ASTM D897-2008(2016) Standard Test Method for Tensile Properties of Adhesive Bonds《胶粘剂拉伸性能的标准试验方法》.pdf

《ASTM D897-2008(2016) Standard Test Method for Tensile Properties of Adhesive Bonds《胶粘剂拉伸性能的标准试验方法》.pdf》由会员分享，可在线阅读，更多相关《ASTM D897-2008(2016) Standard Test Method for Tensile Properties of Adhesive Bonds《胶粘剂拉伸性能的标准试验方法》.pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: D897 08 (Reapproved 2016)Standard Test Method forTensile Properties of Adhesive Bonds1This standard is issued under the fixed designation D897; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last revision.

2、 A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the U.S. Department of Defense.INTRODUCTIONThe accuracy of the results of strength tests

3、of adhesive bonds will depend on the conditions underwhich the bonding process is carried out. Unless otherwise agreed upon by the manufacturer and thepurchaser, the bonding conditions shall be prescribed by the manufacturer of the adhesive. In order toensure that complete information is available t

4、o the individual conducting the tests, the manufacturerof the adhesive shall furnish numerical values and other specific information for each of the followingvariables:(1) Procedure for preparation of surfaces prior to application of the adhesive, including the cleaningand drying of metal surfaces,

5、and special surface treatments which are not specifically limited by thepertinent test method.(2) Complete mixing directions for the adhesive.(3) Conditions for application of the adhesive including the rate of spread or thickness of film,number of coats to be applied, whether to be applied to one o

6、r both surfaces, and the conditions ofdrying where more than one coat is required.(4) Assembly conditions before application of pressure, including the room temperature, length oftime, and whether open or closed assembly is to be used.(5) Curing conditions, including the amount of pressure to be app

7、lied, the length of time underpressure, and the temperature of the assembly when under pressure. It should be stated whether thistemperature is that of the bond line, or of the atmosphere at which the assembly is to be maintained.(6) Conditioning procedure before testing, unless a standard procedure

8、 is specified, including thelength of time, temperature, and relative humidity.Arange may be prescribed for any variable by the manufacturer of the adhesive if it can be assumedby the test operator that any arbitrarily chosen value within such a range or any combination of suchvalues for several var

9、iables will be acceptable to both the manufacturer and the purchaser of theadhesive.1. Scope1.1 This test method covers the determination of the com-parative tensile properties of the adhesive bonds of metal tometal when tested on standard shape specimens and underdefined conditions of pretreatment,

10、 temperature, and testingmachine speed.1.2 The values stated in SI units are to be regarded as thestandard. The values given in parentheses are for informationonly.1.3 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the

11、 user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:2B16/B16M Specification for Free-Cutting Brass Rod, Barand Shapes for Use in Screw Machines1This test method

12、is under the jurisdiction of ASTM Committee D14 onAdhesives and is the direct responsibility of Subcommittee D14.80 on MetalBonding Adhesives.Current edition approved May 1, 2016. Published May 2016. Originallyapproved in 1949. Last previous edition approved in 2008 as D897 08. DOI:10.1520/D0897-08R

13、16.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.Copyright ASTM International, 100 Barr Harbor Drive, PO Bo

14、x C700, West Conshohocken, PA 19428-2959. United States1B107/B107M Specification for Magnesium-Alloy ExtrudedBars, Rods, Profiles, Tubes, and WireB133 Specification for Copper Rod, Bar, And Shapes (With-drawn 1994)3B139/B139M Specification for Phosphor Bronze Rod, Bar,and ShapesB151/B151M Specificat

15、ion for Copper-Nickel-Zinc Alloy(Nickel Silver) and Copper-Nickel Rod and BarB211 Specification for Aluminum and Aluminum-AlloyRolled or Cold Finished Bar, Rod, and WireD907 Terminology of AdhesivesE4 Practices for Force Verification of Testing Machines2.2 Other Documents:AISI 1020 Steel Code Tables

16、43. Terminology3.1 Many of the terms used in this test method are definedin Terminology D907.4. Significance and Use4.1 This test method is primarily comparative. However, itdoes have application as a discriminator in determining varia-tions in adherend surface preparation parameters and adhesiveenv

17、ironmental durability. The test method has found applica-tions in controlling surface preparations, primer, and adhesivesystems for determining strength properties of tested systems.5. Apparatus5.1 Testing Machine, has a force measurement accuracy of61 % when calibrated in compliance with Practices

18、E4 re-quirements and capable of maintaining a specified rate oflading and comprising essentially the following:5.1.1 Fixed MemberA fixed or essentially stationarymember, carrying one grip.5.1.2 Movable Member, carrying a second grip.5.1.3 Grips, for holding a test specimen between the fixedmember an

19、d the movable member. Use the self-aligning type.The grips shall be attached to the fixed and movable member,respectively, in such a way that they will move into alignmentas soon as any load is applied, so that the long axis of the testspecimen will coincide with the direction of the applied pullthr

20、ough the center line of the grip assembly. While the designof grips of this type is optional, one that has been foundsatisfactory is shown in Fig. 1.6. Test Specimens6.1 Use specimens in accordance with Fig. 2. Reuse of thespecimens is allowed by resurfacing those surface areas thatcontained the adh

21、esive. Do this by grinding the adhesive-facedsurface flat and parallel. Metals conforming to the followingASTM specifications are recommended:Metal DesignationBrass ASTM B16/B16M, C3600; half-hard temperCopper ASTM B133, C11000; hard temperAluminum ASTM B211, A92024; G3Steel AISI 1020, G10200; cold-

22、finished barPhosphor bronze ASTM B139/B139M, C54400Magnesium ASTM B107/B107M, Alloy AZ61AF or M1A-F but seeD950Nickel silver ASTM B151/B151M, C77000; quarter-hard6.2 Test 10 specimens.6.3 Discard results if a specimen breaks at a flaw which isremote from the bond line unless such a flaw constitutes

23、avariable, the effect of which is desired to study. Test a substitutespecimen to replace the discarded result.7. Adhesive7.1 Prepare areas that are to be cemented in accordance withthe recommendations of the manufacturer of the adhesive.8. Procedure8.1 Place the specimen in the grips of the testing

24、machine;taking care to align the specimen and the grips with an3The last approved version of this historical standard is referenced onwww.astm.org.4Available from American National Standards Institute (ANSI), 25 W. 43rd St.,4th Floor, New York, NY 10036, http:/www.ansi.org.Corrosion Preventive Finis

25、hin. mm116 1.5316 4.750.3125 7.93751932 15.134 193132 24.6125118 281716 3611516 43.3234 70FIG. 1 Test Grips (Cold-Rolled Steel)D897 08 (2016)2imaginary line joining the points of attachment of the grips tothe machine. Start test loading of the specimen as quickly aspossible.8.2 Speed of TestingFor a

26、ll materials apply a load to thespecimen of 544.3 to 635 kg (1200 to 1400 lb)/min, or adjustthe crosshead speed of the testing machine so that the load canbe accurately determined, but not to exceed 1.3 mm/min (0.05in./min) when the machine is running idle.8.3 RecordRecord the maximum load carried b

27、y thespecimen at failure and also the following:8.3.1 The percentage of cohesion, adhesion, and contactfailures (Note 1). This will be based on a visual inspection.NOTE 1Cohesive failure may be obtained by observing how much ofthe failure has occurred in the adhesive itself. That is, if the cement h

28、asadhered to the metal test pieces and no voids are visual, it represents a 100percent cohesive failure. Adhesion failure refers to the lack of adhering tometals being fastened. Contact failure refers to lack of glue lines being incontact due to uneven surfaces, poor pressure distribution, etc.9. Ca

29、lculations9.1 Tensile strength of the specimens is the breaking load.Express the result in grams per square millimetre (pounds persquare inch) and if possible report to three significant figures.9.2 For each series of tests calculate the arithmetic mean ofall the values obtained and report as the “a

30、verage value.”10. Report10.1 Report the following information:10.1.1 Complete identification of the material tested, includ-ing types, source, manufacturers code numbers, form, etc.10.1.2 Method of preparing test specimens,10.1.3 Average thickness of adhesive layer after formationof the joint, withi

31、n 0.025 mm (0.001 in.). Describe the methodof obtaining the thickness of the adhesive layer includingprocedure, location of measurements, and range of measure-ments.10.1.4 Testing room conditions,10.1.5 Number of specimens tested,10.1.6 Speed of testing, and10.1.7 Average value of the tensile streng

32、th, with an averagevalue of the percentage of cohesion failure for the specimens.11. Precision and Bias11.1 Precision and bias for this test method is being devel-oped and will be available by December 2010.12. Keywords12.1 adhesive bond; tensile buttons; tensile strengthASTM International takes no

33、position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsi

34、bility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to

35、 ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the addr

36、ess shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone),

37、610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the Copyright Clearance Center, 222Rosewood Drive, Danvers, MA 01923, Tel: (978) 646-2600; http:/ 1Surfaces of metal specimens shall be ground flat and parallel.It is preferable to grind all metal specimens at the same time.in.mmin.m14 6.4 1.129 0.005 28.68 0.1358 15.9 178 47.6FIG. 2 Test SpecimenD897 08 (2016)3