ASTM C830-2000(2006)e1 Standard Test Methods for Apparent Porosity Liquid Absorption Apparent Specific Gravity and Bulk Density of Refractory Shapes by Vacuum Pressure《用真空压力法测定成型耐火.pdf

《ASTM C830-2000(2006)e1 Standard Test Methods for Apparent Porosity Liquid Absorption Apparent Specific Gravity and Bulk Density of Refractory Shapes by Vacuum Pressure《用真空压力法测定成型耐火.pdf》由会员分享，可在线阅读，更多相关《ASTM C830-2000(2006)e1 Standard Test Methods for Apparent Porosity Liquid Absorption Apparent Specific Gravity and Bulk Density of Refractory Shapes by Vacuum Pressure《用真空压力法测定成型耐火.pdf（5页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: C 830 00 (Reapproved 2006)1Standard Test Methods forApparent Porosity, Liquid Absorption, Apparent SpecificGravity, and Bulk Density of Refractory Shapes by VacuumPressure1This standard is issued under the fixed designation C 830; the number immediately following the designation indicat

2、es the year oforiginal adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1NOTEUnits of measure statement was added editorially in

3、April 2009.1. Scope1.1 These test methods cover the determination of thefollowing properties of refractory shapes:1.1.1 Apparent porosity,1.1.2 Liquid absorption,1.1.3 Apparent specific gravity, and1.1.4 Bulk density.1.2 These test methods are applicable to all refractoryshapes except those that che

4、mically react with both water andmineral spirits. When testing a material capable of hydration orother chemical reaction with water but which does not chemi-cally react with mineral spirits, mineral spirits is substituted forwater and appropriate corrections for the density differencesare applied wh

5、en making calculations.1.3 UnitsThe values stated in inch-pound units are to beregarded as standard. The values given in parentheses aremathematical conversions to SI units that are provided forinformation only and are not considered standard.1.3.1 ExceptionThe apparatus used in this standard isonly

6、 available in SI units.1.4 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior

7、 to use.NOTE 1Test Methods C20cover procedures for testing properties ofrefractories that are not attacked by water.2. Referenced Documents2.1 ASTM Standards:2C20 Test Methods for Apparent Porosity, Water Absorp-tion, Apparent Specific Gravity, and Bulk Density ofBurned Refractory Brick and Shapes b

8、y Boiling WaterC 134 Test Methods for Size, Dimensional Measurements,and Bulk Density of Refractory Brick and InsulatingFirebrickE 691 Practice for Conducting an Interlaboratory Study toDetermine the Precision of a Test Method3. Significance and Use3.1 Apparent porosity, water absorption, apparent s

9、pecificgravity, and bulk density are primary properties of refractoryshapes. These properties are widely used in the evaluation andcomparison of product quality and as part of the criteria forselection and use of refractory products in a variety ofindustrial applications. These test methods are used

10、 for deter-mining any or all of these properties and are particularly usefulfor testing hydratable products.3.2 These test methods are primary standard methods thatare suitable for use in quality control, research and develop-ment, establishing criteria for and evaluating compliance withspecificatio

11、ns, and providing data for design purposes.3.3 Fundamental assumptions inherent in these test methodsare:3.3.1 The test specimens conform to the requirements forsize, configuration, and original faces,3.3.2 The open pores of the test specimens are fully impreg-nated with liquid during the vacuum-pre

12、ssure treatment, and3.3.3 The blotting of the saturated test specimens is per-formed as specified in a consistent and uniform manner toavoid withdrawing liquid from the pores.3.3.4 Deviation from any of these assumptions adverselyaffects the test results.3.4 In laboratory studies involving castable

13、specimen, a biaswas noted between formed2X2X2in (50 X 50 X 50mm)and specimens quartered from larger 9 X 4.5 X 2.5in (228 X114 X 64mm) cast specimens. Additionally, an error in theapparent porosity determination was found on castables when-ever the specimens were heated to 1500F (816C) and thenexpose

14、d to water as a saturation media. The error was1These test methods are under the jurisdiction of ASTM Committee C08 onRefractories and are the direct responsibility of Subcommittee C08.03 on PhysicalProperties.Current edition approved June 1, 2006. Published June 2006. Originallyapproved in 1976. La

15、st previous edition approved in 2000 as C 830 00.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.1Copyright A

16、STM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.attributed to reactivity of cement with water and subsequentre-hydration of cement phases. The higher the cement level ofthe castable, the greater the error noted. It was concluded thatan error in

17、porosity values could occur for refractory materialshaving a potential to form hydrated species with water. Testingunder the same conditions in kerosene produced results thatwere believed to be more accurate, but the data suggested thatthe kerosene might not have saturated the open pores of castspec

18、imen as readily as water. Supporting data were filed atASTM headquarters and can be obtained by requesting re-search report 1014.3.5 Certain precautions must be exercised in interpretingand using results from these test methods. All four propertyvalues are interrelated by at least two of the three b

19、ase datavalues generated during testing. Thus, an error in any base datavalue will cause an error in at least three of the property valuesfor a given test specimen. Certain of the properties, that is,apparent specific gravity and bulk density, are functions ofother factors such as product compositio

20、n, compositionalvariability within the same product, impervious porosity, andtotal porosity. Generalizations on or comparisons of propertyvalues should be judiciously made between like products testedby these test methods or with full recognition of potentiallyinherent differences between the produc

21、ts being compared orthe test method used.3.6 When a liquid other than water is used, such as types ofkerosene or mineral spirits, specific gravity must be known byeither determination or monitoring on a controlled basis.Specific gravity will change due to different grades of liquids,evaporation, or

22、contamination with dirt or foreign material.The test should not be run if the liquid becomes dirty, foamy,or changes color, because foreign particles can block pores andprevent impregnation of the sample.4. Test Specimens4.1 When testing 9-in. (228-mm) straight brick, use aquarter-brick specimen obt

23、ained by halving the brick along aplane parallel to the 9 by 212 or 3-in. (228 by 64 or 76-mm)face and along a plane parallel to the 412 by 212 or 3-in. (114by 64 or 76-mm) face. Four of the surfaces of the resultantquarter-brick specimen include part of the original moldedfaces.4.2 When testing oth

24、er refractory shapes, cut drill, or breakfrom each shape a specimen having a volume of approximately25 to 30 in.3(410 to 490 cm3). The specimen shall includeinterior and exterior portions of the shape.4.3 Remove all loosely adhering particles from each speci-men.5. Procedures5.1 Determination of Dry

25、 Weight, D:5.1.1 Dry the test specimens to constant weight by heatingto 220 to 230F (105 to 110C) and determine the dry weight,D, in grams to the nearest 0.1 g.5.1.2 The drying procedure may be omitted only when thetest specimens are known to be dry, as may be the case withsamples taken directly fro

26、m kilns.5.1.3 The drying of the specimens to constant weight andthe determination of their dry weight may be done either beforeor after the saturation operation (5.2). Usually, the dry weightis determined before saturation; if, however, the specimens arefriable or evidence indicates that particles h

27、ave broken looseduring the saturating operation, dry and weigh the specimensafter the suspended weight, S, and the saturated weight, W,have been determined as described in 5.3 and 5.4. Use thissecond dry weight in all appropriate calculations.5.2 SaturationPlace the test specimens in a suitablevacuu

28、m-pressure vessel (Note 2) which shall be closed, se-cured, and pumped down to an absolute pressure of not morethan 1.9 in. Hg (6.4 kPa). Hold this pressure for 30 min.Allowthe water or mineral spirits (see 1.2) to enter the vessel whilemaintaining the vacuum for 5 min. Then close the vacuum lineand

29、 pressurize the vessel by means of compressed air or apressure pump. Maintain this pressure at 30 psi (207 kPa) ormore for 60 min. Then release the pressure; the saturatedspecimens are now ready for weighing.NOTE 2The vacuum-pressure vessel should be capable of withstand-ing an absolute pressure of

30、1.0 in. Hg (3.4 kPa) or a pressure of 65 to 70psi (448 to 483 kPa) without deforming or rupturing. It should be providedwith gages or manometers for indicating vacuum or pressure and a reliefvalve, as well as vacuum, pressure, and liquid lines. The liquid may beintroduced at the bottom, in which cas

31、e a dual-acting valve will suffice forboth filling and draining the vessel.5.3 Determination of Suspended Weight, S:5.3.1 Determine the weight, S, of each test specimen ingrams to the nearest 0.1 g after saturation and while suspendedin liquid.5.3.2 This weighing is usually accomplished by suspendin

32、gthe specimen in a loop or halter of AWG Gage-22 (0.643-mm)copper wire hung from one arm of the balance. The balanceshall be previously counter-balanced with the wire in place andimmersed in liquid to the same depth as is used when therefractory specimens are in place.5.4 Determination of Saturated

33、Weight, WAfter determin-ing the suspended weight, blot each specimen lightly with amoistened smooth linen or cotton cloth to remove all drops ofliquid from the surface, and determine the saturated weight, W,in grams to the nearest 0.1 g by weighing in air. Perform theblotting operation by rolling th

34、e specimen lightly on the wetcloth, which has previously been saturated with liquid, andthen press only enough to remove such liquid as will drip fromthe cloth. Excessive blotting will induce error by withdrawingliquid from the pores of the specimen.5.5 Determination of Exterior Volume, VObtain the

35、vol-ume, V, of the test specimens in cubic centimetres by subtract-ing the suspended weight from the saturated weight, both ingrams, as follows:V,cm35 W 2 S(1)NOTE 3This assumes that 1 cm3of water weighs 1 g. This is truewithin about 3 parts in 1000 for water at room temperature.NOTE 4When substitut

36、ing mineral spirits for water, make the follow-ing correction:V,cm35 W 2 S!/density of liquid(2)C 830 00 (2006)125.6 Determination of Volume of Open Pores and ImperviousPortionsCalculate the volume of both the open pores and theimpervious portions of the specimen as follows:Volume of open pores, cm3

37、5 W 2 D (3)Volume of impervious portion, cm35 D 2 S (4)NOTE 5When substituting mineral spirits for water, make the follow-ing corrections:Volume of open pores, cm35 W 2 D!/ density of liquid (5)Volume of impervious portion, cm35 D 2 S!/density of liquid(6)6. Calculation6.1 As noted in 1.2, when mine

38、ral spirits is substituted forwater, appropriate corrections for the density difference be-tween the liquids are required in the calculations. Thus, theequations used when the liquid is mineral spirits differ fromthose used when the liquid is water. To avoid confusion andintermingling of equations,

39、the calculations used for eachliquid are presented in separate sections (see Sections 7 and 8).6.2 When the liquid is water, calculation of the variousvolumes and properties is straightforward, as in Test MethodsC20. The assumption is taken that 1 cm3of water weighs 1 g.This is true within about 3 p

40、arts per 1000 at room temperature.Therefore, no corrections for change in water density withchange in temperature are applied in any calculations. How-ever, use of the 1 g/cm3factor is implicit in all calculationswhere direct weight measurements are converted to volumes.This affects expression of th

41、e results in the proper unit ofmeasure, that is, cm3.6.3 When the liquid is mineral spirits, correction for thedensity difference between mineral spirits and water is requiredin all calculations where direct weight measurements areconverted to volumes. The correction factor is:density of liquid (g/c

42、m3)Use of this factor in calculations also affects expression ofthe results in the proper unit of measure, that is, g/cm3.7. Calculation When Liquid is Water7.1 Volume Calculations:7.1.1 Determination of Exterior Volume, VThe exteriorvolume of the test specimen is its bulk volume, including allsolid

43、 material, open pores, and impervious portions. CalculateV in cubic centimetres by subtracting the suspended weightfrom the saturated weight, both in grams, as follows:V,cm35 W 2 S(7)7.1.2 Determination of Volume of Open Pores and Volumeof Impervious PortionsCalculate the volume of open poresand the

44、 volume of impervious portions in the test specimen incubic centimetres as follows:Volume of open pores, cm35 W 2 D (8)Volume of impervious portions, cm35 D 2 S (9)7.2 Property Calculations:7.2.1 Apparent Porosity, PThe apparent porosity ex-presses as a percentage the relationship of the volume of o

45、penpores in the test specimen to its exterior volume. Calculate P asfollows:P ,%5 W 2 D!/V# 3 100(10)7.2.2 Water Absorption, Aw The water absorption ex-presses as a percentage the relationship of the weight of waterabsorbed to the weight of the dry test specimen. Calculate Awas follows:Aw,% 5 W 2 D!

46、/D# 3 100(11)7.2.3 Apparent Specific Gravity, TThe apparent specificgravity of the test specimen is the quotient of its dry weightdivided by its volume of impervious portions. Since the resultexpresses a type of specific gravity value, it is given that thevalue obtained for T has already been divide

47、d by the assumeddensity of water, thereby rendering the result unitless. Calcu-late T as follows:T 5 D/D 2 S(12)7.2.4 Bulk Density, BThe bulk density of the test speci-men in grams per cubic centimetre is the quotient of its dryweight divided by its exterior volume. Calculate B as follows:B, g/cm35

48、D/ V(13)NOTE 6This test method for determining bulk density is useful forchecking bulk density values obtained by the direct measurement methoddescribed in Test Methods C 134. While this test method is more accuratethan the direct measurement method, the latter is better suited for plantand field te

49、sting since it is a less involved technique. The present testmethod is preferable for specimens that are deeply branded or are irregularin contour.8. Calculation When Liquid Is Mineral Spirits8.1 The calculations when the liquid is mineral spirits arepresented below without commentary or explanation exceptwhere these are essential to understand a particular calculation.However, the commentary, explanations, and Note 6 given inSection 7 for calculations when the liquid is water are fullyapplicable here also.8.1.1 When the term liquid appears in