ASTM D1573 D1573M-1995(2009)e1 Standard Test Method for Heat Aging of Asbestos Textiles《石棉织物热老化的标准试验方法》.pdf

《ASTM D1573 D1573M-1995(2009)e1 Standard Test Method for Heat Aging of Asbestos Textiles《石棉织物热老化的标准试验方法》.pdf》由会员分享，可在线阅读，更多相关《ASTM D1573 D1573M-1995(2009)e1 Standard Test Method for Heat Aging of Asbestos Textiles《石棉织物热老化的标准试验方法》.pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: D1573/D1573M 95 (Reapproved 2009)1Standard Test Method forHeat Aging of Asbestos Textiles1This standard is issued under the fixed designation D1573/D1573M; the number immediately following the designation indicates theyear of original adoption or, in the case of revision, the year of la

2、st revision. A number in parentheses indicates the year of lastreapproval. A superscript epsilon () indicates an editorial change since the last revision or reapproval.1NOTEUnits information was corrected editorially in March 2010.1. Scope1.1 This test method covers the heat aging of asbestostextile

3、s. It may be used to determine the resistance to thedeterioration of tensile strength at temperatures up to 450C800F.1.2 The values stated in either SI units or inch-pound unitsare to be regarded separately as standard. The values stated ineach system may not be exact equivalents; therefore, eachsys

4、tem shall be used independently of the other. Combiningvalues from the two systems may result in non-conformancewith the standard.1.3 WarningBreathing of asbestos dust is hazardous.Asbestos and asbestos products present demonstrated healthrisks for users and for those with whom they come into contac

5、t.In addition to other precautions, when working with asbestos-cement products, minimize the dust that results. For informa-tion on the safe use of chrysoltile asbestos, refer to “Safe Useof Chrysotile Asbestos: A Manual on Preventive and ControlMeasures.”21.4 This standard does not purport to addre

6、ss all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use. For specific safetyhazard, see 1.3.2. Referenced Document

7、s2.1 ASTM Standards:3D123 Terminology Relating to TextilesD1571 Specification for Woven Asbestos ClothD1682 Methods of Test for Breaking Load and Elongationof Textile Fabrics4D2946 Terminology for Asbestos and AsbestosCementProducts3. Terminology3.1 For textile terms, refer to Terminology D123. Fora

8、sbestos terms, refer to Terminology D2946.4. Significance and Use4.1 This test method covers the evaluation of asbestostextiles with regard to (1) quality and (2) elevated temperatureserviceability characteristics. Since asbestos textiles are usu-ally composed of blends of asbestos with cotton or ot

9、herorganic carrier fibers, the latter being present in amounts up to25 %, temperatures above 150C 300F will promote thedegradation of the cotton content and will reduce the structuralreinforcement derived therefrom. In the higher grade asbestostextiles, wherein little or no carrier fibers are used a

10、nd in whichthe longer asbestos fibers are necessary if a satisfactory yarn isto be produced, the degradation in strength resulting fromheat-aging up to 540C 1000F is low. In the case of thelower grade asbestos textiles, however, wherein amounts from15 to 25 % carrier fibers are incorporated, asbesto

11、s fibershaving shorter lengths may be utilized. Under the relativelylow service temperatures to which such materials may besubjected, neither the cotton nor the cloth properties are greatlyaffected. However, the strength-imparting influence of thecarrier fibers is reduced at elevated temperatures an

12、d theentwining properties of the shorter asbestos fibers primarilyserve to establish the resultant tensile strength and otherphysical properties of the textile. In view of this, elevatedtemperature tests may serve to indicate the asbestos fiber gradeor quality that may be used in a textile construct

13、ion.4.2 Another use and perhaps more practical application forthe information to be derived from elevated temperaturestudies is the revelation of the ability of a subject textile towithstand known elevated temperature service conditions. Itwill be appreciated that temperature alone may not be the on

14、ly1This test method is under the jurisdiction of ASTM Committee C17 onFiber-Reinforced Cement Products and is the direct responsibility of C17.03 onAsbestos - Cement Sheet Products and Accessories.Current edition approved Nov. 1, 2009. Published March 2010. Originallyapproved in 1958. Last previous

15、edition approved in 2004 as D1573 95(2004)1.DOI: 10.1520/D1573_D1573M-95R09E01.2Available from The Asbestos Institute, http:/ referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refe

16、r to the standards Document Summary page onthe ASTM website.4Withdrawn.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.degratory influence in the destruction of such materials;however, under normal operating conditions, high tempera-

17、tures are usually the dominating factors in such degradation.The results obtained through such investigations therefore maybe interpreted in terms of elevated temperature serviceability.5. Apparatus5.1 Test Oven:5.1.1 The oven shall be electrically heated and have thenecessary controls to maintain t

18、emperatures to within 63C5.4F at any designated testing temperature up to 430C800F and shall have determinable and controllable aircirculation. The air circulation provisions shall be capableof delivering between 3 and 6 m3/min 100 and 200 ft3/mincontinuously to the oven during the testing period.5.

19、1.2 The minimum inside dimensions of the oven shall be500 by 500 by 500 mm 18 by 18 by 18 in., and it shall beprovided with two hardware cloth trays, 20 mm 0.75 in.mesh, at least 500 by 500 mm 18 by 18 in., upon which thetest specimens may be deployed.5.2 The temperature indicating device shall be a

20、 chromela-lumel thermocouple, or its equivalent, coupled with an accuratepotentiometer capable of being calibrated and adjusted tocompensate for room temperature and cold junction differen-tials. Other devices ensuring at least equal precision andaccuracy may be used.6. Hazards6.1 Warningsee 1.3.7.

21、Preparation of Apparatus7.1 When starting a test, the oven temperature controls shallbe set at the desired test temperature at the beginning of theheating-up period. The oven temperatures shall be determinedby placing the junction of the thermocouple on a specimen ofcloth supported on the upper hard

22、ware cloth tray, which will belocated not less than 150 mm 6 in. from the top of the ovennor less than 150 mm 6 in. above the next lower tray.7.2 Air circulation shall be maintained continually from thebeginning of the heating period throughout the test cycle. Theinitial heating-up period, during wh

23、ich no test specimens shallbe in the oven, shall be maintained for a minimum of2horuntil such a time as the oven conditions have attained thedegree of stability that will assure temperature variations nogreater than prescribed in 5.1.1.8. Procedure8.1 Time and Temperature for Test:8.1.1 All cloths s

24、hall be tested for a period of 2 h.8.1.2 The temperature for testing shall be dependent uponthe grade of the material under investigation, as follows:Commercial Grade 204C 400FUnderwriters Grade 204C 400FGrade A 316C 600FGrade AA 316C 600FGrade AAA 427C 800FGrade AAAA 427C 800F8.1.2.1 Grades are def

25、ined in Specification D1571.8.2 Deployment of Test Samples in OvenFollowing theattainment of stabilized conditions, specimens of the samplesunder test shall be individually positioned on the wire meshtrays. There shall be not less than 150 mm 6 in. placed in theoven and not more than 150 mm 6 in. be

26、tween the top trayand the top of the oven or between the bottom tray and thebottom of the oven. With a hearth size 500 by 500 mm 18 by18 in. the individual trays will be 500 by 500 mm 18 by 18in. and on each may be positioned 12 individual grade testspecimens. The placements shall be made as quickly

27、 aspossible so that the oven door will remain open for a minimumlength of time in order that the oven temperature may not dropmarkedly below the testing temperature in accordance withTest Methods D1682.8.3 Immediately upon closing the oven door begin the testperiod and continue the test for 2 h.8.4

28、Upon completion of the test period, remove the speci-mens from the oven and permit them to condition at roomtemperature for 35 6 5 min. Following this conditioningperiod, test the specimens for tensile strength. It is to beunderstood that tensile strength values (Note 1) and tensilestrength retentio

29、n values must be established on the basis ofcloth constructions, as well as grade, and should be consideredindividually.NOTE 1The determination of actual strength values and the decisionas to whether such values of tensile strength shall be in terms of kilograms(pounds) break resistance by the grab

30、method or in terms of the percentagestrength retention based on the grab test breaks are matters that can bestbe determined on the basis of the ultimate use to which such informationis to be applied.9. Report9.1 Fully identify the samples tested.9.2 Report the tensile strength values and tensile str

31、engthretention values in terms of breaking load in Newtons orpounds force and also in terms of the percentage strengthretention based on the grab test breaks (Note 1).10. Precision and Bias10.1 PrecisionThe variance introduced into the eventualtensile test results obtained on specimens heat-treated

32、by thistest method is statistically insignificant compared against theinter-specimen variance and the variance due to the tensile testmethod.10.2 BiasBias cannot be established on asbestos textilesfor lack of a referee method.11. Keywords11.1 aging; asbestos; heat; heat-aging; tensile; textileD1573/

33、D1573M 95 (2009)12ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement o

34、f such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for

35、additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known t

36、o the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM website (www.astm.org/COPYRIGHT/).D1573/D1573M 95 (2009)13