal Specification, Wax, Floor, Water-EmulsionP-W155C, February 22, 1978Federal Speicfication, Finish, Floor, Water-EmulsionP-F00430C (GSA-FSS) October 26, 1978.3. Terminology3.1 DefinitionsFor definitions of othe

9、r terms used in thisguide refer to Terminology D 2825.3.1.1 specificationa precise statement of a set of require-ments to be satisfied by a material, product, system, or service,indicating, whenever appropriate the procedure by means ofwhich it may be determined whether the requirements givenare sat

10、isfied. As far as practicable, it is desirable that therequirements be expressed numerically in terms of unitstogether with their limits.4. Classification4.1 Buffng-Type Floor PolishA floor polish that requiresbuffing to maintain or enhance appearance, or both.4.2 Self-Polishing-Type Floor PolishA s

11、elf-polishing-type floor polish that dries to a shine.5. Basis of Purchase5.1 Reference MaterialA floor polish which the purchaserhas found to provide the desired characteristics in each of thetests described and which is mutually agreed upon between thepurchaser and the seller, will be used as a re

12、ference material.Other polishes will be compared to this reference material forperformance.5.2 Qualification SampleSeller shall submit a sampletypical of the material he intends to supply for qualificationtesting.1This guide is under the jurisdiction of ASTM Committee D21 on Polishes andis the direc

13、t responsibility of Subcommittee D21.05 on Specifications.Current edition approved Feb. 1, 2007. Published March 2007. Originallyapproved in 1976. Last previous edition approved in 2001 as D 344001.2Withdrawn.3Available from Standardization Documents Order Desk, Bldg. 4 Section D, 700Robbins Ave., P

14、hiladelphia, PA 19111-5094, Attn: NPODS.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.5.3 Acceptance SampleSamples shall be taken from eachshipment and examined for conformation to the qualificationsample.6. Requirements6.1 Physica

15、l:6.1.1 All values in the following tests are to be mutuallyagreed upon between the purchaser and the seller. Infraredspectroscopy and gas chromatography are optional.6.1.2 Infrared SpectroscopyThe infrared spectra shall bemeasured in accordance with 8.1. The peak heights may varywithin 6 10%.6.1.3

16、ColorThe color shall not be greater than (_) whenanalyzed in accordance with Method D 3210.6.1.4 Gas ChromatographyThe sample shall be analyzedin accordance with 8.3.6.1.5 Total SolidsThe solids shall not be greater than(_) or less than (_) when analyzed in accordance with TestMethod D 2834.6.1.6 Se

17、dimentThe maximum allowable sediment shall be(_) as determined by Test Method D 1290.6.1.7 AlkalinityThe pH of the polish shall be between(_) and (_) when determined by Test Method E70.6.1.8 StabilityStability of the product shall be determinedby Test Method D 1791.6.1.9 OdorThe product shall leave

18、no offensive odor.6.1.10 Total Ash and SilicaThe total ash shall be between(_) and (_) and silica shall be between (_) and (_)when analyzed by Test Method D 1288.7. Sampling7.1 For Inspection LotsSample all production batches.Take a minimum of one sample. Protect samples from anypossibility of freez

19、ing. The sample shall consist of at least 1 gal(3.8 L) of floor polish taken in accordance with 7.2.7.2 Method of SamplingSelect samples at random. Takethe number of samples agreed upon between the purchaser andthe seller. Cans or containers should be coded or identified tocorrespond to production b

20、atch codes.7.3 Identification and DispositionAll subdivisions of thesample taken in accordance with 7.1 and 7.2 shall be properlyidentified, including any code or batch numbers, and numberedconsecutively. Samples shall be distributed as directed by thepurchaser or his authorized representative.Any r

21、emaining shallbe retained at the sampling site pending further or finalinstructions.8. Test Methods8.1 Infrared Spectroscopy:8.1.1 Test SpecimenCuta212-in. (64-mm) square ofaluminum foil of 3-mil (0.08-mm) thickness (minimum) hav-ing one side mirror bright. Wash the square with absolutealcohol, and

22、air dry. The mirror bright side should give aspectra that differs less than 2 % transmittance from thestandard front surface test mirror used in the specular reflec-tance accessory (individual spectrophotometers have differentaccessories).Apply approximately 1 mL of floor polish with aneye dropper i

23、n a zig-zag pattern, and produce a uniform layerby means of a 2-in. (51-mm) doctor blade with 0.008-in.(0.20-mm) gap. The sample thus prepared is allowed to dryovernight before use.8.1.2 ProcedureRun the spectrum of the coated foil on aninfrared spectrophotometer equipped with a specular reflec-tanc

24、e accessory. The base line of the spectrum should showapproximately 90 % transmittance, and the most intense bandshould show approximately 10 %. It may be necessary to movethe coated aluminum foil slightly to approach these conditionsas nearly as possible.8.2 ColorMethod D 3210.8.3 Gas Chromatograph

25、y:8.3.1 ApparatusPack a 6-ft by18-in. (1.83-mm by 3.2-mm) stainless steel column with 5 weight % OV-17 phenylm-ethyl silicone on Chromosorb W804100 mesh, acid washedand silanized. Condition the column overnight in helium at340C in the gas chromatograph.8.3.2 ProcedureProgram the oven temperature fro

26、m 100to 325C at 6C/min, with a 2-min post injection hold at 100Cand an upper temperature hold at 325C for 30 min. Set theinjection port and detectors (Note 1) at 325C and gas flows asfollows: helium 75 mL/min and 50 psi (345 kPa), hydrogen 35mL/min and 30 psi (205 kPa) and air, 280 mL/min and 30 psi

27、.The sample size should be 3 L of floor polish. Condition thechromatograph with one prerun of the sample. Discard theresults of this prerun. The evaluation of results may beperformed manually or with any integrator.NOTE 1It is desirable to use a flame detector set at a suitableattenuation range sinc

28、e the organic content of floor polish is low and thereis an upper limit to the amount of water that can be put on a column.NOTE 2This test method was derived from Federal SpecificationsP-W-155C and P-F-00430C (GSA-FSS).8.4 Total SolidsTest Method D 2834.8.5 SedimentTest Method D 1290.8.6 AlkalinityT

29、est Method E70.8.7 StabilityTest Method D 1791.8.8 Total Ash and SilicaTest Method D 1288.9. Performance Testing9.1 All performance tests shall be equal to reference sampleunless a deviation is agreed upon between the purchaser andthe seller.9.1.1 PerformancePractice D 3052.9.1.2 RemovabilityTest Me

30、thod D 1792.9.1.3 Resistance to SoilingTest Method D 3206.9.1.4 Water SpottingTest Method D 1793.9.1.5 RecoatabilityTest Method D 3153.9.1.6 PowderingTest Method D 2048.9.1.7 Static Coeffcient of FrictionTest Method D 2047.9.1.8 Detergent ResistanceTest Method D 3207.9.1.9 GlossTest Method D 1455.10

31、. Inspection10.1 Inspection shall be made by the procuring agency or aduly authorized representative at the time and place designatedby the procuring agency.4Trademark of Celite Corporation, P.O. Box 519T, Lompoc, CA 93438.D 3440 01 (2007)211. Packaging and Marking11.1 Packaging and marking shall be

32、 as mutually agreedupon between the purchaser and the seller.12. Keywords12.1 floor polishes; polishes; specification preparation;water emulsionASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of t

33、his standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five y

34、ears andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical comm

35、ittee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org).D 3440 01 (2007)3