ASTM D635-2010 Standard Test Method for Rate of Burning and or Extent and Time of Burning of Plastics in a Horizontal Position《塑料在水平位置条件下的燃烧速度和 或燃烧范围和时间的标准试验方法》.pdf

《ASTM D635-2010 Standard Test Method for Rate of Burning and or Extent and Time of Burning of Plastics in a Horizontal Position《塑料在水平位置条件下的燃烧速度和 或燃烧范围和时间的标准试验方法》.pdf》由会员分享，可在线阅读，更多相关《ASTM D635-2010 Standard Test Method for Rate of Burning and or Extent and Time of Burning of Plastics in a Horizontal Position《塑料在水平位置条件下的燃烧速度和 或燃烧范围和时间的标准试验方法》.pdf（7页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: D635 10Standard Test Method forRate of Burning and/or Extent and Time of Burning ofPlastics in a Horizontal Position1This standard is issued under the fixed designation D635; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revis

2、ion, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Department of Defense.1. Scope*1.1 This fire-test-resp

3、onse test method covers a small-scalelaboratory screening procedure for comparing the relativelinear rate of burning or extent and time of burning, or both, ofplastics in the form of bars, molded or cut from sheets, plates,or panels, and tested in the horizontal position.NOTE 1This test method, and

4、test method A of IEC 60695-11-10 aretechnically equivalent.NOTE 2For additional information on materials which do not burn tothe first reference mark by this test, see Test Method D3801.1.2 This test method was developed for polymeric materialsused for parts in devices and appliances. The results ar

5、eintended to serve as a preliminary indication of their accept-ability with respect to flammability for a particular application.The final acceptance of the material is dependent upon its usein complete equipment that conforms with the standard appli-cable to such equipment.1.3 The classification sy

6、stem described in Appendix X1 isintended for quality assurance and the preselection of compo-nent materials for products.1.4 The values stated in SI units are to be regarded asstandard. No other units of measurement are included in thisstandard.1.5 This standard is used to measure and describe there

7、sponse of materials, products, or assemblies to heat andflame under controlled conditions, but does not by itselfincorporate all factors required for fire hazards or fire riskassessment of materials, products, or assemblies under actualfire conditions.1.6 This standard does not purport to address al

8、l of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use. For specifichazards statements, see 9.2.2. Referenced Document

9、s2.1 ASTM Standards:2D618 Practice for Conditioning Plastics for TestingD648 Test Method for Deflection Temperature of PlasticsUnder Flexural Load in the Edgewise PositionD883 Terminology Relating to PlasticsD1929 Test Method for Determining Ignition Temperatureof Plastics3D2843 Test Method for Dens

10、ity of Smoke from the Burningor Decomposition of PlasticsD3801 Test Method for Measuring the Comparative Burn-ing Characteristics of Solid Plastics in a Vertical PositionD5025 Specification for Laboratory Burner Used for Small-Scale Burning Tests on Plastic MaterialsD5207 Practice for Confirmation o

11、f 20mm (50W) and125mm (500W) Test Flames for Small-Scale BurningTests on Plastic MaterialsE84 Test Method for Surface Burning Characteristics ofBuilding MaterialsE176 Terminology of Fire StandardsE691 Practice for Conducting an Interlaboratory Study toDetermine the Precision of a Test Method2.2 IEC

12、Standards:1This test method is under the jurisdiction ofASTM Committee D20 on Plasticsand is the direct responsibility of Subcommittee D20.30 on Thermal Properties(Section D20.30.03).Current edition approved July 1, 2010. Published August 2010. Originallyapproved in 1941. Last previous edition appro

13、ved in 2006 as D635 - 06. DOI:10.1520/D0635-10.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.3Withdrawn. Th

14、e last approved version of this historical standard is referencedon www.astm.org.1*A Summary of Changes section appears at the end of this standard.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.IEC 60695-11-10 Fire Hazard TestingPar

15、t 11-10 TestFlames50W Horizontal and Vertical Flame Test Meth-ods43. Terminology3.1 Definitions:3.1.1 Definitions used in this test method are in accordancewith Terminology D883, unless otherwise specified. For termsrelating to fire, the definitions used in this test method are inaccordance with Ter

16、minology E176.4. Summary of Test Method4.1 A bar specimen of the material to be tested is supportedhorizontally at one end. The free end is exposed to a specifiedgas flame for 30 s. Time and extent of burning are measuredand reported if the specimen does not burn 100 mm. Anaverage burning rate is re

17、ported for a material if it burns to the100 mm mark from the ignited end.5. Significance and Use5.1 Tests made on a material under conditions hereinprescribed are of value in comparing the rate of burning orextent and time of burning characteristics, or both, of differentmaterials, in controlling ma

18、nufacturing processes, or as ameasure of deterioration or change in these burning character-istics prior to or during use. Correlation with flammabilityunder actual use conditions is not implied.5.2 The rate of burning and other burning phenomena willbe affected by such factors as density, pigments,

19、 any anisotropyof the material and the thickness of the specimen. Test datashall be compared only for specimens of similar thickness,whether comparisons are being made with the same or differentmaterials. The rate of burning and other burning phenomenawill vary with thickness.5.3 It is feasible that

20、 sheet materials that have been stretchedduring processing will relax during burning and give erraticresults unless they are first heated above their deflectiontemperature, in accordance with Test Method D648, for a timesufficient to permit complete relaxation.5.4 Burning tests require that certain

21、variables be arbitrarilyfixed, for example, specimen size, energy source and applica-tion time, and end points. Materials will be found that areunusually sensitive to one or more of the conditions chosen forthis method leading to highly variable results. Additionalburning characterization by other m

22、ethods is highly desirablein such cases (see Note 2).5.5 In this procedure, the specimens are subjected to specificlaboratory test conditions. If different test conditions aresubstituted or the end-use conditions are changed, it will notalways be possible by or from this test to predict changes in t

23、hefire-test-response characteristics measured. Therefore, the re-sults are valid only for the fire-test-exposure conditions de-scribed in this procedure.6. Apparatus6.1 Test Chamber, enclosed laboratory hood, or chamberfree of induced or forced draft during test, having an insidevolume of at least 0

24、.5 m3. An enclosed laboratory hood with aheat-resistant glass window for observing the test and anexhaust fan for removing the products of combustion after thetests is recommended. The atmosphere in and around the testchamber shall be maintained between 15 to 35C and 45 to75 % relative humidity.NOTE

25、 3The amount of oxygen available to support combustion isnaturally important for the conduct of these fire-test-response tests. Fortests conducted by this test method when burning times are protracted,chamber sizes less than 1 m3may not provide accurate results.NOTE 4Some laboratory hoods have induc

26、ed drafts even with theexhaust fan off. A positive-closing damper is recommended.NOTE 5A mirror in the chamber, to provide a rear view of thespecimen, has been found useful in some enclosures.6.2 Test Fixture, A laboratory ring stand or test fixtureequipped with a means of holding a 125 mm2wire gauz

27、ehorizontal and a small clamp permitting the specimen to beheld with its longitudinal axis horizontal and its transverse axisinclined at 45 6 2 angle as illustrated in Fig. 1.NOTE 6A pan of water may be placed on the floor of the hood inposition to catch any burning particles that may drop during th

28、e test.6.3 Laboratory Burner, constructed in accordance withSpecification D5025.6.4 Gas Supply, a supply of technical-grade methane gaswith suitable regulator and meter for uniform gas flow. Naturalgas mixtures having an energy density of approximately 37MJ/m3have been found to provide similar resul

29、ts. However,technical-grade methane gas shall be used as the referee incases of dispute.6.5 Wire Gauze, 20-mesh (approximately 20 openings per25 mm), made with 0.43 6 0.03 mm diameter iron wire cut toapproximately 125 mm2, to sustain burning or glowing par-ticles falling from the specimens.6.6 Timin

30、g Device, accurate to 0.5 s.6.7 Scale, graduated in millimetres.6.8 Micrometer, accurate to 0.05 mm.6.9 Conditioning Room or Chamber, capable of beingmaintained at 23 6 2C and 50 6 5 % relative humidity.6.10 Flexible Specimen Support Fixture, used to facilitatethe testing of specimens that sag and t

31、ouch the wire gauze. (See9.4 and Fig. 2.)7. Test Specimens7.1 All test specimens shall be cut from a representativesample of the material (sheet or end products), or shall be castor injection-, compression-, transfer- or pultrusion-molded tothe necessary form. After any cutting operation, care shall

32、 betaken to remove all dust and any particles from the surface; cutedges shall be fine sanded to have a smooth finish. Unlessotherwise agreed, fabrication of test specimens shall be inaccordance with the specifications of the material being tested.7.2 Specimens shall be 125 6 5 mm long by 13.0 6 0.5

33、 mmwide, and provided in the minimum thickness and in the 3.0(0.0 +0.2) mm thickness. The 3.0 mm thick specimens are notnecessary if the minimum thickness is greater than 3.0 mm, or4Publications of the International Electrotechnical Commission (IEC) andInternational Organization for Standardization

34、(ISO) are available from AmericanNational Standards Institute (ANSI), 25 W. 43rd St., 4th Floor, New York, NY10036.D635 102the maximum thickness is less than 3.0 mm. The maximumthickness shall not exceed 13 mm. The maximum width shallnot exceed 13.5 mm. The edges shall be smooth, and the radiuson th

35、e corners shall not exceed 1.3 mm.7.3 It is possible that the results of tests carried out on testspecimens of different colors, thicknesses, densities, molecularmasses, directions of anisotropy and types, or with differentadditives, fillers/reinforcements will be different.7.3.1 Test specimens in t

36、he minimum and maximum densi-ties, melt flows and level of fillers/reinforcements contentsshall be considered representative of the range, if the resultsyield the same flame test classification. If the burning charac-teristics are not essentially the same for all specimens repre-senting the range, t

37、he evaluation is to be limited only to thematerials in the densities, melt flows, and fillers/reinforcementscontents tested. Additional specimens in the intermediatedensities, melt flows, and fillers/reinforcements contents are tobe tested.7.3.2 Uncolored test specimens and test specimens with thehi

38、ghest level of organic and inorganic pigment loading byweight are considered representative of the color range, if thetest results are essentially the same. When certain pigments areFIG. 1 Test FixtureFIG. 2 Flexible Specimen Support FixtureD635 103known to affect flammability characteristics, they

39、are also to betested. Specimens to be tested are those that:(a) contain no coloring(b) contain the highest level of organic pigments(c) contain the highest level of inorganic pigments(d) contain pigments which are known to adversely affectflammability characteristics8. Conditioning8.1 Condition ten

40、bar specimens for each material andthickness to be tested in accordance with Procedure A ofPractice D618 for a minimum of 48 hours. Once removed fromthe conditioning atmosphere test the specimens within 1 h.Temperature and humidity tolerances shall be in accordancewith Section 7 of Practice D618.8.2

41、 Conduct testing in a laboratory atmosphere of 15 to35C and 45 to 75 % relative humidity.9. Procedure9.1 Prepare at least ten bar specimens. After measuring andrecording the specimen thickness, mark each specimen withtwo lines perpendicular to the longitudinal axis of the bar,25 6 1 and 100 6 1 mm f

42、rom the end that is to be ignited.9.2 Conduct the burning test in a chamber, enclosure, orlaboratory hood free of induced or forced draft. (WarningProducts of combustion may be toxic. An enclosed laboratoryhood and an exhaust fan for removing the products ofcombustion after the tests are recommended

43、.The exhaust fan isturned off during the test and turned on immediately followingthe test in order to remove products of combustion.)9.3 Clamp the specimen at the end farthest from the 25 mmreference mark, in a support with its longitudinal axis horizon-tal and its transverse axis inclined at 45 6 2

44、 as illustrated inFig. 1. Clamp the wire gauze horizontally beneath the speci-men, with a distance of 10 6 1 mm between the lowest edge ofthe specimen and the wire gauze, and with the free end of thespecimen even with the edge of the gauze. Any materialremaining on the wire gauze from the previous t

45、est must beburned off or a new section of wire gauze used for each test.9.4 If the specimen sags at its free end during the initial setup and is not able to maintain the distance of 10 6 1mmasspecified in 9.2, the flexible specimen support fixture illustratedin Fig. 2 shall be used. Position the sup

46、port fixture under thespecimen with the small extending portion of the supportfixture at least 20 mm from the free end of the specimen.Provide enough clearance at the clamped end of the specimenso that the support fixture can be moved freely sidewards. Asthe flame front progresses along the specimen

47、, withdraw thesupport fixture at the same approximate rate, preventing theflame front from contacting the flexible specimen supportfixture, so that there is no effect on the test flame or on theburning of the specimen.9.5 With the central axis of the burner tube in the verticalposition, place the bu

48、rner remote from the specimen, ignite,and adjust it to produce a blue flame 20 mm high. Adjust thegas supply and the air ports of the burner until a 20-mmyellow-tipped blue flame is produced, and then increase the airsupply until the yellow tip just disappears. Measure the heightof the flame. If the

49、 flame height is not 20 6 2 mm, adjust theburner gas supply to give the proper flame height. Once theflame has been properly set to a height of 20 6 2 mm wait forat least 5 min to allow the burner conditions to reachequilibrium.NOTE 7See Practice D5207 for recommended back pressure and flowrate for the gas supply and calibration procedure for the 20 mm flame.9.6 Place the burner so that the test flame impinges on thefree end of the test specimen to a depth of approximately 6 mmstarting the timing device simultaneously. The central axis ofthe burner tube is to be