ASTM D3381 D3381M-2013 Standard Specification for Viscosity-Graded Asphalt Cement for Use in Pavement Construction《路面建筑用粘度分级沥青水泥的标准规格》.pdf

《ASTM D3381 D3381M-2013 Standard Specification for Viscosity-Graded Asphalt Cement for Use in Pavement Construction《路面建筑用粘度分级沥青水泥的标准规格》.pdf》由会员分享，可在线阅读，更多相关《ASTM D3381 D3381M-2013 Standard Specification for Viscosity-Graded Asphalt Cement for Use in Pavement Construction《路面建筑用粘度分级沥青水泥的标准规格》.pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: D3381/D3381M 12D3381/D3381M 13Standard Specification forViscosity-Graded Asphalt Cement for Use in PavementConstruction1This standard is issued under the fixed designation D3381/D3381M; the number immediately following the designation indicates theyear of original adoption or, in the ca

2、se of revision, the year of last revision. A number in parentheses indicates the year of lastreapproval. A superscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Department of Defense.1. Scope1.1 This spec

3、ification covers asphalt cements graded by viscosity at 60C 140F for use in pavement construction. ThreeFoursets of limits are offered in this specification. The purchaser shall specify the applicable table of limits. In the event the purchaserdoes not specify limits, Table 1 shall apply. For asphal

4、t cements graded by penetration at 25C 77F. See Specification D946.If needed, volume corrections for asphalt cements should be made according to Practice D4311.1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in eachsystem may

5、not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from thetwo systems may result in non-conformance with the standard.2. Referenced Documents2.1 ASTM Standards:2D5 Test Method for Penetration of Bituminous MaterialsD92 Test Method for Flash a

6、nd Fire Points by Cleveland Open Cup TesterD36 Test Method for Softening Point of Bitumen (Ring-and-Ball Apparatus)D70 Test Method for Density of Semi-Solid Bituminous Materials (Pycnometer Method)D95 Test Method for Water in Petroleum Products and Bituminous Materials by DistillationD113 Test Metho

7、d for Ductility of Bituminous MaterialsD140 Practice for Sampling Bituminous MaterialsD946 Specification for Penetration-Graded Asphalt Cement for Use in Pavement ConstructionD1754 Test Method for Effects of Heat and Air on Asphaltic Materials (Thin-Film Oven Test)D2042 Test Method for Solubility of

8、 Asphalt Materials in TrichloroethyleneD2170 Test Method for Kinematic Viscosity of Asphalts (Bitumens)D2171 Test Method for Viscosity of Asphalts by Vacuum Capillary ViscometerD2872 Test Method for Effect of Heat and Air on a Moving Film of Asphalt (Rolling Thin-Film Oven Test)D4311 Practice for De

9、termining Asphalt Volume Correction to a Base TemperatureD7553 Test Method for Solubility of Asphalt Materials in N-Propyl Bromide3. Manufacture3.1 The asphalt cement shall be prepared from crude petroleum by suitable methods.4. Physical Requirements4.1 The asphalt cement shall be homogeneous, free

10、from water, and shall not foam when heated to 175C177C 350F.4.2 The asphalt cements shall conform to the requirements given in Table 1, Table 2, Table 3, or Table 4, as specified by thepurchaser.1 This specification is under the jurisdiction of ASTM Committee D04 on Road and Paving Materials and is

11、the direct responsibility of Subcommittee D04.40 on AsphaltSpecifications.Current edition approved Dec. 1, 2012June 1, 2013. Published December 2012July 2013. Originally approved in 1975. Last previous edition approved in 20092012 asD3381 09a.D3381/D3381M 12. DOI: 10.1520/D3381_D3381M-12.10.1520/D33

12、81_D3381M-13.2 For referencedASTM standards, visit theASTM website, www.astm.org, or contactASTM Customer Service at serviceastm.org. For Annual Book of ASTM Standardsvolume information, refer to the standards Document Summary page on the ASTM website.This document is not an ASTM standard and is int

13、ended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Becauseit may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the curr

14、ent versionof the standard as published by ASTM is to be considered the official document.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States15. Methods of Sampling and Testing5.1 Sample and test asphalt cements in accordance with the fol

15、lowing methods:5.1.1 SamplingPractice D140.5.1.2 WaterTest Method D95.5.1.3 Viscosity at 60C 140FTest Method D2171.5.1.4 Viscosity at 135C 275FTest Method D2170.5.1.5 Penetration Test Method D5.5.1.6 Flash Point, Cleveland Open CupTest Method D92.5.1.7 Solubility in TrichloroethyleneTest Method D204

16、2.5.1.8 Thin-Film Oven TestTest Method D1754 (see Table 1 and Table 2).TABLE 1 Requirements for Asphalt Cement, Viscosity Graded at 60C 140F Based on Original AsphaltNOTE 1Grading based on original asphalt.Test Viscosity GradeAC-2.5 AC-5 AC-10 AC-20 AC-30 AC-40Viscosity, 60C 140F, Pas 25 5 50 10 100

17、 20 200 40 300 60 400 80Viscosity, 135C 275F, min, mm2/s 80 110 150 210 250 300Penetration, 25C 77F, 100 g, 5 s, min 200 120 70 40 30 20Flash point, Cleveland open cup, min,C F 165 325 175 350 220 425 230 450 230 450 230 450Solubility in trichloroethylene,A min, % 99.0 99.0 99.0 99.0 99.0 99.0Tests

18、on residue from thin-film oven test:Viscosity, 60C 140F, max, Pas 125 250 500 1000 1500 2000Ductility, 25C 77F, 5 cm/min, min, cm 100A 100 50 20 15 10Ductility, 25C 77F, 5 cm/min, min, cm 100B 100 50 20 15 10ASolubility in N-Propyl Bromide can be an alternate method to Solubility in TCE.B If ductili

19、ty is less than 100, material will be accepted if ductility at 15C 60F is 100 minimum at a pull rate of 5 cm/min.TABLE 2 Requirements for Asphalt Cement Viscosity Graded at 60C 140F Based on Original AsphaltNOTE 1Grading based on original asphalt.NOTE 1Table 2 specifies asphalts that are less temper

20、ature susceptible than those specified by Table 1. Asphalts that meet Table 2 requirements willalso meet Table 1 requirements of the same grade.Test Viscosity GradeAC-2.5 AC-5 AC-10 AC-20 AC-30 AC-40Viscosity, 60C 140F, Pas 25 5 50 10 100 20 200 40 300 60 400 80Viscosity, 135C 275F, min, mm2/s 125 1

21、75 250 300 350 400Penetration, 25C 77F, 100 g, 5 s, min 220 140 80 60 50 40Flash point, Cleveland open cup, min,C F 165 325 175 350 220 425 230 450 230 450 230 450Solubility in trichloroethylene,A min, % 99.0 99.0 99.0 99.0 99.0 99.0Tests on residue from thin-film oven test:Viscosity, 60C 140F, max,

22、 Pas 125 250 500 1000 1500 2000Ductility, 25C 77F, 5 cm/min, min, cm 100A 100 75 50 40 25DuctilityB , 25C 77F, 5 cm/min, min, cm 100B 100 75 50 40 25ASolubility in N-Propyl Bromide can be an alternate method to Solubility in TCE.B If ductility is less than 100, material will be accepted if ductility

23、 at 15C 60F is 100 minimum at a pull rate of 5 cm/min.TABLE 3 Requirements for Asphalt Cement Viscosity Graded at 60C 140F Based on Residue from Rolling Thin-Film Oven TestNOTE 1Grading based on residue from rolling thin-film oven test.Tests on Residue from Rolling Thin-Film OvenTest:AViscosity Grad

24、eAR-1000 AR-2000 AR-4000 AR-8000 AR-16000Viscosity, 60C 140F, Pas 100 25 200 50 400 100 800 200 1600 400Viscosity, 135C 275F, min, mm2/s 140 200 275 400 550Penetration, 25C 77F, 100 g, 5 s, min 65 40 25 20 20% of original penetration, 25C 77F, min . 40 45 50 52Ductility, 25C 77F, 5 cm/min, min, cm 1

25、00B 100B 75 75 75Tests on original asphalt:Flash point, Cleveland open cup, min, CF205 400 220 425 225 440 230 450 240 460Solubility in trichloroethylene,C min, % 99.0 99.0 99.0 99.0 99.0A Thin-film oven test may be used but the rolling thin-film oven test shall be the referee method.B If ductility

26、is less than 100, material will be accepted if ductility at 15C 60F is 100 minimum at a pull rate of 5 cm/min.C Solubility in N-Propyl Bromide can be an alternate method to Solubility in TCED3381/D3381M 1325.1.9 Rolling Thin-Film Oven TestTest Method D2872 (see Table 3 and Table 4).5.1.10 DuctilityT

27、est Method D113.5.1.11 Softening pointTest Method D36.5.1.12 DensityTest Method D70.5.1.13 Solubility in N-propyl BromideTest Method D7553.6. Keywords6.1 asphalt cement;cements; bitumen; pavement;pavements; viscosityASTM International takes no position respecting the validity of any patent rights as

28、serted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time

29、by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn.Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will rece

30、ive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM Inte

31、rnational, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or throu

32、gh the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM website (www.astm.org/COPYRIGHT/).TABLE 4 Requirements for Asphalt Cement Viscosity Graded at 60C 140F Based on Original AsphaltNOTE 1Grading based on original asphalt.NOTE 1Table 4 was d

33、eveloped by theAssociation Ibero LatinAmerica (AILA)shows the limits typically used in Mexico, Central, and SouthAmericaTest Viscosity GradeAC-6 AC-10 AC-20 AC-30 AC-42Viscosity, 60C 140F, P 600 200 1000 200 2000 400 3000 600 4200 600Viscosity, 135C 275F, min, cSt 175 250 300 350 400Flash point, Cle

34、veland open cup, min,C F 177 350 219 425 232 450 232 450 232 450Solubility in trichloroethylene,C min, % 99.0 99.0 99.0 99.0 99.0Specific gravity 25C/25C 77F/77F Report Report Report Report ReportPenetration indexB -1.5 to +1 -1.5 to +1 -1.5 to +1 -1.5 to +1 -1.5 to +1Tests on residue from rolling t

35、hin-film oventest:Mass Change, %w/w max 1.5 1.0 1.0 1.0 1.0Viscosity, 60C 140F, max, P 3000 5000 8000 12000 20000DuctilityA , 25C 77F, 5 cm/min, min, cm 100 75 50 40 25AIf ductility is less than 100, material will be accepted if ductility at 15.5C 60F is 100 minimum at a pull rate of 5 cm/min.BPenetration Index519522500 log pen220SP50log pen2SP2120 Penetration Index519522500 log pen220SP50log pen2SP2120where:pen = penetration at 25C 77 F, 100g, 5sSP = softening point (C)C Solubility in N-Propyl Bromide can be an alternate method to Solubility in TCED3381/D3381M 133