ASTM C681-2003 Standard Test Method for Volatility of Oil- and Resin-Based Knife-Grade Channel Glazing Compounds《油基及树脂基闸刀级通道上光化合物的挥发性的标准试验方法》.pdf

《ASTM C681-2003 Standard Test Method for Volatility of Oil- and Resin-Based Knife-Grade Channel Glazing Compounds《油基及树脂基闸刀级通道上光化合物的挥发性的标准试验方法》.pdf》由会员分享，可在线阅读，更多相关《ASTM C681-2003 Standard Test Method for Volatility of Oil- and Resin-Based Knife-Grade Channel Glazing Compounds《油基及树脂基闸刀级通道上光化合物的挥发性的标准试验方法》.pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: C 681 03Standard Test Method forVolatility of Oil- and Resin-Based, Knife-Grade, ChannelGlazing Compounds1This standard is issued under the fixed designation C 681; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the y

2、ear of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon (e) indicates an editorial change since the last revision or reapproval.1. Scope1.1 This test method describes the determination of thevolatility of oil- and resin-based, knife-grade, channel gl

3、azingcompounds.1.2 The values stated in inch-pound units are to be regardedas the standard. The values given in parentheses are forinformation only.1.3 The subcommittee with jurisdiction is not aware of anysimilar ISO standard.1.4 This standard does not purport to address all of thesafety concerns,

4、if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:C 717 Terminology of Building Seals and Sealan

5、ts23. Terminology3.1 DefinitionsRefer to Terminology C 717 for definitionsof the following terms: glazing, compound.3.2 Description of TermRefer to Terminology C 717 forthe description of the following term: channel.4. Summary of Test Method4.1 The channel glazing compound is placed into a taredalum

6、inum dish and weighed. The test specimen is then placedinto an oven for a period of 3 h. After cooling, the testspecimen is reweighed and the percent of volatile mattercalculated.5. Significance and Use5.1 This test method provides a guide as to the amount ofvolatile matter that will be emitted from

7、 a channel glazingcompound when tested by this test method.6. Apparatus6.1 Cabinet or Room, capable of maintaining a temperatureof 73.4 6 3.6F (23 6 2C) at 50 6 5 % relative humidity forextended periods of time.6.2 Forced-Draft Oven, capable of maintaining a tempera-ture of 220 6 5F (104 6 3C) for e

8、xtended periods of time.6.3 Dish, aluminum foil, 2.5 in. (64 mm) in diameter by0.75 in. (19 mm) deep, with a flat bottom.6.4 Balance, laboratory analytical type.6.5 Steel Spatula or Putty Knife, with a blade about 4 in.(102 mm) long and 0.75 in. (19 mm) wide.6.6 Desiccator.7. Procedure7.1 Condition

9、a sample of channel glazing compound in atightly closed container 24 h at 73.4 6 3.6F (23 6 2C) priorto testing. Mix the channel glazing compound thoroughly witha spatula to ensure uniformity of the sample to be tested.7.2 Weigh the aluminum foil dish to the nearest 0.01 g andrecord the tare weight.

10、7.3 Transfer approximately 3 to5gofthecompound intothe tared aluminum foil dish, using the spatula, and spread thecompound uniformly over the bottom of the dish.7.4 Weigh the dish containing the compound quickly andaccurately to the nearest 0.01 g. Record the combined weightof the dish and the compo

11、und.7.5 Place the dish containing the compound into an ovencontrolled at 220 6 5F (104 6 3C) for a period of 3 h, coolin desiccator at 73.4 6 3.6F (23 6 2C) for 1 h, weighaccurately to the nearest 0.01 g, and record the weight of thedish plus the sample after heating.8. Calculation8.1 Calculate the

12、percent of volatile matter, V, in the channelglazing compound as follows:V 5A 2 BC3 100 (1)where:A = weight of the dish plus the sample, g,B = weight of the dish plus the sample after heating, g, andC = sample weight, g.1This test method is under the jurisdiction of ASTM Committee C24 on BuildingSea

13、ls and Sealants and is the direct responsibility of Subcommittee C24.20 onGeneral Sealant Standards.Current edition approved May 10, 2003. Published June 2003. Originallyapproved in 1971. Last previous edition approved in 1999 as C 681 99.2Annual Book of ASTM Standards, Vol 04.07.1Copyright ASTM Int

14、ernational, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.9. Report9.1 Report the percent of volatile matter, calculated to thenearest 0.5 %.10. Precision10.1 The multioperator-day precision for the volatility testis 60.5 %.11. Keywords11.1 channel glazing compo

15、und; knife grade; volatilityASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infr

16、ingement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standa

17、rd or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your vie

18、ws known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org).C681032