《ASTM D902-2012 Standard Test Methods for Flexible Resin-Coated Glass Fabrics and Glass Fabric Tapes Used for Electrical Insulation《电绝缘用柔性涂树脂玻璃布和玻璃布带的标准试验方法》.pdf》由会员分享，可在线阅读，更多相关《ASTM D902-2012 Standard Test Methods for Flexible Resin-Coated Glass Fabrics and Glass Fabric Tapes Used for Electrical Insulation《电绝缘用柔性涂树脂玻璃布和玻璃布带的标准试验方法》.pdf（8页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: D902 12An American National StandardStandard Test Methods forFlexible Resin-Coated Glass Fabrics and Glass Fabric TapesUsed for Electrical Insulation1This standard is issued under the fixed designation D902; the number immediately following the designation indicates the year oforiginal

2、adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Department of Defense

3、.1. Scope*1.1 These test methods cover procedures for the testing ofresin-coated glass fabrics and glass fabric tapes (Note 1)tobeused as electrical insulation.NOTE 1Methods of testing varnished cloths and tapes are given inMethods D295.1.2 The warp threads in fabrics are the threads that areparalle

4、l with the length dimension as manufactured.1.3 The procedures appear as follows:Procedure SectionASTM TestMethod ReferenceBreaking Strength 22-28 D828Conditioning 6-8 .Dielectric Breakdown Voltage and Di-electric Strength29-38 D149, D295Dissipation Factor and Relative Permit-tivity52-60 D150, E104,

5、D5032Effect of Elevated Temperature 39-45 D1830Resistance to Oil 46-51 D3487Sampling 3-5 .Thermal Endurance 68 D1830Thickness 16-21 D374Thread Count 12-15 .Weight 9-11 .Weight Loss at Elevated Temperature 61-67 D54231.4 The values stated in inch-pound units are to be regardedas the standard. The val

6、ues in parentheses are for informationonly.1.5 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulato

7、ry limitations prior to use. Specific warningstatement are given in 35.1.1 and 58.1.2. Referenced Documents2.1 ASTM Standards:2D149 Test Method for Dielectric Breakdown Voltage andDielectric Strength of Solid Electrical Insulating Materialsat Commercial Power FrequenciesD150 Test Methods for AC Loss

8、 Characteristics and Per-mittivity (Dielectric Constant) of Solid Electrical Insula-tionD295 Test Methods for Varnished Cotton Fabrics Used forElectrical InsulationD374 Test Methods for Thickness of Solid Electrical Insu-lationD828 Test Method for Tensile Properties of Paper andPaperboard Using Cons

9、tant-Rate-of-Elongation Appara-tus3D1711 Terminology Relating to Electrical InsulationD1830 Test Method for Thermal Endurance of FlexibleSheet Materials Used for Electrical Insulation by theCurved Electrode MethodD3487 Specification for Mineral Insulating Oil Used inElectrical ApparatusD5032 Practic

10、e for Maintaining Constant Relative Humid-ity by Means of Aqueous Glycerin SolutionsD5423 Specification for Forced-Convection LaboratoryOvens for Evaluation of Electrical InsulationE104 Practice for Maintaining Constant Relative Humidityby Means of Aqueous Solutions2.2 IEEE Standard:1These methods a

11、re under the jurisdiction of ASTM Committee D09 onElectrical and Electronic Insulating Materials and are the direct responsibility ofSubcommittee D09.07 on Flexible and Rigid Insulating Materials.Current edition approved April 1, 2012. Published April 2012. Originallyapproved in 1946. Last previous

12、edition approved in 2006 as D902 06. DOI:10.1520/D0902-12.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.3Wi

13、thdrawn. The last approved version of this historical standard is referencedon www.astm.org.1*A Summary of Changes section appears at the end of this standard.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.IEEE No. 1 General Principl

14、es for Temperature Limits inthe Rating of Electrical Equipment4SAMPLING3. Selecting Sample Rolls3.1 Sample shipments of resin-coated glass fabrics and glassfabric tapes as specified in 3.2 and 3.3. Select the rolls or padsin such a manner as to be representative of the shipment.3.2 FabricSelect one

15、roll from each ten rolls or fractionthereof in a shipment of full-width fabric.3.3 TapeThe producer and consumer shall agree upon thenumber of rolls selected. Unless otherwise specified, a mini-mum of three rolls per lot shall be selected. For samplingpurposes, a lot consists of identifiable materia

16、ls of the sametype manufactured in one production run and offered fordelivery at the same time.4. Selecting Samples4.1 Cut off and discard not less than two turns of fabric orsix turns of tape from each roll or pad selected for samplingbefore the samples are selected.4.2 From shipments such as sheet

17、s of fabric or strips of tape,take samples representative of the shipment in accordance with4.1.5. Selecting Test Specimens5.1 Prepare the test specimens from samples as selected inSection 4 and as provided for in the individual test methods.CONDITIONING6. Terminology6.1 Definitions of Terms Specifi

18、c to This Standard:6.1.1 conditioning (of resin-coated glass fabrics or glassfabric tapes), nthe process of exposing test specimens of thematerial to a specified temperature, or to an atmosphere ofspecified relative humidity and temperature, for a specifiedperiod of time.7. Significance and Use7.1 T

19、he electrical properties of resin-coated glass fabrics areaffected by their temperature and moisture content. For thisreason it is necessary to control these properties for a specifiedtime immediately prior to testing in order to attain reasonablygood reproducibility of test values. The time of expo

20、sure to theconditioning atmosphere must be long enough to permit thetest specimen to reach a relatively stable value. Usually themoisture content of these materials has little effect on themechanical properties.8. Conditioning8.1 Unless otherwise specified in the individual test meth-ods, condition

21、test specimens as described in 8.1.1, 8.1.2,or8.1.3. In matters of dispute, consider 8.1.2 the referee method.Use the method described in 8.1.3 only if specifically agreedupon by the producer and consumer.8.1.1 Condition the test specimen for 48 h in the StandardLaboratory Atmosphere (50 6 2 % relat

22、ive humidity at atemperature of 23 6 1C (73.4 6 1.8F), and conduct the testsin the Standard Laboratory Atmosphere.8.1.2 Condition the test specimen for 48 h in the StandardLaboratory Atmosphere (50 6 2 % relative humidity at atemperature of 23 6 1C (73.4 6 1.8F), and conduct the testsimmediately upo

23、n removal of the test specimen from theconditioning room or chamber.8.1.3 Do not condition the test specimens if it is desired totest the material in the condition as received by the purchaser,but allow the packages containing the rolls of cloth or tapefrom which the specimens are to be taken to rea

24、ch approxi-mately test-room temperature before the packages are openedand the specimens cut. Remove the specimens to be testedfrom the roll as required and test immediately, unless otherwisespecified.WEIGHT9. Terminology9.1 Definitions of Terms Specific to This Standard:9.1.1 weight (of resin-coated

25、 glass cloth and glass clothtapes), nthe weight per unit area as determined in accordancewith this method. It is usually expressed in pounds per squareyard for a specified nominal thickness.10. Significance and Use10.1 The ratio of resin weight to glass cloth weight, withinand between shipments, can

26、 be determined from the weight ofresin-coated glass cloth and glass cloth tape and the weight ofthe cloth base. This ratio is a factor in determining the electricalcharacteristics of the material. Weight values are useful forestimating weight in designing electrical equipment containinga constituent

27、 part of resin-coated cloth or tape.11. Procedure11.1 Determine the weight per unit area using the methodgiven in Test Methods D295.THREAD COUNT12. Terminology12.1 Definitions of Terms Specific to This Standard:12.1.1 thread count, nThe thread count of resin-coatedglass cloth refers to the count of

28、the number of threads presentin the base glass cloth per linear inch (centimetre) of length orwidth, respectively.13. Significance and Use13.1 Thread count, together with the weight and the widthof the glass cloth, is accepted as the common means fordesignating and identifying cloth constructions.13

29、.2 Certain of the physical and electrical properties ofwoven fabrics are dependent on thread count. That is, assumingthe same size of yarn, an increase in thread count increases theweight, breaking strength, and density of the cloth. Also, the4Available from Institute of Electrical and Electronics E

30、ngineers, Inc. (IEEE),445 Hoes Ln., P.O. Box 1331, Piscataway, NJ 08854-1331, http:/www.ieee.org.D902 122dielectric strength and power factor of the resin-coated fabricmay be changed by altering the number of threads per inch ofthe cloth.14. Procedure14.1 Determine the thread count in threads per in

31、ch or percentimetre separately on both the warp and filling.15. Report15.1 The results of the warp or filling count shall bereported as threads per inch (centimetre).NOTE 2Before counting black resin-coated materials, it will benecessary to remove the resin film with a knife blade or other suitablei

32、nstrument. As an alternative method, liquid resin removers may be usedfor this purpose, provided specimens are dried before the thread count istaken.THICKNESS16. Terminology16.1 Definition:16.1.1 thickness (of an electrical insulating material),nthe perpendicular distance between the two surfaces of

33、interest, determined in accordance with a standard method.17. Significance and Use17.1 This test is of value in determining whether thematerial meets specified tolerances for thickness. In addition,thickness values are essential because of the importance ofspace factor in designing electrical equipm

34、ent.17.2 Determination of dielectric strength, usually expressedin volts per mil, also necessitates thickness measurements.18. Test Specimens18.1 In the case of fabrics, cut a specimen 1 in. (25.4 mm)wide across the entire width.18.2 In the case of tapes, remove the specimens fromsamples selected in

35、 accordance with Section 3. Prepare speci-mens 36 in. (914 mm) long.19. Procedure19.1 Unless otherwise specified, measure the thickness inaccordance with Method C of Test Methods D374 with thefollowing modifications:19.1.1 In making thickness measurements, use only onelayer of the material.19.1.2 In

36、 the case of fabrics, take ten measurements equallyspaced across the width of the specimen. The thickness of thecloth is the average of the ten measurements.19.1.3 In the case of tapes, unless otherwise specified, taketen measurements equally spaced along the length of eachspecimen. The thickness of

37、 the tape is the average of the tenmeasurements.19.1.4 The diameter of the pressure foot is 0.250 6 0.001in. (6.35 6 0.03 mm) and the diameter of the anvil is at least2 in. (50 mm). The pressure on the pressure foot (dead weight)is 25 6 2 psi or 172 6 14 kPa.19.1.5 Methods A and C of Test Methods D3

38、74 shall not beconsidered interchangeable.19.2 Method B of Test Methods D374 may be used uponspecific agreement between the producer and consumer.20. Report20.1 Report the average, maximum, and minimum thick-nesses, in inches, reported to the nearest 0.0001 in. (0.0025mm).21. Precision and Bias21.1

39、This test method has been in use for many years, but noinformation has been presented to ASTM upon which to basea statement of precision. No activity has been planned todevelop such information.21.2 This test method has no bias because the value forthickness is determined solely in terms of this tes

40、t methoditself.BREAKING STRENGTH22. Terminology22.1 Definitions of Terms Specific to This Standard:22.1.1 breaking strength (of resin-coated glass cloths andglass cloth tapes), nthe force per unit width required to breakthe cloth or tapes when tested under certain prescribed condi-tions.23. Signific

41、ance and Use23.1 The breaking strength of finished cloth and tape is ofimportance as a measure of its ability to withstand reasonablepulling without failure while being applied in service.24. Apparatus24.1 Use a constant rate of elongation type tensile testingmachine as described in Test Method D828

42、.25. Test Specimens25.1 From full-width fabric samples or from sample rolls oftapes over 1 in. (25.4 mm) in width cut specimens 1 in. inwidth (Note 3) and not less than 12 in. (305 mm) in length. Fortape having a nominal width of 1 in. or under, preparespecimens of the original width and not less th

43、an 12 in. inlength.NOTE 3In the case of specimens 1 in. in width and having ultimatebreaking loads above the capacity of the machine, it is permissible toreduce the width of the specimen to 0.5 in. (12.7 mm).25.2 In the case of fabrics, cut five specimens with the sidesparallel to the warp threads a

44、nd five with the sides parallel tothe filling threads (Note 4), from samples selected in accor-dance with Section 4.NOTE 4Frequently the fill threads of glass fabrics used to manufac-ture resin-coated glass fabrics do not run in a straight line and are notperpendicular to the warp threads. Breaking

45、strength from specimens cutperpendicular to the warp thread may, therefore, be highly variable.25.3 In the case of tapes, cut five specimens from each rollselected in accordance with 3.3.26. Procedure26.1 Maintain the clearance distance between jaws at 6 in.(153 mm).D902 12326.2 The rate of separati

46、on of the jaws must be 12 6 0.5in/min (305 6 13 mm/min).26.3 Reject all readings obtained when the specimen breaksat or in the jaws.27. Report27.1 The breaking strength of a roll of fabric or tape is theaverage of the breaking strengths of all the specimens testedfrom the roll. Report the average, m

47、aximum, and minimumbreaking strengths in pounds per inch width (or newtons permetre), together with the width and nominal thickness.27.2 In the case of fabrics, report the breaking strengths ofthe warp threads and the filling threads separately.28. Precision and Bias28.1 This test method has been in

48、 use for many years, but noinformation has been presented to ASTM upon which to basea statement of precision. No activity has been planned todevelop such information.28.2 This test method has no bias because the value forbreaking strength is determined solely in terms of this testmethod itself.DIELE

49、CTRIC BREAKDOWN VOLTAGE ANDDIELECTRIC STRENGTH29. Terminology29.1 Definition:29.1.1 For definitions of dielectric breakdown voltage anddielectric strength refer to Terminology D1711.30. Significance and Use30.1 Dielectric strength of resin-coated glass fabric or tapeinsulating material is of significance for the following reasons:30.1.1 Insulating materials are subjected to electricalstresses in service for long periods of time. Although theseservice stresses are usually a small fraction of the breakdownstresses determined by dielectric strength tests, it has bee