ASTM D1488-2000(2018) Standard Test Method for Amylaceous Matter in Adhesives.pdf

《ASTM D1488-2000(2018) Standard Test Method for Amylaceous Matter in Adhesives.pdf》由会员分享，可在线阅读，更多相关《ASTM D1488-2000(2018) Standard Test Method for Amylaceous Matter in Adhesives.pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: D1488 00 (Reapproved 2018)Standard Test Method forAmylaceous Matter in Adhesives1This standard is issued under the fixed designation D1488; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last revision. A n

2、umber in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the U.S. Department of Defense.1. Scope1.1 This test method covers the determination of the p

3、res-ence or absence of amylaceous (starch-like) material inphenol-, resorcinol-, and melamine-resin adhesives.1.2 The values stated in SI units are to be regarded as thestandard. The values given in parentheses are for informationonly.1.3 This standard does not purport to address all of thesafety co

4、ncerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety, health, and environmental practices and deter-mine the applicability of regulatory limitations prior to use.1.4 This international standard was developed in accor-dance wit

5、h internationally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of International Standards, Guides and Recom-mendations issued by the World Trade Organization TechnicalBarriers to Trade (TBT) Committee.2. Referenced Documents2.1 ASTM Standards

6、:2D907 Terminology of Adhesives3. Terminology3.1 DefinitionsMany terms in this test method are definedin Terminology D907.4. Summary of Test Method4.1 A reagent solution is added to the adhesive in questionwhich causes any starch-like material to become insoluble. Theresultant material then changes

7、color when another reagent isadded if any starch-like matter is present.5. Significance and Use5.1 This test method is used to determine if a melamineresin, a phenol, or a resorcinol adhesive contains any starch-like filler, the presence of which could affect water resistanceor strength, or both.6.

8、Reagents6.1 Iodine Test SolutionAdd 5 g (0.18 oz) of iodine and 5g of potassium iodide to 100 mL (3 oz) of distilled water.6.2 Acetic AcidEthyl Alcohol SolutionAdd 20 parts ofglacial acetic acid and 20 parts of 95 % ethyl alcohol to 60parts of distilled water by volume.7. Sampling7.1 Except in speci

9、al cases, take a composite of the sampleof the adhesive when possible, from three or more separatecontainers, chosen at random. Also, take samples from con-tainers that appear to be nonrepresentative, and test suchsamples separately. Before a sample is taken, thoroughly mixthe contents of the contai

10、ner if there is a tendency for thematerials to separate. Place the samples immediately in airtightcontainers and transport to the testing laboratory in thesecontainers. Take precautions to reduce evaporation or drying toa minimum.8. Procedure8.1 Phenol and Resorcinol AdhesivesWeigh 0.5 g (0.018oz) o

11、f thoroughly mixed adhesive into a small-diameter testtube. Add 5 mL (0.15 oz) of 95 % ethyl alcohol. Shakethoroughly, allow the insoluble matter to settle, and decant thesupernatant liquid. Repeat twice more with the ethyl alcoholand three times with distilled water. After the final decantation,add

12、 one drop of the iodine solution to the residue. A darkeningof the residue denotes a positive test for the presence ofamylaceous matter.8.2 Melamine ResinsUse the same procedure as specifiedin 8.1 except substitute an acetic acid-ethyl alcohol solution.When the melamine adhesive is supplied with sep

13、aratehardener, use ethyl alcohol for the unmixed hardener.9. Report9.1 Report the following information:1This test method is under the jurisdiction of ASTM Committee D14 onAdhesives and is the direct responsibility of Subcommittee D14.30 on WoodAdhesivesCurrent edition approved Aug. 1, 2018. Publish

14、ed August 2018. Originallyapproved in 1957. Last previous edition approved in 2013 as D1488 00 (2013).DOI: 10.1520/D1488-00R18.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information

15、, refer to the standards Document Summary page onthe ASTM website.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United StatesThis international standard was developed in accordance with internationally recognized principles on standardization est

16、ablished in the Decision on Principles for theDevelopment of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.19.1.1 Complete identification of the adhesive tested, includ-ing type, source, manufacturers code numbe

17、r, lot or batchnumber, condition, and date, and9.1.2 Positive or negative reaction to the iodine test.10. Precision and Bias10.1 No information is presented about either the precisionor bias of Test Method D1488 for measuring the presence orabsence of amylaceous matter in adhesives since the result

18、isnonquantitative.11. Keywords11.1 amylaceous matter; iodine test; melamine; phenol;resorcinol; starch-likeASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised th

19、at determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reappr

20、oved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you f

21、eel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual re

22、prints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the Copyright Clearance Center, 222Rosewood Drive, Danvers, MA 01923, Tel: (978) 646-2600; http:/ 00 (2018)2