ASTM D2680-2001(2009) Standard Specification for Acrylonitrile-Butadiene-Styrene (ABS) and Poly(Vinyl Chloride) (PVC) Composite Sewer Piping《丙烯腈-丁二烯-苯乙烯(ABS)和聚氯乙烯(PVC)共聚物污水管的标准规范》.pdf

《ASTM D2680-2001(2009) Standard Specification for Acrylonitrile-Butadiene-Styrene (ABS) and Poly(Vinyl Chloride) (PVC) Composite Sewer Piping《丙烯腈-丁二烯-苯乙烯(ABS)和聚氯乙烯(PVC)共聚物污水管的标准规范》.pdf》由会员分享，可在线阅读，更多相关《ASTM D2680-2001(2009) Standard Specification for Acrylonitrile-Butadiene-Styrene (ABS) and Poly(Vinyl Chloride) (PVC) Composite Sewer Piping《丙烯腈-丁二烯-苯乙烯(ABS)和聚氯乙烯(PVC)共聚物污水管的标准规范》.pdf（8页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: D 2680 01 (Reapproved 2009)An American National StandardStandard Specification forAcrylonitrile-Butadiene-Styrene (ABS) and Poly(VinylChloride) (PVC) Composite Sewer Piping1This standard is issued under the fixed designation D 2680; the number immediately following the designation indic

2、ates the year oforiginal adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of

3、the Department of Defense.1. Scope1.1 This specification covers thermoplastic composite pipe,fittings and a joining system for use in gravity flow, nonpres-sure sanitary sewer, and storm drain installations. The pipe andfittings are made of ABS or PVC plastic material. Recom-mended installation prac

4、tices are referenced in Appendix X1.1.2 The values stated in inch-pound units are to be regardedas standard. The values given in parentheses are mathematicalconversions to SI units that are provided for information onlyand are not considered standard.1.3 The following safety hazards caveat pertains

5、only to thetest method portion, Section 10, of this specification: Thisstandard does not purport to address all of the safety problems,if any, associated with its use. It is the responsibility of the userof this standard to establish appropriate safety and healthpractices and determine the applicabi

6、lity of regulatory limita-tions prior to use. Specific precautionary information is givenin 7.2.4.2. Referenced Documents2.1 ASTM Standards:2D 618 Practice for Conditioning Plastics for TestingD 1084 Test Methods for Viscosity of AdhesivesD 1600 Terminology for Abbreviated Terms Relating toPlasticsD

7、 1784 Specification for Rigid Poly(Vinyl Chloride) (PVC)Compounds and Chlorinated Poly(Vinyl Chloride)(CPVC) CompoundsD 2122 Test Method for Determining Dimensions of Ther-moplastic Pipe and FittingsD 2152 Test Method for Adequacy of Fusion of ExtrudedPoly(Vinyl Chloride) (PVC) Pipe and Molded Fitti

8、ngs byAcetone ImmersionD 2235 Specification for Solvent Cement for Acrylonitrile-Butadiene-Styrene (ABS) Plastic Pipe and FittingsD 2321 Practice for Underground Installation of Thermo-plastic Pipe for Sewers and Other Gravity-Flow Applica-tionsD 2412 Test Method for Determination of External Loadin

9、gCharacteristics of Plastic Pipe by Parallel-Plate LoadingD 2564 Specification for Solvent Cements for Poly(VinylChloride) (PVC) Plastic Piping SystemsD 3138 Specification for Solvent Cements for TransitionJoints Between Acrylonitrile-Butadiene-Styrene (ABS)and Poly(Vinyl Chloride) (PVC) Non-Pressur

10、e PipingComponentsD 3212 Specification for Joints for Drain and Sewer PlasticPipes Using Flexible Elastomeric SealsD 3965 Specification for Rigid Acrylonitrile-Butadiene-Styrene (ABS) Materials for Pipe and FittingsD 4396 Specification for Rigid Poly(Vinyl Chloride) (PVC)and Chlorinated Poly(Vinyl C

11、hloride) (CPVC) Com-pounds for Plastic Pipe and Fittings Used in NonpressureApplicationsF 402 Practice for Safe Handling of Solvent Cements,Primers, and Cleaners Used for Joining Thermoplastic Pipeand FittingsF 412 Terminology Relating to Plastic Piping SystemsF 477 Specification for Elastomeric Sea

12、ls (Gaskets) forJoining Plastic PipeF 913 Specification for Thermoplastic Elastomeric Seals(Gaskets) for Joining Plastic Pipe2.2 Federal Standard:Fed. Std. No. 123 Marking for Shipment (Civil Agencies)32.3 Military Standard:MIL-STD-129 Marking for Shipment and Storage33. Terminology3.1 Definitions:3

13、.1.1 GeneralDefinitions are in accordance with Termi-nology F 412 and abbreviations are in accordance with Termi-nology D 1600, unless otherwise specified. The abbreviation1This specification is under the jurisdiction of ASTM Committee F17 on PlasticPiping Systems and is the direct responsibility of

14、 Subcommittee F17.62 on Sewer.Current edition approved March 1, 2009. Published March 2009. Originallypublished as D 2680 68 T. Last previous edition D 2680 01.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of

15、 ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.3Available from Standardization Documents Order Desk, DODSSP, Bldg. 4,Section D, 700 Robbins Ave., Philadelphia, PA 19111-5098, http:/www.dodssp.daps.mil.1Copyright ASTM International, 100 Barr Harbor

16、Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.for acrylonitrile-butadiene-styrene isABS and the abbreviationfor poly(vinyl chloride) is PVC.3.2 Definitions of Terms Specific to This Standard:3.2.1 acrylonitrile-butadiene-styrene (ABS)plastics con-taining polymers or blends of p

17、olymers, or both, in which theminimum butadiene content is 6 %; the minimum acrylonitrilecontent is 15 %; the minimum styrene or substituted styrenecontent, or both, is 15 %; and the maximum content of all othermonomers is not more than 5 %, plus lubricants, stabilizers,and colorants.3.2.2 poly (vin

18、yl chloride) (PVC)plastic compounds con-taining poly(vinyl chloride) homopolymer, and such additivesas stabilizers, lubricants, processing aids, impact improvers,and colorants as needed to provide the required processing andtoughness characteristics.4. Classification4.1 Pipe produced in accordance w

19、ith this specification shallbe classified as ABS composite pipe or PVC composite pipebased on plastic materials used in manufacture.5. Materials and Manufacture5.1 ABS composite pipe or PVC composite pipe shallconsist of two concentric thermoplastic tubes integrally bracedacross the annulus. The res

20、ultant annular space is filled toprovide continuous support between the inner and outer tubes.5.2 CompoundsThe ABS and PVC composite pipe andfittings shall be produced from the following compounds:5.2.1 ABSThe pipe shall be made from a rigidABS plasticand shall meet or exceed the requirements of Spe

21、cificationD 3965 for a minimum cell classification of 1-0-2-2-3. Thefittings shall be made from ABS plastic and shall meet orexceed the requirements of Specification D 3965 for cellclassifications of 1-0-2-2-3 or 4-2-2-2-2. Clean rework ABS,generated from the manufacturers own pipe extrusion andfitt

22、ings may be used by the same manufacturer, provided thatthe pipe and fittings produced meet all the requirements of thisspecification.5.2.2 PVCThe thermoplastic material shall be a rigidPVC plastic and shall meet or exceed the requirements ofSpecification D 1784, for a minimum cell classification of

23、12454 or of Specification D 4396, for a minimum cell classi-fication of 11432. Homopolymer PVC compounds that havehigher cell classifications, because one or more properties aresuperior to those of the specified compounds, are also accept-able. Clean rework PVC, generated from the manufacturersown p

24、ipe and fittings production may be used by the samemanufacturer provided that the pipe and fittings produced meetall the requirements of this specification.5.3 The other component shall be portland cement-perliteconcrete or other inert filler material exhibiting the samedegree of performance, that e

25、ssentially fills the truss annulus toform a composite pipe that meets the requirements of thisspecification.5.4 GasketsElastomeric seals (gaskets) shall comply withrequirements described in Specifications F 477 and F 913.NOTE 1Gasket joints manufactured for PVC composite pipe only.5.5 LubricantsThe

26、lubricant used for the assembly ofgasket joints shall have no detrimental effect on the gasket oron the pipe.6. Performance Requirements6.1 Pipe StiffnessPipe tested in accordance with 10.2 shallhave a minimum pipe stiffness of 200 lb/in./in. (1380 kPa) at5 % deflection.6.2 Pipe DeflectionPipe teste

27、d in accordance with 10.2shall deflect a minimum of 7.5 % without rupture of inner orouter wall.NOTE 2The purpose of the quality control tests in 6.1 and 6.2 is tofurnish test results for a consumer only upon his request at the time oforder and prior to shipment from the point of manufacture.6.3 Aci

28、d ConditioningPipe tested in accordance with 10.3shall meet the requirements of 6.1 and 6.2.NOTE 3This test is intended only for use as a qualification test, not foruse as a simulated service test nor a quality control test.6.4 Joint Tightness:6.4.1 Solvent Cement JointsPipe and fittings attached to

29、the pipe shall show no signs of leakage when tested inaccordance with 10.4.1 (See Note 3).6.4.2 Gasket Joints for PVC Composite PipeJoints shallshow no signs of leakage when tested in accordance with10.4.2 (See Note 3).6.5 Extrusion QualityWhen tested in accordance with10.5, PVC extruded pipe tubes

30、shall not flake or disintegrate.NOTE 4This test is intended for use as a quality control test, not foruse as a simulated service test.7. Other Requirements7.1 Joints and Fittings as shown in Fig. 1 and Fig. 2, shallbe molded or fabricated from materials described in Section 5.Joints and fittings may

31、 be factory-attached to the pipe orfurnished loose, at the option of the purchaser.FIG. 1 Assembly of JointsD 2680 01 (2009)27.2 Solvent Cement Joints:7.2.1 Solvent Cement JointIn the solvent cement joint, thepipe spigot wedges into the tapered socket and the surfacesfuse together.7.2.2 ABS Solvent

32、Cement JointsPrimer for priming sol-vent cemented joints shall be MEK (methyl ethyl ketone) andthe cement shall be MEK containing a minimum of 20 % byweight of dissolved ABS as described in 5.2.1. The cementviscosity when measured in accordance with Method D of TestMethod D 1084 at 70 to 75 F (21 to

33、 23C) with a No. 5 ZahnCup, shall fall within a range of 60 to 80 s. The solids contentof the cement shall be measured in accordance with Specifi-cation D 2235.7.2.3 PVC Solvent Cement JointsThe cement shall com-ply with Specification D 2564, with the exception that theminimum resin content shall be

34、 16 % and minimum viscosityshall be 3500 cP (3500 mPas).7.2.4 Transition Joints (ABS to PVC) Whenever a transi-tion joint is to be assembled, the cement shall comply withSpecification D 3138.(WarningSolvent cements for plasticFIG. 2 Fittings (see Tables 5 and 6 for dimensions)D 2680 01 (2009)3pipe a

35、re made from flammable liquids and should be kept awayfrom all sources of ignition. Good ventilation should bemaintained to reduce fire hazard and to minimize breathing ofsolvent vapors. Avoid contact of cement with skin and eyes.Refer to Practice F 402 for additional information.)NOTE 5Unless other

36、wise specified, it is permissible to use transitionjoints in accordance with this specification and Specification D 3138.7.3 Elastomeric (Gasket) Joints for PVC Composite Pipe:7.3.1 Elastomeric joints shall be designed so that whenassembled, the gasket will be compressed in the joint to forma positi

37、ve seal.7.3.2 The joint shall be designed to avoid displacement ofthe gasket when assembled in accordance with the manufac-turers recommendation.7.3.3 The assembly of joints shall be in accordance with themanufacturers recommendation.8. Dimensions8.1 Diameters and ThicknessThe pipe shall conform tot

38、he dimensions and tolerances shown in Table 1 for ABScomposite pipe, and Table 2 for PVC composite pipe, whenmeasured in accordance with 10.6.1 and 10.6.2.8.2 Laying LengthPipe shall be furnished in standard1212 ft (3.82 m) lengths with a tolerance of 1 in. (25 mm)when measured in accordance 10.6.1.

39、 There is no limit for plusvariation. Other lengths may be provided, if agreed upon by thepurchaser and the seller.8.3 StraightnessPipe intended to be straight shall have amaximum deviation from straightness of116 in./ft (4.85 mm/m)of length, when measured in accordance with 10.6.1.8.4 End Squarenes

40、sPipe ends shall be cut square to thelongitudinal axis as provided in Table 3, when measured inaccordance with 10.6.3.8.5 Joint Couplings, shall conform to the dimensions shownin Table 4, when measured in accordance with 10.6.1.8.6 Fittings:8.6.1 Molded FittingsThe wall thickness of the water waysha

41、ll be no less than the respective minimum thickness listed inTable 5. The socket dimensions and respective wall thicknessshall conform to Table 4. The dimensions and wall thicknessesshall be determined in accordance with 10.6.1.8.6.2 Fabricated FittingsFabricated fittings shall be con-sidered satisf

42、actory if made from pipe and molded fittingsmeeting the requirements of this specification.8.6.3 The spur (lateral) socket shall be suitable for attachingthe respectiveABS or PVC solid wall pipe or adapters shall befurnished for attaching other types of pipes.9. Workmanship9.1 The inner and outer su

43、rfaces of the pipe, joints, andfittings shall be homogeneous throughout and free from visiblecracks, holes, foreign inclusions, and other injurious defects.The pipe, joints, and fittings shall be as uniform as commer-cially practicable in other physical properties.10. Test Methods10.1 Conditioning:1

44、0.1.1 Referee TestingWhen conditioning is required forreferee tests, condition the specimens in accordance withProcedureAof Methods D 618 at 73.4 6 3.6F (23 6 2C) and50 6 5 % relative humidity for not less than 40 h prior to test.Conduct tests under the same conditions of temperature andhumidity, un

45、less otherwise specified.10.1.2 Quality Control TestingCondition specimens for aminimum of4hinairor1hinwater at 73.4 6 3F (23 6 2C).Test the specimens at 73.4 6 3F without regard to relativehumidity.10.1.3 Test ConditionsConduct tests in the StandardLaboratory Atmosphere of 73.4 6 3.6F (23 6 2C) and

46、 50 65 % relative humidity, unless otherwise specified in the testmethods or in this specification. In cases of disagreement, thetolerances shall be 61.8F (61C) and 62 % relative humid-ity.TABLE 1 Pipe Dimensions for ABS Composite PipeNominalSize, in.Outside Diameter Average Inside DiameterAverage C

47、oncentricTube ThicknessAverage Tolerance max min max Inner, min Outer, minInches8 9.41 +0.040.039.51 7.75 7.90 0.060 0.03510 11.75 +0.040.0411.87 9.75 9.88 0.068 0.03812 14.07 +0.060.0514.22 11.75 11.83 0.079 0.04815 17.62 +0.070.0717.80 14.75 14.80 0.096 0.059Millimetres8 239 +1.00.8242 197 201 1.5

48、2 0.9010 298 +1.21.0302 248 251 1.73 0.9612 357 +1.51.2361 298 301 2.01 1.2215 447 +1.81.5452 375 376 2.44 1.50D 2680 01 (2009)410.2 Stiffness and Deflection:10.2.1 Test three specimens in accordance with Test MethodD 2412. Determine the pipe stiffness at 5 % deflection andverify that pipe will defl

49、ect to 7.5 % without wall rupture.10.2.2 Calculate the percent vertical deflection as follows:Vertical deflection,%5 D y / Nominal ID! 3 100 (1)where:D y = vertical deflection of the inside diameter as mea-sured by the plate travel of the apparatus. Both IDand Dy must be in the same units.10.2.3 Calculate the pipe stiffness at 5 % deflection asfollows:Pipe stiffness PS! 5 F/D y (2)where:F = load recorded at 5 % deflection.NOTE 6If F is expressed in newton metres, and Dy is in metres, thenPS is given in N/m2,ifF i