ASTM C975-1987(2004) Standard Practice for Preparing Test Specimens from Basic Refractory Ramming Products by Pressing《用压力法从捣实碱性耐火产品中制备试验样品的标准实施规程》.pdf

《ASTM C975-1987(2004) Standard Practice for Preparing Test Specimens from Basic Refractory Ramming Products by Pressing《用压力法从捣实碱性耐火产品中制备试验样品的标准实施规程》.pdf》由会员分享，可在线阅读，更多相关《ASTM C975-1987(2004) Standard Practice for Preparing Test Specimens from Basic Refractory Ramming Products by Pressing《用压力法从捣实碱性耐火产品中制备试验样品的标准实施规程》.pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: C 975 87 (Reapproved 2004)Standard Practice forPreparing Test Specimens from Basic Refractory RammingProducts by Pressing1This standard is issued under the fixed designation C 975; the number immediately following the designation indicates the year oforiginal adoption or, in the case of

2、 revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon (e) indicates an editorial change since the last revision or reapproval.1. Scope1.1 This practice covers a procedure for preparing testspecimens from basic refractory ramming pro

3、ducts by pressingprepared material in a mold. Specimens prepared in accordancewith this procedure are intended for use inASTM test methods.1.2 The values stated in inch-pound units are to be regardedas the standard. The values given in parentheses are forinformation only.1.3 This standard does not p

4、urport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2. Significance and Use2.1 This practice de

5、fines a procedure that ensures consistentpreparation of specimens for product testing and evaluation.2.2 This practice can be used in the laboratories of produc-ers, users, and general-interest parties for research and devel-opment or quality-control work. It is particularly useful forinterlaborator

6、y comparisons of products, for repetitive evalua-tions or comparisons of products or product quality, and inspecifying a uniform preparation practice for specimens foracceptance testing.2.3 In using this practice it must be recognized that thestructure of laboratory-pressed specimens may differ sign

7、ifi-cantly from the structure of material rammed in field applica-tions.3. Apparatus3.1 Mixer, bench-type, Hobart or equivalent.3.2 Press, mechanical or hydraulic.3.3 Steel Molds.3.4 Oven, air circulating.3.5 Trowel.4. Procedure4.1 Store the material to be tested at 85 6 2F (29.5 6 1C)for 24 h prior

8、 to testing.4.2 Reduce the sample to the desired batch size with asample splitter or by quartering taking precautions to preventsegregation. Sufficient material should be batched to provide atleast a 10 % excess over test specimen requirements.4.3 Add the weighed, dry batch to the mixer and dry-mix

9、atlow speed for 30 s. Continue to mix at low speed while addingthe required amount of water (see 4.3.1) within 30 s. Wet-mixat low speed for 3 min.4.3.1 Use the amount of water and mixing time (if differentfrom above) recommended by the manufacturer. The watermust be potable and at a temperature of

10、85 6 2F (29.5 61C). Measure the water addition to the nearest 0.1 % byweight.4.4 Specimens of the desired size should be pressed imme-diately after the batch is mixed. Weigh the proper amount ofmaterial for each specimen to the nearest 0.02 lb (10 g), anddistribute the mix uniformly in the mold usin

11、g the narrow edgeof a trowel. The remainder of the batch should be covered witha damp cloth during the pressing procedure. Press test speci-mens at 10 000 psi (68.95 MPa).4.5 Test specimens should be air-dried for 4 h, and thendried for a minimum of8hat2256 5F (107 6 2.5C) in acirculating air dryer

12、prior to testing. Testing should be carriedout within 48 h.5. Calculation and Report5.1 In the report on specimen preparation, include thepercent water addition, drying time, and test specimen size.1This practice is under the jurisdiction ofASTM Committee C08 on Refractoriesand is the direct respons

13、ibility of Subcommittee C08.09 on Monolithics.Current edition approved March 1, 2004. Published March 2006. Originallyapproved in 1982. Last previous edition approved in 1998 as C 975 87 (1998).1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, Unite

14、d States.ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such ri

15、ghts, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additiona

16、l standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the AST

17、M Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org).C 975 87 (2004)2