ASTM C948-1981(2016) Standard Test Method for Dry and Wet Bulk Density Water Absorption and Apparent Porosity of Thin Sections of Glass-Fiber Reinforced Concrete《玻璃纤维增强型混凝土薄片材干湿体积密.pdf
《ASTM C948-1981(2016) Standard Test Method for Dry and Wet Bulk Density Water Absorption and Apparent Porosity of Thin Sections of Glass-Fiber Reinforced Concrete《玻璃纤维增强型混凝土薄片材干湿体积密.pdf》由会员分享,可在线阅读,更多相关《ASTM C948-1981(2016) Standard Test Method for Dry and Wet Bulk Density Water Absorption and Apparent Porosity of Thin Sections of Glass-Fiber Reinforced Concrete《玻璃纤维增强型混凝土薄片材干湿体积密.pdf(2页珍藏版)》请在麦多课文档分享上搜索。
1、Designation: C948 81 (Reapproved 2016)Standard Test Method forDry and Wet Bulk Density, Water Absorption, and ApparentPorosity of Thin Sections of Glass-Fiber ReinforcedConcrete1This standard is issued under the fixed designation C948; the number immediately following the designation indicates the y
2、ear oforiginal adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This test method covers the determinations of dry and
3、wet bulk density, water absorption, and apparent porosity ofthin sections of glass-fiber reinforced concrete.NOTE 1This test method does not involve a determination of absolutespecific gravity. Therefore, such pore space as may be present in thespecimen that is not emptied during the specified dryin
4、g or is not filledwith water during the specified immersion is considered “impermeable”and is not differentiated from the solid portion of the specimen for thecalculations, especially those for percent voids.Depending upon the pore size distribution and the pore entry radii ofthe specimen and on the
5、 purposes for which the test results are desired, theprocedures of this method may be adequate, or they may be insufficientlyrigorous. In the event that it is desired to fill more of the pores than willbe filled by immersion, various techniques involving the use of vacuumtreatment or increased press
6、ure may be used. If a rigorous measure of totalpore space is desired, this can only be obtained by determining absolutespecific gravity by first reducing the sample to discrete particles, each ofwhich is sufficiently small so that no impermeable space can exist withinany of the particles.1.2 The val
7、ues stated in inch-pound units are to be regardedas standard. The values given in parentheses are mathematicalconversions to SI units that are provided for information onlyand are not considered standard.1.3 This standard does not purport to address all of thesafety concerns, if any, associated with
8、 its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2. Significance and Use2.1 Material properties determined by this test method areuseful for quality control of
9、glass-fiber reinforced concrete,ascertaining compliance with governing specifications, andresearch and development.3. Apparatus3.1 Balance, sensitive to 0.025 % of the mass of thespecimen, suitable for determining the mass of the specimen inwater as well as in air.3.2 Container, suitable for immersi
10、ng the specimen andsuitable wire for suspending the specimen in water.4. Sampling4.1 Sampling method shall be in accordance with governingspecifications.5. Test Specimen5.1 Whenever possible, the sample shall consist of indi-vidual portions of glass-fiber reinforced concrete, each to betested separa
11、tely. The individual portions may be pieces of anydesired shape or size, except that the volume of each portionshall be not less than 25 cm3(or 50 g nominal mass glass-fiberreinforced concrete, approximately 1.7 oz, and shall not begreater than 650 cm3or 1300 g nominal glass-fiber reinforcedconcrete
12、, approximately 46 oz); and each portion shall be freeof observable cracks, fissures, or shattered edges.6. Procedure6.1 Immersed Mass and Saturated SurfaceDry Mass AfterImmersion:6.1.1 Immerse the specimen in water at approximately 21C(70F) for not less than 24 h and until two successivedeterminati
- 1.请仔细阅读文档,确保文档完整性,对于不预览、不比对内容而直接下载带来的问题本站不予受理。
- 2.下载的文档,不会出现我们的网址水印。
- 3、该文档所得收入(下载+内容+预览)归上传者、原创作者;如果您是本文档原作者,请点此认领!既往收益都归您。
下载文档到电脑,查找使用更方便
10000 积分 0人已下载
下载 | 加入VIP,交流精品资源 |
- 配套讲稿:
如PPT文件的首页显示word图标,表示该PPT已包含配套word讲稿。双击word图标可打开word文档。
- 特殊限制:
部分文档作品中含有的国旗、国徽等图片,仅作为作品整体效果示例展示,禁止商用。设计者仅对作品中独创性部分享有著作权。
- 关 键 词:
- ASTMC94819812016STANDARDTESTMETHODFORDRYANDWETBULKDENSITYWATERABSORPTIONANDAPPARENTPOROSITYOFTHINSECTIONSOFGLASSFIBERREINFORCEDCONCRETE
链接地址:http://www.mydoc123.com/p-508940.html