ASTM D2048-1992(2002) Standard Test Method for Powdering of Floor Polish Films《地板擦亮膜粉化的测试方法》.pdf

《ASTM D2048-1992(2002) Standard Test Method for Powdering of Floor Polish Films《地板擦亮膜粉化的测试方法》.pdf》由会员分享，可在线阅读，更多相关《ASTM D2048-1992(2002) Standard Test Method for Powdering of Floor Polish Films《地板擦亮膜粉化的测试方法》.pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: D 2048 92 (Reapproved 2002)Standard Test Method forPowdering of Floor Polish Films1This standard is issued under the fixed designation D 2048; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last revision.

2、A number in parentheses indicates the year of last reapproval. Asuperscript epsilon (e) indicates an editorial change since the last revision or reapproval.1. Scope1.1 This test method covers a bench procedure for thedetermination of the degree of powdering of floor polishesunder ambient conditions

3、as well as conditions of low relativehumidity.1.2 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regul

4、atory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:D 3153 Test Method for Recoatability of Water-EmulsionFloor Polishes23. Terminology3.1 Definition:3.1.1 powderingpartial or total disintegration of the pol-ish film resulting in a fine, light colored material.4. Significance an

5、d Use4.1 This is a comparative test method. If this method doesnot indicate powdering, it is still possible that the product inactual use may powder.5. Apparatus5.1 Textile Crockmeter,3weighted with a 1-kg weight. Theweight is placed directly over the abrasion dowel and attachedwith two-faced tape.5

6、.2 Abrading Felt670 Kelly No. 720 billiard cloth cutinto 50 by 50-mm (2 by 2-in.) squares.5.3 SubstrateOfficial Vinyl Composition Tile (OVCT)4shall be used in this test.5.4 Volumetric Pipet, 2-mL.5.5 Cheesecloth Applicator, washed to remove sizing; cutinto 50-mm (2-in.) strips of four-ply cloth; fol

7、ded twice.5.6 Relative Humidity and Temperature Indicator.5.7 Glove BoxAn enclosure that houses the crockmeterkeeping it in a constant humidity and temperature environment;features rubber glove inserts so that the tests may be runkeeping the environment of the crockmeter constant.5.8 DesiccantSilica

8、 gel or calcium chloride.5.9 Salts for Constant Humidity ConditionsLiClH2O,CaCl26H2O, or Mg(NO3)26H2O.NOTE 1Saturated aqueous solutions of the following salts in contactwith an excess of a definite solid phase of salt at the indicatedtemperatures and in an enclosed space will maintain the required c

9、onstanthumidities:LiClH2O at 25C (77F) yields 11.1 % relative humidity.CaCl26H2O at 10C (50F) yields 38.0 % relative humidity.Mg(NO3)26H2O at 23.9C (75F) yields 42.9 % relative humidity.5.10 Fan, small, electric.5.11 Metal Clip, to hold the abrading felt on the crockmetersurface during testing.6. Pr

10、eparation of Test Sample6.1 Clean the tile surface in accordance with Test MethodD 3153, paragraph 9.1.2, to ensure removal of any coatingpresent.6.2 Pipet 2 mL of polish onto the center of the test panel.Place the cheesecloth into the polish and allow it to absorb theemulsion. Distribute the emulsi

11、on evenly over the surface; thendraw the cheesecloth downward in smooth separate strokes,with no more pressure than is exerted by the weight of thehand, until the entire panel has been coated. If 304 by 304-mm(12 by 12-in.) tiles are used, pipet 3.6 mL of polish out thecenter of each tile.6.3 Apply

12、a second coat of polish 1 h after the first. Applythis coat in the same manner as the first coat.6.4 One hour after the second coat of polish has dried, placeone of the test tiles in the glove box in which the relativehumidity is 10 to 15 %. The low humidity is obtained andcontrolled using silica ge

13、l or calcium chloride as the desiccantor by using a saturated salt solution with a small fan to circulatethe air inside the box. Also place inside the glove box thecrockmeter weighted with a 1-kg weight and the green felt testpads. Age the tiles and equipment for 24 h at 10 to 15 %relative humidity

14、at 23.9 6 1.1C (75 6 2F).1This test method is under the jurisdiction of ASTM Committee D21 on Polishesand is the responsibility of Subcommittee D21.04 on Performance Tests.Current edition approved Aug. 15, 1992. Published October 1992. Originallypublished as D 2048 64 T. Last previous edition D 2048

15、 87.2Annual Book of ASTM Standards, Vol 15.04.3The sole source of supply of the apparatus known to the committee at this timeis Atlas Electric Devices Co., Chicago, IL. If you are aware of alternative suppliers,please provide this information to ASTM Headquarters. Your comments will receivecareful c

16、onsideration at a meeting of the responsible technical committee, whichyou may attend.4OVCT is Official Vinyl Composition Tile of the Chemical Specialties Manu-facturers Association, Inc., 1913 Eye St., N.W., Washington, DC 20006.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, Wes

17、t Conshohocken, PA 19428-2959, United States.6.5 Prepare additional test tiles in the same manner and dryfor24hat256 1.1C (77 6 2F) and 55 6 3 % relativehumidity.NOTE 2Prepared samples may also be tested at 10 6 1.1C (50 62F) and 38 6 3 % relative humidity.7. Procedure7.1 Test the prepared samples a

18、t 23.9 6 1.1C (75 6 2F)and 10 to 15 % relative humidity, and at 25 6 1.1C (77 62F) and 55 6 3 % relative humidity.7.2 Place the coated sample on the sandpaper pad. Cover thedowel with the abrading felt using the metal clip. Pass thecovered dowel over each polish film for 50 complete cycles.Use a fre

19、sh surface for each test. Remove the green felt fromthe test machine and observe for degree of powder adhering toit. Observe the test panel carefully for damage which may haveoccurred during the stroking action.8. Report8.1 The report shall include the following:8.1.1 Identification of sample,8.1.2

20、Temperature and humidity conditions of test, and8.1.3 Relative degree of white powder accumulation as seenon both the tile surface and the abrading felt. Report accordingto the following classifications: none, slight, or excessive.9. Precision and Bias9.1 Duplicate samples of polish, when tested by

21、thismethod, show the same degree of powdering.9.2 Since there is no accepted reference material suitable fordetermining the bias for the procedure for measuring thepowdering resistance of floor polish films, bias has not beendetermined.10. Keywords10.1 abrading felt; billiard; crockmeter; desiccant;

22、 floor;glove box; OVCT; polish; powdering; textile crockmeterASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such p

23、atent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited e

24、ither for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fai

25、r hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org).D 2048 92 (2002)2