1、Designation: D413 98 (Reapproved 2017)Standard Test Methods forRubber PropertyAdhesion to Flexible Substrate1This standard is issued under the fixed designation D413; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last

2、 revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the U.S. Department of Defense.1. Scope1.1 These test methods cover the determi

3、nation of theadhesion strength between plies of fabric bonded with rubberor the adhesion of the rubber layer in articles made from rubberattached to other material. They are applicable only when theadhered surfaces are approximately plane or uniformly circularas in belting, hose, tire carcasses, or

4、rubber-covered sheetmetal.1.2 When the adhered surfaces contain sharp bends, angles,or other gross irregularities that cannot be avoided in preparingtest specimens, special test methods must be employed forevaluating adhesion.1.3 The values stated in SI units are to be regarded as thestandard. The v

5、alues given in parentheses are for informationonly.1.4 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety, health, and environmental practices and deter-mine the a

6、pplicability of regulatory limitations prior to use.1.5 This international standard was developed in accor-dance with internationally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of International Standards, Guides and Recom-mendations issued

7、by the World Trade Organization TechnicalBarriers to Trade (TBT) Committee.2. Referenced Documents2.1 ASTM Standards:2D3040 Practice for Preparing Precision Statements for Stan-dards Related to Rubber and Rubber Testing (Withdrawn1987)3D3182 Practice for RubberMaterials, Equipment, and Pro-cedures f

8、or Mixing Standard Compounds and PreparingStandard Vulcanized SheetsD3183 Practice for RubberPreparation of Pieces for TestPurposes from Products3. Summary of Test Method3.1 Two general test methods are given:3.1.1 Static-Mass Method, in which the force required tocause separation between adhered su

9、rfaces is applied by meansof gravity acting on a mass.3.1.2 Machine Method, in which the force required to causeseparation between adhered surfaces is applied by means of atension machine.3.2 Except as may be otherwise specified in these testmethods, the requirements of Practices D3182 and D3183,sha

10、ll be complied with and are made a part of these testmethods.3.3 In case of conflict between the provisions of these testmethods and those of detailed specifications or test methods fora particular material, the latter shall take precedence.3.4 As covered by these test methods, an adhesion testconsi

11、sts of applying to a test specimen, under specifiedconditions, a (measured) force sufficient to strip from thespecimen at a measured rate, a layer of moderate thicknesswith separation (rupture, tearing) at the adhered surfaces. Thenumerical value of the adhesion is expressed as (1) the averageforce

12、required to cause separation at a definite rate, or (2) theaverage rate of separation caused by a known or specifiedforce. In the machine test method, the rate of separation is fixedand the adhesion value must be expressed in terms of themeasured force. With the static-mass test method, either (1)or

13、(2) can be used, but the latter is preferable and will be hereemployed.1These test methods are under the jurisdiction of ASTM Committee D11 onRubber and Rubber-like Materials and are the direct responsibility of SubcommitteeD11.25 on Rubber Adhesive Systems.Current edition approved Oct. 1, 2017. Pub

14、lished December 2017. Originallyapproved in 1935. Last previous edition approved in 2013 as D413 98 (2013).DOI: 10.1520/D0413-98R17.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume inform

15、ation, refer to the standards Document Summary page onthe ASTM website.3The last approved version of this historical standard is referenced onwww.astm.org.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United StatesThis international standard was

16、developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for theDevelopment of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.14. Significanc

17、e and Use4.1 These test methods are used to ensure the quality of aproduct by determining the force per unit width required toseparate a rubber layer from a flexible substrate such as fabric,fibre, wire, or sheet metal. The acceptable value of adhesionmeasured will, of course, vary from product to p

18、roduct due todifferent rubber formulations, flexible substrates, and types ofproducts. However, once a product is established, minimumvalues of separation force can be determined and agreed to byproducer and consumer and both can monitor to assuremaintenance of the agreed-upon minimum value.STATIC-M

19、ASS METHOD5. Apparatus5.1 The apparatus required for the adhesion test by thestatic-mass test method consists of a supporting frame, testingclamps, mandrels, calibrated masses, and mass carriers. Thesupporting frame is of such design that clamps for stripspecimens hang on it vertically and that mand

20、rels for ringspecimens are supported on it horizontally. The frame hassufficient height to permit the mass carrier to be suspendedfrom the test specimens by means of clamps and to hang freelyduring the progress of the test. Provision also is made tosupport the mandrels so that they revolve freely wi

21、th minimumfriction. Suitable apparatus is shown in Fig. 1 and Fig. 2.6. Test Specimens6.1 Strip SpecimensType APlane strips having a widthof 25 + 3, 0 mm (1 + 0.125, 0 in.), and a minimum lengthsuch as to permit 180 peel separation over sufficient distanceto indicate the adhesion value.6.1.1 Cut the

22、 specimen to 25 + 3, 0 mm (1 + 0.125 0in.) wide. The thickness will vary according to the constructionof the article being tested. The maximum thickness of thespecimen is limited to 13 mm (0.5 in.). To comply with thisrequirement, slice or buff the specimen. The ply or layer beingseparated should ne

23、ver be over 6.5 mm (0.25 in.) thick.6.1.2 Cut the specimen from the article in such a mannerthat the adhered parts have the same width where practicable.The technique used in 6.2.2 and 6.2.3 may be applied here.When necessary, or specified, cut only the layer to be separated(by application of load)

24、to the prescribed width. In such cases,remove the portions of that layer remaining outside of the testwidth to avoid edge constriction during separation.6.1.3 Curved specimens for test in strip form shall havecurvature only in the length dimension of the specimen.6.2 Strip SpecimensType BThe same as

25、 Type A, withthe exception of 90 peel and the separation line in the centerof the specimen.6.2.1 Cut the specimen 35 mm (138 in.) wide. Remove theexcess plies to obtain a thickness of 6 mm (14 in.) and leave theseparation line in the center of the specimen to ensure a 90peel.6.2.2 Buff to a width of

26、 30 mm (118 in.) with a coarse gritemery cloth (grit No. 40) with care to prevent burning orgumming the sides of the specimen.6.2.3 Make a 2-mm (116-in.) deep slit with a knife alongeach side exactly where the specimen is to be separated duringtesting. Use a knife with an adjustable blade where only

27、 thedesired depth of cut (2 mm) of blade is exposed.6.3 Ring SpecimensClosed rings having a width of 25 mm(1 in.) and maximum internal diameter of 100 mm (4 in.).6.3.1 Mount the article on a smooth, close-fitting, slightlytapered wooden mandrel.6.3.2 Rotate the mandrel (a lathe is preferred) and cut

28、25-mm (1-in.) wide ring sections by forcing a sharp pointedknife gradually through the article.6.3.3 Cut rings with internal diameters over 100 mm (4 in.)through and open to form strip specimens.7. Procedure7.1 Strip Specimen: Type A, 180 PeelMeasure the widthof the strip cut to the nearest 0.2 mm (

29、0.01 in.) and record.Separate the parts to be tested by hand at one end of the stripspecimen and at a sufficient distance to permit the jaws of thetesting clamp to be attached. Suspend the strip from thesupporting frame by the separated end, holding in the jaws ofDimen-sionmm in.Dimen-sionmm in.A 75

30、.0 3 N 10.018B 45.0 114 P 90.0 312C 37.5 112 R 30.0 114D 15.038 S 20.034E 40.0 11116 T 18.02332F 15.018 U 30.0 118G 10.01118 V3.018H11.01332 W614J 13.012 X3.018K8.0116 Y3764L 16.038 Z8.0516M 50.0 118 AA 6.0732AB 75.0 3FIG. 1 Clamp for Adhesion TestD413 98 (2017)2the testing clamp all separated ends

31、except the one under test.Attach to the lower end of the test specimen a minimum masssufficient to maintain the strip specimen in approximately avertical position. Or, hold the specimen against a vertical platein such a manner as to keep the specimen in approximately avertical position during the te

32、st to ensure a 180 peel. Apply aspecified or known mass by means of a clamp and mass carrierto the layer of which the adhesion is being determined. Includethe mass of the clamp and carrier in the total mass causingseparation. Release the mass slowly without jerking and insuch a manner that the separ

33、ating layer is stripped from thespecimen at an angle of approximately 180.7.2 Strip Specimen: Type B, 90 PeelTest specimens in thesame manner as Type A, with the exception that the unpeeledportion of the specimen is kept in a horizontal position using aplate, if necessary, to ensure a 90 peel.7.3 Ri

34、ng SpecimensPlace the ring specimen snugly on amandrel that has an outside diameter substantially the same asthe internal diameter of the ring. Separate the parts to be testedsufficiently by hand to permit the jaws of the testing clamp tobe attached. With the mandrel resting on the supporting frame,

35、apply a known or specified mass by means of the clamp and amass carrier to the layer of which the adhesion is being tested.Include the mass of the clamp and carrier in the total masscausing separation. Release the mass slowly without jerkingand in such a manner that the separating layer is stripped

36、fromthe specimen at an angle of approximately 90.7.4 Rate of SeparationRecord the time needed to com-plete the separation using a stop watch or a watch having asecond hand. Remove the mass and measure the lengthstripped between marks placed at the beginning and end of thetest on the portion other th

37、an that stripped.MACHINE METHOD8. Apparatus8.1 A tension testing machine, power-driven, accurate towithin 61 % is used for measuring the force required toseparate the layers of the test specimen. A constant rate ofextension testing machine satisfies this condition and is pre-ferred although an incli

38、nation-balance, pendulum-type, or aspring-balance apparatus may be used. Requirements of thetesting machine are in 8.2.1 to 8.2.5.8.2 Testing Machine:8.2.1 The testing machine shall be capable of being operatedwithout any device for maintaining maximum load indication.For pendulum-type machines, do

39、not engage pawls that preventthe mass lever from swinging freely.8.2.2 The machine shall be equipped with the chart wherethe distance separated is one axis and the applied force is theother axis of coordinates. The preferred chart speed is the sameas the cross-head speed for ring specimens and one h

40、alf thecross-head speed for strip specimens.8.2.3 The force applied shall be greater than 15 % and lessthan 85 % of the capacity of the machine.8.2.4 GripsStrip specimens shall be held in the testingmachine by grips that clamp firmly and prevent slipping at alltimes during the test. For ring specime

41、ns, replace the gripattached to the recording head of the machine with a freelyrotating mandrel with an outside diameter substantially theFIG. 2 Mandrels and Frame for Static Mass Adhesion TestD413 98 (2017)3same as the inside diameter of the ring specimen. Mount themandrel so that its axis of rotat

42、ion is in the plane of the plybeing separated and the applied force is normal to the tangentof the ring circumference at the line of separation.8.2.5 The preferred rate of travel of the power-actuated gripis 0.8 mm/s (2 in./min) for strip specimen TypeA, 2.5 mm/s (6in./min) for Type B, and 0.4 mm/s

43、(1 in./min) for ringspecimens. These rates are to be uniform throughout the tests.9. Test Specimens9.1 Prepare the specimens in accordance with Section 6.10. Procedure10.1 Strip Specimens: Type A, 180 PeelMeasure thewidth of the cut strip to the nearest 0.2 mm (0.01 in.) andrecord. Separate the part

44、s to be tested by hand at one end of thetest specimen and at a sufficient distance to permit grips of themachine to be attached. Attach the separated end of thespecimen, with all separate parts except the one under testsecurely gripped, to the recording head by means of a clamp,using care to adjust

45、it symmetrically in order that the tensionshall be distributed uniformly. Provide for maintaining the stripduring the test approximately in the plane of the clamps. Thismay be done either by attaching the minimum mass required tothe free end of the specimen or by holding the specimen againsta plate

46、attached to the stationary clamp but, in either case, takeinto account the added mass in determining the force causingseparation. Grip that layer of the specimen of which theadhesion is to be tested symmetrically and firmly withouttwisting in the power-actuated clamp. Adjust the autographicmechanism

47、 and chart to zero and start the machine. Strip theseparating layer from the specimen at an angle of approxi-mately 180, and continue the separation for a sufficientdistance to indicate the adhesion value.10.2 Strip Specimen: Type B, 90 PeelSeparate by hand asufficient distance along the separation

48、line in the center of thestrip to permit the grips of the machine to be attached. Makeprovision to keep the unpeeled portion of the test specimen ina horizontal position using a plate if necessary to ensure a 90peel. Peel along the previously cut separation layer for 40 to100 mm (112 to 4 in.).10.3

49、Ring SpecimensSeparate by hand a sufficient lengthof a layer of the specimen to be tested to permit the power-actuated clamp of the machine to be attached. Place thespecimen snugly on the test mandrel. With the mandrelattached to the recording head of the machine and the separatedlayer gripped symmetrically and firmly without twisting in thepower-actuated clamp, adjust the autographic mechanism andchart to zero and start the machine. Strip the separating layerfrom the specimen at an angle of approximately 90 to thet