《ASTM C1695-2010 Standard Specification for Fabrication of Flexible Removable and Reusable Blanket Insulation for Hot Service《热供应用柔性可移动和可再重复使用绝缘卷材的制作标准规范》.pdf》由会员分享，可在线阅读，更多相关《ASTM C1695-2010 Standard Specification for Fabrication of Flexible Removable and Reusable Blanket Insulation for Hot Service《热供应用柔性可移动和可再重复使用绝缘卷材的制作标准规范》.pdf（4页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: C1695 10Standard Specification forFabrication of Flexible Removable and Reusable BlanketInsulation for Hot Service1This standard is issued under the fixed designation C1695; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revisi

2、on, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification covers the minimum requirements formaterials and fabrication of flexible removable

3、and reusableblanket insulation for hot service, from above ambient tem-peratures to 1000F (538C).1.2 This specification separately addresses both outdoor andindoor applications.1.3 The values stated in inch-pound units are to be regardedas standard. The values given in parentheses are mathematicalco

4、nversions to SI units that are provided for information onlyand are not considered standard.1.4 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health pract

5、ices and determine the applica-bility of regulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:2C168 Terminology Relating to Thermal InsulationC553 Specification for Mineral Fiber Blanket Thermal In-sulation for Commercial and Industrial ApplicationsC680 Practice for Estimate

6、 of the Heat Gain or Loss and theSurface Temperatures of Insulated Flat, Cylindrical, andSpherical Systems by Use of Computer ProgramsC892 Specification for High-Temperature Fiber BlanketThermal InsulationC1086 Specification for Glass Fiber Mechanically BondedFelt Thermal InsulationC1129 Practice fo

7、r Estimation of Heat Savings by AddingThermal Insulation to Bare Valves and FlangesC1263 Test Method for Thermal Integrity of Flexible WaterVapor RetardersD3389 Test Method for Coated FabricsAbrasion Resistance(Rotary Platform Abrader)D3776 Test Methods for Mass Per Unit Area (Weight) ofFabricD3786

8、Test Method for Bursting Strength of TextileFabricsDiaphragm Bursting Strength Tester MethodD5034 Test Method for Breaking Strength and Elongationof Textile Fabrics (Grab Test)D5035 Test Method for Breaking Force and Elongation ofTextile Fabrics (Strip Method)D5189 Test Method for Temperature Corres

9、ponding toVapor-Liquid Ratio of 20 for Gasoline and Gasoline-Oxgenate Blends (Bomb Method)3D5587 Test Method for Tearing Strength of Fabrics byTrapezoid ProcedureD6413 Test Method for Flame Resistance of Textiles (Ver-tical Test)2.2 Other Standards:3E PlusRInsulation Thickness Computer Program North

10、American Insulation Manufacturers Association(NAIMA)4MIL-C-20079H Military Specification Cloth, Glass; Tape,Textile Glass and Thread, Glass and Wire ReinforcedGlass53. Terminology3.1 GeneralDefinitions included in Terminology C168shall apply to the terms used in this specification.3.2 Definitions of

11、 Terms Specific to This Standard:3.3 removable and reusable blanket insulation, nAn in-sulation blanket, encased in woven fabric and / or woven wiremesh, that has attachment mechanisms designed to allow theassembly to be installed, then later removed and reinstalled,without using any new insulation

12、or fabric materials.1This specification is under the jurisdiction of ASTM Committee C16 onThermal Insulation and is the direct responsibility of Subcommittee C16.40 onInsulation Systems.Current edition approved May 1, 2010. Published June 2010. Originallyapproved in 2009. Last previous edition appro

13、ved in 2009 as C169509. DOI:10.1520/C1695-10.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.3Withdrawn. The

14、last approved version of this historical standard is referencedon www.astm.org.4Available from North American Insulation Manufacturers Association(NAIMA), 44 Canal Center Plaza, Suite 310 Alexandria, VA 22314, http:/www.naima.org5Available from Standardization Documents Order Desk, DODSSP, Bldg. 4,S

15、ection D, 700 Robbins Ave., Philadelphia, PA 19111-5098, http:/www.dodssp.daps.mil.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.3.4 coated fabric, nA woven fabric coated with a rubberor plastic compound such that the woven fabric

16、material itselfis not exposed to the environment.3.5 hook and loop fastener, na woven molded fabricmaterial that has small hooks on one part and small loops onthe other such that, when pressed together, they adhere to oneanother and further, requiring a significant force to separate onanother.3.6 la

17、cing hook, na metal hook that is located on theoutside surface of an insulation blanket and that is securedthrough the blanket; tie wire is wrapped around it so as tosecure an insulation blanket around a pipe component or pieceof equipment.3.7 lacing anchor, na metal disk, located on the outside ofa

18、n insulation blanket, that is secured to a pin that passesthrough the blanket; the assembly is used to wrap tire wirearound so as to secure an insulation blanket around a pipecomponent or piece of equipment.3.8 D-ring, na section of heavy wire which forms acomplete loop in either a rectangular shape

19、 or the shape of thecapital letter “D”, that is used in removable insulation blanketsfor attaching a fabric strap that secures the blanket around apipe component or piece of equipment.4. Materials4.1 Insulation shall be of a flexible fibrous material accept-able for the maximum temperature of the ap

20、plication. Accept-able materials must be one of the following:High Temperature Fiber Blanket per Specification C892, anyType or GradeNeedled Glass Fiber Mechanically Bonded Felt per Specifica-tion C1086Mineral Fiber Blanket, per Specification C553, of the Typesuitable for the application.4.2 Materia

21、l for the outer jacket liner and straps, whereused, shall be woven glass fiber cloth that has been treated witha water resistant compound, such as silicone or fluorocarbon,that is suitable for both interior and exterior use, and having theproperties as shown in Table 1.4.3 Material for the inner jac

22、ket shall be the same as for theouter jacket for surface temperatures less than 500F(260FC).4.3.1 For surfaces from 501F (261C) to 1000F (538C)where leaks of process fluids are not expected, the inner layerand gussets shall be one of the following:4.3.1.1 a plain, heat cleaned, glass fiber fabric,4.

23、3.1.2 a Type 304 stainless steel wire knitted mesh madefrom 0.008 inch (0.20 mm) diameter wire with nominal 6 to 8openings per in.4.3.2 For surfaces from 501F (261C) to 1000F (538C)where leaks of process fluids are expected, such as flange pairsand valves, the inner layer and gussets shall be as spe

24、cified in4.3.1 and 4.3.1.1 above but also with Type 304 stainless steelfoil that has a minimum thickness of 0.001 in. (0.025 mm).This foil shall be placed between the insulation material andthe outer fabric or wire mesh.4.4 Lacing hooks and lacing anchors shall be made of 12Gauge, Type 304 stainless

25、 steel.4.5 Tie-Down Straps:4.5.1 Outdoor ApplicationsThese tie-down straps shall beconstructed of one of the following three types of material: (1)the same material as the outer jacket, (2) a woven glass fiberfabric, or (3) a tape of suitable thickness with the same coatingas the outer jacket materi

26、al. If the same material as the outerjacket is used, then a double thickness is required with an edgetrim sewn in place along both edges. Edge trim shall be appliedto prevent exposed fabric edges. Ends of the straps shall beturned under14 (6.35mm) to12 (13mm) inch and double-stitched to prevent unra

27、veling.4.5.2 Indoor Applications onlyThese tie-down straps shallbe constructed either of the same materials as for OutdoorApplications, specified in 4.5.1, or of a hook and loop fastenerTABLE 1 Physical and Performance Requirements for FabricsPlain, heat cleanedglass fiber fabricAGlass fiber fabricc

28、oated with Silicone, forexterior applicationsGlass fiber fabriccoated with Silicone,for interior applications onlyFiber fabric coatedwith FluorocarbonWeight (minimum)oz/sq. yd (g/m2)per ASTM D377617.7 (602) 16.5 (561) 13.5 (455) 15 (510)Breaking Strengthlbs/inch (kg/cm) perTest Methods D5034or D5035

29、Warp 200 (35.7)Fill 100 (17.9)Warp 225 (40.19)Fill 175 (31.26)Warp 125 (22.4)Fill 100 (17.9)Warp 225 (40.19)Fill 175 (31.26)Tear Strength lbs (kg)per Test Method D5587SeeAWarp 40 (18.14)Fill 25 (11.33)Warp 30 (13.6)Fill 20 (9.1)Warp 40 (18.14)Fill 25 (11.33)Burst Strength psi (kg/cm2)per Test Method

30、 D3786Not Applicable 200 (14) 150 (9.77) 200 (14)Abrasion Resistanceper Test Method D3389SeeACS-10 Wheel, 500g loads500 revs, 15% weight lossmaxCS-10 Wheel, 500g loads500 revs, 15% weight lossmaxCS-10 Wheel, 500g loads500 revs, 15% weight loss maxColor beige Gray Optional GrayTemperature Resistance

31、F (C)per Test Method C12631000 F (538 C) 500 F (260 C) 500 F (260 C) 600 F (315 C)Flame ResistanceTest Method D6413SeeAChar Length 1 in. max.(25.4cm)Afterglow 3 seconds max.Flame out 1 second max.Char Length 1 in. max.(25.4cm)Afterglow 3 seconds max.Flame out 1 second max.Char Length 1 inch max.(25.

32、4cm)Afterglow 3 seconds max.Flame out 1 second max.AMeets MIL-C-20079H, Type 1, Class 9C1695 102material with a maximum use temperature of 220F (104C).Minimum width of the hook and loop fastener material shall be0.75 in. (19 mm).4.6 Drawstrings shall be made from 100% textured glassfiber sleeving wi

33、th plain weave,38 in. inside diameter and 0.03in. wall thickness. Drawstrings shall be suitable for 1000F(538C) services.4.7 PTFE-coated glass fiber thread shall be used for servicetemperatures to 500F (260C). Glass fiber thread shall be0.021 inch (0.53 mm) diameter, minimum 20 lbs (9 kg).breaking s

34、trength.4.8 Stainless steel thread shall be used for service tempera-tures above 500F (260C). Thread shall be minimum 0.015 in.(0.38 mm) diameter and minimum 18 lbs (8.16 kg). breakingstrength.4.9 All hardware such as D-rings, buckles, tags, etc., shallbe Type 304 stainless steel.5. Design and Fabri

35、cation5.1 Insulated items shall be pre-measured to assure a tightfit. Allowances shall be made for valve bonnet height, glandopenings, protrusions, etc. so as to effectively insulate yetallow future removal and reinstallation. Maximum gap sizeshall be14 in. (6mm).5.2 Fabricate blankets to allow easy

36、 access to valve packingglands and flange bolts without having to completely removethe blanket. All valve blankets shall be designed to permit fullfunction of the valves and not to obscure the valves positionindicator, where applicable.5.3 For applications where leaks are expected, any leakfrom the

37、packing gland or flanges must be channeled out of theblanket to prevent soaking the insulation.5.4 Force-folding or bending of blankets is not allowed.5.5 Blankets shall be fabricated with a minimum 2 in. (50mm) of overlap at the end flap to overlap the adjacentinsulation.5.6 Blankets shall be fabri

38、cated with parting faces at theblanket low point to facilitate drainage, if possible. Otherwise,a drainage grommet shall be installed at the blanket low point.5.7 Any single blanket or blanket piece shall not exceed 45lbs (20.4 kg). Blankets with a finished weight of 45 lbs (20.4kg) or less shall be

39、 fabricated in one piece.6. Construction6.1 Outdoor Applications:6.1.1 All fabric seams shall be either sewn or held togetherwith 16 gauge type 304 stainless steel hog ring staples on 1” to3” (25 to 75 mm) centers. Machine stitching shall be usedwherever practical. Hand stitching shall be used when

40、machinesticking is impractical. Sewing shall be double straight stitchedwith minimum 7 stitches per inch. Each row shall be paralleland spaced a minimum of18 in. (3.2 mm) to a maximum of12in. (12.7 mm) apart.6.1.2 All blanket seams shall be turned in or under and sewnto prevent any raw edges from be

41、ing exposed on any surface.6.1.3 Gusset-type (straight sides) construction shall be uti-lized for all blanket thicknesses greater than 1 in. (25mm).6.1.4 Fabric seams shall be inside seams, except that it ispossible that the final closing seam is an outside seam.6.1.5 Secure insulation within the ja

42、cketing with quiltingpins, lacing hooks, or insulation anchors to prevent insulationfrom settling within the cover. These supports shall penetratethe cold face jacketing and the insulation core, but not the hotface jacketing. Point protectors shall be used to preventpenetration of the hot face jacke

43、ting.6.2 Indoor Applications only:6.2.1 All fabric seams shall be as specified for OutdoorApplications in 6.1.1.6.2.2 Gusset-type (straight sides) construction shall be uti-lized for all blanket thicknesses greater than 2 in. (50 mm).Secure insulation within the jacketing as for the OutdoorApplicati

44、ons or with sewn seams passing through the blanketmaterial on both the hot and cold side.7. Tie-Down/Anchor Strap Construction7.1 Outdoor Applications:7.1.1 The terminal ends of splits in blankets shall utilizeflaps or drawcord/flaps to seal the blankets from wind andwater. Flaps shall have no gaps

45、where they come in contactwith adjacent insulation.7.1.2 Use D-ring type buckles or hook-and-loop tie-down/anchor straps, or both. Lacing hooks and wire shall not be usedunless approved by the Purchaser.7.1.3 If Purchasers approval has been given for the use oflacing hooks and wires, the lacing hook

46、s shall be tufted to thecold face jacketing. If lacing hooks penetrate the hot face, thehooks shall be secured by self-locking washers with a patch ofthe hot face jacketing material sewn over the washer.Asiliconerubber patch shall be placed between the washer and theblanket.7.1.4 Ends of straps shal

47、l be turned under14 in. (6.3 mm) to12 in. (12.7 mm) and double stitched to prevent unraveling.7.1.5 Strap length and number of straps for blankets shall besufficient to ensure a snug and proper fit without gaps orsagging of the blanket.7.1.6 Tie-down strap length shall have a minimum of 6 in.(150 mm

48、) excess length for pulling and securing.TABLE 2 Physical and Performance Requirements for Hook and Loop Fastener (for interior use only)PropertyMinimum material width 0.75 in. (18mm)Minimum Shear Strength, New (per Test Method D5189) 8 psi (55kPa)Minimum Shear Strength, after 2000 cycles (per Test

49、MethodD5189)7 psi (48 kPa)Minimum breaking strength (per Test Method D5035) 150 lbs/ in. width (173 kg/cm)C1695 1037.1.7 Drawcords shall be used where terminal ends ofblankets need to be drawn down around adjacent insulation,valve bonnets, nozzles, etc., to seal the covers from wind andwater7.1.7.1 Blanket shall incorporate flaps at the terminal ends.Drawcord shall be located within this flap.7.1.7.2 Tie-down/anchor straps adjacent to cover terminalends shall be spaced a minimum of 2 in. (50 mm) back fromthe drawcord flaps.7.1.7.